CN106835851A - A kind of creped wrapping paper - Google Patents
A kind of creped wrapping paper Download PDFInfo
- Publication number
- CN106835851A CN106835851A CN201710020421.4A CN201710020421A CN106835851A CN 106835851 A CN106835851 A CN 106835851A CN 201710020421 A CN201710020421 A CN 201710020421A CN 106835851 A CN106835851 A CN 106835851A
- Authority
- CN
- China
- Prior art keywords
- oar
- paper
- wrapping paper
- drying
- creped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of creped wrapping paper, with waste paper as raw pulp, step includes:Immersion, broken oar of washing by water, stirring, Centrifugal vibration is separated, and defibrator is separated, and grinds oar, homogenate, copy paper, corrugation, drying, winding;Wet strength agent, the AKD sizing agents of 2.5~5.0 wt %, 0.1~1.5 wt % pigment of 2.0~3.0wt% are added during oar is ground, with the softening agent of 0.05~0.6 wt %, 0.1~1.0 organosilicon quaternary ammonium salts of the wt % with chain alkyl and 0.2~1.6 wt % sodium tripolyphosphates are added in homogenization process, wherein drying temperature is increased using two benches thermograde formula.Improve waste paper oar technique, increase the weight in wet base of wood pulp, significantly improve the uniformity of wet epistasis, tight ness rating and the thickness of creped wrapping paper.
Description
Technical field
The invention belongs to paper production technical field, and in particular to one kind is for being packed for creped wrapping paper.
Background technology
The auxiliary product that crimped paper is widely used as producing, manufactures, repairs, transporting etc..The requirement of crimped paper and be characterized in paper
Opening surface has obvious stretching lines, improves elongation.
Crimped paper divides medical and health use paper, general industry paper, the wherein raw material of Medical grade wrinkle paper again according to use requirement
The requirement such as selection and preparation method is higher, and notification number CN102400410A discloses a kind of medical creped wrapping paper mainly using drift
White softwood pulp, bleached hardwood pulp and HPZ special fibres are beaten through hydrabrusher size degradation, disc grinder according to a certain ratio, add
Plus the auxiliary material such as wet strength agent, sizing agent, softening agent, water repellent agent, in fourdrinier wire or the shaping of inclined wire wire multi-cylinder paper machine wet end, press dewatering, wet
Wet crepe is carried out in a cylinder when web dryness is 30~45%, heat drying is batched, rewind slitting finally by reel machine is received
Into medical creped wrapping paper product.Above-mentioned technical proposal makes the medical creped wrapping paper of production not produce paper scrap, paper powder etc. no
Good phenomenon.
And for general industry wrapping paper, so high, normal recuperable waste paper manufactures paper for the use requirement of paper
Oar, waste paper first with water immersion, separate impurity, then with high pressure water flushing it is broken, stir broken oar, then Centrifugal vibration separates impurity, finally
Increase the fiber content of wood pulp through Celloco fractionator Celloco, then just carry out the operation below such as mill oar, addition auxiliary agent.As obtained in waste paper
Wooden oar, one side raw material is the paper of various multi-forms, carton, and obtained wood pulp cellulose length is uneven, chopped fiber
Content is higher, once impurity is mixed into slurries or mill oar is insufficient, be easy to occur it is local reunite, make crimped paper surface uneven
It is even, and breed bacteria produces biogas;On the other hand, the wood pulp that reclaimed waste paper makes also is required to the thickness of paper, is otherwise existed
Easily there is crackle, and can also reduce the wet epistasis of crimped paper in Wrinkling.
The content of the invention
The technical problems to be solved by the invention are directed to above-mentioned prior art and provide a kind of creped wrapping paper, mainly for
Raw material improves the wet epistasis of paper, improves the equal of paper because employing partially recycled paper, wood pulp middle short fiber content slurries high
Even property.
The present invention the used technical scheme that solves the above problems is:A kind of creped wrapping paper, with waste paper as raw pulp,
Step includes:Immersion, broken oar of washing by water, is stirred, and Centrifugal vibration is separated, and defibrator is separated, and grinds oar, and homogenate, copy paper wrinkles,
Drying, winding;Added during oar is ground the wet strength agent of 2.0~3.0wt%, the AKD sizing agents of 2.5~5.0 wt %, 0.1~
1.5 wt % pigment, and 0.05~0.6 wt % softening agent, in homogenization process add 0.1~1.0 wt % band chain alkyl
Organosilicon quaternary ammonium salt and 0.2~1.6 wt % sodium tripolyphosphates, wherein drying temperature using two benches thermograde formula increase.
Sodium tripolyphosphate is added in homogenization process, with good water-retaining property, the weight in wet base of wood pulp is improved.
It is described to grind oar oar degree to 40~65 ° of SR.
Preferably, organosilicon quaternary ammonium salt is selected from 3-(Trihydroxy silicyl)Propyl-dimethyl-octadecyl ammonium chloride or 3-
(Trihydroxy silicyl)Propyl-dimethyl-cetyl chloride ammonium.Chain alkyl organosilicone quaternary ammonium is added in homogenization process
Salt, on the one hand with good antibacterial action, prevents from growing biogas, and on the other hand the Special composition steric hindrance in wood pulp, prevents wood pulp
In chopped fiber itself reunite, and form absorption between hydroxyl on methoxyl group and fiber on its molecular end chain, equivalent to
Fibre length is increased, fiber is effectively kept, be not easy crackle occur in Wrinkling, the wet strong of wrapping paper is improve again
Property.Not allowing volatile, good stability, paper due to chain alkyl organosilicon quaternary ammonium salt after drying has excellent tight ness rating.
