CN106833337A - A kind of scratch resistance water-borne wood coating and preparation method thereof - Google Patents
A kind of scratch resistance water-borne wood coating and preparation method thereof Download PDFInfo
- Publication number
- CN106833337A CN106833337A CN201710099277.8A CN201710099277A CN106833337A CN 106833337 A CN106833337 A CN 106833337A CN 201710099277 A CN201710099277 A CN 201710099277A CN 106833337 A CN106833337 A CN 106833337A
- Authority
- CN
- China
- Prior art keywords
- scratch resistance
- parts
- agent
- coalescents
- wood coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of scratch resistance water-borne wood coating, by weight, including following weight portion component：70~95 parts of organosilicon-modified acrylic polyaminoester emulsion, 2~20 parts of deionized water, 0.1~0.2 part of defoamer, 0.1~0.3 part of wetting agent, 2~5 parts of coalescents, 1~5 part of scratch resistance auxiliary agent, 0.1~0.3 part of levelling agent, 0.1~0.7 part of thickener, 0.05~0.15 part of preservative.The invention also discloses a kind of preparation method of scratch resistance water-borne wood coating.The coating is environmentally friendly, have the advantages that hardness of film is high, richness is good, early stage anti-after-tackiness is good, scratch resistance, and the preparation method is simple, is adapted to industrialized production.
Description
Technical field
The invention belongs to technical field of paint preparation, and in particular to a kind of scratch resistance water-borne wood coating and its preparation side
Method.
Background technology
As people are to the high speed development of industry and going from bad to worse for environment, people realize gradually to the low-carbon environment-friendly of environment
Enhancing, the especially feature of environmental protection requirement to raw material in coating are higher, and the environmental regulation that current various countries formulate is all to volatility in coating
Organic compound (VOC) has strict limitation.
Woodwork coating has water-borne wood coating and solvent wood coatings.Water-borne wood coating and solvent wood coatings phase
Than, there is environmental protection, energy-conservation, safe and reliable, easy to use, thus the development of water-borne wood coating is contained very much in recent years
OK, but water-borne wood coating (one-component) generally existing that hardness of film is low, richness is poor, early stage anti-after-tackiness is poor, do not resist
The problems such as scuffing.
The content of the invention
In view of the defect that above-mentioned prior art is present, the purpose of the present invention is to propose to a kind of scratch resistance water-borne wood coating.
The coating is environmentally friendly, have the advantages that hardness of film is high, richness is good, early stage anti-after-tackiness is good, scratch resistance.Another mesh of the invention
Be to propose a kind of preparation method of scratch resistance water-borne wood coating.The preparation method is simple, is adapted to industrialized production.
The purpose of the present invention will be achieved by the following technical programs：
A kind of scratch resistance water-borne wood coating, by weight, including following weight portion component：Organic-silicon-modified propylene
70~95 parts of sour polyaminoester emulsion, 2~20 parts of deionized water, 0.1~0.2 part of defoamer, 0.1~0.3 part of wetting agent, film forming is helped
2~5 parts of agent, 1~5 part of scratch resistance auxiliary agent, 0.1~0.3 part of levelling agent, 0.1~0.7 part of thickener, preservative 0.05~0.15
Part.
A kind of above-mentioned scratch resistance water-borne wood coating, by weight, including following weight portion component：Organosilicon changes
75~90 parts of property acroleic acid polyurethane emulsion, 4~18 parts of deionized water, 0.12~0.18 part of defoamer, wetting agent 0.15~
0.25 part, 3~5 parts of coalescents, 2~4 parts of scratch resistance auxiliary agent, 0.15~0.25 part of levelling agent, 0.2~0.6 part of thickener is prevented
0.08~0.12 part of rotten agent.
Above-mentioned a kind of scratch resistance water-borne wood coating, by weight including the component of following weight portion：Organosilicon changes
78~85 parts of property acroleic acid polyurethane emulsion, 5~15 parts of deionized water, 0.14~0.16 part of defoamer, 0.2 part of wetting agent, into
4~5 parts of film auxiliary agent, 2~4 parts of scratch resistance auxiliary agent, 0.2 part of levelling agent, 0.3~0.5 part of thickener, 0.1 part of preservative.
