CN106863141A - Sandblasting cleaning procedure for turning over crusher drill - Google Patents
Sandblasting cleaning procedure for turning over crusher drill Download PDFInfo
- Publication number
- CN106863141A CN106863141A CN201611235867.0A CN201611235867A CN106863141A CN 106863141 A CN106863141 A CN 106863141A CN 201611235867 A CN201611235867 A CN 201611235867A CN 106863141 A CN106863141 A CN 106863141A
- Authority
- CN
- China
- Prior art keywords
- drill bit
- sandblasting
- selection
- turning over
- drill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sandblasting cleaning procedure for turning over crusher drill, by using the oscillation action of the percussion and ultrasonic wave of sandblasting in water, even if the foreign matter for firmly clinging on drill bit can also be completely removed, and the influence of infringement property will not be produced to drill bit, the purpose of cleaning treatment is rapidly carried out to drill bit therefore, it is possible to reach, and very easily the foreign matter being manually difficult to clean off can be removed totally, it is excessive and cause the situation of the breaking of rod because manually turning over mill dynamics so as to avoid, so as to drastically increase the cleaning efficiency of drill bit.
Description
Technical field
The present invention relates to a kind of sandblasting cleaning procedure for turning over crusher drill, it is particularly well-suited to carry out cleaning of doing over again to drill bit
Treatment.
Background technology
After the drill bit drilled to PCB is by long-time use, can be various under the knife edge part of drill bit residual
The foreign matter being difficult to clean off, if not clearing up the foreign matter of bit wing blade portion, easily the knife edge part to drill bit produces abrasion or disconnected
The serious problems such as brill.Tradition is that workman is cleaned using hairbrush to drill bit to the cleaning mode of drill bit foreign matter, but this clear
Clean mode can only be clean the foreign matter cleaning for easily removing, and the foreign matter for being difficult to clean off then needs workman to change other instruments pair
The knife edge part of drill bit turn over mill, but workman easily occur when turning over crusher drill manually it is excessive and cause the breaking of rod because turning over mill dynamics
Situation, therefore be unfavorable for the cleaning treatment to drill bit.
The content of the invention
To solve the above problems, it is an object of the invention to provide a kind of sandblasting cleaning procedure for turning over crusher drill, energy
It is enough that cleaning treatment is rapidly carried out to drill bit, and can be very easily that the foreign matter removing being manually difficult to clean off is clean, from
And can avoid because manually turning over that mill dynamics is excessive and cause the situation of the breaking of rod, and the effect of cleaning drill bit can be greatly enhanced
Rate.
The present invention solves the technical scheme that is used of its problem:
Sandblasting cleaning procedure for turning over crusher drill, including following process step:
A, the drill bit to needing to be cleaned are classified, according to the different sand grains using different model specification of drill bit species;
B, blasting treatment is carried out to drill bit at different angles;
C, the drill bit by blasting treatment is positioned in water, drill bit is cleaned with reference to the effect of ultrasonic wave;
D, the mode dried up using compressed air or the drying effect using drier are dried treatment to drill bit;
E, arrangement is carried out to the drill bit by dried process turn over mill.
Further, the blasting treatment for being carried out in step B, comprises the following steps:
A1, drill bit is positioned in sand-blasting machine;
B1, the different pressure for adjusting sandblastings according to bite type, make impulsive force during sandblasting meet the requirement that is hit of drill bit;
C1, sandblasting is carried out to drill bit, and constantly the direction of adjustment drill bit makes its each several part be subject to blasting treatment.
Further, mill is turned over to the arrangement that drill bit is carried out in step E, is comprised the following steps:
A2, the knife edge part of drill bit is carried out turning over mill using mill;
B2, the knife edge part to drill bit carry out DLC coating treatments.
Further, it is necessary to the drill bit for being cleaned it is a diameter of less than 150um when, the model specification of the sand grains of selection is
400#, the pressure of the sandblasting of selection is 0.25-0.35Mpa, and the ultrasonic wave working strength of selection is 30%-45%.
Further, it is necessary to during a diameter of 0.15-0.25mm of the drill bit for being cleaned, the model specification of the sand grains of selection is
320#, the pressure of the sandblasting of selection is 0.30-0.40Mpa, and the ultrasonic wave working strength of selection is 40%-55%.
