CN106926486A - Fiberglass water pond renovation method - Google Patents
Fiberglass water pond renovation method Download PDFInfo
- Publication number
- CN106926486A CN106926486A CN201710168836.6A CN201710168836A CN106926486A CN 106926486 A CN106926486 A CN 106926486A CN 201710168836 A CN201710168836 A CN 201710168836A CN 106926486 A CN106926486 A CN 106926486A
- Authority
- CN
- China
- Prior art keywords
- water pond
- fiberglass water
- built
- fiberglass
- skid resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Fiberglass water pond renovation method belongs to fiberglass water pond service technique field used for rail vehicle, in order to solve there is a problem of that the renewal of the built-in fittings such as crackle, seepy question, repaired by hand closet, floor drain causes fiberglass water pond to expose decorative cover and damages irregular attractive in appearance with the heterochromatic problem of non-fray, stainless steel closet and fiberglass water pond junction at glass fiber reinforced plastic water mill damage after prior art is overhauled.The present invention is comprised the following steps:Polishing removes the anti-skidding boss of fiberglass water pond, and surfacing is smooth after polishing, and surface slope meets drawing or prototype requirement;Fiberglass water pond built-in pipe, floor drain, closet are overhauled, if damaged, damaged built-in fitting removed and is updated;If not damaged, clear dirty polishing is carried out;The new skid resistant course of manufacture;Bonding plane is treated according to fiberglass water pond, built-in fitting is exposed and closet size is cut to skid resistant course;Brand-new skid resistant course is pasted on the fiberglass water pond that surface polishes flat;Gel coat is sprayed to the fiberglass water pond interior surface after bonding.
Description
Technical field
The invention belongs to fiberglass water pond service technique field used for rail vehicle, and in particular to a kind of fiberglass water pond renovation
Method.
Background technology
Train toilet, chamber wash, drinking water boiler and sanitary equipment room water pond majority use glass steel material, and vehicle is in operation, maintenance
During the corrosion equivalent damage that is produced to it of the abrasion that causes, damaged and wet environment, the destruction to fiberglass water pond is more serious,
Fiberglass water pond leak may be caused, serious situation can make its internal corrosion, cause water pond surface to collapse, this just gives maintenance band
Carry out very big difficulty, sometimes even because corroded area excessive cannot reparation and caused by whole water pond scrap, considerably increase vehicle
The cost of overhaul, and general reparation of the repair method to anti-skidding boss is unable to reach neat appearance, therefore studies more preferable glass
Glass molten steel disk maintenance craft is particularly important.The renovation of fiberglass water pond is that one kind is effectively increased protection against the tide, anticorrosion, wearability,
And make outward appearance and performance close to the repair method of new product state.
The repair method to fiberglass water pond generally comprises following several ways in the prior art:
1) fiberglass water pond exposes decorative cover and uses Manual Repair Methods, and the anti-skidding boss of glass fiber reinforced plastic water panel surface slightly breaks
Damage, defect is made up a deficiency using putty;After being repaired using the method, anti-skidding boss is unable to reach neat appearance effect, and
And fiberglass water pond exposes decoration surface wear and exposes prototype base material during long-time is runed, after prototype substrate color and maintenance
Decorative cover color has differences, and causes heterochromatic problem;
2) with fiberglass junction there is crackle, seepy question in fiberglass water pond stainless steel closet, be carried out using resin glue
Make up a deficiency, seal;The repair method only does encapsulation process to crack surfaces, and crackle is still present, and fiberglass water pond is used for a long time
Surface reconditioning layer is damaged afterwards, and leak, crack problem are not fully solved, and existing crackle, leak repair method cannot ensure a factory
Repair the phase;
3) built-in fitting such as fiberglass water pond closet, floor drain badly broken must update, and update built-in fitting and fiberglass water pond is made
Into breakage, repaired by hand using resin glue, putty;After being repaired using the method, expose decorative cover and be unable to reach neatly
Aesthetic.
The content of the invention
In order to, to fiberglass water pond after reparation, prototype base material is exposed in abrasion in the repair method for solving existing fiberglass water pond
With the heterochromatic problem of repair layer;Thoroughly solve stainless steel closet and there is crackle, seepy question with fiberglass water pond junction;And hand
Work is repaired the renewal of the built-in fittings such as closet, floor drain and causes fiberglass water pond to expose the decorative cover irregular problem attractive in appearance of damage, this hair
It is bright to propose a kind of fiberglass water pond renovation method.
