CN106905840A - A kind of powdery paints containing boron oxide and preparation method thereof - Google Patents
A kind of powdery paints containing boron oxide and preparation method thereof Download PDFInfo
- Publication number
- CN106905840A CN106905840A CN201510973106.4A CN201510973106A CN106905840A CN 106905840 A CN106905840 A CN 106905840A CN 201510973106 A CN201510973106 A CN 201510973106A CN 106905840 A CN106905840 A CN 106905840A
- Authority
- CN
- China
- Prior art keywords
- boron oxide
- parts
- powdery paints
- film forming
- forming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of powdery paints containing boron oxide and preparation method thereof, the weight portion of its constitutive material is:Pioloform, polyvinyl acetal 33-38, tetraphenolic ethane tetraglycidel ether epoxy resin 30-35, polybenzimidazoles 68-75, precipitated calcium carbonate 25-30, boron oxide 13-18, nano brick ground-slag end 8-10, antimony oxide 1-3, methenamine 1.5-2.5 and film forming agent 5.0-6.0;It is primary raw material present invention employs Pioloform, polyvinyl acetal, tetraphenolic ethane tetraglycidel ether epoxy resin, with the addition of boron oxide, antimony oxide and film forming agent, strengthen the Combination between each raw material, the surface levelling of powdery paints is improved simultaneously, with gloss retention high, the dicoration of powdery paints is improve, the product qualified rate for preparing is high.
Description
Technical field
The present invention relates to powdery paints, and in particular to a kind of powdery paints containing boron oxide and preparation method thereof.
Background technology
With the sustained, stable growth and the continuous improvement of living standards of the people of China's economy, the powder of hardware is applied
Dress business is also continuously increased, especially the industry such as instrument and meter, means of transportation, aluminium section bar, and powder coating can provide excellent to metal
Good anti-corrosion protection and decoration performance, but because the antifouling property of the existing coating for above-mentioned field is undesirable, on coating
Often adhere to all kinds of dusts, dirt even greasy dirt;Anti-stick patch ability is also undesirable, and the coating that existing powdery paints is formed exists
Open air is exposed to the sun, drenches with rain etc. under effect of natural conditions and the phenomenons such as foaming, cracking, stripping easily occurs for a long time, therefore, the mechanicalness of coating
Can be also undesirable.
The content of the invention
It is an object of the invention to provide a kind of powdery paints containing boron oxide and preparation method thereof.
The present invention is adopted the following technical scheme that to achieve these goals:
Powdery paints containing boron oxide, the weight portion of its constitutive material is:Pioloform, polyvinyl acetal 33-38, four phenolic group ethane four
Tetraglycidel ether epoxy resin 30-35, polybenzimidazoles 68-75, precipitated calcium carbonate 25-30, boron oxide 13-18, nano brick slag
Powder 8-10, antimony oxide 1-3, methenamine 1.5-2.5 and film forming agent 5.0-6.0.
Powdery paints containing boron oxide, the weight portion of its constitutive material is:Pioloform, polyvinyl acetal 35, four phenolic group ethane four
Tetraglycidel ether epoxy resin 32, polybenzimidazoles 72, precipitated calcium carbonate 28, boron oxide 15, nano brick ground-slag end 9, three aoxidize
Two antimony 2, methenamine 2.0 and film forming agent 5.5.
