CN106854442A - High tenacity flame-retardant aluminium foil adhesive tape manufacturing process - Google Patents
High tenacity flame-retardant aluminium foil adhesive tape manufacturing process Download PDFInfo
- Publication number
- CN106854442A CN106854442A CN201611258875.7A CN201611258875A CN106854442A CN 106854442 A CN106854442 A CN 106854442A CN 201611258875 A CN201611258875 A CN 201611258875A CN 106854442 A CN106854442 A CN 106854442A
- Authority
- CN
- China
- Prior art keywords
- aluminium foil
- adhesive tape
- layer
- high tenacity
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process, wherein, the aluminium foil layers of a. first are preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；B. in the upper surface coating release agent of the first aluminium foil layer, the first fire retardant glue water layer is coated in the lower surface of the first aluminium foil layer；C. plastic film layers are pressed by lower surface in the first fire retardant glue water layer, as high tenacity aluminum foil and adhesive tape by pressure roller；D. the second aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；E. the lower surface in the second aluminium foil layer is coated with the 3rd fire retardant glue water layer, and heated drying；F. the second fire retardant glue water layer is coated with the upper surface of the second aluminium foil layer, the high tenacity aluminum foil and adhesive tape is pressed together on the upper surface of the second fire retardant glue water layer, as high tenacity flame-retardant aluminium foil adhesive tape by pressure roller；G. the lower surface in high tenacity flame-retardant aluminium foil adhesive tape is coated with primer layer, and winding, cutting obtains aluminum foil and adhesive tape finished product.
Description
Technical field
The present invention relates to a kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process.
Background technology
At present, conventional aluminium foil glue carries three kinds：First, there is aluminium-foil with paper lining adhesive tape, it is traditional aluminum foil and adhesive tape, it is
The multiple last layer release liners on aluminium foil rubberised layer, the release paper weight is in 80g/cm2More than, so there is the weight of aluminium-foil with paper lining adhesive tape
Amount is heavier, is made troubles to using or transporting；In addition, opening release liners, occupied ground is big later, and release liners are difficult back again
Receive and utilize, largely to use body paper, collateral damage earth environment.2nd, aluminium foil tape without lining paper, it be coated on aluminium foil it is release
Agent, but this adhesive tape when in use in order to increase the toughness of aluminum foil and adhesive tape and roll when fastness, often aluminium foil layer is set
Very thick, the waste aluminium foil resource of meter.3rd, laminated adhesive aluminium foil band, it is to bond aluminium foil and plastic sheeting, but this adhesive tape exists
Not easily openable when using, in-convenience in use.In process, existing process contamination weight, efficiency are low, and yield rate is low.
The content of the invention
It is an object of the invention to provide a kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process, to solve existing manufacturing process
The problem that efficiency is low, high cost, sticking effect are bad.
What the present invention was realized in：A kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process, wherein,
A. the first aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
B. in the upper surface coating release agent of the first aluminium foil layer, the first flame-retardant glue is coated in the lower surface of the first aluminium foil layer
Layer；
C. plastic film layers are pressed by lower surface in the first fire retardant glue water layer, as high tenacity aluminium foil glue by pressure roller
Band；
D. the second aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
E. the lower surface in the second aluminium foil layer is coated with the 3rd fire retardant glue water layer, and heated drying；
F. the second fire retardant glue water layer is coated with the upper surface of the second aluminium foil layer, by pressure roller by the high tenacity aluminum foil and adhesive tape
It is pressed together on the upper surface of the second fire retardant glue water layer, as high tenacity flame-retardant aluminium foil adhesive tape；
G. the lower surface in high tenacity flame-retardant aluminium foil adhesive tape is coated with primer layer, and winding, cutting obtains aluminum foil and adhesive tape finished product.
Drying temperature in the preferred step a is 100 DEG C~200 DEG C, a length of 4~20 meters of drying tunnel, and transfer rate is
15~20m/min.
Preferably, the drying temperature in the step d is 90 DEG C~150 DEG C, a length of 20~35 meters of drying tunnel, and transfer rate is
50~120m/min.