The technical solution adopted for solving the technical problem of the present invention is as follows:
Fiberglass water pond renovation method is comprised the following steps:
Step one:Glass fiber reinforced plastic water panel surface is polished, remove anti-skidding boss and come unglued, aliquation, damaged top layer, beat
Surfacing is smooth after mill, and gradient meets drawing or prototype requirement;
Step 2:Fiberglass water pond built-in pipe, floor drain, closet are overhauled, if damaged, step 3 is performed by breakage
Built-in fitting is removed and updated;If not damaged, clear dirty polishing is carried out to built-in fitting, and perform step 4;
Step 3:Built-in fitting is removed and updated, is concretely comprised the following steps:
A) after removing fiberglass water pond built-in pipe, floor drain, closet, using makita 4100NH on fiberglass water pond according to figure
Paper or prototype closet location dimension cutting closet mounting groove;
B) protective treatment is carried out to built-in fitting exposed surface;
C) mixture of full resin glue and talcum powder, squatting pan hole centralized positioning size are filled in squatting pan installation region
Meet drawing or prototype size, and squatting pan is tentatively fixed;
D) according to drawing or prototype built-in pipe, small opening centralized positioning size determine that new built-in fitting loads fiberglass water pond position
Put, and it is fixed using resin glue;
E) space between built-in fitting and fiberglass water pond is filled with the mixture of resin glue and talcum powder, it is thoroughly fixed pre-
Embedded part, dries 24h;
F) built-in fitting such as fiberglass water pond and built-in pipe, floor drain, closet is Nian Jie firmly, sealing is tight;
Step 4:The new skid resistant course of manufacture;
Step 5:According to glass fiber reinforced plastic water dribbling bonding plane, built-in fitting and closet size are exposed to acquisition in step 4
Skid resistant course is cut, and closestool port size is than the small 4~6mm of the every side length of side of closet on new skid resistant course;
Step 6:The new skid resistant course obtained after being cut in step 5 pastes the glass fiber reinforced plastic water treated through step one
On disk;
Step 7:Fiberglass water pond inside exposed face spraying gel coat after to being bonded in step 6, concretely comprises the following steps:
A) decorative cover breakage is exposed to fiberglass water pond or scuffing part putty repairing is smooth;
B) the built-in fitting junctions such as fiberglass water pond and built-in pipe, squatting pan are made up a deficiency with putty, makes up a deficiency place round and smooth
Transition;
C) according to host and curing agent ratio requirement allotment gel coat, and add diluent to stir, it is quiet put 5min~
10min eliminates bubble;
D) gel coat obtained in step c) is sprayed on the exposed face of fiberglass water pond inside, and is dried;
E) dried gel coat surface defect in step d) is repaired, then carries out secondary spraying gel coat, it is ensured that surface
Uniform ground, without stream pendant, cut.
Exposed inside fiberglass water pond after to being bonded in step 6 during spraying gel coat two in step d) and step e)
Secondary spraying gel coat gross thickness is not less than 0.3mm.
Surface stress is no less than 600N in preliminary fixation procedure for squatting pan described in step 3, and bonding plane laminating is tight
It is close, surface uniform force, and use level chi measurement closet surface levelness, it is ensured that closet surface level.
Concretely comprising the following steps for new skid resistant course is manufactured described in step 4:
A) in the uniform brushing releasing agent of skid resistant course die surface;
B) gel coat is obtained according to host and the allotment of curing agent ratio requirement, and is stirred;
C) uniform brushing gel coat on the skid resistant course die surface after step a) treatment, gel coat thickness is not less than 0.9mm, does
Dry 2h;
D) mated formation on gel coat using glass wool cloth, glass wool cloth is impregnated with resin glue, dry and obtain new skid resistant course.Step 6
Described in will in step 5 cut after obtain new skid resistant course paste through step one treat fiberglass water pond on have
Body step is:
A) judge whether releasing agent influences gel coat to spray, if so, must then remove totally, step b) is performed if not;
That b) removes fiberglass water pond and new skid resistant course treats bonding plane surface dirt;
C) mixture of bonding plane brushing resin glue and talcum powder is treated in fiberglass water pond;
D) skid resistant course that will be obtained in step 5 is put on fiberglass water pond, and position aligns, to skid resistant course in glass fiber reinforced plastic water
Tentatively fixed on disk, every square metre of stress is not less than 2000N in fixation procedure, it is desirable to surface uniform force, bonding plane patch
Close tight.
