CN106906669A - A kind of knitting fabric of waterproof and its manufacturing process and application - Google Patents
A kind of knitting fabric of waterproof and its manufacturing process and application Download PDFInfo
- Publication number
- CN106906669A CN106906669A CN201710159957.4A CN201710159957A CN106906669A CN 106906669 A CN106906669 A CN 106906669A CN 201710159957 A CN201710159957 A CN 201710159957A CN 106906669 A CN106906669 A CN 106906669A
- Authority
- CN
- China
- Prior art keywords
- fabric
- waterproof
- mixer
- glass bar
- afterwards
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of knitting fabric of waterproof and its manufacturing process and application, including the raw material that following parts by weight are matched：Polyvinyl alcohol：100g, amorphous state a olefin copolymers：60g, pH value conditioning agent：10g, styrene-acrylic emulsion：40g, acrylic elastic emulsion：50g, epoxy resin：60g, calcium carbonate：30g, fusion agent：25g, antioxidant：20g, surfactant：40g, oleic acid：30g, numb viscose：20g, Chinese fiber crops：300g, cotton：260g, terylene：200g, paraffin：50g, pure water：180g.The knitting fabric of the waterproof and its manufacturing process and application, by adding styrene-acrylic emulsion, acrylic elastic emulsion and epoxy resin in fabric, under the booster action of calcium carbonate, fabric can be made to possess certain waterproof action, so as to improve the service life of waterproof fabrics, by adding polyvinyl alcohol, amorphous state a olefin copolymers and paraffin, the soft material for possessing viscosity can be formed such that it is able to make adhesively more to be consolidated between waterproof material and fabric.
Description
Technical field
The present invention relates to technical field of textile fabric, specially a kind of knitting fabric of waterproof and its manufacturing process and application.
Background technology
Waterproof is no longer already a fresh topic, whether tunnel, bridge, dykes and dams, road, building or our days
The house often lived, waterproof all can not be ignored.Meanwhile, the fabric product used in our daily lifes there is also and must face directly
Waterproof and dampproof problem.
Waterproof material never has a unified definition, the waterproof material that the continuous renewal of waterproof technique is also accelerated in fact
Variation, prevent wet in rainwater, underground water, industrial and civilian plumbing, corrosive liquids and air on the whole
The material of the intrusion building such as gas and steam is substantially all and is referred to as waterproof material.Waterproof material mainly has three classes：Waterproof roll,
Polyurethane waterproof material and new polymers cement group water-proofing material.
Knitting fabric is to utilize knitting needle by yarn bends lopping and mutually go here and there to cover and the fabric of formation.Knitting fabric and shuttle
The difference of knitted fabric is that form of the yarn in fabric is different.It is knitting to be divided into weft knitting and warp knit.At present, knitting fabric is wide
It is general to be applied in the products such as garment material and lining, home textile, liked by consumers in general.
Knitting fabric can be divided into two major classes from weaving mode：Weft knitted fabric and warp knitted fabric.
1) weft-knitted fabric yarn is that traverse motion (or circular motion) is done from one side of machine to another side, is coordinated
Needle motion can just form new maille.What weft-knitted fabric yarn was walked is that laterally, fabric is formed by knitting needle
Knit out what the row being coupled each other up and down of the row of a row one was formed on row direction.The institute of one row is wired
Circle is all formed by one thread braiding.Weft-knitted fabric can be completed on straight-bar machines or circular knitting machine.
2) warp knit yarn is warp-wise braiding in knitted fabric, and the warp thread as woven fabric is the same, and yarn is supplied by warp beam, passes through
A large amount of yarns arranged in parallel are wound with axle, it is similar with the warp beam in woven.Trend of the yarn in knitted fabric is warp-wise
's.A vertical coil is formed in a row, it is then oblique to move to another stringer, form another in next row
One coil.Yarn in fabric along its length from one side to another side form of zigzag advance, in a row each
Coil is all have different yarns to work out.
Existing fabric when in use, does not possess the function of waterproof typically, therefore, under special circumstances, the fabric is not
Work clothes fabric is suitable as, part fabric is filled with waterproof material inside it, possesses the function of waterproof for this, but this is anti-
Merged between water material and fabric and not enough consolidate, in the case of rainwater or air oxidation, can make anti-in fabric
Water material gradually comes off, so as to the waterproof life-span of the fabric can be influenceed.
The content of the invention
(1) technical problem for solving
In view of the shortcomings of the prior art, the invention provides a kind of knitting fabric of waterproof and its manufacturing process and application, tool
The advantages of standby waterproof, solve fabric not aspect and the unsteady problem of waterproof.
