CN106928484A - One kind is high performance to exempt from inflatable bicycle PU tire production foaming agents - Google Patents
One kind is high performance to exempt from inflatable bicycle PU tire production foaming agents Download PDFInfo
- Publication number
- CN106928484A CN106928484A CN201710200148.3A CN201710200148A CN106928484A CN 106928484 A CN106928484 A CN 106928484A CN 201710200148 A CN201710200148 A CN 201710200148A CN 106928484 A CN106928484 A CN 106928484A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- parts
- tire production
- foaming agents
- high performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind it is high performance exempt from inflatable bicycle PU tire production foaming agents, its raw material is as follows by weight:Component A and B component, component A is 70 parts of PPG, 30 parts of high-performance polyalcohol, 12 parts of alcohols chain extender according to composition by weight ratio, 3 parts of amine chain extender, first 0.01 part of catalyst, the second 0.01 part of catalyst, the 3rd 0.01 part of catalyst, 0.05 part of foam stabiliser, 0.1 part of emulsifying agent, 0.4 part of water, B component is 90 parts of MDI according to composition by weight ratio.The a kind of high performance of present invention offer exempts from inflatable bicycle PU tire production foaming agents, cause that foaming agent is optimized in PU tire productions to PU microcellular structures by the addition of the first catalyst, the second catalyst and the 3rd catalyst and foam stabiliser, make microcellular structure more fine and closely woven, it is rich in rebound performance, while also suitably improving tear resistance.
Description
Technical field
Used the present invention relates to PU tyre technologies, more particularly to a kind of high performance inflatable bicycle PU tire productions of exempting from
Foaming agent.
Background technology
Often by the way of the inner tube of a tyre of inflation, PU foaming tires internal structure is the structure of micropore to tire, is assigned good
Damping performance, rebound performance, while having stronger compressive strength, tensile strength and tearing strength;It is extensive abroad
Be applied to the fields such as medical treatment, the elderly's vehicle.PU foaming tires can be realized exempting from inflation using the characteristic of itself so that wheel
Tire is more preferable using characteristic.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of high performance of proposition exempts from inflation
Bicycle PU tire production foaming agents.
To achieve these goals, present invention employs following technical scheme:
One kind is high performance to exempt from inflatable bicycle PU tire production foaming agents, and its raw material is as follows by weight:Component A and B groups
Part, component A is 70 parts of PPG according to composition by weight ratio, and 30 parts of high-performance polyalcohol, 12 parts of alcohols chain extender, amine expands
3 parts of chain agent, the first 0.01 part of catalyst, the second 0.01 part of catalyst, the 3rd 0.01 part of catalyst, 0.05 part of foam stabiliser,
0.1 part of emulsifying agent, 0.4 part of water, B component is 90 parts of MDI according to composition by weight ratio.
Preferably, first catalyst is amines catalyst, and second catalyst is modified amine catalyst, described
3rd catalyst is environment-friendly type organo-metallic catalyst.
Preferably, the foam stabiliser is polyether modified siloxane class A foam A stabilizer.
A kind of high performance application method for exempting from inflatable bicycle PU tire production foaming agents in tire production, including
Following steps:
S1:According to formula design allocation of raw materials, and the storage tank of cast polyurethane equipment will be respectively squeezed into, and adjust operation
Parameter etc. is to be cast;
S2:Mould is fixed on centrifuge, mould is opened and high strength polyester rope is fixed on mould;
S3:Start centrifuge, and set rotary speed, after mould centrifugal speed reaches design requirement, start casting machine
Cast knob, PU materials are injected in mould, treat that the reaction solidification of PU materials is completed;
S4:Finished product is removed from the molds, and removes tool, conduit, pruned flash and be finished product.
Preferably, the high strength polyester rope limits tire with wheel rim by being compounded in the both sides of bicycle PU tires
Coordinate, prevent tire from coming off.
The a kind of high performance of present invention offer exempts from inflatable bicycle PU tire production foaming agents, by the first catalysis
The addition of agent, the second catalyst and the 3rd catalyst and foam stabiliser causes foaming agent in PU tire productions to PU micropores
Structure is optimized, and makes microcellular structure more fine and closely woven, is rich in rebound performance, while also suitably improving tear resistance.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, to this
Invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, not
For limiting the present invention.