Further, it is necessary to during a diameter of 0.25-0.45mm of the drill bit for being cleaned, the model specification of the sand grains of selection is
280#, the pressure of the sandblasting of selection is 0.40-0.55Mpa, and the ultrasonic wave working strength of selection is 50%-75%.
Further, it is necessary to during a diameter of 0.50-1.20mm of the drill bit for being cleaned, the model specification of the sand grains of selection is
220#, the pressure of the sandblasting of selection is 0.50-0.65Mpa, and the ultrasonic wave working strength of selection is 60%-80%.
Further, it is necessary to during a diameter of 1.20-3.175mm of the drill bit for being cleaned, the model specification of the sand grains of selection
It is 180# or 220#, the pressure of the sandblasting of selection is 0.60-0.75Mpa, and the ultrasonic wave working strength of selection is 65%-85%.
Further, it is necessary to the drill bit for being cleaned it is a diameter of more than 3.20mm when, the model specification of the sand grains of selection is
150# or 220#, the pressure of the sandblasting of selection is 0.64-0.79Mpa, and the ultrasonic wave working strength of selection is more than 75%.
The beneficial effects of the invention are as follows:Sandblasting cleaning procedure for turning over crusher drill of the invention, sand grains during using sandblasting
Percussion, even if firmly the foreign matter that clings on drill bit also can be caused to loosen or be come off by sand impinging, with reference to
Oscillation action of the ultrasonic wave in water, can be fully erased the foreign matter and sand grains on drill bit, and will not produce damage to drill bit
The influence of evil property, rapidly carries out the purpose of cleaning treatment therefore, it is possible to reach to drill bit, and can very easily
The artificial foreign matter being difficult to clean off is removed clean such that it is able to avoid it is excessive and cause the situation of the breaking of rod because manually turning over mill dynamics,
So as to drastically increase the cleaning efficiency of drill bit.
Brief description of the drawings
The invention will be further described with example below in conjunction with the accompanying drawings.
Fig. 1 is the present invention for turning over the flow chart of the sandblasting cleaning procedure of crusher drill;
Fig. 2 is the flow chart of blasting treatment;
Fig. 3 is to arrange the flow chart for turning over mill.
Specific embodiment
Reference picture 1- Fig. 3, the sandblasting cleaning procedure for turning over crusher drill of the invention, including following process step:
A, the drill bit to needing to be cleaned are classified, according to the different sand grains using different size of drill bit species;
B, blasting treatment is carried out to drill bit at different angles;
C, the drill bit by blasting treatment is positioned in water, drill bit is cleaned with reference to the effect of ultrasonic wave;
D, the mode dried up using compressed air or the drying effect using drier are dried treatment to drill bit;
E, arrangement is carried out to the drill bit by dried process turn over mill.
When carrying out blasting treatment to it towards the different angles of drill bit, foreign matter of the sand grains constantly to being bonded on drill bit is carried out
Clash into, with the continuous action for clashing into, firmly cling the foreign matter on drill bit is caused to loosen or come off by sand impinging, from
And the preliminary effect for cleaning is realized, because drill bit can be infected with upper sand grains when carrying out sandblasting to drill bit, it is therefore desirable to by spraying
The drill bit of sand treatment is positioned in water, and mode using ultrasonic wave is cleaned to drill bit, and ultrasonic wave is in water transmission
The effect of vibration can be produced in water, and water can be rinsed under the drive of oscillation action to drill bit, therefore, it is possible to residual
It is fully erased in the foreign matter and sand grains on drill bit, and be not in that the shadow for damaging property is produced to drill bit in whole treatment
Ring, therefore the purpose that cleaning treatment is rapidly carried out to drill bit can not only be reached, and also can very easily artificial
The foreign matter that is difficult to clean off is removed clean such that it is able to avoid it is excessive and cause the situation of the breaking of rod because manually turning over mill dynamics so that
Drastically increase the cleaning efficiency of drill bit.For the different types of drill bit for needing to carry out blasting treatment, it is necessary to select difference
The sand grains of model specification, in commercial Application, in units of " # ", such as model specification is the sand of 120# to the model specification of sand grains
Grain, represents its sieve number for 100-140, and micron number is 105-150.
