CN106867110A - A kind of air conditioning exhausting grid for producing anion - Google Patents
A kind of air conditioning exhausting grid for producing anion Download PDFInfo
- Publication number
- CN106867110A CN106867110A CN201710144103.9A CN201710144103A CN106867110A CN 106867110 A CN106867110 A CN 106867110A CN 201710144103 A CN201710144103 A CN 201710144103A CN 106867110 A CN106867110 A CN 106867110A
- Authority
- CN
- China
- Prior art keywords
- parts
- air conditioning
- conditioning exhausting
- air
- hokutolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of air conditioning exhausting grid for producing anion, it is prepared from the following raw materials in parts by weight, including 5 10 parts of negative ion powder, 68 parts of Tea Polyphenols, 9 15 parts of Strange ice stone, 6 10 parts of hokutolite, 20 22 parts of styrene-acrylonitrile copolymer, 15 20 parts of Fypro, 6 14 parts of diisononyl phthalate, 20 23 parts of calcium silicates, 9 14 parts of aerosil, 57 parts of aminoethyl piperazine, 10 13 parts of polyphenylene sulfide, 10 15 parts of glass fibre, 30 parts of polipropene 25, 10 14 parts of isopropanol, 79 parts of silica white, 58 parts of polyethylene glycol, 4, 16 20 parts of 4 ' 17 22 parts of biphenylenes and polyolefine fiber.Air conditioning exhausting grid of the invention can produce anion, and structural strength is high, and antiageing effect is good.
Description
Technical field
The present invention relates to a kind of air conditioning exhausting grid for producing anion.
Background technology
Air grille can improve indoor air quality, reduce building energy consumption, and carry out large space part thermal and humidity environment
Control, progressively as the important directions of current office buildings Air-conditioning Development, while also being set to office building traditional air-conditioning system
Meter proposes new challenge.Traditional office building central air-conditioner grille air port system is:Fan coil plus fresh air unit air-conditioning system,
Centralized Constant air volume system, and air conditioning system with variable.These systems are generally using the sky of ceiling air-supply (upper air-supply)
Tune mode, it emphasizes to blow being sufficiently mixed of air-flow and room air, the whole of generation in the air absorption chamber sent out by furred ceiling
It is waste heat, remaining wet and dilute pollutant, so make the humiture in indoor all spaces basically identical.This kind of control mode can not be fine
Different users are required temperature and the different of ventilation during ground meets same use space.And, after system is installed, just not
The position in air port is changed after being easy to as needed.The air outlet of grid air-supply is typically concordant with ground to be set, and ground need to make somebody a mere figurehead,
Lower space is used as arrangement ajutage or is directly used as air supply plenum chamber, and air-supply is got in by floor air supply register, with interior
Air occurs to be discharged from the air outlet of room top (on ceiling or workspace) after caloic is exchanged.20 century 70s with
Come, Europe starts to be applied to office buildings.Particularly the mid-80, the Lloyd of London, s buildings and Hong Kong Huifeng
Bank causes the concern of various countries' air-conditioning technical circle using the success of under-floor air distribution air-conditioning system.At present, grid supply air system is in China
Research and application be in the starting stage.The main distinction of air grille supply air system and traditional supply air system is with regard to cold and hot source device
For airhandling equipment, grid supply air system is similar to traditional upper air supply air-conditioner system.Grid supply air system master
The difference wanted is:It is from the air-supply of floor lower space;Wind pushing temperature during cooling is (generally 17~18 DEG C) higher;Same
Different mesoclimate environment can be formed in one large space;Room test be from floor to ceiling under serve return-air stream
Pattern.It is easy to building fits up again and work as office use change with the renewal and reform of existing building, it is necessary to rearrange, fit up
When, the air outlet being arranged on movable floor is easy to change, and floor lower space can facilitate power circuit, communication line, water
Pipe etc. is reinstalled, and this can greatly reduce the newly-decorated expense of weight.According to Koi carp, only labour can save 32%<1
>.Floor air supply system can be used for building renewal and reform, although increases floor and can run into story height, stair and elevator and stops
The problems such as raising of adjustment, accomodation ground by position, but these problems can be resolved.In addition, the peace of plenum chamber
Dress process is a process for relatively dry, and the destruction to other building structure can be reduced to minimum.