The preparation method of the powdery paints containing boron oxide, comprises the following steps:
(1)Carbon coating boron oxide:
a:Boron oxide powder is broken to 150-200 mesh, is then added in deionized water by the weight portion of constitutive material, boron oxide and
Deionized water weight ratio is 1:2.0-5.5, uniform mixing;
b:The glucose of boron oxide quality 8-12% is accounted for addition in gained mixed liquor, then stirring, uniform mixing adds and account for
The molybdenum carbide of glucose quality 1.5-2.8%, stir mixing;Mist projection granulating, obtains the boron oxide powder of organic carbon coating,
170-200 DEG C of the inlet temperature of spray drying, 68-75 DEG C of outlet temperature;
c:Gained boron oxide powder is fitted into crucible, vacuumizes, and is passed through inert atmosphere, keeps being heated under inert atmosphere conditions
275-320 DEG C of sintering 3.2-3.8h, then cooling obtains carbon coating boron oxide;
(2)The preparation of film forming agent:
a:First by 25-30 parts of neoprene CR322,3.3-3.8 part dimethylbenzene, 1.3-1.5 parts of ethylene glycol diglycidylether,
9-11 parts of E-12 epoxy resin mixing is added in reactor, is reacted 2-3 hours at a temperature of 75-95 DEG C;
b:In step(1)Reactor in add 19-21 parts of maleic anhydride, 1.8-2.2 parts of 2,6 BHT,
1.5-2.0 parts of vinyltrimethoxy silane, 1.7-2.3 parts of crosslinking agent TAIC, stirring mixing, under 50-80 DEG C of temperature conditionss
Reaction 3-5 hours, obtains final product;
(3)Then and step each raw material in addition to boron oxide and film forming agent is weighed by the weight portion of constitutive material,(1)With(2)
Raw material after treatment carries out dispensing and is put into mixing in mixer, and the compound that will be mixed is put into double screw extruder extrusion;
After sheet material cooling after extrusion, put into pulverizer and crush, grind to form the powder of 150-200 mesh, packaging and storage, powder is solid
Change condition is:190-200 DEG C of solidification temperature, is incubated 15-20 minutes.
Advantages of the present invention:
It is primary raw material present invention employs Pioloform, polyvinyl acetal, tetraphenolic ethane tetraglycidel ether epoxy resin, with the addition of
Boron oxide, antimony oxide and film forming agent, strengthen the Combination between each raw material, while improving the surface stream of powdery paints
It is flat, with gloss retention high, the dicoration of powdery paints is improve, the product qualified rate for preparing is high.
Specific embodiment
Embodiment 1:Powdery paints containing boron oxide, the weight portion of its constitutive material(kg)For:Pioloform, polyvinyl acetal 35,
Tetraphenolic ethane tetraglycidel ether epoxy resin 32, polybenzimidazoles 72, precipitated calcium carbonate 28, boron oxide 15, nano brick slag
Powder 9, antimony oxide 2, methenamine 2.0 and film forming agent 5.5.
The preparation method of the powdery paints containing boron oxide, comprises the following steps:
(1)Carbon coating boron oxide:
a:Boron oxide powder is broken to 180 mesh, is then added in deionized water by the weight portion of constitutive material, boron oxide and go from
Sub- water weight ratio is 1:2.2, uniform mixing;
b:The glucose of boron oxide quality 10% is accounted for addition in gained mixed liquor, then stirring, uniform mixing adds and account for Portugal
The molybdenum carbide of grape saccharic amount 2.0%, stir mixing;Mist projection granulating, obtains the boron oxide powder of organic carbon coating, and spraying is dry
180 DEG C of dry inlet temperature, 70 DEG C of outlet temperature;
c:Gained boron oxide powder is fitted into crucible, vacuumizes, and is passed through inert atmosphere, keeps being heated under inert atmosphere conditions
300 DEG C of sintering 3.5h, then cooling obtains carbon coating boron oxide;
(2)The preparation of film forming agent:
a:First by 28 parts of neoprene CR322,3.5 parts of dimethylbenzene, 1.4 parts of ethylene glycol diglycidylethers, 10 parts of E-12 rings
Oxygen mixed with resin is added in reactor, is reacted 2.5 hours at a temperature of 85 DEG C;
b:In step(1)Reactor in add 20 parts of maleic anhydrides, 2.0 part of 2,6 BHT, 1.8 parts of second
Alkenyl trimethoxy silane, 2.0 parts of crosslinking agent TAIC, stirring mixing, react 3-5 hours under 65 DEG C of temperature conditionss, obtain final product;
(3)Then and step each raw material in addition to boron oxide and film forming agent is weighed by the weight portion of constitutive material,(1)With(2)
Raw material after treatment carries out dispensing and is put into mixing in mixer, and the compound that will be mixed is put into double screw extruder extrusion,
After sheet material cooling after extrusion, put into pulverizer and crush, grind to form the powder of 150-200 mesh, packaging and storage, powder is solid
Change condition is:195 DEG C of solidification temperature, is incubated 18 minutes.
