CN106826136A - A kind of stainless steel pipes production procedure - Google Patents
A kind of stainless steel pipes production procedure Download PDFInfo
- Publication number
- CN106826136A CN106826136A CN201710185890.1A CN201710185890A CN106826136A CN 106826136 A CN106826136 A CN 106826136A CN 201710185890 A CN201710185890 A CN 201710185890A CN 106826136 A CN106826136 A CN 106826136A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- steel tube
- cleaned
- production procedure
- inspection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of stainless steel pipes production procedure, comprise the following steps, first experimental material, then mark is marked, mechanically polished after finishing mark, then cleaned, then electrobrightening, by port shaping equating after the completion of polishing, then it is passivated, size is checked after the completion of passivation, is then placed in pure water cleaning drying in dust free room, surface roughness and oil are checked after drying, last packaging and storage, procedure of processing of the present invention is simple, and the product external surfaces light for processing is smooth, and light weight, it is easier to carry than traditional steel pipe.
Description
Technology field
The present invention relates to a kind of stainless steel pipes production procedure, belong to pipeline production technical field.
Background technique
In recent years, thin-walled stainless steel tube has obtained increasingly being widely applied in many industries such as chemical industry, medicine, light industry, uses
Various stainless steel hot-rollings, cold rolling stainless steel tube is widely used in the stainless steel knot of oil, chemical industry equipment pipeline and various uses
Structure part, it is all to ensure that the water pressure test is qualified as the steel pipe for bearing Fluid pressure except should ensure that chemical composition and mechanical performance,
In recent years, developed to cavitation direction with mitigating the Axle Parts of weight, these hollow parts are in tube axial direction variation in diameter shape
Shape is more, but tube reducing phenomenon occurs because tube outer diameter is smaller than mold for molding position internal diameter, but this method meeting for mitigating weight
Occur rupture, and surface spikes phenomenon.
The content of the invention
Goal of the invention:In order to overcome the rupture embathed, and surface spikes problem, the present invention provides a kind of stainless steel pipes
Production procedure
Process program:The present invention discloses a kind of stainless steel pipes production procedure, comprises the following steps:
The first step:Inspection raw material, the raw material are stainless steel tube;
Second step:The stainless steel tube mark that will be verified is marked;
3rd step:Stainless steel tube is mechanically polished, is polished flat stainless steel pipe surface is rough, then cleaned;
4th step:By stainless steel tube electrobrightening, stainless steel tube is put into electrolytic cell, passes to direct current ionization reaction and produced
The anodic solution of selectivity, trickle burr is removed by stainless steel pipe surface;
5th step:By the shaping equating of stainless steel tube port, then it is passivated, HNO3 liquid is used to acid-washing stainless steel passivation,
Corrosion inhibiter such as Lan-826,93 DEG C of temperature, time 6h, temperature:121 DEG C, time:6h, then with hot water injection and immerses 10mg/L
In ammonium hydroxide+100mg/L hydrazines;
6th step, drying is cleaned by the stainless steel tube after passivation, then checks size;
7th step:Stainless steel tube after the assay was approved, is put into 100 grades of dust free room, is cleaned with pure water and dried up, diseases caused by external factors inspection after drying
Test, surface roughness is checked, oil content inspection;
8th step:After the assay was approved dust free room pack, double casing, it is interior vacuumize, be finally put in storage.
Procedure of processing of the present invention is simple, and the product external surfaces light for processing is smooth, and light weight, than traditional steel pipe more
Easily carry.
Further, during the electrobrightening electrolytic cell using sulfuric acid, phosphoric acid, hydrofluoric acid and it is sweet be electrolysed, so
Layer protecting film can be formed in stainless steel pipe surface by grease.
Brief description of the drawings
Fig. 1:The structured flowchart of the present embodiment stainless steel pipes production procedure.
Specific embodiment
The present invention is further elaborated below in conjunction with accompanying drawing and by specific embodiment, it should be pointed out that:For this technique
For the common process personnel in field, under the premise without departing from the principles of the invention, the various equivalent form of values of the invention are repaiied
Change and fall within the application appended claims limited range.
Embodiment 1:
A kind of stainless steel pipes production procedure as shown in Figure 1, comprises the following steps:
The first step:Inspection raw material, the raw material are stainless steel tube;
Second step:The stainless steel tube mark that will be verified is marked;
3rd step:Stainless steel tube is mechanically polished, sand papering stainless steel surfaces are used, by the polishing of stainless steel pipe surface projection
It is smooth, then cleaned;
4th step:By stainless steel tube electrobrightening, stainless steel tube is put into electrolytic cell, passes to direct current ionization reaction and produced
The anodic solution of selectivity, trickle burr is removed by stainless steel pipe surface, the electrolytic cell using sulfuric acid, phosphoric acid, hydrofluoric acid and
It is sweet to be electrolysed, so layer protecting film can be formed in stainless steel pipe surface by grease;
5th step:By the shaping equating of stainless steel tube port, then it is passivated, HNO3 liquid is used to acid-washing stainless steel passivation,
Corrosion inhibiter such as Lan-826,93 DEG C of temperature, time 6h, temperature:121 DEG C, time:6h, then with hot water injection and immerses 10mg/L
In ammonium hydroxide+100mg/L hydrazines;
6th step, drying is cleaned by the stainless steel tube after passivation, then checks size;
7th step:Stainless steel tube after the assay was approved, is put into 100 grades of dust free room, is cleaned with pure water and dried up, diseases caused by external factors inspection after drying
Test, surface roughness is checked, oil content inspection;
8th step:After the assay was approved dust free room pack, double casing, it is interior vacuumize, be finally put in storage.
Procedure of processing of the present invention is simple, and the product external surfaces light for processing is smooth, and light weight, than traditional steel pipe more
Easily carry.
Claims (2)
1. a kind of stainless steel pipes production procedure, it is characterised in that comprise the following steps:
The first step:Inspection raw material, the raw material are stainless steel tube;
Second step:The stainless steel tube mark that will be verified is marked;
3rd step:Stainless steel tube is mechanically polished, is polished flat stainless steel pipe surface is rough, then cleaned;
4th step:By stainless steel tube electrobrightening, stainless steel tube is put into electrolytic cell, passes to direct current ionization reaction and produced
The anodic solution of selectivity, trickle burr is removed by stainless steel pipe surface;
5th step:By the shaping equating of stainless steel tube port, then it is passivated, HNO3 liquid is used to acid-washing stainless steel passivation,
Corrosion inhibiter such as Lan-826,93 DEG C of temperature, time 6h, temperature:121 DEG C, time:6h, then with hot water injection and immerses 10mg/L
In ammonium hydroxide+100mg/L hydrazines;
6th step, drying is cleaned by the stainless steel tube after passivation, then checks size;
7th step:Stainless steel tube after the assay was approved, is put into 100 grades of dust free room, is cleaned with pure water and dried up, diseases caused by external factors inspection after drying
Test, surface roughness is checked, oil content inspection;
8th step:After the assay was approved dust free room pack, double casing, it is interior vacuumize, be finally put in storage.
2. a kind of stainless steel pipes production procedure according to claim 1, it is characterised in that electricity during the electrobrightening
Solution groove is using sulfuric acid, phosphoric acid, hydrofluoric acid and sweet is electrolysed.