CN106824715A - A kind of automobile brake disc short-term corrosion prevention processing method - Google Patents
A kind of automobile brake disc short-term corrosion prevention processing method Download PDFInfo
- Publication number
- CN106824715A CN106824715A CN201710013310.0A CN201710013310A CN106824715A CN 106824715 A CN106824715 A CN 106824715A CN 201710013310 A CN201710013310 A CN 201710013310A CN 106824715 A CN106824715 A CN 106824715A
- Authority
- CN
- China
- Prior art keywords
- brake disc
- automobile brake
- processing method
- minutes
- corrosion prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of automobile brake disc short-term corrosion prevention processing method, comprise the following steps:Step 1)Automobile brake disc is carried out into degreasing, cleaning treatment;Step 2)Automobile brake disc is preheated 30-50 seconds at 180 DEG C-200 DEG C;Step 3)Automobile brake disc great circle facade and automobile brake disc roundlet facade are sprayed with Dyclo paint, is then toasted 5-8 minutes at 180 DEG C-200 DEG C;Step 4)Automobile brake disc is toasted 30-35 minutes at 380 DEG C-400 DEG C, then natural cooling.The automobile brake disc processed using the method; it is prevented within the shipping storage cycle of about 30-90 days; the brake area and wheel rim mounting surface of automobile brake disc get rusty because of non-spray-on coating, it is ensured that the antiseptic power during brake disc shipping storage, reduce the anti-corrosion protection cost of brake disc.
Description
Technical field
The present invention relates to anti-corrosion of metal protection field, and in particular to a kind of automobile brake disc short-term corrosion prevention processing method.
Background technology
Automobile brake disc is universal only to carry out coating spraying anti-corrosion in great circle facade and roundlet facade, because automobile brake disc
Brake area and wheel rim mounting surface do not carry out spray-on coating anti-corrosion, cast iron base material directly it is exposed in atmosphere, in transport and storehouse
Cycle of deposit inside brake rubbing surface and wheel rim mounting surface easily get rusty, at present to drag friction more by the way of waterborne anti-rust oil is smeared
Face and wheel rim the mounting surface anti-corrosion within inventory cycle, but painting antirust oil can increase parts cost, and smear lack of homogeneity, anti-corrosion
Effect on driving birds is not good.
The content of the invention
It is an object of the invention to provide a kind of automobile brake disc short-term corrosion prevention processing method, it is prevented from about 30-90
In it shipping storage cycle, the brake area and wheel rim mounting surface of automobile brake disc get rusty because of non-spray-on coating, it is ensured that
Antiseptic power during brake disc shipping storage, reduces the anti-corrosion protection cost of brake disc.
A kind of automobile brake disc short-term corrosion prevention processing method of the present invention, it is comprised the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 30-50 seconds at 180 DEG C-200 DEG C, drying brake disc on moisture;
3)By step 2)Automobile brake disc great circle facade and automobile brake disc roundlet facade sprayed with Dyclo paint, so
Afterwards by brake disc at 180 DEG C-200 DEG C preliminary drying 5-8 minutes, be that sintering curing is prepared;
4)By step 3)Automobile brake disc at 380 DEG C-400 DEG C sintering curing 30-35 minutes, then natural cooling.
Further, the step 2)In 200 DEG C preheat 30 seconds.
Further, the step 3)In at 180 DEG C preliminary drying 5 minutes.
Further, the step 4)In at 390 DEG C sintering curing 30 minutes.
The beneficial effects of the invention are as follows:Due to by automobile brake disc at 380 DEG C -400 DEG C sintering curing, can in automobile
Brake disc surface forms the oxide-film of the ferroso-ferric oxide of black, and this oxide-film is the oxide of the iron of stabilization, possesses certain
Corrosion resistance, ensure that automobile brake disc possesses certain antiseptic power within the shipping storage cycle of about 30-90 days,
Avoid automobile brake disc causes to reprocess rust cleaning because getting rusty, and reduces manufacturing cost.