Step 4 must not exceed 6h to step 6 brand-new and bonding skid resistant course engineering time.
Step one can also be replaced using following method, specially:Cut downwards along prototype fiberglass water pond stile border
Go out groove, surface anti-skidding layer entirety is excavated.
Step 7 can also be replaced using following method, specially:After the completion of brand-new skid resistant course bonding, existed using putty
Brand-new skid resistant course and fiberglass water pond handing-over gap are made up a deficiency, and make up a deficiency that transition is round and smooth, and putty is made up a deficiency after drying using gel coat.
Beneficial effects of the present invention are:Glass fiber reinforced plastic water renovation method of the invention is all anti-for removal glass fiber reinforced plastic water panel surface
Sliding boss, gel coat is sprayed after being bonded brand-new skid resistant course again, therefore brand-new skid resistant course integral color is identical, will not be produced after abrasion
Heterochromatic problem;Brand-new skid resistant course uses Mold Making, and surface anti-skidding boss marshalling is attractive in appearance, can make the glass fiber reinforced plastic water after renovation
Disk outward appearance is close to new product state.Again skid resistant course covering glass molten steel panel surface crackle, the leakage area being bonded, to reach reparation
Crackle, places seepy question;The damaged renovation fiberglass water pond that renewal built-in fitting is caused perfect can be repaired.General maintenance craft without
Method overhauls the fiberglass water pond of badly broken, if being renovated, single fiberglass water pond averagely saves 1000 yuan of the cost of overhaul, turns over
New glass molten steel disk faster 10 days than update cycle.
Brief description of the drawings
Fig. 1 is fiberglass water pond renovation method flow chart of the present invention.
Specific embodiment
The present invention is described in further details below in conjunction with the accompanying drawings.
Fiberglass water pond renovation method is comprised the following steps:
Step one:Glass fiber reinforced plastic water panel surface is polished, remove anti-skidding boss and come unglued, aliquation, damaged top layer, beat
Surfacing is smooth after mill, and gradient meets drawing or prototype requirement;Fiberglass water pond gradient can ensure water pond not water, only
Meet prototype or drawing gradient, full water not water;
Step 2:Fiberglass water pond built-in pipe, floor drain, closet are overhauled, if damaged, step 3 is performed by breakage
Built-in fitting is removed and updated;If not damaged, clear dirty polishing is carried out to built-in fitting, and perform step 4;
Step 3:Built-in fitting is removed and updated, is concretely comprised the following steps:
A) after removing fiberglass water pond built-in pipe, floor drain, closet, using makita 4100NH on fiberglass water pond according to figure
Paper or prototype closet location dimension cutting closet mounting groove;
B) protective treatment is carried out to built-in fitting exposed surface;
C) mixture of full resin glue and talcum powder, squatting pan hole centralized positioning size are filled in squatting pan installation region
Meet drawing or prototype size, and squatting pan is tentatively fixed;
D) according to drawing or prototype built-in pipe, small opening centralized positioning size determine that new built-in fitting loads fiberglass water pond position
Put, and it is fixed using resin glue;
E) space between built-in fitting and fiberglass water pond is filled with the mixture of resin glue and talcum powder, it is thoroughly fixed pre-
Embedded part, dries 24h;
F) built-in fitting such as fiberglass water pond and built-in pipe, floor drain, closet is Nian Jie firmly, sealing is tight.
Step 4:The new skid resistant course of manufacture;
Step 5:According to glass fiber reinforced plastic water dribbling bonding plane, built-in fitting and closet size are exposed to acquisition in step 4
Skid resistant course is cut, and closestool port size is than the small 4~6mm of the every side length of side of closet on new skid resistant course;
Step 6:The new skid resistant course obtained after being cut in step 5 pastes the glass fiber reinforced plastic water treated through step one
On disk;
Step 7:Fiberglass water pond inside exposed face spraying gel coat after to being bonded in step 6, concretely comprises the following steps:
A) decorative cover breakage is exposed to fiberglass water pond or scuffing part putty repairing is smooth;
B) the built-in fitting junctions such as fiberglass water pond and built-in pipe, squatting pan are made up a deficiency with putty, makes up a deficiency place round and smooth
Transition;
C) according to host and curing agent ratio requirement allotment gel coat, and add diluent to stir, it is quiet put 5min~
10min eliminates bubble;
D) gel coat obtained in step c) is sprayed on the exposed face of fiberglass water pond inside, and is dried;
E) dried gel coat surface defect in step d) is repaired, then carries out secondary spraying gel coat, it is ensured that surface
Uniform ground, without stream pendant, cut.
