CN106832223B - The black paste generated in vitamin B6 industrial processes is in anticorrosive paint as the application of curing agent - Google Patents
The black paste generated in vitamin B6 industrial processes is in anticorrosive paint as the application of curing agent Download PDFInfo
- Publication number
- CN106832223B CN106832223B CN201611248444.2A CN201611248444A CN106832223B CN 106832223 B CN106832223 B CN 106832223B CN 201611248444 A CN201611248444 A CN 201611248444A CN 106832223 B CN106832223 B CN 106832223B
- Authority
- CN
- China
- Prior art keywords
- film
- epoxy resin
- black cream
- naoh
- hcl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Application the present invention relates to the black paste generated in a kind of vitamin B6 industrial processes (hereinafter referred to as black cream) as the curing agent component of anticorrosive paint, the black paste generated in vitamin B6 industrial processes and epoxy resin reaction product are applied to metal surface, at a certain temperature solidification drying and forming-film barrier chemical reagent with reach corrosion-resistant purpose the beneficial effects of the invention are as follows for vitamin B6 waste residue resource reutilization and to the effective anti-corrosion of metal, industrial effective income is improved, while solving environmental issue.
Description
Technical field
The present invention relates to trade waste resource technology fields, more particularly to a kind of vitamin B6 industrial processes
Application of the black paste (hereinafter referred to as black cream) of middle generation as the curing agent component of anticorrosive paint.
Background technology
The phenomenon that metal is damaged by chemistry or the electrochemical action of surrounding medium referred to as metal erosion.With society
It can develop and industrial technological advancement, the use scope of metal is more and more extensive, and corrosion of metal problem has spread national economy
Every field, according to the investigation statistics of World Developed Countries, every year since direct losses caused by corrosion account for about national economy production
The 2.5%~4.2% of total value, and it is estimated that there are about 20% metal materials can not be recycled because being corroded in the world, thus
Corrosion of metal and protection question cause the most attention of countries in the world.In order to reduce the loss of corrosion, people take very
More measures, but safeguard measure or coating protection most universal, most economical, most practical so far, anticorrosion with coat are constructed with it
It is easy, economic and practical, not by device area, shape constraint and have the characteristics that certain decorative effect and widely answered
With.
Chemical industry equipment preserving method:(1) method (3) electrical anticorrosion method of method (2) face coat of environmental treatment.
The present invention is mainly to consider that the method for face coat carrys out anti-corrosion.
Corrosion mechanism can substantially be divided into three classes:Chemical attack, physics corruption candle, electrochemistry corruption candle
Mainly there are three aspects for the anticorrosion mechanism of anticorrosive paint:The passivation corrosion inhibition of matrix, Isolated Shield are acted on and
Form electro-chemical protection
Refer to changing the surface property of matrix, for example pass through the pigment in paint coatings to the passivation corrosion inhibition of matrix
Change, its matrix current potential is made to be moved towards positive direction, thus metal begins to be passivated, and can thus play the mesh for delaying corrosion
's.
Isolated Shield acts on, and is the coating by being formed in metal base surface, is just forming one in metal base surface
A barrier layer can be isolated and shield the medium such as contact of oxygen gas and water and acid-alkali salt with metallic matrix, to reach to Metal Substrate
The purpose of body protection.
Electro-chemical protection is formed, is by the way that current potential metal packing more more negative than parent metal is added in anticorrosive paint
Such as zinc powder or aluminium powder, when there is coating of the electrolyte through Isolated Shield to penetrate into metal surface, such electronegative metals
Filler just forms battery with metallic matrix, and sacrifice dissolving occurs first is the metal packing as anode, such metallic matrix
Just protect, to have the function that matrix protect, this kind of coating thus be sacrificial anticorrosive paint.
Invention content
The technical problem to be solved by the present invention is to provide a kind of more carboxylic class solid wastes of polyamines for the above-mentioned prior art to exist
As the application of curing agent in anticorrosive paint, the remaining waste residue that vitamin B6 is produced in industrial production can be efficiently used, and right
The effective anti-corrosion of metal equipment.
The technical solution adopted in the present invention is:The black paste generated in vitamin B6 industrial processes is in anti-corrosion
As the application of curing agent in coating.
By said program:The black paste generated in vitamin B6 industrial processes is reacted into generation with epoxy resin
Object is applied to metal surface, cures drying and forming-film at a certain temperature and obstructs chemical reagent to reach corrosion-resistant purpose.
By said program:Solidification temperature is 120~150 DEG C.
By said program:Hardening time is 30~60min.
By said program:The black paste and asphalt mixtures modified by epoxy resin generated in the added vitamin B6 industrial processes of reaction
Fat mass ratio is 3:1~1:3.
By said program, it is characterised in that:The black paste and asphalt mixtures modified by epoxy resin generated in vitamin B6 industrial processes
Fat reaction temperature is that 0.5-5h is first heated at 50-90 DEG C, improves temperature to 60-200 DEG C of heating 0.5-3h.