Embodiment 1
One kind is high performance to exempt from inflatable bicycle PU tire production foaming agents, and its raw material is as follows by weight:Component A and B groups
Part, component A is 70 parts of PPG according to composition by weight ratio, and 30 parts of high-performance polyalcohol, 12 parts of alcohols chain extender, amine expands
3 parts of chain agent, the first 0.01 part of catalyst, the second 0.01 part of catalyst, the 3rd 0.01 part of catalyst, 0.05 part of foam stabiliser,
0.1 part of emulsifying agent, 0.4 part of water, B component is 90 parts of MDI according to composition by weight ratio.
First catalyst is amines catalyst, and second catalyst is modified amine catalyst, and the described 3rd urges
Agent is environment-friendly type organo-metallic catalyst.The foam stabiliser is polyether modified siloxane class A foam A stabilizer.
A kind of high performance application method for exempting from inflatable bicycle PU tire production foaming agents in tire production, including
Following steps:
S1:According to formula design allocation of raw materials, and the storage tank of cast polyurethane equipment will be respectively squeezed into, and adjust operation
Parameter etc. is to be cast;
S2:Mould is fixed on centrifuge, mould is opened and high strength polyester rope is fixed on mould;
S3:Start centrifuge, and set rotary speed, after mould centrifugal speed reaches design requirement, start casting machine
Cast knob, PU materials are injected in mould, treat that the reaction solidification of PU materials is completed;
S4:Finished product is removed from the molds, and removes tool, conduit, pruned flash and be finished product.
The high strength polyester rope is prevented by the cooperation for being compounded in the both sides of bicycle PU tires to limit tire and wheel rim
Only tire comes off.
The a kind of high performance of present invention offer exempts from inflatable bicycle PU tire production foaming agents, by the first catalysis
The addition of agent, the second catalyst and the 3rd catalyst and foam stabiliser causes foaming agent in PU tire productions to PU micropores
Structure is optimized, and makes microcellular structure more fine and closely woven, is rich in rebound performance, while also suitably improving tear resistance.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept is subject to equivalent or change, should all be included within the scope of the present invention.
Claims (5)
1. one kind is high performance exempts from inflatable bicycle PU tire production foaming agents, it is characterised in that:Its raw material is by weight such as
Under:Component A and B component, component A are 70 parts of PPG, 30 parts of high-performance polyalcohol, alcohols chain extension according to composition by weight ratio
12 parts of agent, 3 parts of amine chain extender, the first 0.01 part of catalyst, the second 0.01 part of catalyst, the 3rd 0.01 part of catalyst, foam
0.05 part of stabilizer, 0.1 part of emulsifying agent, 0.4 part of water, B component is 90 parts of MDI according to composition by weight ratio.
2. one kind according to claim 1 is high performance exempts from inflatable bicycle PU tire production foaming agents, and its feature exists
In:First catalyst is amines catalyst, and second catalyst is modified amine catalyst, and the 3rd catalyst is
Environment-friendly type organo-metallic catalyst.
3. one kind according to claim 1 is high performance exempts from inflatable bicycle PU tire production foaming agents, and its feature exists
In:The foam stabiliser is polyether modified siloxane class A foam A stabilizer.
4. the high performance inflatable bicycle PU tire production foaming agents of exempting from described in a kind of claim 1 are in tire production
Application method, it is characterised in that:Comprise the following steps:
S1:According to formula design allocation of raw materials, and the storage tank of cast polyurethane equipment will be respectively squeezed into, and adjust operation
Parameter etc. is to be cast;
S2:Mould is fixed on centrifuge, mould is opened and high strength polyester rope is fixed on mould;
S3:Start centrifuge, and set rotary speed, after mould centrifugal speed reaches design requirement, start casting machine
Cast knob, PU materials are injected in mould, treat that the reaction solidification of PU materials is completed;
S4:Finished product is removed from the molds, and removes tool, conduit, pruned flash and be finished product.
5. the high performance inflatable bicycle PU tire production foaming agents of exempting from of one kind according to claim 4 are in tire production
In application method, it is characterised in that:The high strength polyester rope limits wheel by being compounded in the both sides of bicycle PU tires
Tire and the cooperation of wheel rim, prevent tire from coming off.