Exposed inside fiberglass water pond after to being bonded in step 6 during spraying gel coat two in step d) and step e)
Secondary spraying gel coat gross thickness is not less than 0.3mm.
Surface stress is no less than 600N in preliminary fixation procedure for squatting pan described in step 3, and bonding plane laminating is tight
It is close, surface uniform force, and use level chi measurement closet surface levelness, it is ensured that closet surface level.
Concretely comprising the following steps for new skid resistant course is manufactured described in step 4:
A) in the uniform brushing releasing agent of skid resistant course die surface;
B) gel coat is obtained according to host and the allotment of curing agent ratio requirement, and is stirred;
C) uniform brushing gel coat on the skid resistant course die surface after step a) treatment, gel coat thickness is not less than 0.9mm, does
Dry 2h;
D) mated formation on gel coat using glass wool cloth, glass wool cloth is impregnated with resin glue, dry and obtain new skid resistant course.
The new skid resistant course that will be obtained after cutting in step 5 described in step 6 pastes the glass processed through step one
Concretely comprised the following steps on glass molten steel disk:
A) judge whether releasing agent influences gel coat to spray, if so, must then remove totally, step b) is performed if not;
That b) removes fiberglass water pond and new skid resistant course treats bonding plane surface dirt;
C) mixture of bonding plane brushing resin glue and talcum powder is treated in fiberglass water pond;
D) skid resistant course that will be obtained in step 5 is put on fiberglass water pond, and position aligns, to skid resistant course in glass fiber reinforced plastic water
Tentatively fixed on disk, every square metre of stress is not less than 2000N in fixation procedure, it is desirable to surface uniform force, bonding plane patch
Close tight.
Step 4 must not exceed 6h to step 6 brand-new and bonding skid resistant course engineering time.
Step one can also be replaced using following method, specially:Cut downwards along prototype fiberglass water pond stile border
Go out groove, surface anti-skidding layer entirety is excavated.
Step 7 can also be replaced using following method, specially:The gel coat one-shot forming of brand-new skid resistant course surface, is not required to spray
Gel coat is applied, after the completion of brand-new skid resistant course bonding, is joined gap in brand-new skid resistant course and fiberglass water pond using putty and is looked for
Mend, it is round and smooth to make up a deficiency transition, putty is made up a deficiency after drying using gel coat.
Structure is followed successively by fiberglass water pond after renovation from top to bottom:Thickness is not less than the gel coating resin of 1.2mm;Thickness is not low
In the imitative reason stone layer of 1mm, specific composition is resin, glass fibre etc.;Gel coating resin and imitative reason stone layer solid colour, surface is set up defences cunning
Boss;Adhesive layer, specific composition is resin;Glass fiber reinforced plastic water panel surface light such as new, anti-skidding boss marshalling after renovation.