(2) technical scheme
To realize above-mentioned waterproof purpose, the present invention provides following technical scheme：A kind of knitting fabric of waterproof and its manufacture work
Skill and application, including the raw material that following parts by weight are matched：
Polyvinyl alcohol：100g；
Amorphous state a- olefin copolymers：60g；
PH value conditioning agent：10g；
Styrene-acrylic emulsion：40g；
Acrylic elastic emulsion：50g；
Epoxy resin：60g；
Calcium carbonate：30g；
Fusion agent：25g；
Antioxidant：20g；
Surfactant：40g；
Oleic acid：30g；
Numb viscose：20g；
Chinese fiber crops：300g；
Cotton：260g；
Terylene：200g；
Paraffin：50g；
Pure water：180g.
A kind of knitting fabric of waterproof and its manufacturing process and application, flow are comprised the following steps：
A1, prepare adhesive：The reaction utensil of 500ml 1, electronic scale 1, glass bar 1, workshop temperature is maintained at 30
DEG C -35 DEG C or so, workshop keeps clean, and workshop is sealed, and 100g polyvinyl alcohol is weighed first, and is put into reaction utensil, then
130g pure water is weighed, 10s is stirred clockwise with glass bar, then weigh 60g amorphous state a- olefin copolymers and 50g paraffin, and
In input reaction utensil, 30g oleic acid and 25g fusion agents being added afterwards, and stirring 20s clockwise with glass bar, adhesive is obtained；
A2, purification adhesive：20g antioxidant is added first in obtained adhesive, is stirred clockwise by glass bar
5s, then adds 10gPH value conditioning agents, waits for 10s quietly, stirs 15s clockwise by glass bar afterwards such that it is able to neutralize viscous
The acid-base property of mixture, and prevent it from aoxidizing；
A3, prepare waterproofing agent main material：The reaction utensil of 600ml 1, electronic scale weighs 40g styrene-acrylic emulsions, 50g third
Olefin(e) acid elastic emulsion and 60g epoxy resin, then three is interval reaction of the input equipped with 50g pure water successively with the time of 5s
In ware, and at each time interval between in glass bar stir 3s, be subsequently adding 40g surfactants, wait for 5min quietly afterwards, be obtained
Waterproofing agent main material；
A4, prepare waterproofing agent：30g calcium carbonate is added first in obtained waterproofing agent main material, and it is suitable with glass bar
Hour hands stir 20s, and 25g fusion agents are added again, and respectively stir 10s clockwise and anticlockwise with glass bar, and waterproof is then obtained
Agent；
A5, prepare fabric：1, mixer, first electronic scale weigh 300g Chinese fiber crops, 260g cottons and 200g terylene, and
Three is put into simultaneously in mixer, 10s is stirred first, then stop stirring, opened mixer and put into 20g fiber crops viscoses, then
In secondary stirring 10s, wait for 15s quietly afterwards, be drawn off, and be put into storage tank；
A6, prepare waterproof fabrics：First by obtained fabric input mixer, obtained waterproofing agent is then put into again,
Mixer is then shut off, and stirs 2min, then open mixer, and internal waterproof fabrics is taken out, be put into parcel tray
Preserve；
A7, preparation stable type waterproof fabrics：First by obtained waterproof material input mixer, then put into and purified
Adhesive, open mixer, 5min is stirred clockwise, then put into 15g fusion agents be again stirring for 2min, afterwards take out be obtained
Waterproof shell fabric；
A8, drying waterproof shell fabric：Dryer one, first takes out obtained waterproof shell fabric, is disperseed and divided
Bar, then in input dryer, and is 40 DEG C by the temperature adjustment of dryer, and drying time is 3min, then takes out water proof type
Fabric, carries out dredging whole to its surface；
A9, thin whole softening fabric：Obtained waterproof shell fabric is placed in machine table first, then by combing brush,
Slightly scratched from top to bottom on the surface of fabric, and combing, the time is scratched for 5min, afterwards in the web surface of combing
Addition softening agent, after addition, fabric, and slight jitter up and down is picked up with tweezers, and shaky time is 5min, is then hung up clothes hanger
On, being air-dried, clothes hanger is placed on the position of dark, and it is 25 DEG C to air-dry temperature.
(3) beneficial effect
Compared with prior art, the invention provides a kind of knitting fabric of waterproof, possesses following beneficial effect：
1st, the knitting fabric of the waterproof, by adding styrene-acrylic emulsion, acrylic elastic emulsion and epoxy resin in fabric,
Under the booster action of calcium carbonate, fabric can be made to possess certain waterproof action, and antioxidant can avoid four in reaction
During occur oxidation phenomenon such that it is able to improve the service life of waterproof fabrics.
