CN106854324A - A kind of wear-resistant floor tile and preparation method thereof - Google Patents
A kind of wear-resistant floor tile and preparation method thereof Download PDFInfo
- Publication number
- CN106854324A CN106854324A CN201611100891.3A CN201611100891A CN106854324A CN 106854324 A CN106854324 A CN 106854324A CN 201611100891 A CN201611100891 A CN 201611100891A CN 106854324 A CN106854324 A CN 106854324A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor tile
- wear
- pvc
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resistant floor tile and preparation method thereof, it is made up of following mass fraction formula components：50 parts of PVC40,35 parts of rosin foaming agent, 12 14 parts of fine sand, 15 25 parts of kaolin, 68 parts of calcium carbonate, 46 parts of sulfur-containing compound, 46 parts of polyethylene beads, 12 14 parts of white cement, 13 parts of plasticizer, 46 parts of epoxidized soybean oil, 57 parts of silver oxide, 46 parts of ethoxylated fat race alkylamine, 6 10 parts of pigment, present invention reduces cost, the stability of product has been heightened.
Description
Technical field
The present invention relates to floor tile field, in particular to a kind of wear-resistant floor tile and preparation method thereof.
Background technology
At present, with the continuous improvement of people's living standard, everybody require that more and more higher to healthy living environment,
PVC plastic floor has environment-friendly type very high due to it, is increasingly favored by people.Compared to wood floors, from product sheet
Body sees, PVC plastic floor has the advantages that uvioresistant, acid-alkali-corrosive-resisting, anti-olive be mothproof, good flame resistance, and non-skid property is good,
Walking safety and comfort；From from the point of view of environmental protection, environmental protection is nontoxic, and human body and environment are free from side effects, maintenance side
Just, usually cleaned with clear water, having if spot just can wiped clean well with erasing rubber.
The content of the invention
The invention provides a kind of wear-resistant floor tile and preparation method thereof, present invention reduces cost, product has been heightened
Stability.
To achieve the above object, the present invention provides following technical scheme：
A kind of wear-resistant floor tile and preparation method thereof, is made up of following mass fraction formula components：PVC 40-50 parts,
3-5 parts of rosin foaming agent, fine sand 12-14 parts, kaolin 15-25 parts, calcium carbonate 6-8 parts, sulfur-containing compound 4-6 parts, polyethylene
Pearl 4-6 parts, white cement 12-14 parts, plasticizer 1-3 parts, epoxidized soybean oil 4-6 parts, silver oxide 5-7 parts, ethoxylated fat race
Alkylamine 4-6 parts, pigment 6-10 parts.
Further：It is made up of following mass fraction formula components：40 parts of PVC, 3 parts of rosin foaming agent, 12 parts of fine sand, height
15 parts of ridge soil, 6 parts of calcium carbonate, 4 parts of sulfur-containing compound, 4 parts of polyethylene beads, 12 parts of white cement, 1 part of plasticizer, epoxidized soybean oil 4
Part, 5 parts of silver oxide, 4 parts of ethoxylated fat race alkylamine, 6 parts of pigment.
Further：It is made up of following mass fraction formula components：45 parts of PVC, 4 parts of rosin foaming agent, 13 parts of fine sand, height
20 parts of ridge soil, 7 parts of calcium carbonate, 5 parts of sulfur-containing compound, 5 parts of polyethylene beads, 13 parts of white cement, 2 parts of plasticizer, epoxidized soybean oil 5
Part, 6 parts of silver oxide, 5 parts of ethoxylated fat race alkylamine, 8 parts of pigment.
Further：It is made up of following mass fraction formula components：50 parts of PVC, 5 parts of rosin foaming agent, 14 parts of fine sand, height
25 parts of ridge soil, 8 parts of calcium carbonate, 6 parts of sulfur-containing compound, 6 parts of polyethylene beads, 14 parts of white cement, 3 parts of plasticizer, epoxidized soybean oil 6
Part, 7 parts of silver oxide, 6 parts of ethoxylated fat race alkylamine, 10 parts of pigment.
Further：Preparation method of the present invention has following steps：
Step one, by raw material according to aforementioned proportion distribute, it is standby；
Step 2, PVC, fine sand, kaolin are put into mixer successively, after stirring at low speed 15-25 minutes, added surplus
Remaining raw material, then carry out high-speed stirred 20-25 minutes, temperature control is obtained compound at 100-120 DEG C；
Step 3, extruder is added mixture into, the barrel zone temperature of extruder is 120-150 DEG C, the extrusion of extruder
Material places into tri-roll press machine, and the upper roller of tri-roll press machine, central roll, lower roll temperatures are respectively 140 DEG C, 152 DEG C, 145 DEG C, most
Floor tile finished product is obtained eventually.
The beneficial effects of the invention are as follows：
1st, present invention reduces cost, the stability of product has been heightened；
2nd, preparation method of the present invention is simple, reduces artificial operation, the generation beyond reduction；
3rd, frictional force of the present invention is strong, is not in the situation for sliding into tumble injury.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of wear-resistant floor tile is made up of following mass fraction formula components：PVC 40-50 parts, rosin foaming agent 3-5
Part, fine sand 12-14 parts, kaolin 15-25 parts, calcium carbonate 6-8 parts, sulfur-containing compound 4-6 parts, polyethylene beads 4-6 parts, white cement
12-14 parts, plasticizer 1-3 parts, epoxidized soybean oil 4-6 parts, silver oxide 5-7 parts, 4-6 parts of ethoxylated fat race alkylamine, face
6-10 parts of material.