Wherein, reference picture 2, the blasting treatment carried out in step B, comprise the following steps:
A1, drill bit is positioned in sand-blasting machine;
B1, the different pressure for adjusting sandblastings according to bite type, make impulsive force during sandblasting meet the requirement that is hit of drill bit;
C1, sandblasting is carried out to drill bit, and constantly the direction of adjustment drill bit makes its each several part be subject to blasting treatment.
Because the knife edge part of different type drill bit is differed, therefore the drill bit knife edge part that there are is very small, has
The more large situation of drill bit knife edge part, therefore the pressure of sandblasting must be adjusted when carrying out blasting treatment to drill bit so that
Blasting pressure and the type matching of drill bit, cause the small drill bit of knife edge part to occur disconnected so as to avoid blasting pressure excessive
The situation of brill.
Wherein, reference picture 3, mill is turned in step E to the arrangement that drill bit is carried out, and is comprised the following steps:
A2, the knife edge part of drill bit is carried out turning over mill using mill;
B2, the knife edge part to drill bit carry out DLC coating treatments.
After the drill bit drilled to PCB is by long-time use, not only can be under the knife edge part of drill bit residual
The various foreign matters being difficult to clean off, and its knife edge part can be worn and become coarse, not sharp enough, therefore, in order that drill bit
Can continue to use by after sandblasting cleaning, it is therefore desirable to which the knife edge part to drill bit carries out turning over mill treatment, by turning at mill
Although the knife edge part after reason becomes sharp again, also very easily there is oxidation reaction with air, so that blade part
Dividing becomes fragile, coarse, it is therefore desirable to DLC coating treatments are carried out to knife edge part, DLC coating treatments are the blade in drill bit
Part covers one layer of DLC film so that drill bit not only has excellent wearability, but also with very low friction system
Number, so that drill bit has preferably drilling performance, so as to improve the quality of product.
When sandblasting cleaning is carried out to different types of drill bit using sandblasting cleaning procedure of the invention, for different type
Drill bit, it is necessary to using the ultrasonic wave of the sand grains of different model specification, the blasting pressure of different parameters and varying strength so that
The sandblasting of drill bit must be cleaned can be quick and effective, so as to avoid causing bit damage because of unaccommodated processing environment
Situation, therefore, for different types of drill bit, there is examples below:
Embodiment one:
When the drill bit for needing to be cleaned it is a diameter of less than 150um when, it is necessary to the model specification of the sand grains selected is for 400#, need
The pressure of the sandblasting to be selected is 0.25-0.35Mpa, it is necessary to the ultrasonic wave working strength selected is 30%-45% such that it is able to protects
Drill bit of the card diameter less than 150um is quick and effective when sandblasting cleaning is carried out.
Embodiment two:
As a diameter of 0.15-0.25mm of the drill bit for needing to be cleaned, it is necessary to the model specification of the sand grains selected is 320#,
The pressure for needing the sandblasting selected is 0.30-0.40Mpa, it is necessary to the ultrasonic wave working strength selected is 40%-55% such that it is able to
Ensure that the drill bit of a diameter of 0.15-0.25mm is quick and effective when sandblasting cleaning is carried out.
Embodiment three:
As a diameter of 0.25-0.45mm of the drill bit for needing to be cleaned, it is necessary to the model specification of the sand grains selected is 280#,
The pressure for needing the sandblasting selected is 0.40-0.55Mpa, it is necessary to the ultrasonic wave working strength selected is 50%-75% such that it is able to
Ensure that the drill bit of a diameter of 0.25-0.45mm is quick and effective when sandblasting cleaning is carried out.
Example IV:
As a diameter of 0.50-1.20mm of the drill bit for needing to be cleaned, it is necessary to the model specification of the sand grains selected is 220#,
The pressure for needing the sandblasting selected is 0.50-0.65Mpa, it is necessary to the ultrasonic wave working strength selected is 60%-80% such that it is able to
Ensure that the drill bit of a diameter of 0.50-1.20mm is quick and effective when sandblasting cleaning is carried out.
