CN106916354A - A kind of heat resistant plastice - Google Patents
A kind of heat resistant plastice Download PDFInfo
- Publication number
- CN106916354A CN106916354A CN201510984658.5A CN201510984658A CN106916354A CN 106916354 A CN106916354 A CN 106916354A CN 201510984658 A CN201510984658 A CN 201510984658A CN 106916354 A CN106916354 A CN 106916354A
- Authority
- CN
- China
- Prior art keywords
- parts
- coupling agent
- plastics
- heat resistance
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to plastic material technical field, specifically a kind of heat resistant plastice is by the material composition of following parts by weight：ABS resin 25-45 parts, nitrile rubber 15-25 parts, crosslinked polyethylene 50-60 parts, polytetrafluoroethylene (PTFE) 20-35 parts, 15-25 parts, polyacrylamide 15-25 parts, odium stearate 15-25 parts, antimony oxide 15-25 parts, dioctyl phthalate 15-25 parts, zinc oxide 10-15 parts, ethylene glycol 25-35 parts, silica 1 0-20 parts, potassium titanate crystal whisker 15-25 parts, coupling agent 5-10 parts of the benzoic acid tert-butyl group of oxidation.The heat resistance plastics that the present invention is provided, with good heat resistance, also with certain fire resistance, the ABS resin of addition makes plastics of the invention have good wearability, good stability, with good intensity.
Description
Technical field
The present invention relates to plastic material technical field, specifically a kind of heat resistant plastice.
Background technology
The extensive use of plastics, synthetic rubber, the big synthetic material of synthetic fibers three in the world today be it is well known that and it is most first with plastics, used as one of present social four big basic material, plastics are at present in building, electric power, telecommunication, electrical equipment, energy
The number of applications and range of application in the fields such as source, communications and transportation, agricultural, health care, aerospace, information and national defense industry are all growing day by day.Plastics have many premium properties as a kind of important alternative materials, such as light weight, have great plasticity,
But most plastics have the common weakness of one, and being exactly that their chemical properties in the case where temperature is higher are unstable easily produces irritant gas, such as plastic tea cup, Space cup etc..At present, the range of application of plastics is very wide, and with domestic and international economic fast development, plastic industry has also obtained hypergrowth.
Plastics kind is different on current market, and function is each different, but quality is also uneven.
The content of the invention
In order to solve the above problems, the invention provides a kind of with good heat-resisting, fire-retardant, wear-resisting, stable, safety plastics.
Technical scheme is as follows：
A kind of heat resistance plastics, are by the material composition of following parts by weight：ABS resin 25-45 parts, nitrile rubber 15-25 parts, crosslinked polyethylene 50-60 parts, polytetrafluoroethylene (PTFE) 20-35 parts, oxidation 15-25 parts of the benzoic acid tert-butyl group, polyacrylamide 15-25 parts, odium stearate 15-25 parts, antimony oxide 15-25 parts, dioctyl phthalate 15-25 parts, zinc oxide 10-15 parts, ethylene glycol 25-35
Part, silica 1 0-20 parts, potassium titanate crystal whisker 15-25 parts, coupling agent 5-10 parts.
Further, above-mentioned heat resistance plastics, coupling agent is titante coupling agent.
Beneficial effects of the present invention：
Compared with prior art, the heat resistance plastics that the present invention is provided, with good heat resistance, also with certain fire resistance, the ABS resin of addition makes plastics of the invention have good wearability, good stability, with good intensity.
Specific embodiment
Embodiment 1
A kind of heat resistance plastics, are by the material composition of following parts by weight：25 parts of ABS resin, 15 parts of nitrile rubber, 50 parts of crosslinked polyethylene, 20 parts of polytetrafluoroethylene (PTFE), 15 parts of the oxidation benzoic acid tert-butyl group, 15 parts of polyacrylamide, 15 parts of odium stearate, 15 parts of antimony oxide, 15 parts of dioctyl phthalate, 10 parts of zinc oxide, 25 parts of ethylene glycol, 0 part of silica 1,15 parts of potassium titanate crystal whisker, 5 parts of coupling agent.
Further, above-mentioned heat resistance plastics, coupling agent is titante coupling agent.
Embodiment 2
A kind of heat resistance plastics, are by the material composition of following parts by weight：45 parts of ABS resin, 25 parts of nitrile rubber, 60 parts of crosslinked polyethylene, 35 parts of polytetrafluoroethylene (PTFE), 25 parts of the oxidation benzoic acid tert-butyl group, 25 parts of polyacrylamide, 25 parts of odium stearate, 25 parts of antimony oxide, 25 parts of dioctyl phthalate, 15 parts of zinc oxide, 35 parts of ethylene glycol, 20 parts of silica, 25 parts of potassium titanate crystal whisker, 10 parts of coupling agent.
Further, above-mentioned heat resistance plastics, coupling agent is titante coupling agent.
Embodiment 3
A kind of heat resistance plastics, are by the material composition of following parts by weight：35 parts of ABS resin, 20 parts of nitrile rubber, 55 parts of crosslinked polyethylene, 30 parts of polytetrafluoroethylene (PTFE), 20 parts of the oxidation benzoic acid tert-butyl group, 20 parts of polyacrylamide, 20 parts of odium stearate, 20 parts of antimony oxide, 20 parts of dioctyl phthalate, 12 parts of zinc oxide, 30 parts of ethylene glycol, 5 parts of silica 1,20 parts of potassium titanate crystal whisker, 8 parts of coupling agent.
Further, above-mentioned heat resistance plastics, coupling agent is titante coupling agent.
Claims (2)
1. a kind of heat resistance plastics, it is characterised in that be by the material composition of following parts by weight：ABS resin 25-45 parts, nitrile rubber 15-25 parts, crosslinked polyethylene 50-60 parts, polytetrafluoroethylene (PTFE) 20-35 parts, oxidation 15-25 parts of the benzoic acid tert-butyl group, polyacrylamide 15-25 parts, odium stearate 15-25 parts, antimony oxide 15-25 parts, dioctyl phthalate 15-25 parts, zinc oxide 10-15 parts, ethylene glycol 25-35
Part, silica 1 0-20 parts, potassium titanate crystal whisker 15-25 parts, coupling agent 5-10 parts.
2. as claimed in claim 1, a kind of heat resistance plastics, it is characterised in that the coupling agent is titante coupling agent.