CN106893455A - A kind of hydrophilic coating that can be fully cured under Weak ultraviolet photograph - Google Patents
A kind of hydrophilic coating that can be fully cured under Weak ultraviolet photograph Download PDFInfo
- Publication number
- CN106893455A CN106893455A CN201710025388.4A CN201710025388A CN106893455A CN 106893455 A CN106893455 A CN 106893455A CN 201710025388 A CN201710025388 A CN 201710025388A CN 106893455 A CN106893455 A CN 106893455A
- Authority
- CN
- China
- Prior art keywords
- fully cured
- hydrophilic coating
- under weak
- weak ultraviolet
- ultraviolet photograph
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, by following constituting by weight proportion:50 74% performed polymer, 8 30% acrylic monomer, 4 14% light trigger, 1 12% aided initiating, 1 5% auxiliary agent.Present invention employs brand-new UV curing technologies, using in UV ultraviolet lights, shortwave(300 800 nanometers)Under uv radiation, light trigger in liquid UV materials is stimulated to be changed into free radical or cation, so as to trigger the macromolecular material containing active function groups(Resin)Aggregate into insoluble solid paint film, this film and be typically free of volatile organic compound.Can integrated UV photocuring technology main feature, human body is damaged while be avoided that again, can be fully cured under conventional ultraviolet germicidal, and material property meets use requirement after solidification.
Description
Technical field
The present invention relates to technical field of coatings, specifically a kind of hydrophilic coating that can be fully cured under Weak ultraviolet photograph.
Background technology
Existing UV is the abbreviation of ultraviolet, UV hydrophilic coatings, that is, ultraviolet light polymerization hydrophilic coating.Traditional UV solidifications
Contain substantial amounts of low molecule sensitising agent in aqueous coating formulation, mostly hardening time is more long, or period of storage is shorter, or material valency
Lattice are expensive, and being difficult of having overcomes the inhibition of oxygen in material surface air, and is difficult to surface cure and does not possess practicality.Even if solidification
Completely, also also a large amount of sensitising agent fragments are remained, and cause UV durability of coating poor, are easily turned to be yellow and easy under sunlight exposure
Come off.
The content of the invention
The technical problem to be solved in the present invention is the defect for overcoming prior art, there is provided one kind can be complete under Weak ultraviolet photograph
The hydrophilic coating of all solidstate.Pure organic UV hydrophilic coatings are prepared using photocured cross-linked mode, the advantage that both make use of UV to solidify
Hydrophily requirement can be met again.The present invention can just solidify under normal temperature ultraviolet light conditions, and curing rate is fast, energy ezpenditure is low, because
This greatly reduces operating cost, adapts to produce in enormous quantities.And film can just be dried immediately without high temperature barbecue, gained film
Flat smooth, glossiness is high, with it is energy-efficient the characteristics of.
In order to solve the above technical problems, the present invention provides following technical scheme:One kind can be completely solid under Weak ultraviolet photograph
The hydrophilic coating of change, by following constituting by weight proportion:The performed polymer of 50-74%, the acrylic monomer of 8-30%, 4-
14% light trigger, the aided initiating of 1-12%, the auxiliary agent of 1-5%.
Preferably, described performed polymer is at least one in epoxy acrylate, urethane acrylate.
Preferably, described acrylic monomer is ethoxyquin trimethylolpropane olefin(e) acid ester, polyethylene glycol(600)Dipropyl
At least one in olefin(e) acid ester, acryloyl morpholine.
Preferably, described light trigger be the acetone of 2- hydroxy-2-methyl -1- phenyl one, 1- hydroxycyclohexylphenylketones,
Benzophenone, 2,4,6 one trimethyl benzoyl diphenyl base phosphine oxides, 2- methyl isophthalic acids-[4- (methyl thio) phenyl] -2- (4-
Morpholinyl) at least one in -1- acetone.
Preferably, described aided initiating is ethyl-p-(Dimethylamino)Benzoic ether, amine three acrylic acid of modified two contracting
At least one in ester or triethanolamine.
Preferably, described auxiliary agent be in fragrant acid methacrylate, acrylated phosphate class, semicarbazide acid ester extremely
Few one kind.
Present invention employs brand-new UV curing technologies, using in UV ultraviolet lights, shortwave(300-800 nanometers)In UV radiation
Under, light trigger in liquid UV materials is stimulated to be changed into free radical or cation, so as to trigger the high score containing active function groups
Sub- material(Resin)Aggregate into insoluble solid paint film, this film and be typically free of volatile organic compound.Can be comprehensively purple
Outer photocuring technology main feature, damages while be avoided that again to human body, can consolidate completely under conventional ultraviolet germicidal
Change, and material property meets use requirement after solidification.
The present invention has an advantageous effect in that compared with prior art:The present invention takes curing system twice, effective solution
Single coating of having determined hydrophily and it is weather-proof, corrosion-resistant between contradiction, accomplished superperformance and it is durable in use between harmony.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment
It is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, by following constituting by weight proportion:50-
74% performed polymer, the acrylic monomer of 8-30%, the light trigger of 4-14%, the aided initiating of 1-12%, the auxiliary agent of 1-5%.
Preferably, described performed polymer is at least one in epoxy acrylate, urethane acrylate.
