CN106893194A - Plastics preparation method - Google Patents
Plastics preparation method Download PDFInfo
- Publication number
- CN106893194A CN106893194A CN201510961539.8A CN201510961539A CN106893194A CN 106893194 A CN106893194 A CN 106893194A CN 201510961539 A CN201510961539 A CN 201510961539A CN 106893194 A CN106893194 A CN 106893194A
- Authority
- CN
- China
- Prior art keywords
- plastics preparation
- weight portion
- plastics
- raw material
- paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of plastics preparation method, is prepared from by the raw material of following weight portion:Polypropylene 76-78%, nylon 1-3%, paraffin 6-7.2%, borax 6-8%, calcium carbonate 4-5%, antistatic additive 1-2.5%, mineral oil 2.2%, stabilizer 3-3.5%;Above-mentioned raw materials are sufficiently mixed, are molded afterwards.Environment protecting well of the invention, and low production cost.
Description
Technical field
The present invention relates to a kind of plastics preparation method.
Background technology
Plastics are with monomer as raw material, by addition polymerization or the producing high-molecular of polycondensation polymerized
Compound, is commonly called as plastics or resin, can freely change composition and body styles.Existing plastics
Not environmentally.
The content of the invention
(1) technical problem to be solved
The problem to be solved in the present invention is to provide a kind of plastics preparation method, to overcome prior art
In defect not environmentally.
(2) technical scheme
To solve the technical problem, the present invention provides a kind of plastics preparation method, by following heavy
The raw material for measuring part is prepared from:Polypropylene 76-78%, nylon 1-3%, paraffin 6-7.2%,
Borax 6-8%, calcium carbonate 4-5%, antistatic additive 1-2.5%, mineral oil 2.2%, stabilizer
3-3.5%;Above-mentioned raw materials are sufficiently mixed, are molded afterwards.
Further, the polypropylene weight part is 77%.
Further, the nylon weight portion is 2%.
Further, the paraffin weight portion is 7.2%.
(3) beneficial effect
Plastics preparation method of the invention, good environment protecting, and low production cost.
Specific embodiment
With reference to embodiment, specific embodiment of the invention is described in further detail.
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
A kind of plastics preparation method of the invention, is prepared from by the raw material of following weight portion:It is poly-
Propylene 76-78%, nylon 1-3%, paraffin 6-7.2%, borax 6-8%, calcium carbonate 4-5%,
Antistatic additive 1-2.5%, mineral oil 2.2%, stabilizer 3-3.5%;Above-mentioned raw materials are filled
Divide mixing, be molded afterwards.
The preferably described polypropylene weight part of the present embodiment is 77%.The present embodiment preferably Buddhist nun
Imperial weight portion is 2%.The present embodiment preferably paraffin weight portion is 7.2%.
In sum, above-mentioned implementation method is not restricted implementation method of the invention, all
Modification or wait that the technical staff in field is carried out on the basis of substance of the invention
Effect deformation, in technology category of the invention.
Claims (4)
1. a kind of plastics preparation method, it is characterised in that prepared by the raw material of following weight portion
Form:Polypropylene 76-78%, nylon 1-3%, paraffin 6-7.2%, borax 6-8%, carbonic acid
Calcium 4-5%, antistatic additive 1-2.5%, mineral oil 2.2%, stabilizer 3-3.5%;Will be above-mentioned
Raw material is sufficiently mixed, and is molded afterwards.
2. plastics preparation method according to claim 1, it is characterised in that:It is described poly-
Propylene weight part is 77%.
3. plastics preparation method according to claim 1, it is characterised in that:The Buddhist nun
Imperial weight portion is 2%.
4. plastics preparation method according to claim 1, it is characterised in that:The stone
Wax weight portion is 7.2%.