CN106835472A - For the 150D facecloths of automotive trim epidermis - Google Patents
For the 150D facecloths of automotive trim epidermis Download PDFInfo
- Publication number
- CN106835472A CN106835472A CN201610977523.0A CN201610977523A CN106835472A CN 106835472 A CN106835472 A CN 106835472A CN 201610977523 A CN201610977523 A CN 201610977523A CN 106835472 A CN106835472 A CN 106835472A
- Authority
- CN
- China
- Prior art keywords
- treatment
- dye vat
- present
- speed
- facecloths
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to inner lining of automobile technology field, and in particular to for the 150D facecloths of automotive trim epidermis, including following technique：The first step：Fabric is weaved；Second step：Pre-treatment dye vat is washed；3rd step：Post processing sizing；The beneficial effects of the invention are as follows：The present invention is to arrange pin and Final finishing setting process by changing traditional knitting, epidermis base fabric is met pulling force, tear and the requirement of static load tensile strength, and reduction grammes per square metre and thickness can be reached again.Reduce use cost.
Description
Technical field
The present invention relates to inner lining of automobile technology field, the 150D one sides of automotive trim epidermis are particularly used for
Cloth.
Background technology
Automotive trim (Automotive Interior) is primarily referred to as the used automobile product of automotive interior repacking, relates to
And to the every aspect of automotive interior, such as automobile steering wheel cover, automobile cushion, automatic foot-mat, automobile perfume, automobile pendant,
Internal goods of furniture for display rather than for use, containing box etc. are all automotive trim products.Automotive trim described in our country, in fact in English
Interiors System.Because this partial automobile parts has certain dicoration, so common at present in the industry turn over
Translate and be all called " automotive trim ".But from English " Interiors ", we it is known that, this parts thereof not only only has
Decoration function, feature, security and engineering attribute involved by them are very abundant.Wherein automotive trim table
Dermatome must have specific pulling force, tear and static load tensile strength, and other specific physical property requirements according to different automobile types,
In Japanese auto project interior trim epidermis, need to such as reach physical property requirement and quality is qualified, the base fabric for using must will reach corresponding
Physical property standard specification, traditional handicraft is appeared in when meeting pulling force, tear and the requirement of the physical property such as static load tensile strength, is existed gram
Weighting, thickness are bigger than normal again, corresponding production cost situation higher.
Based on above reason, it is necessary to the new base fabric for automotive trim epidermis is devised, change by raw material
Enter, weaving process, the lifting of postfinishing process, develop meet Japanese auto project interior trim epidermis base fabric pulling force, tear and
While static load tensile strength, have in grammes per square metre and thickness and be significantly improved, reduce the cost of client, i.e., for automobile
The 150D facecloths of interior trim epidermis.
The content of the invention
In order to solve the technical problem that above-mentioned existing facecloth technique is present, the present invention is provided to automotive trim epidermis
150D facecloths.
The technical solution adopted for the present invention to solve the technical problems is：
For the 150D facecloths of automotive trim epidermis, including following technique：
The first step：Fabric is weaved.
Raw material：75D/72F DTY+30DOP
30D terylene mono-filaments；
Weaving board size：34 inches of diameter；
Knitting needle：Pin number is 28 pins/inch, and total needle amount is 2976 pieces；
Yarn is long：75D/72F DTY 14cm/50G
30DOP 6cm/50G
30D terylene mono-filament 18cm/50G, by that analogy.
Row's pin technique：
The mode of pin is arranged for A, B, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 80 DEG C, and the speed that heats up is 2 DEG C/min, and soaking time is 30 minutes, and soaking time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and cylinder is gone out to normal temperature；
3) cleaning machine is cleaned 2 times；
4) dewater treatment is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance treatment, was carried out according to order demand from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST
Material treatment.
2) heat treatment, Uneven Width width is set as 170cm during sizing, and oven temperature is 215 DEG C, and rotation speed of fan is 1000
Rev/min, speed is 20M/ minutes, overfeeding 25 of shaping, sizing thickness 1.5-3.0mm.
3) finished product clot treatment.
The beneficial effects of the invention are as follows：The present invention is to arrange pin and Final finishing setting process by changing traditional knitting,
Epidermis base fabric is met pulling force, tear and the requirement of static load tensile strength, reduction grammes per square metre and thickness can be reached again.Reduce
Use cost.
Brief description of the drawings
The present invention is further described with reference to the accompanying drawings and examples.
Fig. 1 is the knitting flow chart making of facecloth in the present invention；
Fig. 2 is pre-treatment dye vat washing process schematic diagram of the present invention；
Fig. 3 is present invention post processing sizing schematic flow sheet.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, it is right below in conjunction with drawings and Examples
The present invention is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and
It is not used in the restriction present invention.
As shown in Figure 1-Figure 3, the 150D facecloths for automotive trim epidermis of the present invention, including following technique：
The first step：Fabric is weaved.
Raw material：75D/72F DTY+30DOP
30D terylene mono-filaments；
Weaving board size：34 inches of diameter；
Knitting needle：Pin number is 28 pins/inch, and total needle amount is 2976 pieces；
Yarn is long：75D/72F DTY 14cm/50G
30DOP 6cm/50G
30D terylene mono-filament 18cm/50G, by that analogy.
Row's pin technique：
The mode of pin is arranged for A, B, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 80 DEG C, and the speed that heats up is 2 DEG C/min, and soaking time is 30 minutes, and soaking time is arrived, and is opened
Begin to lower the temperature, cooling speed is 3 DEG C/min, and cylinder is gone out to normal temperature；
3) cleaning machine is cleaned 2 times；
4) dewater treatment is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance treatment, was carried out according to order demand from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST
Material treatment.
2) heat treatment, Uneven Width width is set as 170cm during sizing, and oven temperature is 215 DEG C, and rotation speed of fan is 1000
Rev/min, speed is 20M/ minutes, overfeeding 25 of shaping, sizing thickness 1.5-3.0mm.
3) finished product clot treatment.
General principle of the invention, principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (1)
1. the 150D facecloths of automotive trim epidermis are used for, it is characterised in that including following technique：
The first step：Fabric is weaved.
Raw material：75D/72F DTY+30DOP
30D terylene mono-filaments；
Weaving board size：34 inches of diameter；
Knitting needle：Pin number is 28 pins/inch, and total needle amount is 2976 pieces；
Yarn is long：75D/72F DTY 14cm/50G
30DOP 6cm/50G
30D terylene mono-filament 18cm/50G, by that analogy.
Row's pin technique：
The mode of pin is arranged for A, B, by that analogy.
Second step：Pre-treatment dye vat is washed；
1) fabric enters dye vat；
2) dye vat temperature is set as 80 DEG C, and the speed that heats up is 2 DEG C/min, and soaking time is 30 minutes, and soaking time is arrived, and starts drop
Temperature, cooling speed is 3 DEG C/min, and cylinder is gone out to normal temperature；
3) cleaning machine is cleaned 2 times；
4) dewater treatment is carried out with dewaterer；
3rd step：Post processing sizing；
1) punishment in advance treatment, is carried out at punishment in advance according to order demand from fire retardant 509 or hydrophilic silicone oil finishing agent or stiffening agent SST
Reason.
2) heat treatment, Uneven Width width is set as 170cm during sizing, and oven temperature is 215 DEG C, and rotation speed of fan is 1000 revs/min
Clock, speed is 20M/ minutes, overfeeding 25 of shaping, sizing thickness 1.5-3.0mm.
3) finished product clot treatment.