Embodiment five:
As a diameter of 1.20-3.175mm of the drill bit for needing to be cleaned, it is necessary to the model specification of the sand grains selected is 180#
Or 220#, it is necessary to select sandblasting pressure be 0.60-0.75Mpa, it is necessary to select ultrasonic wave working strength be 65%-85%,
Drill bit so as to ensure a diameter of 1.20-3.175mm is quick and effective when sandblasting cleaning is carried out.
Embodiment six:
When the drill bit for needing to be cleaned it is a diameter of more than 3.20mm when, it is necessary to the sand grains selected model specification for 150# or
220#, it is necessary to select sandblasting pressure be 0.64-0.79Mpa, it is necessary to select ultrasonic wave working strength be more than 75%, from
And ensure that the drill bit with diameter greater than 3.20mm is quick and effective when sandblasting cleaning is carried out.
Above is preferable implementation of the invention is illustrated, but the invention is not limited in above-mentioned embodiment party
Formula, those of ordinary skill in the art can also make a variety of equivalent variations or replace on the premise of without prejudice to spirit of the invention
Change, these equivalent deformations or replacement are all contained in the application claim limited range.
Claims (9)
1. it is used to turn over the sandblasting cleaning procedure of crusher drill, it is characterised in that:Including following process step:
A, the drill bit to needing to be cleaned are classified, according to the different sand grains using different model specification of drill bit species;
B, blasting treatment is carried out to drill bit at different angles;
C, the drill bit by blasting treatment is positioned in water, drill bit is cleaned with reference to the effect of ultrasonic wave;
D, the mode dried up using compressed air or the drying effect using drier are dried treatment to drill bit;
E, arrangement is carried out to the drill bit by dried process turn over mill.
2. the sandblasting cleaning procedure for turning over crusher drill according to claim 1, it is characterised in that:Enter in the step B
Capable blasting treatment, comprises the following steps:
A1, drill bit is positioned in sand-blasting machine;
B1, the different pressure for adjusting sandblastings according to bite type, make impulsive force during sandblasting meet the requirement that is hit of drill bit;
C1, sandblasting is carried out to drill bit, and constantly the direction of adjustment drill bit makes its each several part be subject to blasting treatment.
3. the sandblasting cleaning procedure for turning over crusher drill according to claim 1, it is characterised in that:It is right in the step E
Mill is turned in the arrangement that drill bit is carried out, and is comprised the following steps:
A2, the knife edge part of drill bit is carried out turning over mill using mill;
B2, the knife edge part to drill bit carry out DLC coating treatments.
4. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
Clean drill bit it is a diameter of less than 150um when, the model specification of the sand grains of selection is 400#, and the pressure of the sandblasting of selection is
0.25-0.35Mpa, the ultrasonic wave working strength of selection is 30%-45%.
5. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
During a diameter of 0.15-0.25mm of clean drill bit, the model specification of the sand grains of selection is 320#, and the pressure of the sandblasting of selection is
0.30-0.40Mpa, the ultrasonic wave working strength of selection is 40%-55%.
6. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
During a diameter of 0.25-0.45mm of clean drill bit, the model specification of the sand grains of selection is 280#, and the pressure of the sandblasting of selection is
0.40-0.55Mpa, the ultrasonic wave working strength of selection is 50%-75%.
7. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
During a diameter of 0.50-1.20mm of clean drill bit, the model specification of the sand grains of selection is 220#, and the pressure of the sandblasting of selection is
0.50-0.65Mpa, the ultrasonic wave working strength of selection is 60%-80%.
8. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
During a diameter of 1.20-3.175mm of clean drill bit, the model specification of the sand grains of selection is 180# or 220#, the sandblasting of selection
Pressure is 0.60-0.75Mpa, and the ultrasonic wave working strength of selection is 65%-85%.
9. the sandblasting cleaning procedure for turning over crusher drill according to claim 2, it is characterised in that:The needs carry out clear
Clean drill bit it is a diameter of more than 3.20mm when, the model specification of the sand grains of selection is 150# or 220#, the pressure of the sandblasting of selection
Power is 0.64-0.79Mpa, and the ultrasonic wave working strength of selection is more than 75%.