2nd, the knitting fabric of the waterproof, by adding polyvinyl alcohol, amorphous state a- olefin copolymers and stone in waterproof fabrics
Wax, can form the soft material for possessing viscosity, wherein numb viscose can make adhesively more to be consolidated between fabric such that it is able to
Make adhesively more to be consolidated between waterproof material and fabric.
Specific embodiment
Below in conjunction with embodiments of the invention, the technical scheme in the embodiment of the present invention is clearly and completely retouched
State, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
A kind of knitting fabric of waterproof and its manufacturing process and application, including the raw material that following parts by weight are matched：
Polyvinyl alcohol：100g；
Amorphous state a- olefin copolymers：60g；
PH value conditioning agent：10g；
Styrene-acrylic emulsion：40g；
Acrylic elastic emulsion：50g；
Epoxy resin：60g；
Calcium carbonate：30g；
Fusion agent：25g；
Antioxidant：20g；
Surfactant：40g；
Oleic acid：30g；
Numb viscose：20g；
Chinese fiber crops：300g；
Cotton：260g；
Terylene：200g；
Paraffin：50g；
Pure water：180g.
A kind of knitting fabric of waterproof and its manufacturing process and application, flow are comprised the following steps：
A1, prepare adhesive：The reaction utensil of 500ml 1, electronic scale 1, glass bar 1, workshop temperature is maintained at 30
DEG C -35 DEG C or so, workshop keeps clean, and workshop is sealed, and 100g polyvinyl alcohol is weighed first, and is put into reaction utensil, then
130g pure water is weighed, 10s is stirred clockwise with glass bar, then weigh 60g amorphous state a- olefin copolymers and 50g paraffin, and
In input reaction utensil, 30g oleic acid and 25g fusion agents being added afterwards, and stirring 20s clockwise with glass bar, adhesive is obtained；
A2, purification adhesive：20g antioxidant is added first in obtained adhesive, is stirred clockwise by glass bar
5s, then adds 10gPH value conditioning agents, waits for 10s quietly, stirs 15s clockwise by glass bar afterwards such that it is able to neutralize viscous
The acid-base property of mixture, and prevent it from aoxidizing；
A3, prepare waterproofing agent main material：The reaction utensil of 600ml 1, electronic scale weighs 40g styrene-acrylic emulsions, 50g third
Olefin(e) acid elastic emulsion and 60g epoxy resin, then three is interval reaction of the input equipped with 50g pure water successively with the time of 5s
In ware, and at each time interval between in glass bar stir 3s, be subsequently adding 40g surfactants, wait for 5min quietly afterwards, be obtained
Waterproofing agent main material；
A4, prepare waterproofing agent：30g calcium carbonate is added first in obtained waterproofing agent main material, and it is suitable with glass bar
Hour hands stir 20s, and 25g fusion agents are added again, and respectively stir 10s clockwise and anticlockwise with glass bar, and waterproof is then obtained
Agent；
A5, prepare fabric：1, mixer, first electronic scale weigh 300g Chinese fiber crops, 260g cottons and 200g terylene, and
Three is put into simultaneously in mixer, 10s is stirred first, then stop stirring, opened mixer and put into 20g fiber crops viscoses, then
In secondary stirring 10s, wait for 15s quietly afterwards, be drawn off, and be put into storage tank；
A6, prepare waterproof fabrics：First by obtained fabric input mixer, obtained waterproofing agent is then put into again,
Mixer is then shut off, and stirs 2min, then open mixer, and internal waterproof fabrics is taken out, be put into parcel tray
Preserve；
A7, preparation stable type waterproof fabrics：First by obtained waterproof material input mixer, then put into and purified
Adhesive, open mixer, 5min is stirred clockwise, then put into 15g fusion agents be again stirring for 2min, afterwards take out be obtained
Waterproof shell fabric；
A8, drying waterproof shell fabric：Dryer one, first takes out obtained waterproof shell fabric, is disperseed and divided
Bar, then in input dryer, and is 40 DEG C by the temperature adjustment of dryer, and drying time is 3min, then takes out water proof type
Fabric, carries out dredging whole to its surface；
A9, thin whole softening fabric：Obtained waterproof shell fabric is placed in machine table first, then by combing brush,
Slightly scratched from top to bottom on the surface of fabric, and combing, the time is scratched for 5min, afterwards in the web surface of combing
Addition softening agent, after addition, fabric, and slight jitter up and down is picked up with tweezers, and shaky time is 5min, is then hung up clothes hanger
On, being air-dried, clothes hanger is placed on the position of dark, and it is 25 DEG C to air-dry temperature.
