CN106824994A - Shell class waste material turns to the process of road engineering material - Google Patents
Shell class waste material turns to the process of road engineering material Download PDFInfo
- Publication number
- CN106824994A CN106824994A CN201710081640.3A CN201710081640A CN106824994A CN 106824994 A CN106824994 A CN 106824994A CN 201710081640 A CN201710081640 A CN 201710081640A CN 106824994 A CN106824994 A CN 106824994A
- Authority
- CN
- China
- Prior art keywords
- shell class
- discarded object
- road engineering
- class discarded
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the process that a kind of shell class waste material turns to road engineering material, including roughing, drying, broken, calcification, it is dehydrated and grinds;Calcification:Shell class discarded object after crushing pours into calcification pond, and to shell class discarded object quality quick lime is added in calcification pond, mechanical agitation is mixed the shell class discarded object and quick lime after crushing thoroughly, then adds water;Dehydration:By be stirred it is broken after shell class discarded object, quick lime and water blend take out, be laid in dry, the plane of cleaning, in natural environment drying >=1d;Blend is put into drying and dehydrating 1h 24h in thermostatic drying chamber after completing to spontaneously dry, thermostatic box temperature is 50 100 DEG C;Grind:After completing dehydration, blend is transferred to grinder, grinds to form size<0.6mm powder body materials, the powder body material for being ground can be used for road engineering material.Economy of the invention, environmental protection, scale, resource.
Description
Technical field
Material Field is handed over the invention belongs to disposition of solid waste and road engineering, a kind of shell class salvage property is related generally to
Source turns to the process of road engineering material.
Background technology
The seafood shell class discarded objects, only China's Along Zhejiang Coast such as global annual generation millions of tons shell, shrimp shell, crab shell
Annual production is just more than 100,000 tons of discarded objects.A large amount of shell class discarded object abandoneds cause the pressure of sternness to environment in environment.
Containing compositions such as abundant calcium carbonate, chitin, protein in shell class discarded object, feed can be processed into, for making
The shell class such as medicine, papermaking, construction material, but the processing in these zone materials and use cost mistake by shell class changing rejected material to useful resource
Height, thus digestion shell class discarded object amount it is minimum, most shell class discarded objects can only abandoned in environment.
Road engineering has the features such as extensive, simple, raw material are less demanding all the time, shell class discarded object high content
The portion of material that the roadbed of calcium carbonate and field of road, basic unit and road surface are used, such as flyash, lime, miberal powder etc.
Main component is close.Therefore, develop a kind of processing cost it is low, can resource shell class discarded object be on a large scale road engineering material
Process, existing lasting environment protection significance, has certain economy concurrently again.
The content of the invention
It is an object of the invention to be directed to above-mentioned the deficiencies in the prior art, there is provided a kind of shell class waste material turns to road
Engineering material process, this shell class waste material turns to road engineering material process can be by the shell big rule of class discarded object
Mould resource turns to road engineering material, the features such as with economic, environmental protection.
In order to realize the object of the invention, the technical scheme that this law is taken is:
Shell class waste material turns to the process of road engineering material, and its feature is comprised the following steps:It is roughing, drying, broken
Broken, calcification, it is dehydrated and grinds.
Further, the roughing step is:One or more in roughing shell class discarded object.
Further, the drying steps are:First shell class discarded object is dried in the shade under ventilated environment, environment temperature of drying in the shade is
10-25 DEG C, time span is 10d-30d;Shell class discarded object is put into 100 DEG C of -200 DEG C of baking ovens afterwards continues to dry 1h-5h.
Further, the destruction step is:To be carried out stoving process operation shell class discarded object take out, and with rush
Hammer is broken into fragment, and fragment size distribution ranges are 0-10mm.
Further, the calcification step is:Shell class discarded object after will be broken pours into calcification pond, is added in calcification pond
The quick lime of shell class discarded object quality 10%-50%, mechanical agitation mixes the shell class discarded object and quick lime after crushing, stirring thoroughly
5min-30min, stirring is with degree 1r-5r/s;Then water, amount of water are added>65% Lime Quality, stirs 30-180min, stirs
Mix speed 1r-30r/s.
Further, the dehydration is:By be stirred it is broken after shell class discarded object, quick lime and water blend
Take out, the plane for drying, cleaning is laid in, in natural environment drying >=1d;Complete that blend is put into constant temperature after spontaneously drying
Drying and dehydrating 1h-24h in drying box, thermostatic box temperature is 50-100 DEG C.
Further, the step that grinds is:After completing dehydration, blend is transferred to grinder, grinds to form chi
It is very little<0.6mm powder body materials, the powder body material for being ground can be used for road engineering material.