Brief description of the drawings
Fig. 1 is automobile brake disc anti-corrosion spray area schematic.
In figure, 1-automobile brake disc roundlet facade, 2-automobile brake disc rubbing surface, 3-automobile brake disc great circle facade,
4-automobile brake disc and wheel rim mating surface.
Specific embodiment
Embodiment 1:A kind of automobile brake disc short-term corrosion prevention processing method, comprises the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 30 seconds at 200 DEG C;
3)By step 2)Automobile brake disc great circle facade 3 and automobile brake disc roundlet facade 1 sprayed with Dyclo paint,
Automobile brake disc rubbing surface 2 and automobile brake disc are not sprayed with wheel rim mating surface 4, then preliminary drying 5 minutes at 180 DEG C;
4)By step 3)Automobile brake disc at 390 DEG C sintering curing 30 minutes, then natural cooling.
Embodiment 2:A kind of automobile brake disc short-term corrosion prevention processing method, comprises the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 50 seconds at 180 DEG C;
3)By step 2)Automobile brake disc great circle facade 3 and automobile brake disc roundlet facade 1 sprayed with Dyclo paint,
Automobile brake disc rubbing surface 2 and automobile brake disc are not sprayed with wheel rim mating surface 4, then preliminary drying 8 minutes at 200 DEG C;
4)By step 3)Automobile brake disc at 400 DEG C sintering curing 35 minutes, then natural cooling.
Embodiment 3:A kind of automobile brake disc short-term corrosion prevention processing method, comprises the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 40 seconds at 180 DEG C;
3)By step 2)Automobile brake disc great circle facade 3 and automobile brake disc roundlet facade 1 sprayed with Dyclo paint,
Automobile brake disc rubbing surface 2 and automobile brake disc are not sprayed with wheel rim mating surface 4, then preliminary drying 6 minutes at 190 DEG C;
4)By step 3)Automobile brake disc at 390 DEG C sintering curing 32 minutes, then natural cooling.
Embodiment 4:A kind of automobile brake disc short-term corrosion prevention processing method, comprises the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 45 seconds at 185 DEG C;
3)By step 2)Automobile brake disc great circle facade 3 and automobile brake disc roundlet facade 1 sprayed with Dyclo paint,
Automobile brake disc rubbing surface 2 and automobile brake disc are not sprayed with wheel rim mating surface 4, then preliminary drying 7 minutes at 195 DEG C;
4)By step 3)Automobile brake disc at 400 DEG C sintering curing 34 minutes, then natural cooling.
Embodiment described above is a kind of preferred version of this patent, and any formal limit is not made to this patent
System, also has other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (4)
1. a kind of automobile brake disc short-term corrosion prevention processing method, it is characterised in that:Comprise the following steps:
1)Automobile brake disc is carried out into degreasing, cleaning treatment;
2)By step 1)Automobile brake disc preheated 30-50 seconds at 180 DEG C-200 DEG C;
3)By step 2)Automobile brake disc great circle facade and automobile brake disc roundlet facade sprayed with Dyclo paint, so
Afterwards by brake disc at 180 DEG C-200 DEG C preliminary drying 5-8 minutes;
4)By step 3)Automobile brake disc at 380 DEG C-400 DEG C sintering curing 30-35 minutes, then natural cooling.
2. a kind of automobile brake disc short-term corrosion prevention processing method according to claim 1, it is characterised in that:The step 2)
In 200 DEG C preheat 30 seconds.
3. a kind of automobile brake disc short-term corrosion prevention processing method according to claim 1, it is characterised in that:The step 3)
In at 180 DEG C preliminary drying 5 minutes.
4. a kind of automobile brake disc short-term corrosion prevention processing method according to claim 1, it is characterised in that:The step 4)
In at 390 DEG C sintering curing 30 minutes.