Existing air outlet grate can not produce anion, and structural strength is not high, and antiageing effect is bad.
The content of the invention
In view of this, it is high it is an object of the present invention to provide a kind of structural strength, good the produced anion of antiageing effect
Air conditioning exhausting grid.
In order to solve the above-mentioned technical problem, the technical scheme is that:
A kind of air conditioning exhausting grid for producing anion, is prepared from the following raw materials in parts by weight, including negative ion powder
5-10 parts, Tea Polyphenols 6-8 parts, Strange ice stone 9-15 parts, hokutolite 6-10 parts, styrene-acrylonitrile copolymer 20-22 parts, polyamides
15-20 parts of amine fiber, diisononyl phthalate 6-14 parts, calcium silicates 20-23 parts, aerosil 9-14 parts, ammonia second
5-7 parts of base piperazine, polyphenylene sulfide 10-13 parts, glass fibre 10-15 parts, -30 parts of polipropene 25, isopropanol 10-14 parts,
Silica white 7-9 parts, polyethylene glycol 5-8 parts, 4,4 '-biphenylene 17-22 parts and polyolefine fiber 16-20 parts.
Preferably, be prepared from the following raw materials in parts by weight, including 5 parts of negative ion powder, 6 parts of Tea Polyphenols, Strange ice stone 9
Part, 6 parts of hokutolite, styrene -20 parts of acrylonitrile copolymer, 15 parts of Fypro, 6 parts of diisononyl phthalate, silicon
20 parts of sour calcium, 9 parts of aerosil, 5 parts of aminoethyl piperazine, 10 parts of polyphenylene sulfide, 10 parts of glass fibre, polipropene 25
16 parts of part, 10 parts of isopropanol, 7 parts of silica white, 5 parts of polyethylene glycol, 4,17 parts of 4 '-biphenylene and polyolefine fiber.
Preferably, be prepared from the following raw materials in parts by weight, including 7.5 parts of negative ion powder, 7 parts of Tea Polyphenols, Strange ice stone
12 parts, 8 parts of hokutolite, styrene -21 parts of acrylonitrile copolymer, 17.5 parts of Fypro, diisononyl phthalate 10
Part, 21.5 parts of calcium silicates, 11.5 parts of aerosil, 6 parts of aminoethyl piperazine, 11.5 parts of polyphenylene sulfide, glass fibre
12.5 parts, 27.5 parts of polypropylene, 12 parts of isopropanol, 8 parts of silica white, 6.5 parts of polyethylene glycol, 4,19.5 parts of 4 '-biphenylene and
18 parts of polyolefine fiber.
Preferably, be prepared from the following raw materials in parts by weight, including 10 parts of negative ion powder, 8 parts of Tea Polyphenols, Strange ice stone 15
Part, 10 parts of hokutolite, styrene -22 parts of acrylonitrile copolymer, 20 parts of Fypro, 14 parts of diisononyl phthalate,
23 parts of calcium silicates, 14 parts of aerosil, 7 parts of aminoethyl piperazine, 13 parts of polyphenylene sulfide, 15 parts of glass fibre, poly- third
20 parts of 30 parts of alkene, 14 parts of isopropanol, 9 parts of silica white, 8 parts of polyethylene glycol, 4,22 parts of 4 '-biphenylene and polyolefine fiber.