The present invention has advantages below:
(1) shell class discarded object characteristic and road engineering material performance have been had concurrently:Shell class discarded object in addition to also having a large amount of calcium carbonate,
Also containing a certain proportion of free water, with reference to water, and the organic matter such as chitin, protein, on the one hand for stable curing shell
Active ingredient-the calcium carbonate of class discarded object, furthermore the ingredients calcium carbonate of solidification is met road engineering material performance requirement, this
The techniques such as invention is with drying in the shade, dry, quick lime heat of hydration high temperature and calcification stabilize and solidify the carbon in shell class discarded object
Sour calcium component, and the material for meeting field of road requirement specification is processed into using broken, grinding technics.
(2) it is economical:The deep process such as feed, medicine are processed into compared to by shell class discarded object, the processing of this technique is simple,
Low cost.
(3) environmental protection:Compared to other shell class changing rejected material to useful resource processes, present invention process method does not introduce any
Additional chemical reagent and chemical materials, the quick lime only applied are also conventional engineering material, in the absence of problem of environmental pollution.This
Outward, extensive resource shell class discarded object is road engineering material, and field of road can be also greatly decreased to natural mineral aggregate
Consumption, beneficial to environmental protection.
Specific embodiment
Embodiment 1
The process that this shell class waste material turns to road engineering material is comprised the following steps:Roughing, drying, broken, calcium
Change, be dehydrated and grind.The roughing step is:One or more in roughing shell class discarded object.The drying steps are:First will
Shell class discarded object dries in the shade under ventilated environment, and environment temperature of drying in the shade is 10-25 DEG C, and time span is 10d-30d;Afterwards by shell class
Discarded object continues to dry 1h-5h in being put into 100 DEG C of -200 DEG C of baking ovens.The destruction step is:Stoving process behaviour will be carried out
The shell class discarded object of work takes out, and is broken into fragment with jump bit, and fragment size distribution ranges are 0-10mm.It is described
Calcification step is:Shell class discarded object after crushing pours into calcification pond, to addition shell class discarded object quality 10%-50% in calcification pond
Quick lime, mechanical agitation mix thoroughly it is broken after shell class discarded object and quick lime, stir 5min-30min, stirring is with degree 1r-5r/
s;Then water, amount of water are added>65% Lime Quality, stirs 30-180min, mixing speed 1r-30r/s.The dehydration step
Suddenly it is:By be stirred it is broken after shell class discarded object, quick lime and water blend take out, be laid in dry, the plane of cleaning,
In natural environment drying >=1d;Blend is put into drying and dehydrating 1h-24h, constant temperature in thermostatic drying chamber after completing to spontaneously dry
Spin manifold temperature is 50-100 DEG C.The step that grinds is:After completing dehydration, blend is transferred to grinder, ground to form
Size<0.6mm powder body materials, the powder body material for being ground can be used for road engineering material.
Claims (7)
1. shell class waste material turns to the process of road engineering material, and its feature is comprised the following steps:Roughing, drying,
Broken, calcification, it is dehydrated and grinds.
2. resource shell class discarded object according to claim 1 is road engineering material process, it is characterised in that institute
Stating roughing step is:One or more in roughing shell class discarded object.
3. resource shell class discarded object according to claim 1 is road engineering material process, it is characterised in that institute
Stating drying steps is:First shell class discarded object is dried in the shade under ventilated environment, environment temperature of drying in the shade is 10-25 DEG C, time span is
10d-30d;Shell class discarded object is put into 100 DEG C of -200 DEG C of baking ovens afterwards continues to dry 1h-5h.
4. resource shell class discarded object according to claim 1 is road engineering material process, it is characterised in that institute
Stating destruction step is:The shell class discarded object that stoving process operation will be carried out takes out, and is broken into jump bit broken
Thing, fragment size distribution ranges are 0-10mm.
5. resource shell class discarded object according to claim 1 is road engineering material process, it is characterised in that institute
Stating calcification step is:Shell class discarded object after crushing pours into calcification pond, to addition shell class discarded object quality 10%- in calcification pond
50% quick lime, mechanical agitation mixes the shell class discarded object and quick lime after crushing thoroughly, stirs 5min-30min, and stirring is with degree 1r-
5r/s;Then water, amount of water are added>65% Lime Quality, stirs 30-180min, mixing speed 1r-30r/s.
6. a kind of shell class waste material according to claim 1 turns to the process of road engineering material, its feature
It is that the dehydration is:By be stirred it is broken after shell class discarded object, quick lime and water blend take out, be laid in dry
Dry, cleaning plane, in natural environment drying >=1d;Blend is put into be dried in thermostatic drying chamber after completing to spontaneously dry and is taken off
Water 1h-24h, thermostatic box temperature is 50-100 DEG C.
7. a kind of shell class waste material according to claim 1 turns to the process of road engineering material, its feature
Grinding step described in being is:After completing dehydration, blend is transferred to grinder, grinds to form size<0.6mm powder materials
Material, the powder body material for being ground can be used for road engineering material.