The beneficial effects of the invention are as follows：The knitting fabric of the waterproof, by adding styrene-acrylic emulsion, acrylic acid elasticity in fabric
Emulsion and epoxy resin, under the booster action of calcium carbonate, can make fabric possess certain waterproof action, and antioxidant energy
Four phenomenons for occurring oxidation during the course of the reaction are enough avoided such that it is able to improve the service life of waterproof fabrics, by anti-
Polyvinyl alcohol, amorphous state a- olefin copolymers and paraffin are added in water surface material, the soft material for possessing viscosity can be formed, so that
Can make adhesively more to be consolidated between waterproof material and fabric.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (1)
1. a kind of knitting fabric of waterproof and its manufacturing process and application, it is characterised in that：Original including following parts by weight proportioning
Material：
Polyvinyl alcohol：100g；
Amorphous state a- olefin copolymers：60g；
PH value conditioning agent：10g；
Styrene-acrylic emulsion：40g；
Acrylic elastic emulsion：50g；
Epoxy resin：60g；
Calcium carbonate：30g；
Fusion agent：25g；
Antioxidant：20g；
Surfactant：40g；
Oleic acid：30g；
Numb viscose：20g；
Chinese fiber crops：300g；
Cotton：260g；
Terylene：200g；
Paraffin：50g；
Pure water：180g.
A kind of knitting fabric of waterproof and its manufacturing process and application, it is characterised in that：Flow is comprised the following steps:
A1, prepare adhesive：The reaction utensil of 500ml 1, electronic scale 1, glass bar 1, workshop temperature is maintained at 30 DEG C -35
DEG C or so, workshop keeps clean, and workshop is sealed, and 100g polyvinyl alcohol is weighed first, and is put into reaction utensil, then weighs
130g pure water, 10s is stirred with glass bar clockwise, then weighs 60g amorphous state a- olefin copolymers and 50g paraffin, and is put into
In reaction utensil, 30g oleic acid and 25g fusion agents being added afterwards, and stirring 20s clockwise with glass bar, adhesive is obtained；
A2, purification adhesive：20g antioxidant is added first in obtained adhesive, 5s is stirred by glass bar clockwise, so
After add 10gPH value conditioning agents, wait for 10s quietly, 15s is stirred by glass bar clockwise afterwards such that it is able to neutralize adhesive
Acid-base property, and prevent it from aoxidizing；
A3, prepare waterproofing agent main material：The reaction utensil of 600ml 1, electronic scale weighs 40g styrene-acrylic emulsions, 50g acrylic acid
Elastic emulsion and 60g epoxy resin, then three is interval reaction utensil of the input equipped with 50g pure water successively with the time of 5s
In, and at each time interval between in stir 3s with glass bar, be subsequently adding 40g surfactants, wait for 5min quietly afterwards, be obtained anti-
Aqua main material；
A4, prepare waterproofing agent：30g calcium carbonate is added first in obtained waterproofing agent main material, and it is clockwise with glass bar
Stirring 20s, adds 25g fusion agents again, and respectively stirs 10s clockwise and anticlockwise with glass bar, and waterproofing agent is then obtained；
A5, prepare fabric：1, mixer, first electronic scale weigh 300g Chinese fiber crops, 260g cottons and 200g terylene, and by three
Person is put into mixer simultaneously, and 10s is stirred first, then stops stirring, is opened mixer and is put into 20g fiber crops viscoses, is stirred again
Mix in 10s, wait for 15s quietly afterwards, be drawn off, and be put into storage tank；
A6, prepare waterproof fabrics：First by obtained fabric input mixer, obtained waterproofing agent is then put into again, then
Mixer is closed, and stirs 2min, then open mixer, and internal waterproof fabrics is taken out, be put into preservation in parcel tray；
A7, preparation stable type waterproof fabrics：During obtained waterproof material put into mixer first, purified viscous is then put into
Mixture, opens mixer, and 5min is stirred clockwise, then puts into 15g fusion agents and is again stirring for 2min, takes out obtained anti-afterwards
Water type fabric；
A8, drying waterproof shell fabric：Dryer one, first takes out obtained waterproof shell fabric, is disperseed and slitting, so
Afterwards in input dryer, and it is 40 DEG C by the temperature adjustment of dryer, drying time is 3min, then takes out waterproof shell fabric；
A9, thin whole softening fabric：Obtained waterproof shell fabric is placed in machine table first, then by combing brush, in face
The surface of material is slightly scratched from top to bottom, and combing, scratches the time for 5min, and the web surface in combing is added afterwards
Softening agent, after addition, fabric, and slight jitter up and down is picked up with tweezers, and shaky time is 5min, is then hung up on clothes hanger,
Air-dried, clothes hanger is placed on the position of dark, it is 25 DEG C to air-dry temperature.