One of concrete scheme is:Black cream and 1,2-PD are added in the reaction vessel, after black cream is completely dissolved,
It is added in the epoxy resin to reaction vessel of corrresponding quality for 1: 1 according to the mass ratio of black cream and epoxy resin, in 90 DEG C of oil
2h is stirred in bath, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.
The beneficial effects of the invention are as follows for vitamin B6 waste residue resource reutilization and to the effective anti-corrosion of metal, improve
Industrial effective income, while solving environmental issue.
Specific implementation mode
With reference to specific embodiment, the present invention will be described in detail.Following embodiment will be helpful to the skill of this field
Art personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the common skill of this field
For art personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to this hair
Bright protection domain.
Embodiment 1
Black cream (the black paste generated in vitamin B6 industrial processes of certain mass is added in four-hole boiling flask
The more carboxylic class solid wastes of object, mainly polyamines) and 1,2-PD, after black cream is completely dissolved, according to the matter of black cream and epoxy resin
Amount is added than 1: 1 in the epoxy resin to four-hole boiling flask of corrresponding quality, and 2h is stirred in 90 DEG C of oil bath pan, improves temperature extremely
180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in the tinplate sheet by polishing, washing, drying
On, it is quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film is 125 μm, then by iron
It is dry 30min in 130 DEG C of baking oven that piece, which is placed in temperature, after dried coating film, by the 2/3 of film be soaked in 10% HCl, 30%
NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl the anti-corrosion time be respectively 7d, 8d and
9d。
Embodiment 2
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 9d.
Embodiment 3
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 8d, 9d and 9d.
Embodiment 4
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 7d, 9d and 9d.
Embodiment 5
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 10d and 10d.
Embodiment 6
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 9d.
Embodiment 7
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 8d and 8d.
Embodiment 8
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 10d and 9d.
Embodiment 9
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 9d.
Embodiment 10
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 9d.
Embodiment 11
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 10d.
Embodiment 12
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 130 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 9d.
Embodiment 13
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 10d.
Embodiment 14
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d, 10d and 10d.
Embodiment 15
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 10d, 10d and 10d.
Embodiment 16
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively 9d, 9d and 10d.
Embodiment 17
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d, 10d and 10d.
Embodiment 18
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 19
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 20
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 21
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 22
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 23
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 24
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 140 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 25
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 26
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 27
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
With the mass ratio 1 of epoxy resin;3 add in the epoxy resin to four-hole boiling flask of corrresponding quality, are stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 30min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 28
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 29
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 40min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 30
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 50 DEG C of oil bath pan
2h is mixed, improves temperature to 60 DEG C of stirring 1h, until for use after viscosity is suitable.By the mixture of preparation be placed in by polishing, washing,
In dry tinplate sheet, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film is
125 μm, iron plate is then placed in temperature as dry 40min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is soaked in
10% HCl, 30% NaOH and 30% NaCl solution in see film variation.The anti-corrosion time in HCl, NaOH and NaCl
Respectively>10d,>10d and>10d.
Embodiment 31
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 32
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 33
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 50min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 34
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 1 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 35
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 2 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Embodiment 36
The black cream and 1,2-PD of certain mass are added in four-hole boiling flask, after black cream is completely dissolved, according to black cream
It adds in the epoxy resin to four-hole boiling flask of corrresponding quality with the mass ratio 1: 3 of epoxy resin, is stirred in 90 DEG C of oil bath pan
2h is mixed, improves temperature to 180 DEG C of stirring 1h, until for use after viscosity is suitable.The mixture of preparation is placed in by polishing, washing
In the tinplate sheet wash, dried, quickly and evenly brushed along direction in length and breadth in tinplate sheet using spreader, the thickness of film
It is 125 μm, iron plate is then placed in temperature as dry 60min in 150 DEG C of baking oven, after dried coating film, the 2/3 of film is impregnated
In 10% HCl, 30% NaOH and 30% NaCl solution in see film variation.In HCl, NaOH and NaCl when anti-corrosion
Between be respectively>10d,>10d and>10d.
Claims (1)
1. the black paste containing the more carboxylic substances of polyamines generated in vitamin B6 industrial processes is in anticorrosive paint
It is to contain the more carboxylic substances of polyamines by what is generated in vitamin B6 industrial processes as the application of epoxy curing agent
Black paste and epoxy resin reaction product be applied to metal surface, the added vitamin B6 industrial production mistake of reaction
The black paste containing the more carboxylic substances of polyamines generated in journey is 3 with epoxy resin mass ratio:1~1:3, in certain temperature
The lower solidification drying and forming-film of degree obstructs chemical reagent to reach corrosion-resistant purpose, is generated in the vitamin B6 industrial processes
The black paste containing the more carboxylic substances of polyamines and epoxy resin reaction temperature be that 0.5-5h is first heated at 50-90 DEG C, carry
High-temperature to 60-200 DEG C heating 0.5-3h;Solidification temperature is 120~150 DEG C, and hardening time is 30~60 min.