Specifically, the drying tube temperature of the drying temperature first stage is 55 DEG C, 65 DEG C, 75 DEG C, 85 DEG C, second stage
Drying tube temperature is 80 DEG C, 95 DEG C, 110 DEG C, 125 DEG C.
Compared with prior art, the advantage of the invention is that:The invention discloses one kind using reclaimed waste paper as production
The creped wrapping paper production method of raw material, for raw material defect in itself, increased homogenate operation, and by adding specificization
Reagent, short this defect of fiber in improvement waste paper oar are learned, and increases the weight in wet base of wood pulp, significantly improve the wet of creped wrapping paper
The uniformity of epistasis, tight ness rating and thickness.
Specific embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
By reclaimed waste paper such as newspaper, tobacco and wine packaging, express delivery box, books, chancery paper, printing picture album etc., through manually picking, then soak
Bubble, clears up plastics, broken oar of then washing by water, stirring, Centrifugal vibration separating and removing impurities, through defibrator in time in immersion process
Further impurity elimination, increases fiber content;Then oar is ground, wet strength agent, the AKD sizing agents of 2.5wt %, the 0.5wt of 2.0wt% is added
% pigment, and 0.6wt % SFI softening agents, mill oar more than 4 hours, mill oar oar degree to 40~65 ° of SR.Subsequently enter homogenate work
Sequence, adds the 3- of 0.5wt %(Trihydroxy silicyl)Propyl-dimethyl-octadecyl ammonium chloride and 1.0wt % trimerization phosphorus
Sour sodium, is homogenized two hours, and weight in wet base is 13g, then copy paper, creping doctor corrugation, is dried through continuous drying cylinder, and drying uses two benches
Thermograde formula heats up:The drying tube temperature of first stage is 55 DEG C, 65 DEG C, 75 DEG C, 85 DEG C, and the drying tube temperature of second stage is
80℃、95℃、110℃、125℃.Winding, cutting, packaging.
Embodiment 2
Reclaimed waste paper is soaked after hand picking, the plastics for floating, broken oar of then washing by water is cleared up in immersion process in time, and stir
Mix, Centrifugal vibration separating and removing impurities, through the further impurity elimination of defibrator(Gravel, nail, plastic film, cotton yarn, grass cuttings),
Increase fiber content;Then oar is ground, wet strength agent, the AKD sizing agents of 3.0 wt %, the 1.0wt % pigment of 2.2wt% is added, and
The SFI softening agents of 0.6wt %, mill oar more than 4 hours, mill oar oar degree to 40~65 ° of SR.Homogenate operation is subsequently entered, is added
The 3- of 0.8wt %(Trihydroxy silicyl)Propyl-dimethyl-octadecyl ammonium chloride and 0.5 wt % sodium tripolyphosphates, it is even
Slurry two hours, weight in wet base is 11g, then copy paper, creping doctor corrugation, is dried through continuous drying cylinder, and drying is using two benches temperature ladder
Degree formula heats up:The drying tube temperature of first stage is 55 DEG C, 65 DEG C, 75 DEG C, 85 DEG C, and the drying tube temperature of second stage is 80 DEG C, 95
℃、110℃、125℃.Winding, cutting, packaging.
The quality standard such as following table of above-described embodiment gained wrapping paper
In addition to the implementation, present invention additionally comprises having other embodiment, all use equivalents or equivalence replacement mode
The technical scheme of formation, all should fall within the scope of the hereto appended claims.
Claims (4)
1. a kind of creped wrapping paper, it is characterised in that:With waste paper as raw pulp, step includes:Immersion, broken oar of washing by water, stirring,
Centrifugal vibration is separated, and defibrator is separated, and grinds oar, homogenate, copy paper, corrugation, drying, winding;2.0 are added during oar is ground
The wet strength agent of~3.0wt%, the AKD sizing agents of 2.5~5.0 wt %, 0.1~1.5 wt % pigment, and 0.05~0.6 wt %
Softening agent, in homogenization process add 0.1~1.0 organosilicon quaternary ammonium salts of the wt % with chain alkyl and 0.2~1.6 wt %
Sodium tripolyphosphate, wherein drying temperature are increased using two benches thermograde formula.
2. creped wrapping paper according to claim 1, it is characterised in that:It is described to grind oar oar degree to 40~65 ° of SR.
3. creped wrapping paper according to claim 1, it is characterised in that:The organosilicon quaternary ammonium salt is selected from 3-(Trihydroxy
Silicyl)Propyl-dimethyl-octadecyl ammonium chloride or 3-(Trihydroxy silicyl)Propyl-dimethyl-cetyl
Ammonium chloride.
4. creped wrapping paper according to claim 1, it is characterised in that:The drying tube temperature of the drying temperature first stage
It it is 55 DEG C, 65 DEG C, 75 DEG C, 85 DEG C, the drying tube temperature of second stage is 80 DEG C, 95 DEG C, 110 DEG C, 125 DEG C.