A kind of preparation method according to above-mentioned scratch resistance water-borne wood coating, by organosilicon-modified acrylic polyaminoester emulsion
Input dispersion cylinder, sequentially adds deionized water, defoamer, wetting agent, coalescents and scratch resistance auxiliary agent, 1200r/ while stirring
Min disperses at a high speed, without shrinkage cavity phenomenon, levelling agent, thickener, preservative is then put into successively until in fineness plate upper scraping plate, stirs
Mix uniform, adjustment viscosity 80-100 seconds (applying 4 glasss of surveys), filtering and discharging is obtained final product.
A kind of preparation method of above-mentioned scratch resistance water-borne wood coating, the defoamer is Airex902W defoamers, institute
Wetting agent is stated for BYK341 wetting agents, the coalescents are OXFILM351 coalescents, the scratch resistance auxiliary agent is polyolefin
Aqueous dispersion, the levelling agent is EFKA-3772 levelling agents, and the thickener is RM-8W thickeners, and institute's Hu preservative is
Kathon CG.
A kind of preparation method of above-mentioned scratch resistance water-borne wood coating, the organosilicon-modified acrylic polyurethane copolymerization
Emulsion selects SY8908 emulsions.
Compared with prior art, a kind of scratch resistance water-borne wood coating that the present invention is provided and preparation method thereof, reaches
Have the technical effect that：Preparation method of the present invention is simple, is adapted to industrialized production, the water-borne wood coating environmental protection of preparation, with film
Hardness is high, richness is good, good early stage anti-after-tackiness, scratch resistance the advantages of；The present invention uses organosilicon-modified acrylic polyurethane
Emulsion has hardness high, and damage resistant is heat-resisting, water-tolerant, and rate of drying is fast, the features such as environmental pollution is small；Adopted in the present invention
OXFILM351 coalescents are a kind of low smell, the almost coalescents of Diamond Search, traditional coalescents such as alcohol ester,
It is water-soluble that glycol ethers have some, is partially interposed between the watery phase with high polymer, and OXFILM351 is insoluble in water,
And completely into polymer particle, this causes that OXFILM351 is more in hgher efficiency than traditional coalescents；Used in the present invention
Polyolefin aqueous dispersion is the organic particle aqueous dispersion based on alkene, in spherical, narrow particle distribution, particle warp
0.01-9.5 μm, 110-148 DEG C of softening point so that with good adhesion strength and early stage anti-after tack performance.
Below just in conjunction with the embodiments, specific embodiment of the invention is described in further detail, so that technical scheme is more
Should be readily appreciated that, grasp.
Specific embodiment
Below by specific embodiment, the present invention will be described, but the invention is not limited in this.In following embodiments
The experimental technique, unless otherwise specified, is conventional method；The reagent and material, unless otherwise specified, can be from business
Approach is obtained, and example below simultaneously is not used to limit the scope of the claims of the invention, all equivalence enforcements without departing from carried out by the present invention
Or change, it is intended to be limited solely by this patent protection domain.
Embodiment 1
A kind of scratch resistance water-borne wood coating, by weight, including following weight portion component：Organic-silicon-modified propylene
78 parts of sour polyaminoester emulsion, 14.85 parts of deionized water, 0.15 part of defoamer, 0.2 part of wetting agent, 4 parts of coalescents, scratch resistance
2 parts of auxiliary agent, 0.2 part of levelling agent, 0.5 part of thickener, 0.1 part of preservative.
A kind of scratch resistance water-borne wood coating, is prepared from by following mass parts by following preparation methods：By organosilicon
78 parts of input dispersion cylinders of modified acrylic polyurethane emulsion, sequentially add 14.85 parts of deionized water, defoamer 0.15 while stirring
2 parts of part, 0.2 part of wetting agent, 4 parts of coalescents and scratch resistance auxiliary agent, dispersion (1200rpm/min) is until on fineness plate at a high speed
Then scraper plate puts into 0.2 part of levelling agent, 0.5 part of thickener, 0.1 part of preservative successively without shrinkage cavity phenomenon, stirs, and adjusts
Viscosity 80-100 seconds (applying 4 glasss of surveys), filtering and discharging is obtained final product.
Defoamer is Foamex810 in this example, and wetting agent is Wet KL245, and coalescents are OXFILM351, anti-zoned
Hinder auxiliary agent for polyolefin aqueous dispersion, levelling agent is EFKA-3772, and thickener is RM-2020, and preservative is Kathon CG, is had
Machine fluorine-silicon modified acrylic polyurethane copolymerization emulsion is from the SY8908 emulsions for having row shark (Shanghai) Science and Technology Co., Ltd..
