CN107988612A - The method of high-efficiency washing aluminum alloy part - Google Patents
The method of high-efficiency washing aluminum alloy part Download PDFInfo
- Publication number
- CN107988612A CN107988612A CN201711289252.0A CN201711289252A CN107988612A CN 107988612 A CN107988612 A CN 107988612A CN 201711289252 A CN201711289252 A CN 201711289252A CN 107988612 A CN107988612 A CN 107988612A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy part
- part surface
- ultrasonic wave
- frequency
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method of high-efficiency washing aluminum alloy part, including step:A, with medal polish lapping liquid grinding aluminum alloy part surface;B, aluminum alloy part is soaked in 30 45s in organic solvent, aluminum alloy part surface is wiped with Beaver;C, using ultrasonic cleaning aluminum alloy part surface 30s.The method of high-efficiency washing aluminum alloy part of the present invention, due to first using medal polish lapping liquid to grind, then wipes after being soaked with organic solvent, then using being cleaned by ultrasonic aluminum alloy part surface, easy to operate, effectively to remove washmarking, cleaning performance obvious.
Description
Technical field
The present invention relates to aluminum alloy part cleaning technique field.A kind of it is more particularly related to high-efficiency washing aluminium
The method of alloy part.
Background technology
Cleaning aluminum alloy remove be aluminium alloy part surface treatment in significant process, if aluminum alloy surface cleaning do not do
Only, then later processing work will be difficult to.Existing deoiling method can be divided into solvent oil removing, electrochemical deoiling, electrochemistry are removed
Oil etc., existing technical operation is complicated, cleaning performance is bad, influences follow-up process process.
The content of the invention
It is an object of the invention to solve at least the above, and provide the advantages of at least will be described later.
It is a still further object of the present invention to provide a kind of side of high-efficiency washing aluminum alloy part easy to operate, effect is good
Method.
In order to realize these purposes and further advantage according to the present invention, there is provided a kind of high-efficiency washing aluminum alloy part
Method, including step:A, with medal polish lapping liquid grinding aluminum alloy part surface;B, aluminum alloy part is soaked in organic molten
30-45s in agent, aluminum alloy part surface is wiped with Beaver;C, using ultrasonic cleaning aluminum alloy part surface 30s, ultrasound
30s's concretely comprises the following steps:S1:Use the ultrasonic wave 2s that frequency is 5W/mL for 10Khz and power;S2:Frequency is used as 15Khz
And the ultrasonic wave 3s that power is 5W/mL;S3:Use the ultrasonic wave 15s that frequency is 5W/mL for 20Khz and power;S4:Using frequency
The ultrasonic wave 5s that rate is 15Khz and power is 5W/mL;S5:Use the ultrasonic wave 5s that frequency is 5W/mL for 10Khz and power.
Preferably, before the step A, hydro-peening is carried out to aluminum alloy part surface with water, and use carbon dioxide
Aluminum alloy part surface is dried up.
Preferably, the organic solvent is hydrocarbon cleaning liquid.
Preferably, further included after the step C, hydro-peening is carried out to aluminum alloy part surface with water, and use titanium dioxide
Carbon gas dries up aluminum alloy part surface, then is dried.
Preferably, the temperature dried to aluminum alloy part surface is 100-110 DEG C, when the time is 2-4 small.
Preferably, in the step C, during using being cleaned by ultrasonic, in water temperature is 20-25 DEG C of 18,000,000 deionized waters
Carry out.
The present invention includes at least following beneficial effect:
The method of high-efficiency washing aluminum alloy part of the present invention, due to first using medal polish lapping liquid to grind, then is used
Wiped after organic solvent immersion, then using being cleaned by ultrasonic aluminum alloy part surface, it is easy to operate, can effectively remove washmarking, cleaning
Positive effect.
Further advantage, target and the feature of the present invention embodies part by following explanation, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Embodiment
With reference to embodiment, the present invention is described in further detail, to make those skilled in the art with reference to specification
Word can be implemented according to this.
It should be noted that experimental method described in following embodiments, is conventional method unless otherwise specified, institute
Reagent and material are stated, unless otherwise specified, is commercially obtained.
