CN106916646A - A kind of high ferro special-purpose nanometer plates cleaning agents of membrane and application method - Google Patents

A kind of high ferro special-purpose nanometer plates cleaning agents of membrane and application method Download PDF

Info

Publication number
CN106916646A
CN106916646A CN201710152069.XA CN201710152069A CN106916646A CN 106916646 A CN106916646 A CN 106916646A CN 201710152069 A CN201710152069 A CN 201710152069A CN 106916646 A CN106916646 A CN 106916646A
Authority
CN
China
Prior art keywords
weight portion
weight portions
weight
membrane
high ferro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710152069.XA
Other languages
Chinese (zh)
Inventor
卢明强
卢艺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710152069.XA priority Critical patent/CN106916646A/en
Publication of CN106916646A publication Critical patent/CN106916646A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of high ferro special-purpose nanometer plating cleaning agents of membrane and application method, including following constituent：Double amodimethicone crude oil, emulsifying agent, glycine betaine, polyether-modified trisiloxanes, glacial acetic acid, preservative, spices, deionized water；Described each constituent compares mixed preparing using following weight：Double weight portions of amodimethicone crude oil 10 30, the weight portion of emulsifying agent 5 15, the weight portion of glycine betaine 20 45, the weight portion of polyether-modified trisiloxanes 28, the weight portion of glacial acetic acid 0.2 0.5, the weight portion of preservative 0.2 0.5, the weight portion of spices 0.1, the weight portion of deionized water 10 50.Detergency ability of the present invention is strong, and high-effective penetrating does not hinder lacquer painting, with extremely strong hydrophobicity; moisture can be quickly dispersed, while reaching the effect of glazing, high molecular nanometer diaphragm can be formed in compartment outer surface, it is non-ignitable not quick-fried; not phosphate-containing, nontoxic pollution-free, waste liquid can degrade.