The invention solves the problems that another technical problem be that a kind of preparation of the air conditioning exhausting grid for producing anion is provided
Method, comprises the following steps:
1) by negative ion powder 5-10 parts, Tea Polyphenols 6-8 parts, Strange ice stone 9-15 parts, hokutolite 6-10 parts, styrene-propylene
Lonitrile copolymer 20-22 parts, Fypro 15-20 parts, diisononyl phthalate 6-14 parts, calcium silicates 20-23 parts, gas phase
It is standby during silica 9-14 parts, aminoethyl piperazine 5-7 parts is put into pulverizer;
2) regulating step 1) in pulverizer rotating speed be 4000-4200r/min, vacuum state turn crush 6-8 minutes, it is standby
With;
3) by step 2) during gained raw material puts into drying box, regulation heating-up temperature is 62-68 DEG C, is dried 16-20 minutes,
It is standby;
4) by 10 parts of polyphenylene sulfide, 10 parts of glass fibre, polipropene 25 part, 10 parts of isopropanol, 7 parts of silica white, poly-
5 parts of ethylene glycol, 4,16 parts of 17 parts of 4 '-biphenylene and polyolefine fiber are put into reactor, standby;
5) regulating step 4) in reactor speed of agitator be 1200-1400r/min, heating-up temperature be 110-140 DEG C, instead
Answer 15-20 minutes, it is standby;
6) by step 3) gained raw material and step 5) gained raw material put into banbury, lifting heating-up temperature is 180
DEG C, the heat time is 2-5 minutes, standby;
7) by step 6) gained raw material puts into and be heated into injection machine molten condition, injects in-mold molding.
The technology of the present invention effect major embodiment is in the following areas:The negative ion powder of addition, Tea Polyphenols, Strange ice stone, hokutolite
Anion, air small particle anion can be produced reduces brain by promoting the oxidative deamination of monoamine oxidase (MAO)
And 5-HT (serotonin) level in tissue, cause endocrine and the obvious physiological change of nervous system, it is high to autonomic nerve
Level maincenter and automatic nervous system have good adjustment effect.So as to improve corticocerebral function, inspire enthusiasm, eliminate
Fatigue, improves operating efficiency, improves the health care of sleep, and increases appetite.Normocyte, colloid particle in blood etc. are negatively charged, it
Between it is mutually exclusive, maintain a certain distance, and the aging red blood cell of lesion is fought for due to electronics, it is positively charged, due to
It is positive and negative attracting, then that red blood cell condensation is agglomerating.Small particle anion can effectively repair aging cell membrane potential, promote it to become
Normal electronegative cell, negative negative reprimand slows down erythrocyte sedimentation rate, while small particle anion adds so as to effectively reduce blood viscosity
Colloid particle negative polarity trend in itself in strong blood, making the colloidal stability of plasma protein increases.The glass fibre of addition, poly- third
Alkene, isopropanol, silica white, polyethylene glycol, 4,4 '-biphenylene and polyolefine fiber holding structure intensity are high, antiageing effect
It is good.
Specific embodiment
Embodiment 1
A kind of air conditioning exhausting grid for producing anion, is prepared from the following raw materials in parts by weight, including negative ion powder 5
Part, 6 parts of Tea Polyphenols, 9 parts of Strange ice stone, 6 parts of hokutolite, styrene -20 parts of acrylonitrile copolymer, 15 parts of Fypro, adjacent benzene
6 parts of dioctyl phthalate dinonyl, 20 parts of calcium silicates, 9 parts of aerosil, 5 parts of aminoethyl piperazine, 10 parts of polyphenylene sulfide,
10 parts of glass fibre, polipropene 25 part, 10 parts of isopropanol, 7 parts of silica white, 5 parts of polyethylene glycol, 4,17 parts of 4 '-biphenylene and
16 parts of polyolefine fiber.
