CN106867383A - A kind of water and oil applicable type woodenware renovation clear finish and preparation method thereof - Google Patents
A kind of water and oil applicable type woodenware renovation clear finish and preparation method thereof Download PDFInfo
- Publication number
- CN106867383A CN106867383A CN201710164207.6A CN201710164207A CN106867383A CN 106867383 A CN106867383 A CN 106867383A CN 201710164207 A CN201710164207 A CN 201710164207A CN 106867383 A CN106867383 A CN 106867383A
- Authority
- CN
- China
- Prior art keywords
- water
- aqueous
- agent
- oil
- applicable type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of water and oil applicable type woodenware renovation clear finish and preparation method thereof, water and oil applicable type woodenware renovation clear finish, including following components, and the percentage by weight of each component is：Aqueous aromatic urethane 50 90%；Aqueous defoamer 0.1 0.5%；Aqueous wetting agent 0.1 0.5%；Aqueous levelling agent 0.1 0.5%；Aqueous wear-resistant auxiliary agent 1 2%；Slipping agent 0.2 1%；Aqueous dispersion 0.1 1%；Adhesion promoter 1 2%；Water-based thickener 0.1 0.5%；Water surplus.The water and oil applicable type woodenware renovation clear finish that the present invention is obtained, zero VOC, without the harmful substance such as benzene,toluene,xylene and free TDI, heavy metal, good adhesive force is respectively provided with melamine sheet material, PVC board, oiliness PU paints sheet material, NC paints sheet material, water paint sheet material, up to 0 grade, the hardness of paint film is high, wearability is good for the adhesive force of paint film.
Description
Technical field
The present invention relates to woodcare paint field, a kind of renovation of water and oil applicable type woodenware clear finish and its preparation are specifically disclosed
Method.
Background technology
The timeworn furniture of in the market, furniture in personal family after using several years, no matter furniture surface water paint or
Different degrees of damage can all occur in oil paint, its surface.If how much the furniture thrown away with regard to this or renewed understands some unfortunately, after all
Some furniture use superior in quality solid wood to make and form, and cost is higher.Accordingly, it would be desirable to study one kind both can be suitably used for
Water paint also can be suitably used for oil paint, and burst size of methanal is relatively low, can avoid the renovation finish paint of secondary pollution, reduces cost,
Reduce the injury to human body.
The content of the invention
Defect it is an object of the invention to overcome prior art, there is provided a kind of water and oil applicable type woodenware renovates clear finish
And preparation method thereof, water and oil applicable type woodenware renovation clear finish both can be suitably used for water paint or can be suitably used for oil paint, and
Burst size of methanal is relatively low, it is to avoid oiliness renovates the secondary pollution of varnish-treated tape.
In order to realize object above and other purposes, the present invention is realized by including following technical scheme：A kind of water
The universal woodenware renovation clear finish of oil, at least including following components, the percentage by weight of each component is：
Preferably, the water and oil applicable type woodenware renovation clear finish includes following components, the percentage by weight of each component
For：
Preferably, the water and oil applicable type woodenware renovation clear finish also includes color inhibition agent pyrophosphoric acid and hydroxy silicon oil,
The color inhibition agent pyrophosphoric acid is (0.01-0.4) with the weight ratio of the aqueous aromatic urethane：(50-95), the hydroxyl
Silicone oil is (0.5-2) with the weight ratio of the aqueous aromatic urethane：(50-95).The present invention adds color inhibition agent pyrophosphoric acid
The anti-yellowing property that water and oil applicable type woodenware renovates clear finish can be effectively improved with hydroxy silicon oil.
Preferably, the water and oil applicable type woodenware renovation clear finish also includes flatting silica, the flatting silica and the water
Property aromatic polyurethane resins weight ratio be (0.1-1)：(50-95).The change of the addition according to flatting silica, can obtain
The water and oil applicable type woodenware renovation clear finish of bloom, semi-gloss or matt.
Preferably, the flatting silica is aerosil or delustring microballoon.
Preferably, the solid content 34%-36% of the aqueous aromatic urethane, its molecular weight is 3-5 ten thousand.Aqueous fragrance
Adoption urethane is used to improve richness, hardness, impact resistance and the freexing tolerance of woodenware renovation clear finish.