Description

A kind of high ferro special-purpose nanometer plates cleaning agents of membrane and application method
Technical field
It is clear the present invention relates to high ferro railway car surface cleaning technical field, more particularly to a kind of high ferro special-purpose nanometer plated film Lotion.
Background technology
With continuing to develop for economic society, track traffic has turned into the main means of transport of today's society (such as：High ferro, Motor train unit train, subway, light rail, magnetic suspension train etc.), wherein high ferro, motor train unit train in the process of running because speed is fast, Environment changing factor is more in long distance running, and the outer surface of car body is highly prone to pollution, dust such as in air, by electric arc and wheel Rust water, insect and its excreta that the carbon dust and iron filings, metal bridge or brandreth that rail friction is produced fall add car body surface for a long time The influence of the factors such as the oxidation caused with air contact, causes various dirts to be combined together to form mixed dirt, car body surface Pollution is usually expressed as overall flavescence, and local macula lutea and strip current mark etc. have had a strong impact on the good appearance of train, to vehicle Later maintenance brings very big workload, increased vehicle maintenance operation cost.
The content of the invention
The present invention be in order to solve the problems, such as high ferro railway car outer surface cleaning and maintenance, there is provided one kind can delay car body Turn to be yellow spot on surface, strong detergency, good penetrability, scavenging period short and fast high ferro special-purpose nanometer plating cleaning agents of membrane and user Method.
To achieve these goals, the present invention uses following technical scheme：A kind of high ferro special-purpose nanometer plates cleaning agents of membrane, bag Include following constituent：Double amodimethicone crude oil, emulsifying agent, glycine betaine, polyether-modified trisiloxanes, glacial acetic acid, preservative, perfume (or spice) Material, deionized water；Described each constituent compares mixed preparing using following weight：Double amodimethicone crude oil 10-30 weight Part, emulsifying agent 5-15 weight portions, glycine betaine 20-45 weight portions, polyether-modified trisiloxanes 2-8 weight portions, glacial acetic acid 0.2-0.5 Weight portion, preservative 0.2-0.5 weight portions, the weight portion of spices 0.1, deionized water 10-50 weight portions.
Preferably, described each constituent carries out mixed preparing, step 1 using following steps) by deionized water 10- 50 weight portions are poured into stirred tank, add emulsifying agent 5-15 weight portions, are evenly stirred until foaming；Step 2) add double amodimethicones Crude oil 10-30 weight portions, stir half an hour；Step 3) glacial acetic acid 0.2-0.5 weight portions are added, add glycine betaine 20-45 weights Amount part, adds polyether-modified trisiloxanes 2-8 weight portions, adds preservative 0.2-0.5 weight portions, the weight portion of spices 0.1, then stir Stop after mixing half an hour；Step 4) by step 3) finished product cleaning agent and filling is obtained after gained liquid filtering.
The neutral environment-friendly cleaning agent of this programme product category, using unique efficient barrier formulations, does not hinder lacquer painting, is a with strong Effect decontamination, it is small to car paint and metal protection, without harmful ion, the product that waste liquid can degrade；In this programme product component Double amodimethicone crude oil contain amino, hydroxyl reactive group, and have self-crosslinking energy, produce nano-coating to protect by emulsifying Cuticula, therefore also there is extremely strong hydrophobicity, moisture can be quickly dispersed, while the effect of glazing is reached, in cleaning vehicle body table The high molecular nanometer diaphragm for being attached to bodywork surface can be produced while face, suction of the dirt in bodywork surface can be effectively intercepted Attached formation, so as to reach the double effects of cleaning and nursing, and can delay the time of car body surface jaundice spot.
Preferably, described emulsifying agent is NP-1047.
High ferro special-purpose nanometer plates the application method of cleaning agents of membrane, high ferro special-purpose nanometer plating cleaning agents of membrane with clear water according to 1 Ratio than 20~30 is diluted and obtains dilution, and described dilution pH value is 6.5-7.5, and high ferro is cleaned using dilution During compartment outer surface, dilution spray after fully wetting is permeated 1-3 minutes, is used into banister brush in high-iron carriage outer surface first High-iron carriage outer surface is cleaned comprehensively, then high-iron carriage surface is cleaned with clear water or reuse recirculated water, it is last high Iron compartment outer surface natural air drying is dried up using blower fan.This programme product can be used at normal temperatures, and dilution ratio is big, can have Effect reduces cost；This programme product is harmless, is also suitable for mechanical automation cleaning, can substantially reduce labour cost, has Have non-ignitable not quick-fried, not phosphate-containing, nontoxic pollution-free, the features such as waste liquid can degrade.
This programme product, in the cleaning nursing of automobile and aircraft outer surface, equally can effectively be used, and be obtained Same effect.
Therefore, the present invention has the advantages that：(1) detergency ability is strong；(2) high-effective penetrating, does not hinder lacquer painting；(3) have There is extremely strong hydrophobicity, can quickly disperse moisture, while reaching the effect of glazing, macromolecule can be formed in compartment outer surface and received Rice diaphragm, effectively intercepts absorption of the dirt in compartment outer surface and is formed；(4) non-ignitable not quick-fried, phosphate-containing, not nontoxic without dirt Dye, waste liquid can degrade.
Specific embodiment
A kind of embodiment one, high ferro special-purpose nanometer plates cleaning agents of membrane, including following constituent：Double amodimethicone crude oil, Emulsifying agent, glycine betaine, polyether-modified trisiloxanes, glacial acetic acid, preservative, spices, deionized water；Each constituent is using following Weight compare mixed preparing：Double weight portions of amodimethicone crude oil 10, the weight portion of emulsifying agent (NP-1047) 5, the weight of glycine betaine 30 Part, the weight portion of polyether-modified trisiloxanes (bleeding agent) 5, the weight portion of glacial acetic acid 0.4, the weight portion of preservative 0.5, the weight of spices 0.1 Amount part, the weight portion of deionized water 49；
Each constituent carries out mixed preparing, step 1 using following steps) weight portion of deionized water 49 is poured into stirred tank In, emulsifying agent (NP-1047) 5 weight portion is added, it is evenly stirred until foaming；Step 2) add double weight of amodimethicone crude oil 10 Part, stir half an hour；Step 3) weight portion of glacial acetic acid 0.4 is added, the weight portion of glycine betaine 30 is added, add polyether-modified three silicon The weight portion of oxygen alkane (bleeding agent) 5, adds the weight portion of preservative 0.5, the weight portion of spices 0.1, stops after being stirred for half an hour；Step 4) by step 3) finished product cleaning agent and filling is obtained after gained liquid filtering；
High ferro special-purpose nanometer plates the application method of cleaning agents of membrane, high ferro special-purpose nanometer plating cleaning agents of membrane with clear water according to 1 Ratio than 20 is diluted and obtains dilution, and dilution pH value is 6.5-7.5, using dilution cleaning high-iron carriage outer surface When, first by dilution spray in high-iron carriage outer surface, after fully wetting is permeated 1-3 minutes, with banister brush to high-iron carriage Outer surface is cleaned comprehensively, and high-iron carriage surface, last high-iron carriage appearance are then cleaned with clear water or reuse recirculated water Face natural air drying is dried up using blower fan.
A kind of embodiment two, high ferro special-purpose nanometer plates cleaning agents of membrane, including following constituent：Double amodimethicone crude oil, Emulsifying agent, glycine betaine, polyether-modified trisiloxanes, glacial acetic acid, preservative, spices, deionized water；Each constituent is using following Weight compare mixed preparing：Double weight portions of amodimethicone crude oil 20, the weight portion of emulsifying agent (NP-1047) 10, the weight of glycine betaine 35 Part, the weight portion of polyether-modified trisiloxanes (bleeding agent) 6, the weight portion of glacial acetic acid 0.4, the weight portion of preservative 0.5, the weight of spices 0.1 Amount part, the weight portion of deionized water 28；
Each constituent carries out mixed preparing, step 1 using following steps) weight portion of deionized water 28 is poured into stirred tank In, emulsifying agent (NP-1047) 10 weight portion is added, it is evenly stirred until foaming；Step 2) add double weight of amodimethicone crude oil 20 Part, stir half an hour；Step 3) weight portion of glacial acetic acid 0.4 is added, the weight portion of glycine betaine 35 is added, add polyether-modified three silicon The weight portion of oxygen alkane (bleeding agent) 6, adds the weight portion of preservative 0.5, the weight portion of spices 0.1, stops after being stirred for half an hour；Step 4) by step 3) finished product cleaning agent and filling is obtained after gained liquid filtering；
High ferro special-purpose nanometer plates the application method of cleaning agents of membrane, high ferro special-purpose nanometer plating cleaning agents of membrane with clear water according to 1 Ratio than 30 is diluted and obtains dilution, and dilution pH value is 6.5-7.5, using dilution cleaning high-iron carriage outer surface When, first by dilution spray in high-iron carriage outer surface, after fully wetting is permeated 1-3 minutes, with banister brush to high-iron carriage Outer surface is cleaned comprehensively, and high-iron carriage surface, last high-iron carriage appearance are then cleaned with clear water or reuse recirculated water Face natural air drying is dried up using blower fan.