A kind of preparation method of the air conditioning exhausting grid for producing anion, comprises the following steps:
1) by 5 parts of negative ion powder, 6 parts of Tea Polyphenols, 9 parts of Strange ice stone, 6 parts of hokutolite, styrene-acrylonitrile copolymer 20
Part, 15 parts of Fypro, 6 parts of diisononyl phthalate, 20 parts of calcium silicates, 9 parts of aerosil, aminoethyl piperazine
It is standby during 5 parts are put into pulverizer;
2) regulating step 1) in pulverizer rotating speed be 4000-4200r/min, vacuum state turn crush 6-8 minutes, it is standby
With;
3) by step 2) during gained raw material puts into drying box, regulation heating-up temperature is 62-68 DEG C, is dried 16-20 minutes,
It is standby;
4) by 10 parts of polyphenylene sulfide, 10 parts of glass fibre, polipropene 25 part, 10 parts of isopropanol, 7 parts of silica white, poly-
5 parts of ethylene glycol, 4,16 parts of 17 parts of 4 '-biphenylene and polyolefine fiber are put into reactor, standby;
5) regulating step 4) in reactor speed of agitator be 1200-1400r/min, heating-up temperature be 110-140 DEG C, instead
Answer 15-20 minutes, it is standby;
6) by step 3) gained raw material and step 5) gained raw material put into banbury, lifting heating-up temperature is 180
DEG C, the heat time is 2-5 minutes, standby;
7) by step 6) gained raw material puts into and be heated into injection machine molten condition, injects in-mold molding.
Embodiment 2
A kind of air conditioning exhausting grid for producing anion, is prepared from the following raw materials in parts by weight, including negative ion powder
7.5 parts, 7 parts of Tea Polyphenols, 12 parts of Strange ice stone, 8 parts of hokutolite, styrene -21 parts of acrylonitrile copolymer, Fypro 17.5
Part, 10 parts of diisononyl phthalate, 21.5 parts of calcium silicates, 11.5 parts of aerosil, 6 parts of aminoethyl piperazine, poly- Asia
11.5 parts of aralkyl sulfid, 12.5 parts of glass fibre, 27.5 parts of polypropylene, 12 parts of isopropanol, 8 parts of silica white, polyethylene glycol 6.5
18 parts of part, 4,19.5 parts of 4 '-biphenylene and polyolefine fiber.
A kind of preparation method of the air conditioning exhausting grid for producing anion, comprises the following steps:
1) by 7.5 parts of negative ion powder, 7 parts of Tea Polyphenols, 12 parts of Strange ice stone, 8 parts of hokutolite, styrene-acrylonitrile copolymer
21 parts, 17.5 parts of Fypro, 10 parts of diisononyl phthalate, 21.5 parts of calcium silicates, 11.5 parts of aerosil,
6 parts of aminoethyl piperazine is put into pulverizer, standby;
2) regulating step 1) in pulverizer rotating speed be 4000-4200r/min, vacuum state turn crush 6-8 minutes, it is standby
With;
3) by step 2) during gained raw material puts into drying box, regulation heating-up temperature is 62-68 DEG C, is dried 16-20 minutes,
It is standby;
4) by 11.5 parts of polyphenylene sulfide, 12.5 parts of glass fibre, 27.5 parts of polypropylene, 12 parts of isopropanol, silica white 8
Part, 6.5 parts of polyethylene glycol, 4,18 parts of 19.5 parts of 4 '-biphenylene and polyolefine fiber are put into reactor, standby;
5) regulating step 4) in reactor speed of agitator be 1200-1400r/min, heating-up temperature be 110-140 DEG C, instead
Answer 15-20 minutes, it is standby;
6) by step 3) gained raw material and step 5) gained raw material put into banbury, lifting heating-up temperature is 180
DEG C, the heat time is 2-5 minutes, standby;
7) by step 6) gained raw material puts into and be heated into injection machine molten condition, injects in-mold molding.
Embodiment 3
A kind of air conditioning exhausting grid for producing anion, is prepared from the following raw materials in parts by weight, including negative ion powder
10 parts, 8 parts of Tea Polyphenols, 15 parts of Strange ice stone, 10 parts of hokutolite, styrene -22 parts of acrylonitrile copolymer, 20 parts of Fypro,
14 parts of diisononyl phthalate, 23 parts of calcium silicates, 14 parts of aerosil, 7 parts of aminoethyl piperazine, polyphenylene sulfide
13 parts, 15 parts of glass fibre, 30 parts of polypropylene, 14 parts of isopropanol, 9 parts of silica white, 8 parts of polyethylene glycol, 4,4 '-biphenylene 22
20 parts of part and polyolefine fiber.
