CN106893188A - A kind of automobile heat-shrink tube and preparation method thereof - Google Patents
A kind of automobile heat-shrink tube and preparation method thereof Download PDFInfo
- Publication number
- CN106893188A CN106893188A CN201710135738.2A CN201710135738A CN106893188A CN 106893188 A CN106893188 A CN 106893188A CN 201710135738 A CN201710135738 A CN 201710135738A CN 106893188 A CN106893188 A CN 106893188A
- Authority
- CN
- China
- Prior art keywords
- parts
- shrink tube
- automobile heat
- preparation
- original
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile heat-shrink tube and preparation method thereof, a kind of automobile heat-shrink tube, it is characterised in that：According to parts by weight, including 25~30 parts of polyvinyl acetate ethene, 25~30 parts of polyethylene, 10~20 parts of EPDM ethylene propylene diene rubbers, 20~30 parts of TDE, 5~10 parts of antimony oxide, 0~1 part of antioxidant, 0~1 part of lubricant.The invention has the advantages that：Adjustment with original accounting is increased by new raw material in formula, in the case where its original physical property is not changed, realizes that fire-retardant rank is greatly improved, penetrating odor is eliminated.
Description
Technical field
The present invention relates to automotive wire bundle production technical field, and in particular to a kind of automobile heat-shrink tube and its preparation side
Method.
Background technology
The main material for being presently used for producing heat-shrink tube includes：1. olefin polymer or copolymer；2. rubber type of material
Or thermoplastic elastomer SBS (SBS), styrene-isoprene block copolymer
(SIS) one or more the material in；3. other attached help material.But there is flame retardant rating in existing heat-shrink tube raw material
Difference, containing penetrating odor the problems such as.
The content of the invention
It is an object of the invention to provide a kind of automobile heat-shrink tube and preparation method thereof, realize fire-retardant rank and significantly carry
Height, penetrating odor is eliminated.
To achieve the above object, the present invention provides following technical scheme：
A kind of automobile heat-shrink tube, it is characterised in that：According to parts by weight, including
Compared with prior art, the invention has the advantages that：
Adjustment with original accounting is increased by new raw material in formula, in the case where its original physical property is not changed,
Realize that fire-retardant rank is greatly improved, penetrating odor is eliminated.
Specific embodiment
Below in conjunction with the embodiment in the present invention, the technical scheme in the embodiment of the present invention is carried out clearly and completely
Description, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on this hair
Embodiment in bright, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1
Embodiment 2
Embodiment 3
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (1)
1. a kind of automobile heat-shrink tube, it is characterised in that：According to parts by weight, including