Claims (4)

1. a kind of high ferro special-purpose nanometer plates cleaning agents of membrane, it is characterised in that including following constituent：Double amodimethicone crude oil, Emulsifying agent, glycine betaine, polyether-modified trisiloxanes, glacial acetic acid, preservative, spices, deionized water；Described each constituent is adopted Compare mixed preparing with following weight：Double amodimethicone crude oil 10-30 weight portions, emulsifying agent 5-15 weight portions, glycine betaine 20-45 Weight portion, polyether-modified trisiloxanes 2-8 weight portions, glacial acetic acid 0.2-0.5 weight portions, preservative 0.2-0.5 weight portions, spices 0.1 weight portion, deionized water 10-50 weight portions.
2. a kind of high ferro special-purpose nanometer according to claim 1 plates cleaning agents of membrane, it is characterized in that, described each constituent Mixed preparing, step 1 are carried out using following steps) deionized water 10-50 weight portions are poured into stirred tank, add emulsifying agent 5- 15 weight portions, are evenly stirred until foaming；Step 2) double amodimethicone crude oil 10-30 weight portions are added, stir half an hour；Step 3) Glacial acetic acid 0.2-0.5 weight portions are added, glycine betaine 20-45 weight portions are added, polyether-modified trisiloxanes 2-8 weight is added Part, preservative 0.2-0.5 weight portions, the weight portion of spices 0.1 are added, stop after being stirred for half an hour；Step 4) by step 3) institute Obtain finished product cleaning agent and filling after liquid filtering.
3. a kind of high ferro special-purpose nanometer according to claim 1 and 2 plates cleaning agents of membrane, it is characterized in that, described emulsifying agent It is NP-1047.
4. the application method of cleaning agents of membrane is plated according to the gained high ferro special-purpose nanometer of claim 1 or 2, it is characterized in that, high ferro is special It is diluted according to 1 to 20~30 ratio with nano-coating cleaning agent and clear water and obtains dilution, described dilution pH value It is 6.5-7.5, when cleaning high-iron carriage outer surface using dilution, dilution spray is filled in high-iron carriage outer surface first Share in the benefit after wet infiltration 1-3 minutes, high-iron carriage outer surface is cleaned comprehensively with banister brush, then followed with clear water or reuse Ring water cleaning high-iron carriage surface, last high-iron carriage outer surface natural air drying or use blower fan drying.
CN201710152069.XA 2017-03-15 2017-03-15 A kind of high ferro special-purpose nanometer plates cleaning agents of membrane and application method Pending CN106916646A (en)