Claims (8)
1. fiberglass water pond renovation method, it is characterised in that comprise the following steps:
Step one:Glass fiber reinforced plastic water panel surface is polished, remove anti-skidding boss and come unglued, aliquation, damaged top layer, after polishing
Surfacing is smooth, and gradient meets drawing or prototype requirement;
Step 2:Fiberglass water pond built-in pipe, floor drain, closet are overhauled, if damaged, step 3 is performed breakage is pre-buried
Part is removed and updated;If not damaged, clear dirty polishing is carried out to built-in fitting, and perform step 4;
Step 3:Built-in fitting is removed and updated, is concretely comprised the following steps:
A) after removing fiberglass water pond built-in pipe, floor drain, closet, using makita 4100NH on fiberglass water pond according to drawing or
Prototype closet location dimension cuts closet mounting groove;
B) protective treatment is carried out to built-in fitting exposed surface;
C) mixture of full resin glue and talcum powder is filled in squatting pan installation region, centralized positioning size in squatting pan hole meets
Drawing or prototype size, and squatting pan is tentatively fixed;
D) according to drawing or prototype built-in pipe, small opening centralized positioning size determine that new built-in fitting loads fiberglass water pond position,
And it is fixed using resin glue;
E) space between built-in fitting and fiberglass water pond is filled with the mixture of resin glue and talcum powder, thoroughly fixes pre-buried
Part, dries 24h;
F) built-in fitting such as fiberglass water pond and built-in pipe, floor drain, closet is Nian Jie firmly, sealing is tight;
Step 4:The new skid resistant course of manufacture;
Step 5:According to glass fiber reinforced plastic water dribbling bonding plane, expose built-in fitting and closet size in step 4 obtain it is anti-skidding
Layer is cut, and closestool port size is than the small 4~6mm of the every side length of side of closet on new skid resistant course;
Step 6:The new skid resistant course obtained after being cut in step 5 pastes the fiberglass water pond treated through step one
On;
Step 7:Fiberglass water pond inside exposed face spraying gel coat after to being bonded in step 6, concretely comprises the following steps:
A) decorative cover breakage is exposed to fiberglass water pond or scuffing part putty repairing is smooth;
B) the built-in fitting junctions such as fiberglass water pond and built-in pipe, squatting pan are made up a deficiency with putty, makes up a deficiency place's rounding off;
C) according to host and curing agent ratio requirement allotment gel coat, and diluent is added to stir, quiet 5min~10min of putting disappears
Bubble removing;
D) gel coat obtained in step c) is sprayed on the exposed face of fiberglass water pond inside, and is dried;
E) dried gel coat surface defect in step d) is repaired, then carries out secondary spraying gel coat, it is ensured that surface is uniform
It is smooth, without stream pendant, cut.
2. fiberglass water pond renovation method according to claim 1, it is characterised in that the glass after to being bonded in step 6
Exposed inside molten steel disk and spray gel coat gross thickness twice in step d) and step e) during spraying gel coat and be not less than 0.3mm.
3. fiberglass water pond renovation method according to claim 1 and 2, it is characterised in that the crouching described in step 3 is just
Device surface stress in preliminary fixation procedure is no less than 600N, and bonding plane laminating is tight, surface uniform force, and use level chi
Measurement closet surface levelness, it is ensured that closet surface level.
4. fiberglass water pond renovation method according to claim 1, it is characterised in that the manufacture described in step 4 is new
Skid resistant course is concretely comprised the following steps:
A) in the uniform brushing releasing agent of skid resistant course die surface;
B) gel coat is obtained according to host and the allotment of curing agent ratio requirement, and is stirred;
C) uniform brushing gel coat on the skid resistant course die surface after step a) treatment, gel coat thickness is not less than 0.9mm, dries
2h;
D) mated formation on gel coat using glass wool cloth, glass wool cloth is impregnated with resin glue, dry and obtain new skid resistant course.
5. fiberglass water pond renovation method according to claim 1, it is characterised in that described in step 6 by step 5
The new skid resistant course obtained after middle cutting is pasted and concretely comprised the following steps on the fiberglass water pond treated through step one:
A) judge whether releasing agent influences gel coat to spray, if so, must then remove totally, step b) is performed if not;
That b) removes fiberglass water pond and new skid resistant course treats bonding plane surface dirt;
C) mixture of bonding plane brushing resin glue and talcum powder is treated in fiberglass water pond;
D) skid resistant course that will be obtained in step 5 is put on fiberglass water pond, and position aligns, to skid resistant course on fiberglass water pond
Tentatively fixed, every square metre of stress is not less than 2000N in fixation procedure, it is desirable to surface uniform force, bonding plane laminating is tight
It is close.
6. fiberglass water pond renovation method according to claim 1, it is characterised in that step 4 to step 6 brand-new and viscous
Taking over control the slip layer engineering time must not exceed 6h.
7. fiberglass water pond renovation method according to claim 1, it is characterised in that step one can also use following side
Method is replaced, specially:Groove is cut out downwards along prototype fiberglass water pond stile border, and surface anti-skidding layer entirety is excavated.
8. fiberglass water pond renovation method according to claim 1, it is characterised in that step 7 can also use following side
Method is replaced, specially:After the completion of brand-new skid resistant course bonding, gap is joined in brand-new skid resistant course and fiberglass water pond using putty
Made up a deficiency, it is round and smooth to make up a deficiency transition, putty is made up a deficiency after drying using gel coat.