A kind of preparation method of the air conditioning exhausting grid for producing anion, comprises the following steps:
1) by 10 parts of negative ion powder, 8 parts of Tea Polyphenols, 15 parts of Strange ice stone, 10 parts of hokutolite, styrene-acrylonitrile copolymer
22 parts, 20 parts of Fypro, 14 parts of diisononyl phthalate, 23 parts of calcium silicates, 14 parts of aerosil, aminoethyl
7 parts of piperazine is put into pulverizer, standby;
2) regulating step 1) in pulverizer rotating speed be 4000-4200r/min, vacuum state turn crush 6-8 minutes, it is standby
With;
3) by step 2) during gained raw material puts into drying box, regulation heating-up temperature is 62-68 DEG C, is dried 16-20 minutes,
It is standby;
4) by 13 parts of polyphenylene sulfide, 15 parts of glass fibre, 30 parts of polypropylene, 14 parts of isopropanol, 9 parts of silica white, poly-
8 parts of ethylene glycol, 4,20 parts of 22 parts of 4 '-biphenylene and polyolefine fiber are put into reactor, standby;
5) regulating step 4) in reactor speed of agitator be 1200-1400r/min, heating-up temperature be 110-140 DEG C, instead
Answer 15-20 minutes, it is standby;
6) by step 3) gained raw material and step 5) gained raw material put into banbury, lifting heating-up temperature is 180
DEG C, the heat time is 2-5 minutes, standby;
7) by step 6) gained raw material puts into and be heated into injection machine molten condition, injects in-mold molding.
Experimental example
Experimental subjects:Using common air conditioning exhausting grid as a control group, made using special air conditioning exhausting grid
It is control group two, the air conditioning exhausting grid of the produced anion of the application is used as experimental group.
Requirement of experiment:The thickness of three groups of materials of experiment is consistent with size.
Experimental technique:Negative ion concentration is tested according to GB-T30128 standards using negative ion concentration detector, measurement
Negative ion concentration around air conditioning exhausting grid within 30cm;Structural strength is using JISK7093-2012 standard methods by anti-
Compressive Strength detector is measured;Antiageing effect is used and detected by ageing oven, and adjusts test temperature temperature
It is 85 DEG C to spend, and relative humidity is 85%, and air pressure is 106kPa, and ozone concentration is 45%, and ultraviolet irradiation intensity is 500mW/ ㎡,
Obtain ageing time.
Concrete outcome is as shown in the table:
With reference to upper table, the different experimental subjects of three groups of contrast is by the data obtained by experiment, air conditioning exhausting lattice of the invention
Grid can produce anion, and structural strength is higher, and antiageing effect is more preferable.
The technology of the present invention effect major embodiment is in the following areas:The negative ion powder of addition, Tea Polyphenols, Strange ice stone, hokutolite
Anion, air small particle anion can be produced reduces brain by promoting the oxidative deamination of monoamine oxidase (MAO)
And 5-HT (serotonin) level in tissue, cause endocrine and the obvious physiological change of nervous system, it is high to autonomic nerve
Level maincenter and automatic nervous system have good adjustment effect.So as to improve corticocerebral function, inspire enthusiasm, eliminate
Fatigue, improves operating efficiency, improves the health care of sleep, and increases appetite.Normocyte, colloid particle in blood etc. are negatively charged, it
Between it is mutually exclusive, maintain a certain distance, and the aging red blood cell of lesion is fought for due to electronics, it is positively charged, due to
It is positive and negative attracting, then that red blood cell condensation is agglomerating.Small particle anion can effectively repair aging cell membrane potential, promote it to become
Normal electronegative cell, negative negative reprimand slows down erythrocyte sedimentation rate, while small particle anion adds so as to effectively reduce blood viscosity
Colloid particle negative polarity trend in itself in strong blood, making the colloidal stability of plasma protein increases.The glass fibre of addition, poly- third
Alkene, isopropanol, silica white, polyethylene glycol, 4,4 '-biphenylene and polyolefine fiber holding structure intensity are high, antiageing effect
It is good.