Embodiment two：
A kind of wear-resistant floor tile is made up of following mass fraction formula components：It is 40 parts of PVC, 3 parts of rosin foaming agent, thin
Husky 12 parts, 15 parts of kaolin, 6 parts of calcium carbonate, 4 parts of sulfur-containing compound, 4 parts of polyethylene beads, 12 parts of white cement, 1 part of plasticizer, ring
4 parts of oxygen soybean oil, 5 parts of silver oxide, 4 parts of ethoxylated fat race alkylamine, 6 parts of pigment.
Embodiment three：
A kind of wear-resistant floor tile is made up of following mass fraction formula components：It is 45 parts of PVC, 4 parts of rosin foaming agent, thin
Husky 13 parts, 20 parts of kaolin, 7 parts of calcium carbonate, 5 parts of sulfur-containing compound, 5 parts of polyethylene beads, 13 parts of white cement, 2 parts of plasticizer, ring
5 parts of oxygen soybean oil, 6 parts of silver oxide, 5 parts of ethoxylated fat race alkylamine, 8 parts of pigment.
Example IV：
A kind of wear-resistant floor tile is made up of following mass fraction formula components：It is 50 parts of PVC, 5 parts of rosin foaming agent, thin
Husky 14 parts, 25 parts of kaolin, 8 parts of calcium carbonate, 6 parts of sulfur-containing compound, 6 parts of polyethylene beads, 14 parts of white cement, 3 parts of plasticizer, ring
6 parts of oxygen soybean oil, 7 parts of silver oxide, 6 parts of ethoxylated fat race alkylamine, 10 parts of pigment.
Embodiment five：
A kind of preparation method preparation method of wear-resistant floor tile comprises the following steps：
Step one, by raw material according to aforementioned proportion distribute, it is standby；
Step 2, PVC, fine sand, kaolin are put into mixer successively, after stirring at low speed 15-25 minutes, added surplus
Remaining raw material, then carry out high-speed stirred 20-25 minutes, temperature control is obtained compound at 100-120 DEG C；
Step 3, extruder is added mixture into, the barrel zone temperature of extruder is 120-150 DEG C, the extrusion of extruder
Material places into tri-roll press machine, and the upper roller of tri-roll press machine, central roll, lower roll temperatures are respectively 140 DEG C, 152 DEG C, 145 DEG C, most
Floor tile finished product is obtained eventually.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of wear-resistant floor tile, it is characterised in that：It is made up of following mass fraction formula components：
PVC 40-50 parts, 3-5 parts of rosin foaming agent, fine sand 12-14 parts, kaolin 15-25 parts, calcium carbonate 6-8 parts, Containing Sulfur
Compound 4-6 parts, polyethylene beads 4-6 parts, white cement 12-14 parts, plasticizer 1-3 parts, epoxidized soybean oil 4-6 parts, silver oxide 5-7
Part, 4-6 parts, pigment 6-10 parts of ethoxylated fat race alkylamine.
2. a kind of wear-resistant floor tile according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
40 parts of PVC, 3 parts of rosin foaming agent, 12 parts of fine sand, 15 parts of kaolin, 6 parts of calcium carbonate, 4 parts of sulfur-containing compound, polyethylene
4 parts of pearl, 12 parts of white cement, 1 part of plasticizer, 4 parts of epoxidized soybean oil, 5 parts of silver oxide, 4 parts of ethoxylated fat race alkylamine, face
6 parts of material.
3. a kind of wear-resistant floor tile according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
45 parts of PVC, 4 parts of rosin foaming agent, 13 parts of fine sand, 20 parts of kaolin, 7 parts of calcium carbonate, 5 parts of sulfur-containing compound, polyethylene
5 parts of pearl, 13 parts of white cement, 2 parts of plasticizer, 5 parts of epoxidized soybean oil, 6 parts of silver oxide, 5 parts of ethoxylated fat race alkylamine, face
8 parts of material.
4. a kind of wear-resistant floor tile according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
50 parts of PVC, 5 parts of rosin foaming agent, 14 parts of fine sand, 25 parts of kaolin, 8 parts of calcium carbonate, 6 parts of sulfur-containing compound, polyethylene
6 parts of pearl, 14 parts of white cement, 3 parts of plasticizer, 6 parts of epoxidized soybean oil, 7 parts of silver oxide, 6 parts of ethoxylated fat race alkylamine, face
10 parts of material.
5. a kind of a kind of preparation method of wear-resistant floor tile according to claim 1, it is characterised in that：Including following step
Suddenly：
Step one, by raw material according to aforementioned proportion distribute, it is standby；
Step 2, PVC, fine sand, kaolin are put into mixer successively, after stirring at low speed 15-25 minutes, added remaining former
Material, then carry out high-speed stirred 20-25 minutes, temperature control is obtained compound at 100-120 DEG C；
Step 3, extruder is added mixture into, the barrel zone temperature of extruder is 120-150 DEG C, and the extruded stock of extruder is again
Tri-roll press machine is put into, the upper roller of tri-roll press machine, central roll, lower roll temperatures are respectively 140 DEG C, 152 DEG C, 145 DEG C, final system
Obtain floor tile finished product.