CN106894130A - A kind of mixed yarn of cotton fiber, bark fiber and acetate fiber - Google Patents
A kind of mixed yarn of cotton fiber, bark fiber and acetate fiber Download PDFInfo
- Publication number
- CN106894130A CN106894130A CN201710229430.4A CN201710229430A CN106894130A CN 106894130 A CN106894130 A CN 106894130A CN 201710229430 A CN201710229430 A CN 201710229430A CN 106894130 A CN106894130 A CN 106894130A
- Authority
- CN
- China
- Prior art keywords
- fiber
- bark
- acetate
- mixed yarn
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the mixed yarn of a kind of cotton fiber, bark fiber and the acetate fiber for belonging to textile material technical field.It is made up of the component comprising following weight portion：18 25 parts of cotton fiber, 15 22 parts of bark fiber, 26 32 parts of acetate fiber, 12 35 parts of ramee.Mixed yarn of the invention has good heat-insulating property, in temperature, subzero 4 degree remain able to good heat insulation effect, and material can do thin, while, there is certain permeability, wearing does not result in sweat accumulation for a long time, feels that uncomfortable situation is present, while, with water-proof function, can also be gone on a journey without band umbrella in sleet sky, heat insulation effect be cleaned repeatedly and is not subtracted, long service life.
Description
Technical field
The invention belongs to textile material technical field, and in particular to a kind of cotton fiber, bark fiber and acetate fiber it is mixed
Spinning.
Background technology
It is typically warming by the way of cotton dress is worn in outdoor activity in cold district, or down jackets are worn, but, with
The raising of people's aesthetic standards and during the journey for the requirement of portability, increasingly requires light and thin fabric product.Though down jackets
Can so be made thin light, but, volume ratio is larger, and the body that wears is too fat to move, is not suitable for outdoor exercises and such as climbs the mountain.Fur
Although thermal property is good, fur is heavier, is also not suitable for wearing outdoors, some heating clothes, although can be incubated
Effect is preferably, also lighter, but, poor air permeability, having worn long internal sweat can not discharge well, cause body not relax
It is suitable.
Out of doors, sleet sky is frequently encountered, it is necessary to hold up an umbrella, cumbersome, existing clothing fabric waterproof can not be high,
Meanwhile, high temperature Exposure to Sunlight weather is being run into, meeting balling-up or oxidation so that clothing fabric is hardened are not suitable for wearing.
The content of the invention
It is an object of the invention to provide the mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber.
Preparation side the present invention also aims to provide the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber
Method.
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton is fine
18-25 parts, bark fiber 15-22 parts, acetate fiber 26-32 parts, ramee 12-35 parts of dimension.
The bark fiber is glossy privet hide fiber, laricis cortex fiber, ginkgo bark fiber, mulberry tree hide fiber, mongolian oak bark
One or more in fiber.
The preparation method of the glossy privet hide fiber or laricis cortex fiber is：Take glossy privet bark or laricis cortex is dried, manually
Or machinery is beaten into silk, is soaked 1-3 days in the buck of mass fraction 1-3%, plus acetic acid is neutralized to pH=6.5-7.5, drags for
Go out, clear water is rinsed 3-6 times, is dried, and is made.
The preparation method of the ginkgo bark fiber or mulberry tree hide fiber is：Take ginkgo bark or paper mulberry bark is dried, manually
Or machinery is beaten into silk, is soaked 1-3 days in the acetum of mass fraction 1-3%, plus limewash is neutralized to pH=6.5-
7.5, to pull out, clear water is rinsed 3-6 times, is dried, and is made.
The preparation method of the mongolian oak bark fiber is：Mongolian oak bark is taken, mongolian oak bark is soaked in the aqueous tartaric acid solution of 1-2%
Middle immersion 10-30 days, is pulled out, and clear water is rinsed 3-6 times, and artificial or machinery is beaten into silk, is rinsed 3-6 times with clear water again,
Dry, be made.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, bark fiber, acetate fiber, respectively through combing, three road draftings are carried out ramee after being processed into rove
Mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
Beneficial effects of the present invention：Mixed yarn of the invention has good heat-insulating property, still can for subzero 4 degree in temperature
Enough there is good heat insulation effect, material can do thin, meanwhile, there is certain permeability, wearing does not result in sweat for a long time
Accumulation, feels that uncomfortable situation is present, meanwhile, with water-proof function, can also be gone on a journey without band umbrella in sleet sky, clean repeatedly
Heat insulation effect does not subtract, long service life.
Specific embodiment
With reference to specific embodiment, the present invention will be further described.
In following embodiments, the preparation method of glossy privet hide fiber or laricis cortex fiber is：Take glossy privet bark or laricis cortex
Dry, artificial or machinery is beaten into silk, is soaked 1-3 days in the buck of mass fraction 1-3%, plus acetic acid is neutralized to pH=
6.5-7.5, is pulled out, and clear water is rinsed 3-6 times, is dried, and is made.
In following embodiments, the preparation method of ginkgo bark fiber or mulberry tree hide fiber is：Take ginkgo bark or paper mulberry bark
Dry, artificial or machinery is beaten into silk, is soaked 1-3 days in the acetum of mass fraction 1-3%, plus limewash is neutralized
To pH=6.5-7.5, pull out, clear water is rinsed 3-6 times, is dried, and is made.
In following embodiments, the preparation method of mongolian oak bark fiber is：Mongolian oak bark is taken, mongolian oak bark is soaked in the winestone of 1-2%
Soaked 10-30 days in aqueous acid, pulled out, clear water is rinsed 3-6 times, artificial or machinery is beaten into silk, is floated with clear water again
Wash 3-6 times, dry, be made.