Certainly, it is more than representative instance of the invention, in addition, the present invention can also have other various specific implementations
The technical scheme that mode, all use equivalents or equivalent transformation are formed, all falls within the scope of protection of present invention.
Claims (4)
1. a kind of air conditioning exhausting grid for producing anion, it is characterised in that:It is prepared from the following raw materials in parts by weight, including
Negative ion powder 5-10 parts, Tea Polyphenols 6-8 parts, Strange ice stone 9-15 parts, hokutolite 6-10 parts, styrene-acrylonitrile copolymer 20-
22 parts, Fypro 15-20 parts, diisononyl phthalate 6-14 parts, calcium silicates 20-23 parts, aerosil 9-
14 parts, aminoethyl piperazine 5-7 parts, polyphenylene sulfide 10-13 parts, glass fibre 10-15 parts, -30 parts of polipropene 25, isopropanol
10-14 parts, silica white 7-9 parts, polyethylene glycol 5-8 parts, 4,4 '-biphenylene 17-22 parts and polyolefine fiber 16-20 parts.
2. a kind of air conditioning exhausting grid for producing anion as claimed in claim 1, it is characterised in that:By following weight portion
Several raw materials are made, including 5 parts of negative ion powder, 6 parts of Tea Polyphenols, 9 parts of Strange ice stone, 6 parts of hokutolite, styrene-acrylonitrile compolymer
20 parts of thing, 15 parts of Fypro, 6 parts of diisononyl phthalate, 20 parts of calcium silicates, 9 parts of aerosil, aminoethyl
5 parts of piperazine, 10 parts of polyphenylene sulfide, 10 parts of glass fibre, polipropene 25 part, 10 parts of isopropanol, 7 parts of silica white, poly- second two
16 parts of 5 parts of alcohol, 4,17 parts of 4 '-biphenylene and polyolefine fiber.
3. a kind of air conditioning exhausting grid for producing anion as claimed in claim 1, it is characterised in that:By following weight portion
Several raw materials are made, including 7.5 parts of negative ion powder, 7 parts of Tea Polyphenols, 12 parts of Strange ice stone, 8 parts of hokutolite, styrene-acrylonitrile
21 parts of copolymer, 17.5 parts of Fypro, 10 parts of diisononyl phthalate, 21.5 parts of calcium silicates, aerosil
11.5 parts, 6 parts of aminoethyl piperazine, 11.5 parts of polyphenylene sulfide, 12.5 parts of glass fibre, 27.5 parts of polypropylene, isopropanol 12
18 parts of part, 8 parts of silica white, 6.5 parts of polyethylene glycol, 4,19.5 parts of 4 '-biphenylene and polyolefine fiber.
4. a kind of air conditioning exhausting grid for producing anion as claimed in claim 1, it is characterised in that:By following weight portion
Several raw materials are made, including 10 parts of negative ion powder, 8 parts of Tea Polyphenols, 15 parts of Strange ice stone, 10 parts of hokutolite, styrene-acrylonitrile
22 parts of copolymer, 20 parts of Fypro, 14 parts of diisononyl phthalate, 23 parts of calcium silicates, 14 parts of aerosil,
7 parts of aminoethyl piperazine, 13 parts of polyphenylene sulfide, 15 parts of glass fibre, 30 parts of polypropylene, 14 parts of isopropanol, 9 parts of silica white,
20 parts of 8 parts of polyethylene glycol, 4,22 parts of 4 '-biphenylene and polyolefine fiber.