Preferably, the aqueous KT200A of model Hefei section day of the aqueous aromatic urethane.Hefei section it is aqueous
The aqueous aromatic urethane of KT200A is carried and can realize there is preferable interlayer tack with oil paint, water paint.
Preferably, the aqueous defoamer is any one in the modified defoamer of organosilicon, mineral oil or polyethers.
It is highly preferred that model TEGO902W, SP-994 of organic-silicon-modified defoamer, TEGO270 or OT-75.Mineral
The model DF-877 or DF-840 of the modified defoamer of oil；Modified defoamer model L-61, BX-106107108 of polyethers or
DS-2001。
Preferably, the aqueous wetting agent is polyether silicone class wetting agent or silanol class non-ionic wetting agent.
It is highly preferred that the model TEGO245 of the aqueous wetting agent.
Preferably, the aqueous levelling agent is dimethyl silicone polymer class levelling agent or polyether polyester azo polyether polyeste
Class levelling agent.
It is highly preferred that the model TEGO450 of the aqueous levelling agent.
Preferably, the aqueous wear-resistant auxiliary agent is type siloxane antiwear assistant.Addition aqueous wear-resistant auxiliary agent improves paint film table
The anti-wear performance in face.
It is highly preferred that the model DC-51 of the aqueous wear-resistant auxiliary agent.Addition aqueous wear-resistant auxiliary agent makes coating surface more
It is smooth.
Preferably, the slipping agent is type siloxane slipping agent.
It is highly preferred that the model 482 of the slipping agent.
Preferably, the aqueous dispersion is ammonium polyacrylate dipersant.Addition aqueous dispersion improves aqueous fragrance
Adoption urethane is to the parcel ability of powder and prevents re-uniting for powder.
It is highly preferred that model the TEGO 715w or A168 of the aqueous dispersion.
Preferably, the water-based thickener is that association type Polyacrylate thickeners or non-ionic polyurethane association type are thickened
Agent.
It is highly preferred that the model DSX 3551 of the water-based thickener.
Preferably, the adhesion promoter is closure silane compound adhesion promoter.Addition adhesive force promotes
Agent improves adhesive force of the paint film on sheet material.
It is highly preferred that the model silok-628 of the adhesion promoter.
Invention additionally discloses a kind of method for preparing water and oil applicable type woodenware renovation clear finish as described above, including
Following steps：
1) from A, B, C and D mode any one carry out：
A, under stirring at low speed, sequentially add the aqueous aromatic urethane, described aqueous resistance to according to percentage by weight
Milling aid, the slipping agent, the adhesion promoter and the water, rotating speed are improved to 400-600r/min, stirred；
B, under stirring at low speed, sequentially add the aqueous aromatic urethane, described aqueous resistance to according to percentage by weight
Milling aid, the slipping agent, the adhesion promoter, the water, the color inhibition agent pyrophosphoric acid and the hydroxy silicon oil, turn
Speed is improved to 400-600r/min, is stirred；
C, under stirring at low speed, sequentially add the aqueous aromatic urethane, described aqueous resistance to according to percentage by weight
Milling aid, the slipping agent, the adhesion promoter, the water and the flatting silica, rotating speed are improved to 400-600r/min,
Stir；
D, under stirring at low speed, sequentially add the aqueous aromatic urethane, described aqueous resistance to according to percentage by weight
Milling aid, the slipping agent, the adhesion promoter, the water, the flatting silica, the color inhibition agent pyrophosphoric acid and described
Hydroxy silicon oil, rotating speed is improved to 400-600r/min, is stirred；
2) aqueous defoamer, aqueous wetting agent, the aqueous dispersion, aqueous levelling are sequentially added according to percentage by weight
Agent and the water-based thickener, adjustment of rotational speed stir to 700-800r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
In sum, the present invention provides a kind of water and oil applicable type woodenware renovation clear finish and preparation method thereof, the present invention
Beneficial effect：
The water and oil applicable type woodenware renovation clear finish that the present invention is obtained, it is nonpoisonous and tasteless with Source of life water as solvent, surpass
Low VOC, without the harmful substance such as benzene,toluene,xylene and free TDI, heavy metal, environmental-protecting performance is excellent.Water and oil applicable type wood
Device renovation clear finish is respectively provided with good adhesive force in melamine sheet material, PVC board, in melamine sheet material, PVC board
The adhesive force of paint film has reached 0 grade of national testing standard on material, NC paints sheet material, water paint sheet material, it is only necessary to somewhat polish
It is that can reach superpower adhesive force to be renovated clear finish and covered with paint, lacquer, colour wash, etc. with water and oil applicable type woodenware afterwards；The hardness high-wearing feature of paint film is good：Paint
The hardness of film is high, toughness is strong.Water and oil applicable type woodenware renovation clear finish color inhibition ability is strong.Because water paint is not contained in itself
Free TDI etc. causes the harmful substance of xanthochromia, along with aqueous aromatic urethane and color inhibition agent pyrophosphoric acid, hydroxy silicon oil
Use cooperatively so that paint film molecule has more preferable stability.In addition, water and oil applicable type woodenware renovation clear finish easy construction,
Safety, low cost；Renovation construction can be carried out on oiliness lacquer painting, so as to avoid using oiliness paint stripper bring two degree of pollutions,
Material consumption, the increase equivalent risk of construction cost.