The present invention provides a kind of method of high-efficiency washing aluminum alloy part, including step:A, ground with medal polish lapping liquid
Grind aluminum alloy part surface;B, aluminum alloy part is soaked in 30-45s in organic solvent, aluminium alloy zero is wiped with Beaver
Part surface;C, using aluminum alloy part surface 30s is cleaned by ultrasonic, ultrasonic 30s's concretely comprises the following steps:S1:Frequency is used as 10Khz
And the ultrasonic wave 2s that power is 5W/mL;S2:Use the ultrasonic wave 3s that frequency is 5W/mL for 15Khz and power;S3:Using frequency
The ultrasonic wave 15s for being 5W/mL for 20Khz and power;S4:Use the ultrasonic wave 5s that frequency is 5W/mL for 15Khz and power;S5:
Use the ultrasonic wave 5s that frequency is 5W/mL for 10Khz and power.
Before the step A, hydro-peening is carried out to aluminum alloy part surface with water, and with carbon dioxide by aluminium alloy
Piece surface dries up.
The organic solvent is hydrocarbon cleaning liquid.
Further included after the step C, hydro-peening is carried out to aluminum alloy part surface with water, and will with carbon dioxide
Aluminum alloy part surface dries up, then is dried.
The temperature dried to aluminum alloy part surface is 100-110 DEG C, when the time is 2-4 small.
In the step C, during using being cleaned by ultrasonic, carried out in water temperature is 20-25 DEG C of 18,000,000 deionized waters.
Embodiment one
A kind of method of high-efficiency washing aluminum alloy part, including step:A, aluminium alloy zero is ground with medal polish lapping liquid
Part surface;B, aluminum alloy part is soaked in 30s in hydrocarbon cleaning liquid, aluminum alloy part surface is wiped with Beaver;C, adopt
With aluminum alloy part surface 30s is cleaned by ultrasonic, ultrasonic 30s's concretely comprises the following steps:S1:It for 10Khz and power is 5W/ to use frequency
The ultrasonic wave 2s of mL;S2:Use the ultrasonic wave 3s that frequency is 5W/mL for 15Khz and power;S3:Frequency is used as 20Khz and work(
Rate is the ultrasonic wave 15s of 5W/mL;S4:Use the ultrasonic wave 5s that frequency is 5W/mL for 15Khz and power;S5:Use frequency for
10Khz and the ultrasonic wave 5s that power is 5W/mL.
Before the step A, hydro-peening is carried out to aluminum alloy part surface with water, and with carbon dioxide by aluminium alloy
Piece surface dries up.
Further included after the step C, hydro-peening is carried out to aluminum alloy part surface with water, and will with carbon dioxide
Aluminum alloy part surface dries up, then is dried.
The temperature dried to aluminum alloy part surface is 100 DEG C, when the time is 2 small.
In the step C, during using being cleaned by ultrasonic, carried out in water temperature is 20 DEG C of 18,000,000 deionized waters.
Embodiment two
A kind of method of high-efficiency washing aluminum alloy part, including step:A, aluminium alloy zero is ground with medal polish lapping liquid
Part surface;B, aluminum alloy part is soaked in 30-45s in hydrocarbon cleaning liquid, aluminum alloy part surface is wiped with Beaver;C、
Using aluminum alloy part surface 30s is cleaned by ultrasonic, ultrasonic 30s's concretely comprises the following steps:S1:The frequency is used to be for 10Khz and power
The ultrasonic wave 2s of 5W/mL;S2:Use the ultrasonic wave 3s that frequency is 5W/mL for 15Khz and power;S3:Frequency is used as 20Khz
And the ultrasonic wave 15s that power is 5W/mL;S4:Use the ultrasonic wave 5s that frequency is 5W/mL for 15Khz and power;S5:Using frequency
The ultrasonic wave 5s that rate is 10Khz and power is 5W/mL.
Before the step A, hydro-peening is carried out to aluminum alloy part surface with water, and with carbon dioxide by aluminium alloy
Piece surface dries up.