Preferably, described acrylic monomer is ethoxyquin trimethylolpropane olefin(e) acid ester, polyethylene glycol(600)Dipropyl
At least one in olefin(e) acid ester, acryloyl morpholine.
Preferably, described light trigger be the acetone of 2- hydroxy-2-methyl -1- phenyl one, 1- hydroxycyclohexylphenylketones,
Benzophenone, 2,4,6 one trimethyl benzoyl diphenyl base phosphine oxides, 2- methyl isophthalic acids-[4- (methyl thio) phenyl] -2- (4-
Morpholinyl) at least one in -1- acetone.
Preferably, described aided initiating is ethyl-p-(Dimethylamino)Benzoic ether, amine three acrylic acid of modified two contracting
At least one in ester or triethanolamine.
Preferably, described auxiliary agent be in fragrant acid methacrylate, acrylated phosphate class, semicarbazide acid ester extremely
Few one kind.
Now coating of the invention can be detected into membrane sample progressive, data are obtained as follows:
Project | Content |
Adhesive force | A:Network test B:5mm AEG-process C:T-shaped bend test 100% does not fall off |
Alkali resistance | (20 ± 1 DEG C) the immersion corrosion-free points of 20min in 10% NaOH solution |
Salt fog resistance | 72 hours >=9.8 grades of neutral salt spray test, surface is corroded without large area or perforation occurs |
Solvent resistance | Butanone is stained with absorbent cotton to be wiped repeatedly repeatedly, coating does not fall off |
Heat resistance | 200 ± 5 DEG C/10min nondiscolourings micro- flavescence of 300 ± 5 DEG C/10min |
Oil resistivity | Fin oil immersion is steeped 24 hours → 140 DEG C/10min → be cooled to room temperature → hydrophily and does not decline≤10 ° substantially |
Initial hydrophily | ≤ 5o (is directly determined) with contact angle instrument |
Protracted hydrophilicity | More than 300 times≤20o of continuous flowing water 200 hours≤25o drying and watering cycles |
Principle of the invention and advantage:
(1)The UV principles of solidification are that ultraviolet light polymerization needs to produce free radical or cation to trigger polymerization, crosslinking by light trigger
Reaction is carried out by unsaturated double-bond, and under uv radiation, the light trigger in liquid UV materials is excited, and produces free radical or sun
Ion, triggers the compound with unsaturated double-bond in material(Polymer, prepolymer and monomer)Generation polymerisation, is cross-linked into net
Shape cured film.
(2)The main mode of UV hydrophilic coating film forming be chemical membrane, that is, convert film forming, after aqueous solvent is largely volatilized into
Film thing will occur a series of chemical reaction and be just changed into the polymeric membrane with certain performance its structure to be mostly netted big point
Minor structure, therefore the polymerization of chain lock addition polymerization and Step Condensation film forming two ways can be divided into.1. chain lock addition polymerization polymerization:In film forming matter
Unsaturated double-bond triggers the free chain polymerization of generation to form macromolecule membranous layer by the free radical in initiator.2. Step Condensation into
Film:Contain substantial amounts of reactive functional group group in film forming matter, such as hydroxyl, carboxyl, amino etc. itself can occur progressively to be polymerized
And form macromolecule membranous layer.
(3)This project takes brand-new UV curing technologies, and a kind of technology new solidification means for water paint is provided subtract
The hardening time of water paint is lacked, coating stability is good, without organic solvent, has eliminated conventional ultra-violet photocureable coating and carry
The problems such as polluting and stimulate caused by VOC, has the advantages that curing rate is fast, environment-friendly, good hydrophilic property.
Presently preferred embodiments of the present invention is the foregoing is only, is not intended to limit the invention, it is all in essence of the invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (6)
1. it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:By following group by weight proportion
In groups into:The performed polymer of 50-74%, the acrylic monomer of 8-30%, the light trigger of 4-14%, the aided initiating of 1-12%, 1-
5% auxiliary agent.
2. it is according to claim 1 it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:Institute
The performed polymer stated is at least one in epoxy acrylate, urethane acrylate.
3. it is according to claim 1 it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:Institute
The acrylic monomer stated is ethoxyquin trimethylolpropane olefin(e) acid ester, polyethylene glycol(600)Diacrylate, acryloyl morpholine
In at least one.
4. it is according to claim 1 it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:Institute
The light trigger stated is the acetone of 2- hydroxy-2-methyl -1- phenyl one, 1- hydroxycyclohexylphenylketones, benzophenone, 2,4,6 one
In trimethyl benzoyl diphenyl base phosphine oxide, 2- methyl isophthalic acids-[4- (methyl thio) phenyl] -2- (4- morpholinyls) -1- acetone
At least one.
5. it is according to claim 1 it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:Institute
The aided initiating stated is ethyl-p-(Dimethylamino)In the modified two contracting triacrylates of benzoic ether, amine or triethanolamine extremely
Few one kind.
6. it is according to claim 1 it is a kind of can under Weak ultraviolet photograph the hydrophilic coating that be fully cured, it is characterised in that:Institute
The auxiliary agent stated is at least one in fragrant acid methacrylate, acrylated phosphate class, semicarbazide acid ester.