Specific embodiment
The present invention is expanded on further with reference to embodiment.It should be understood that embodiment is merely to illustrate the present invention, and it is unrestricted
The scope of the present invention.
It is the proportioning of each raw material components in embodiment 1~5 in table 1, the content of each raw material components is weight portion in table.
The weight proportion of each raw material components in the embodiment 1~5 of table 1
Embodiment 1
A kind of preparation method of water and oil applicable type woodenware renovation clear finish is comprised the following steps：
1) in the case where rotating speed is 300r/min stirring conditions, 94kg aqueous aromatic urethanes, 1kg aqueous wear-resistants are sequentially added
Auxiliary agent, 0.5kg slipping agents, 1kg adhesion promoters and 1kg water, rotating speed are improved to 500r/min, stirring 30-40min until
It is even；
2) 0.2kg aqueous defoamers, 0.2kg aqueous wetting agents, 0.8kg aqueous dispersions, 0.1kg aqueous flows are sequentially added
Flat agent and 1.2kg water-based thickeners, adjustment of rotational speed stir to 700r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
Embodiment 2
A kind of preparation method of water and oil applicable type woodenware renovation clear finish is comprised the following steps：
1) in the case where rotating speed is 300r/min stirring conditions, 90kg aqueous aromatic urethanes, 1kg aqueous wear-resistants are sequentially added
Auxiliary agent, 0.5kg slipping agents, 1kg adhesion promoters, 5.5kg water and 0.5kg flatting silicas, rotating speed are improved to 500r/min, stirring
Uniformly；
2) 0.2kg aqueous defoamers, 0.2kg aqueous wetting agents, 0.8kg aqueous dispersions, 0.1kg aqueous flows are sequentially added
Flat agent and 1.2kg water-based thickeners, adjustment of rotational speed stir to 800r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
Embodiment 3
A kind of preparation method of water and oil applicable type woodenware renovation clear finish is comprised the following steps：
1) in the case where rotating speed is 300r/min stirring conditions, 88kg aqueous aromatic urethanes, 1kg aqueous wear-resistants are sequentially added
Auxiliary agent, 0.5kg slipping agents, 1kg adhesion promoters, 7kg water and 1kg flatting silicas, rotating speed are improved to 600r/min, stirring
40min is until stir；
2) 0.2kg aqueous defoamers, 0.2kg aqueous wetting agents, 0.8kg aqueous dispersions, 0.1kg aqueous flows are sequentially added
Flat agent and 1.2kg water-based thickeners, adjustment of rotational speed stir to 800r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
Embodiment 4
A kind of preparation method of water and oil applicable type woodenware renovation clear finish is comprised the following steps：
1) in the case where rotating speed is 300r/min stirring conditions, 88kg aqueous aromatic urethanes, 1kg aqueous wear-resistants are sequentially added
Auxiliary agent, 0.5kg slipping agents, 1kg adhesion promoters, 6.9kg water, 0.2kg color inhibition agent pyrophosphoric acids and 0.8kg hydroxy silicon oils,
Rotating speed is improved to 600r/min, is stirred；
2) 0.2kg aqueous defoamers, 0.2kg aqueous wetting agents, 0.8kg aqueous dispersions, 0.2kg aqueous flows are sequentially added
Flat agent and 1.2kg water-based thickeners, adjustment of rotational speed stir to 800r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
Embodiment 5
A kind of preparation method of water and oil applicable type woodenware renovation clear finish is comprised the following steps：
1) in the case where rotating speed is 300r/min stirring conditions, 84kg aqueous aromatic urethanes, 1kg aqueous wear-resistants are sequentially added
Auxiliary agent, 0.5kg slipping agents, 1kg adhesion promoters, 9.4kg water, 1kg flatting silicas, 0.4kg color inhibition agent pyrophosphoric acids and 1.1kg
Hydroxy silicon oil, rotating speed is improved to 600r/min, is stirred；
2) 0.2kg aqueous defoamers, 0.2kg aqueous wetting agents, 0.8kg aqueous dispersions, 0.2kg aqueous flows are sequentially added
Flat agent and 1.2kg water-based thickeners, adjustment of rotational speed stir to 800r/min, obtain the renovation of water and oil applicable type woodenware transparent
Finish paint.