Embodiment 2
A kind of scratch resistance water-borne wood coating, by weight, including following weight portion component：Organic-silicon-modified propylene
82 parts of sour polyaminoester emulsion, 10.05 parts of deionized water, 0.15 part of defoamer, 0.2 part of wetting agent, 4 parts of coalescents, scratch resistance
3 parts of auxiliary agent, 0.2 part of levelling agent, 0.3 part of thickener, 0.1 part of preservative.
A kind of scratch resistance water-borne wood coating, is prepared from by following mass parts by following preparation methods：
By 82 parts of input dispersion cylinders of organosilicon-modified acrylic polyaminoester emulsion, deionization is sequentially added under stirring
3 parts of 10.05 parts of water, 0.15 part of defoamer, 0.2 part of wetting agent, 4 parts of coalescents and scratch resistance auxiliary agent, disperse at a high speed
(1200rpm/min) until in fineness plate upper scraping plate without shrinkage cavity phenomenon.Then 0.2 part of levelling agent, thickener 0.3 are put into successively
Part, 0.1 part of preservative, are stirred, adjustment viscosity 80-100 seconds (applying 4 glasss of surveys), and filtering and discharging is obtained final product.
Defoamer is Foamex810 in this example, and wetting agent is Wet KL245, and coalescents are OXFILM351, anti-zoned
Hinder auxiliary agent for polyolefin aqueous dispersion, levelling agent is EFKA-3772, and thickener is RM-2020, and preservative is Kathon CG, is had
Machine fluorine-silicon modified acrylic polyurethane copolymerization emulsion is from the SY8908 emulsions for having row shark (Shanghai) Science and Technology Co., Ltd..
Embodiment 3
A kind of scratch resistance water-borne wood coating, by weight, including following weight portion component：Organic-silicon-modified propylene
85 parts of sour polyaminoester emulsion, 5.55 parts of deionized water, 0.15 part of defoamer, 0.2 part of wetting agent, 4.5 parts of coalescents, scratch resistance
4 parts of auxiliary agent, 0.2 part of levelling agent, 0.3 part of thickener, 0.1 part of preservative.
A kind of scratch resistance aqueous woodware paint, is prepared from by following mass parts by following preparation methods：Organosilicon is changed
Property 85 parts of input dispersion cylinders of acroleic acid polyurethane emulsion, 5.55 parts of deionized water is sequentially added under stirring, defoamer
0.15 part, 0.2 part of wetting agent, 4 parts of 4.5 parts of coalescents and scratch resistance auxiliary agent, dispersion (1200rpm/min) is until thin at a high speed
Degree plate upper scraping plate is without shrinkage cavity phenomenon.Then 0.2 part of levelling agent, 0.3 part of thickener, 0.1 part of preservative are put into successively, and stirring is equal
It is even, adjustment viscosity 80-100 seconds (applying 4 glasss of surveys), filtering and discharging is obtained final product.
Defoamer is Foamex810 in this example, and wetting agent is Wet KL245, and coalescents are OXFILM351, anti-zoned
Hinder auxiliary agent for polyolefin aqueous dispersion, levelling agent is EFKA-3772, and thickener is RM-2020, and preservative is Kathon CG, is had
Machine fluorine-silicon modified acrylic polyurethane copolymerization emulsion is from the SY8908 emulsions for having row shark (Shanghai) Science and Technology Co., Ltd..
Comparative example 1
Difference from Example 1 is that organosilicon-modified acrylic polyaminoester emulsion replaces with commercially available conventional propylene yogurt
Liquid.
Comparative example 2
Difference from Example 1 is that polyolefin aqueous dispersion replaces with micronizing wax class scratch resistance auxiliary agent.
Comparative example 3
Difference from Example 1 is that OXFILM351 coalescents replace with the Texanol of alcohol ester 12.
Through inspection, both film-formation results show that the consumption of OXFILM35 coalescents need to only reach organic in embodiment 1
The 5% of fluorine-silicon modified acrylic polyaminoester emulsion can reach preferable low temperature (less than 10 DEG C) film-formation result, and work as OXFILM35
Coalescents equivalent does not reach effect during using OXFILM351 then when changing 12 Texanol of alcohol ester into, it is impossible to complete film forming.