Embodiment 1
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 19
Part, 18 parts of glossy privet hide fiber, 29 parts of acetate fiber, 22 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, glossy privet hide fiber, acetate fiber, respectively through combing, three road draftings are processed into rove laggard to ramee
Row mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 20 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Embodiment 2
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 18
Part, 15 parts of laricis cortex fiber, 26 parts of acetate fiber, 12 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, laricis cortex fiberoptic fiber, acetate fiber, respectively through combing, three road draftings are processed into thick ramee
Mixed after yarn, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 18 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Embodiment 3
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 25
Part, 22 parts of ginkgo bark fiber, 32 parts of acetate fiber, 35 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, ginkgo bark fiber, acetate fiber, ramee respectively through combing, three road draftings, after being processed into rove
Mixed, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 20 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Embodiment 4
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 25
Part, 22 parts of mulberry tree hide fiber, 32 parts of acetate fiber, 35 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, mulberry tree hide fiber, acetate fiber, respectively through combing, three road draftings are processed into rove laggard to ramee
Row mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 22 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Embodiment 5
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 22
Part, 20 parts of mongolian oak bark fiber, 30 parts of acetate fiber, 16 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, mongolian oak bark fiber, acetate fiber, respectively through combing, three road draftings are processed into rove laggard to ramee
Row mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 20 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Embodiment 6
The mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, is made up of the component comprising following weight portion：Cotton fiber 19
Part, 18 parts of glossy privet hide fiber, 29 parts of acetate fiber, 22 parts of ramee, 10 parts of typha minima fiber.
The preparation method of the typha minima fiber is：The stem of typha minima is taken, is dried, be then soaked in mass fraction 30%
Soaked 4-5 days in aqueous solution of propylene glycol, pulled out, clear water is rinsed 3-6 times, artificial or machinery is beaten into silk, and clear water is used again
Rinsing 3-6 times, dries, and is made.
The preparation method of the mixed yarn of above-mentioned cotton fiber, bark fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, glossy privet bark fiberoptic fiber, acetate fiber, ramee, respectively through combing, three roads are simultaneously for typha minima fiber
Bar, is mixed after being processed into rove, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 6 DEG C, with good insulation
Performance, puts on comfortable warm, also with water-proof function, can also be gone on a journey without band umbrella in sleet sky, and 80 insulation effects are cleaned repeatedly
Fruit does not subtract, long service life.
Comparative example 1
The mixed yarn of a kind of cotton fiber and acetate fiber, is made up of the component comprising following weight portion：19 parts of cotton fiber, acetic acid is fine
29 parts of dimension, 22 parts of ramee.
The preparation method of the mixed yarn of above-mentioned cotton fiber and acetate fiber, is carried out in accordance with the following steps：
First by cotton fiber, glossy privet hide fiber, acetate fiber, respectively through combing, three road draftings are processed into rove laggard to ramee
Row mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.
The mixed yarn of above-mentioned preparation is made the fabric of 0.5-1 mm of thickness under the conditions of subzero 4 DEG C, poor thermal insulation property, no
With water-proof function, 10 heat insulation effects being cleaned repeatedly and being reduced, service life is short.
Claims (6)
1. the mixed yarn of a kind of cotton fiber, bark fiber and acetate fiber, it is characterised in that by the component comprising following weight portion
Composition：Cotton fiber 18-25 parts, bark fiber 15-22 parts, acetate fiber 26-32 parts, ramee 12-35 parts.
2. the mixed yarn of cotton fiber, bark fiber and acetate fiber according to claim 1, it is characterised in that the bark
Fiber is glossy privet hide fiber, laricis cortex fiber, ginkgo bark fiber, mulberry tree hide fiber, one kind in mongolian oak bark fiber or
More than kind.
3. the mixed yarn of cotton fiber, bark fiber and acetate fiber according to claim 2, it is characterised in that the glossy privet
The preparation method of hide fiber or laricis cortex fiber is：Take glossy privet bark or laricis cortex dried, artificial or machinery beat into
Silk, is soaked 1-3 days in the buck of mass fraction 1-3%, plus acetic acid is neutralized to pH=6.5-7.5, pulls out, and clear water is rinsed 3-6 times,
Dry, be made.
4. the mixed yarn of cotton fiber, bark fiber and acetate fiber according to claim 2, it is characterised in that the ginkgo
The preparation method of bark fiber or mulberry tree hide fiber is：Take ginkgo bark or paper mulberry bark dried, artificial or machinery beat into
Silk, soaks 1-3 days in the acetum of mass fraction 1-3%, plus limewash is neutralized to pH=6.5-7.5, pulls out, clear water rinsing
3-6 times, dry, be made.
5. the mixed yarn of cotton fiber, bark fiber and acetate fiber according to claim 2, it is characterised in that the toothed oak tree
The preparation method of hide fiber is：Mongolian oak bark is taken, mongolian oak bark is soaked in the aqueous tartaric acid solution of 1-2% and soaked 10-30 days, dragged for
Go out, clear water is rinsed 3-6 times, artificial or machinery is beaten into silk, is rinsed 3-6 times with clear water again, dries, and is made.
6. the preparation method of the mixed yarn of cotton fiber, bark fiber and acetate fiber described in claim 1, it is characterised in that press
Carried out according to following steps：
First by cotton fiber, bark fiber, acetate fiber, respectively through combing, three road draftings are carried out ramee after being processed into rove
Mixing, then through spun yarn, electricity is clear, and last doubling is twisted thread and formed.