Water and oil applicable type woodenware renovates the performance detection of clear finish：
(1) appearance that will be coated respectively with the melamine plate of water paint is cleared up, and is then coated with melamine plate
The water and oil applicable type woodenware renovation clear finish that embodiment 1 to 5 is obtained.Using GB GBT 23999-2009《Indoor dress
Decorations finishing water-borne wood coating》The water and oil applicable type woodenware renovation clear finish obtained to embodiment 1 to 5 carries out performance survey
Examination.Its test result is as shown in table 2.
The water and oil applicable type woodenware that 2 embodiment of table 1 to 5 is obtained renovates the performance test results of clear finish
From table 2 it can be seen that the water and oil applicable type woodenware renovation clear finish stable performance that embodiment 1 to 5 is obtained, it is easy to
Storage, by embodiment 1 to 5 obtain water and oil applicable type woodenware renovation clear finish coat be originally water paint melamine plate
On, the finish paint paint film property for obtaining complies fully with national standard, or even remote superstate standard, and embodiment 4 and embodiment 5 have good
Good anti-yellowing property.
(2) appearance that will be coated respectively with the melamine plate of oil paint is cleared up, and is then coated with melamine plate
The water and oil applicable type woodenware renovation clear finish that embodiment 1 to 5 is obtained.Performance survey is carried out to the paint film on melamine plate
Examination.Its test result is as shown in table 3.
The water and oil applicable type woodenware that 3 embodiment of table 1 to 5 is obtained renovates the performance test results of clear finish
From table 3 it can be seen that it be originally oil that the water and oil applicable type woodenware renovation clear finish that embodiment 1 to 5 is obtained is coated
Property paint melamine plate on, the finish paint paint film property for obtaining complies fully with national standard, or even remote superstate standard, embodiment
4 and embodiment 5 have good anti-yellowing property.
In sum, the water and oil applicable type woodenware renovation clear finish that the present invention is obtained, with Source of life water as solvent, nothing
Malicious tasteless, zero VOC, without the harmful substance such as benzene,toluene,xylene and free TDI, heavy metal, environmental-protecting performance is excellent.Water oil
Universal woodenware renovation clear finish is in melamine sheet material, PVC board, oiliness PU paints sheet material, NC paints sheet material, water paint sheet material
On be respectively provided with good adhesive force, melamine sheet material, PVC board, oiliness PU paint sheet material, NC paint sheet material, water paint sheet material
The adhesive force of upper paint film reaches 0 grade of national testing standard, it is only necessary to renovate transparent with water and oil applicable type woodenware after somewhat polishing
Finish paint is covered with paint, lacquer, colour wash, etc. and can reach superpower adhesive force；The hardness high-wearing feature of paint film is good：The hardness of paint film is high, toughness is strong.So, this hair
It is bright effectively to overcome various shortcoming of the prior art and have high industrial utilization.