Furthermore, proved through substantial amounts of experiment, the amount of the Texanol of alcohol ester 12 to be added to more than the 7% of emulsion content reach it is good low
Warm film-formation result, but paint film can be caused to feel like jelly when Texanol dosages are excessive, hardness does not reach requirement.
Scratch resistance water-borne wood coating prepared by embodiment 1-3, comparative example 1-2 is carried out by the method that GB/T9279 specifies
Test, test result is as follows：
The scratch resistance water-borne wood coating performance testing index result of table 1
As shown in Table 1, have hardness high using organosilicon-modified acrylic polyaminoester emulsion, damage resistant is heat-resisting, water-fast
Property, rate of drying is fast, the features such as environmental pollution is small；Add the good adhesion strength of polyolefin aqueous dispersion physical efficiency and morning
Phase anti-after tack performance；
Described above has shown and described some preferred embodiments of the invention, but as previously described, it should be understood that the present invention
Be not limited to form disclosed herein, be not to be taken as the exclusion to other embodiment, and can be used for various other combinations,
Modification and environment, and can be in invention contemplated scope described herein, by above-mentioned teaching or the technology or knowledge of association area
It is modified.And the change and change that those skilled in the art are carried out do not depart from the spirit and scope of the present invention, then all should be in this hair
In the protection domain of bright appended claims.
Claims (6)
1. a kind of scratch resistance water-borne wood coating, it is characterised in that by weight, including following weight portion component：It is organic
70~95 parts of fluorine-silicon modified acrylic polyaminoester emulsion, 2~20 parts of deionized water, 0.1~0.2 part of defoamer, wetting agent 0.1~
0.3 part, 2~5 parts of coalescents, 1~5 part of scratch resistance auxiliary agent, 0.1~0.3 part of levelling agent, 0.1~0.7 part of thickener, anti-corrosion
0.05~0.15 part of agent.
2. a kind of scratch resistance water-borne wood coating according to claim 1, it is characterised in that by weight, including such as
The component of lower weight portion：75~90 parts of organosilicon-modified acrylic polyaminoester emulsion, 4~18 parts of deionized water, defoamer 0.12
~0.18 part, 0.15~0.25 part of wetting agent, 3~5 parts of coalescents, 2~4 parts of scratch resistance auxiliary agent, levelling agent 0.15~0.25
Part, 0.2~0.6 part of thickener, 0.08~0.12 part of preservative.
3. a kind of scratch resistance water-borne wood coating according to claim 2, it is characterised in that by weight, including such as
The component of lower weight portion：78~85 parts of organosilicon-modified acrylic polyaminoester emulsion, 5~15 parts of deionized water, defoamer 0.14
~0.16 part, 0.2 part of wetting agent, 4~5 parts of coalescents, 2~4 parts of scratch resistance auxiliary agent, 0.2 part of levelling agent, thickener 0.3~
0.5 part, 0.1 part of preservative.
4. a kind of preparation method of the scratch resistance water-borne wood coating according to claim any one of 1-3, it is characterised in that will
Organosilicon-modified acrylic polyaminoester emulsion puts into dispersion cylinder, sequentially adds deionized water while stirring, defoamer, wetting agent,
Coalescents and scratch resistance auxiliary agent, 1200r/min disperse at a high speed, until in fineness plate upper scraping plate without shrinkage cavity phenomenon, then successively
Input levelling agent, thickener, preservative, are stirred, adjustment viscosity 80-100 seconds (applying 4 glasss of surveys), and filtering and discharging is obtained final product.
5. a kind of preparation method of scratch resistance water-borne wood coating according to claim 4, it is characterised in that the froth breaking
Agent is Airex902W defoamers, and the wetting agent is BYK341 wetting agents, and the coalescents are OXFILM351 coalescents,
The scratch resistance auxiliary agent is polyolefin aqueous dispersion, and the levelling agent is EFKA-3772 levelling agents, and the thickener is
RM-8W thickeners, the preservative is Kathon CG.
6. the preparation method of a kind of scratch resistance water-borne wood coating according to claim 5, it is characterised in that described organic
Fluorine-silicon modified acrylic polyurethane copolymerization emulsion selects SY8908 emulsions.