CN106916479A - A kind of radiation proof putty - Google Patents
A kind of radiation proof putty Download PDFInfo
- Publication number
- CN106916479A CN106916479A CN201510978651.2A CN201510978651A CN106916479A CN 106916479 A CN106916479 A CN 106916479A CN 201510978651 A CN201510978651 A CN 201510978651A CN 106916479 A CN106916479 A CN 106916479A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation proof
- agent
- proof putty
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to decoration material field, specifically a kind of radiation proof putty.It is by following white cement 100-120 parts, barium sulfate 40-50 parts, sierozem power 20-30 parts, cobalt acetate 0.8-1.5 parts, polyvinyl alcohol 30-40 parts, diethylene glycol (DEG) 10-15 parts, white glue with vinyl 25-45 parts, polyurethane 15-20 parts, modified carboxymethylcellulose calcium 15-20 parts of Allyl thiourea, anti-settling agent 1-3 parts, palm oil is 15-25 parts, defoamer 0.5-0.8 parts, dispersant 0.5-0.8 parts, wetting agent 1-3 parts, initiator 3-5 parts, thixotropic agent 3-5 parts, fumaric acid 10-15 parts, hydroquinones 5-10 parts.The radiation proof putty that the present invention is provided, simple production process, low production cost, adhesive force are good, and shielding is stronger, and high hard, anticracking is water-fastness, will never fade.
Description
Technical field
The present invention relates to decoration material field, specifically a kind of radiation proof putty.
Background technology
Putty is a kind of decoration type material of smooth surface of wall, is a kind of thick slurry coating material, and being must not before coating is painted
A kind of product that can lack.Painting is imposed on priming paint or directly applied and imposes on object, is used to remove rugged on coated article surface
Defect.Be formulated using a small amount of paint base, auxiliary agent, mass filler and appropriate coloring pigment, pigment used be mainly iron oxide red,
Carbon black, chrome yellow etc..Filler is mainly calcium bicarbonate, talcum powder etc..Part can be filled up the working surface of depression, also can be in whole
Surface is struck off, and typically after prime coat is parched, is applied over primer coat surface.It is required that tack is good, do not produce in baking process
Crackle, present people's life be unable to do without various electronic products, so, a kind of putty for being capable of radiation proof is needed for life.
The content of the invention
In order to solve the above problems, the invention provides a kind of radiation proof putty.
Technical scheme is as follows：
A kind of radiation proof putty, is by following white cement 100-120 parts, barium sulfate 40-50 parts, sierozem power 20-30 parts, cobalt acetate
0.8-1.5 parts, polyvinyl alcohol 30-40 parts, diethylene glycol (DEG) 10-15 parts, white glue with vinyl 25-45 parts, polyurethane 15-20 parts, acrylic sulphur
Urea modified carboxymethylcellulose calcium 15-20 part, anti-settling agent 1-3 part, palm oil be 15-25 parts, defoamer 0.5-0.8 parts, disperse
Agent 0.5-0.8 parts, wetting agent 1-3 parts, initiator 3-5 parts, thixotropic agent 3-5 parts, fumaric acid 10-15 parts, hydroquinones 5-
10 parts.
Further, above-mentioned radiation proof putty, anti-settling agent is the polybasic carboxylic acid salt of polynary amine amide, is modified in urea solution
One kind or and several.
Beneficial effects of the present invention：
Compared with prior art, the radiation proof putty that the present invention is provided, simple production process, low production cost, adhesive force are good, screen
Covering property is stronger, and high hard, anticracking is water-fastness, will never fade.
Specific embodiment
Embodiment 1
A kind of radiation proof putty, is by 100 parts of following white cement, 40 parts of barium sulfate, 20 parts of sierozem power, 0.8 part of cobalt acetate, poly-
15 parts modified of carboxymethylcellulose calcium of 30 parts of vinyl alcohol, 10 parts of diethylene glycol (DEG), 25 parts of white glue with vinyl, 15 parts of polyurethane, Allyl thiourea,
1 part of anti-settling agent, palm oil be 15 parts, 0.5 part of defoamer, 0.5 part of dispersant, 1 part of wetting agent, 3 parts of initiator, 3 parts of thixotropic agent,
10 parts of fumaric acid, 5 parts of hydroquinones.
Further, above-mentioned radiation proof putty, anti-settling agent is the polybasic carboxylic acid salt of polynary amine amide, is modified in urea solution
One kind or and several.
Embodiment 2
A kind of radiation proof putty, is by 120 parts of following white cement, 50 parts of barium sulfate, 30 parts of sierozem power, 1.5 parts of cobalt acetate, poly- second
It is 20 parts modified of carboxymethylcellulose calcium of 40 parts of enol, 15 parts of diethylene glycol (DEG), 45 parts of white glue with vinyl, 20 parts of polyurethane, Allyl thiourea, anti-
Heavy 3 parts of agent, palm oil are 25 parts, 0.8 part of defoamer, 0.8 part of dispersant, 3 parts of wetting agent, 5 parts of initiator, 5 parts of thixotropic agent, anti-
15 parts of butene dioic acid, 10 parts of hydroquinones.
Further, above-mentioned radiation proof putty, anti-settling agent is the polybasic carboxylic acid salt of polynary amine amide, is modified in urea solution
One kind or and several.
Embodiment 3
A kind of radiation proof putty, is by 110 parts of following white cement, 45 parts of barium sulfate, 25 parts of sierozem power, 1.2 parts of cobalt acetate, poly-
18 parts modified of carboxymethylcellulose calcium of 35 parts of vinyl alcohol, 12 parts of diethylene glycol (DEG), 35 parts of white glue with vinyl, 18 parts of polyurethane, Allyl thiourea,
2 parts of anti-settling agent, palm oil be 20 parts, 0.7 part of defoamer, 0.7 part of dispersant, 2 parts of wetting agent, 4 parts of initiator, 4 parts of thixotropic agent,
12 parts of fumaric acid, 8 parts of hydroquinones.
Further, above-mentioned radiation proof putty, anti-settling agent is the polybasic carboxylic acid salt of polynary amine amide, is modified in urea solution
One kind or and several.
Claims (2)
1. a kind of radiation proof putty, it is characterised in that be by following white cement 100-120 parts, barium sulfate 40-50 parts, sierozem power
20-30 parts, cobalt acetate 0.8-1.5 parts, polyvinyl alcohol 30-40 parts, diethylene glycol (DEG) 10-15 parts, white glue with vinyl 25-45 parts, polyurethane
15-20 parts, Allyl thiourea modified carboxymethylcellulose calcium 15-20 part, anti-settling agent 1-3 parts, palm oil be 15-25 parts, froth breaking
Agent 0.5-0.8 parts, dispersant 0.5-0.8 parts, wetting agent 1-3 parts, initiator 3-5 parts, thixotropic agent 3-5 parts, fumaric acid 10-
15 parts, hydroquinones 5-10 parts.
2. a kind of as claimed in claim 1, radiation proof putty, it is characterised in that the anti-settling agent is the polynary of polynary amine amide
One kind or and several in metal carboxylate, modified urea solution.