The above, only presently preferred embodiments of the present invention, it is not any to the present invention in form and substantial limitation,
It should be pointed out that for those skilled in the art, on the premise of the inventive method is not departed from, can also make
Some improvement and supplement, these are improved and supplement also should be regarded as protection scope of the present invention.All those skilled in the art,
Without departing from the spirit and scope of the present invention, when made using disclosed above technology contents it is a little more
Dynamic, modification and the equivalent variations for developing, are Equivalent embodiments of the invention；Meanwhile, it is all according to substantial technological pair of the invention
The variation, modification and evolution of any equivalent variations that above-described embodiment is made, still fall within the scope of technical scheme
It is interior.
Claims (10)
1. a kind of water and oil applicable type woodenware renovates clear finish, it is characterised in that at least including following components, the weight of each component
Percentage is：
2. water and oil applicable type woodenware as claimed in claim 1 renovates clear finish, it is characterised in that：The water and oil applicable type wood
Device renovation clear finish also includes color inhibition agent pyrophosphoric acid and hydroxy silicon oil, the color inhibition agent pyrophosphoric acid and the aqueous fragrance
The weight ratio of adoption urethane is (0.01-0.4)：(50-95), the weight of the hydroxy silicon oil and the aqueous aromatic urethane
Than being (0.5-2)：(50-95).
3. water and oil applicable type woodenware as claimed in claim 1 or 2 renovates clear finish, it is characterised in that：The water and oil applicable
Type woodenware renovation clear finish also includes flatting silica, and the flatting silica is with the weight ratio of the aqueous aromatic urethane resin
(0.1-1)：(50-95).
4. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The aqueous aromatic gathers
The solid content 34%-36% of urethane, its molecular weight is 3-5 ten thousand.
5. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The aqueous aromatic gathers
The aqueous KT200A of model Hefei section day of urethane.
6. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The aqueous defoamer is
In the modified defoamer of organosilicon, mineral oil or polyethers any one；
And/or, the aqueous wetting agent is polyether silicone class wetting agent or silanol class non-ionic wetting agent；
And/or, the aqueous levelling agent is dimethyl silicone polymer class levelling agent or polyether polyester azo polyether polyeste class stream
Flat agent.
7. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The aqueous wear-resistant auxiliary agent
It is type siloxane antiwear assistant；
And/or, the slipping agent is type siloxane slipping agent；
And/or, the aqueous dispersion is ammonium polyacrylate dipersant.
8. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The water-based thickener is
Association type Polyacrylate thickeners or non-ionic polyurethane association thickener.
9. water and oil applicable type woodenware as claimed in claim 3 renovates clear finish, it is characterised in that：The adhesion promoter
It is closure silane compound adhesion promoter.
10. a kind of method that water and oil applicable type woodenware prepared as described in claim 1 to 8 is any renovates clear finish, it is special
Levy and be：Comprise the following steps：
1) from A, B, C and D mode any one carry out：
A, under stirring at low speed, sequentially add the aqueous aromatic urethane, the aqueous wear-resistant according to percentage by weight and help
Agent, the slipping agent, the adhesion promoter and the water, rotating speed are improved to 400-600r/min, stirred；
B, under stirring at low speed, sequentially add the aqueous aromatic urethane, the aqueous wear-resistant according to percentage by weight and help
Agent, the slipping agent, the adhesion promoter, the water, the color inhibition agent pyrophosphoric acid and the hydroxy silicon oil, rotating speed are carried
Up to 400-600r/min, stirs；
C, under stirring at low speed, sequentially add the aqueous aromatic urethane, the aqueous wear-resistant according to percentage by weight and help
Agent, the slipping agent, the adhesion promoter, the water and the flatting silica, rotating speed are improved to 400-600r/min, stirring
Uniformly；
D, under stirring at low speed, sequentially add the aqueous aromatic urethane, the aqueous wear-resistant according to percentage by weight and help
Agent, the slipping agent, the adhesion promoter, the water, the flatting silica, the color inhibition agent pyrophosphoric acid and the hydroxyl
Silicone oil, rotating speed is improved to 400-600r/min, is stirred；
2) according to percentage by weight sequentially add aqueous defoamer, aqueous wetting agent, the aqueous dispersion, aqueous levelling agent and
The water-based thickener, adjustment of rotational speed stirs to 700-800r/min, obtains water and oil applicable type woodenware renovation transparent area
Paint.