The powdery paints is acted in the steel tube surface through spray treatment using electrostatic spraying construction method, through 200 DEG C
Abundant solidification, naturally cool to room temperature, after placing 24h, determine coating performance, its coating impact strength >=94cm, salt spray resistance
Time >=2980h, the artificial accelerated aging time >=3350h, heat resistance >=590, exposure to weather(ing) 14 months is non-foaming, do not give birth to
Become rusty, do not ftracture, do not peel off.
Claims (2)
1. a kind of powdery paints containing boron oxide, it is characterised in that the weight portion of its constitutive material is:Pioloform, polyvinyl acetal 33-
38th, tetraphenolic ethane tetraglycidel ether epoxy resin 30-35, polybenzimidazoles 68-75, precipitated calcium carbonate 25-30, boron oxide
13-18, nano brick ground-slag end 8-10, antimony oxide 1-3, methenamine 1.5-2.5 and film forming agent 5.0-6.0;Described contains
There is the preparation method of the powdery paints of boron oxide, comprise the following steps:
(1)Carbon coating boron oxide:
a:Boron oxide powder is broken to 150-200 mesh, is then added in deionized water by the weight portion of constitutive material, boron oxide and
Deionized water weight ratio is 1:2.0-5.5, uniform mixing;
b:The glucose of boron oxide quality 8-12% is accounted for addition in gained mixed liquor, then stirring, uniform mixing adds and account for
The molybdenum carbide of glucose quality 1.5-2.8%, stir mixing;Mist projection granulating, obtains the boron oxide powder of organic carbon coating,
170-200 DEG C of the inlet temperature of spray drying, 68-75 DEG C of outlet temperature;
c:Gained boron oxide powder is fitted into crucible, vacuumizes, and is passed through inert atmosphere, keeps being heated under inert atmosphere conditions
275-320 DEG C of sintering 3.2-3.8h, then cooling obtains carbon coating boron oxide;
(2)The preparation of film forming agent:
a:First by 25-30 parts of neoprene CR322,3.3-3.8 part dimethylbenzene, 1.3-1.5 parts of ethylene glycol diglycidylether,
9-11 parts of E-12 epoxy resin mixing is added in reactor, is reacted 2-3 hours at a temperature of 75-95 DEG C;
b:Added in the reactor of step a 19-21 parts of maleic anhydride, 1.8-2.2 parts of 2,6 BHT,
1.5-2.0 parts of vinyltrimethoxy silane, 1.7-2.3 parts of crosslinking agent TAIC, stirring mixing, under 50-80 DEG C of temperature conditionss
Reaction 3-5 hours, obtains final product;
(3)Then and step each raw material in addition to boron oxide and film forming agent is weighed by the weight portion of constitutive material,(1)With(2)
Raw material after treatment carries out dispensing and is put into mixing in mixer, and the compound that will be mixed is put into double screw extruder extrusion;
After sheet material cooling after extrusion, put into pulverizer and crush, grind to form the powder of 150-200 mesh, packaging and storage, powder is solid
Change condition is:190-200 DEG C of solidification temperature, is incubated 15-20 minutes.
2. the powdery paints containing boron oxide according to claim 1, it is characterised in that the weight portion of its constitutive material is:
Pioloform, polyvinyl acetal 35, tetraphenolic ethane tetraglycidel ether epoxy resin 32, polybenzimidazoles 72, precipitated calcium carbonate 28, oxygen
Change boron 15, nano brick ground-slag end 9, antimony oxide 2, methenamine 2.0 and film forming agent 5.5.