Using above-mentioned technical proposal, the present invention does not use lining paper, reduces overall weight, has saved paper, reduces
Cost.The present invention is provided with plastic sheeting as the support of aluminium foil, considerably increases the robustness and toughness of aluminum foil and adhesive tape.This hair
It is bright to be coated with mould release, it is easy to tear.Flame-retardant glue is provided with plastic film layers of the invention, aluminum foil and adhesive tape is provided with
Fire-retardant effect.The method can be widely used in the bonding of refrigerator, refrigerator-freezer, air-conditioning and building heat preservation pipeline and need to use aluminum foil and adhesive tape
The product of bonding.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, on the premise of not paying creative work, can be with
Other accompanying drawings are obtained according to these accompanying drawings.
Fig. 1 is structural representation of the invention.
In figure：1-parting agent layer, the 2-the first aluminium foil layer, the 3-the first fire retardant glue water layer, 4-plastic film layers, 5-the
Two fire retardant glue water layers, the 6-the second aluminium foil layer, the 7-the three fire retardant glue water layer, 8-primer layer.
Specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only section Example of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
As shown in figure 1, the parting agent layer 1 for including from top to bottom setting gradually of the invention, the first aluminium foil layer 2, first are fire-retardant
Glue layer 3, plastic film layers 4, the second fire retardant glue water layer 5, the second aluminium foil layer 6, the 3rd fire retardant glue water layer 7 and primer layer 8.
A kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process, it is characterized in that,
A. the first aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
B. in the upper surface coating release agent of the first aluminium foil layer, the first flame-retardant glue is coated in the lower surface of the first aluminium foil layer
Layer；
C. plastic film layers are pressed by lower surface in the first fire retardant glue water layer, as high tenacity aluminium foil glue by pressure roller
Band；
D. the second aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
E. the lower surface in the second aluminium foil layer is coated with the 3rd fire retardant glue water layer, and heated drying；
F. the second fire retardant glue water layer is coated with the upper surface of the second aluminium foil layer, by pressure roller by the high tenacity aluminum foil and adhesive tape
It is pressed together on the upper surface of the second fire retardant glue water layer, as high tenacity flame-retardant aluminium foil adhesive tape；
G. the lower surface in high tenacity flame-retardant aluminium foil adhesive tape is coated with primer layer, and winding, cutting obtains aluminum foil and adhesive tape finished product.
Drying temperature in the step a is 100 DEG C~200 DEG C, a length of 4~20 meters of drying tunnel, transfer rate is 15~
20m/min。
Drying temperature in the step d is 90 DEG C~150 DEG C, a length of 20~35 meters of drying tunnel, transfer rate is 50~
120m/min。
Claims (3)
1. a kind of high tenacity flame-retardant aluminium foil adhesive tape manufacturing process, it is characterized in that,
A. the first aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
B. in the upper surface coating release agent of the first aluminium foil layer, the first fire retardant glue water layer is coated in the lower surface of the first aluminium foil layer；
C. plastic film layers are pressed by lower surface in the first fire retardant glue water layer, as high tenacity aluminum foil and adhesive tape by pressure roller；
D. the second aluminium foil layer is preheated into drying tunnel, aluminium foil surface temperature is reached 100 DEG C~150 DEG C；
E. the lower surface in the second aluminium foil layer is coated with the 3rd fire retardant glue water layer, and heated drying；
F. the second fire retardant glue water layer is coated with the upper surface of the second aluminium foil layer, is pressed the high tenacity aluminum foil and adhesive tape by pressure roller
In the upper surface of the second fire retardant glue water layer, as high tenacity flame-retardant aluminium foil adhesive tape；
G. the lower surface in high tenacity flame-retardant aluminium foil adhesive tape is coated with primer layer, and winding, cutting obtains aluminum foil and adhesive tape finished product.
2. high tenacity flame-retardant aluminium foil adhesive tape manufacturing process according to claim 1, it is characterized in that, the baking in the step a
Dry temperature is 100 DEG C~200 DEG C, a length of 4~20 meters of drying tunnel, and transfer rate is 15~20m/min.
3. high tenacity flame-retardant aluminium foil adhesive tape manufacturing process according to claim 1, it is characterized in that, the baking in the step d
Dry temperature is 90 DEG C~150 DEG C, a length of 20~35 meters of drying tunnel, and transfer rate is 50~120m/min.