Further included after the step C, hydro-peening is carried out to aluminum alloy part surface with water, and will with carbon dioxide
Aluminum alloy part surface dries up, then is dried.
The temperature dried to aluminum alloy part surface is 105 DEG C, when the time is 3 small.
In the step C, during using being cleaned by ultrasonic, carried out in water temperature is 22.5 DEG C of 18,000,000 deionized waters.
Embodiment three
A kind of method of high-efficiency washing aluminum alloy part, including step:A, aluminium alloy zero is ground with medal polish lapping liquid
Part surface;B, aluminum alloy part is soaked in 45s in hydrocarbon cleaning liquid, aluminum alloy part surface is wiped with Beaver;C, adopt
With aluminum alloy part surface 30s is cleaned by ultrasonic, ultrasonic 30s's concretely comprises the following steps:S1:It for 10Khz and power is 5W/ to use frequency
The ultrasonic wave 2s of mL;S2:Use the ultrasonic wave 3s that frequency is 5W/mL for 15Khz and power;S3:Frequency is used as 20Khz and work(
Rate is the ultrasonic wave 15s of 5W/mL;S4:Use the ultrasonic wave 5s that frequency is 5W/mL for 15Khz and power;S5:Use frequency for
10Khz and the ultrasonic wave 5s that power is 5W/mL.
Before the step A, hydro-peening is carried out to aluminum alloy part surface with water, and with carbon dioxide by aluminium alloy
Piece surface dries up.
Further included after the step C, hydro-peening is carried out to aluminum alloy part surface with water, and will with carbon dioxide
Aluminum alloy part surface dries up, then is dried.
The temperature dried to aluminum alloy part surface is 110 DEG C, when the time is 4 small.
In the step C, during using being cleaned by ultrasonic, carried out in water temperature is 25 DEG C of 18,000,000 deionized waters.
Although embodiment of the present invention is disclosed as above, it is not restricted in specification and embodiment listed
With it can be applied to various suitable the field of the invention completely, can be easily for those skilled in the art
Realize other modification, therefore under the universal limited without departing substantially from claim and equivalency range, it is of the invention and unlimited
In specific details and shown here as the embodiment with description.
Claims (6)
- A kind of 1. method of high-efficiency washing aluminum alloy part, it is characterised in that including step:A, with medal polish lapping liquid grinding aluminum alloy part surface;B, aluminum alloy part is soaked in 30-45s in organic solvent, aluminum alloy part surface is wiped with Beaver;C, using aluminum alloy part surface 30s is cleaned by ultrasonic, ultrasonic 30s's concretely comprises the following steps:S1:Use frequency for 10Khz and Power is the ultrasonic wave 2s of 5W/mL;S2:Use the ultrasonic wave 3s that frequency is 5W/mL for 15Khz and power;S3:Use frequency for 20Khz and the ultrasonic wave 15s that power is 5W/mL;S4:Use the ultrasonic wave 5s that frequency is 5W/mL for 15Khz and power;S5:Adopt The ultrasonic wave 5s that with frequency be 10Khz and power is 5W/mL.
- 2. the method for high-efficiency washing aluminum alloy part according to claim 1, it is characterised in that before the step A, Hydro-peening is carried out to aluminum alloy part surface with water, and is dried up aluminum alloy part surface with carbon dioxide.
- 3. the method for high-efficiency washing aluminum alloy part according to claim 1, it is characterised in that the organic solvent is Hydrocarbon cleaning liquid.
- 4. the method for high-efficiency washing aluminum alloy part according to claim 1, it is characterised in that after the step C Further include, hydro-peening is carried out to aluminum alloy part surface with water, and dried up aluminum alloy part surface with carbon dioxide, then into Row drying.
- 5. the method for high-efficiency washing aluminum alloy part according to claim 4, it is characterised in that to aluminum alloy part surface The temperature dried is 100-110 DEG C, when the time is 2-4 small.
- 6. the method for cleaning aluminum alloy parts according to claim 1, it is characterised in that in the step C, using super When sound cleans, carried out in 18,000,000 deionized waters that water temperature is 20-25 DEG C.