CN106821030A - A kind of dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog and its production technology - Google Patents
A kind of dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog and its production technology Download PDFInfo
- Publication number
- CN106821030A CN106821030A CN201611242103.4A CN201611242103A CN106821030A CN 106821030 A CN106821030 A CN 106821030A CN 201611242103 A CN201611242103 A CN 201611242103A CN 106821030 A CN106821030 A CN 106821030A
- Authority
- CN
- China
- Prior art keywords
- coating
- material frame
- frame body
- dust
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog and its production technology, and the material frame that the grill is used to hold food materials includes：Material frame body；It is coated on antimicrobial coating, high-temperaure coating and the dust-proof coating of the material frame body internal surface successively from the inside to the outside；It is coated on corrosion-resistant finishes, salt-fog preventing coating, moisture barrier coatings and the automatic cleaning coating of the material frame body outer surface successively from the inside to the outside.The grill is designed by multicoat, possesses preferable antibacterial, dust-proof, Defend salt fog effect, and with self-cleaning function, long service life can be used polytype food, the barbecue of multi-form, and environmental protection and energy saving, low production cost is good in economic efficiency.
Description
Technical field
The invention belongs to hardware products production field, in particular it relates to a kind of dust-proof automatically cleaning of antibacterial high temperature resistant Defend salt fog
Grill and its production technology.
Background technology
Barbecue（barbecue）, it may be possible to the cooking method of mankind's most original, is to be heated with fuel and dry air, and handle
Heat food in the position that food is positioned in hot dry air a relatively thermal source.In general, barbecue is incited somebody to action on fire
Food（Mostly meat, seafood, vegetables）Cook to edible, therefore Taiwan is also referred to as barbecue；Modern society, it is many due to having
Plant with fiery mode, roast mode also gradually variation, develop various oven, barbecue rack, barbecue sauce etc..
Barbecue also turns into a kind of many people's party amusement and recreation mode or businesses in itself.No matter in Qiqihar or whole
Individual Asia, America and Europe, barbecue are typically as low as family, greatly to the collective activity of school and the collective of some company organizations
Activity.
And there is diversified form as the indispensable instrument of barbecue in grill, such as roasting grill of grilled grill, electricity etc., but
All there is a common fault in these grills, that is, carry the material disc of food after a period of time use, meeting is rotten because of reasons such as greasy dirts
Erosion, if now continuing on for barbecue, can influence food cleannes, and baking the food for taking can influence health of human body, such as change
Grill, then can increase barbecue cost.
For grill, the current country is primarily present following patent document：
Chinese patent Authorization Notice No.：CN205493600U, discloses a kind of environmental protection and energy saving lampblack-preventing barbecue rack, including by supporting leg
The table frame constituted with framework, and the barbecue support set with table frame split, the supporting leg are vertically set on each corner of framework
The oil groove that excess oil is roasted with frame parallel, for access is provided between lower section, and two neighboring supporting leg；The interior angle of the framework
It is provided with the bearing diagonal for accepting barbecue support；The barbecue support is to be spaced apart on pyramid-shaped structures, and each side
There is the bonding jumper with its base vertical.Barbecue support Design of the invention is pyramid-shaped structures, and during barbecue, pyramid burns
The bonding jumper of roasting side face distribution guides unnecessary edible oil to flow in the oil groove below framework, it is to avoid edible oil falls into charcoal fire
On, and then prevent the generation for altering fiery phenomenon, it is to avoid brochette is charred influence mouthfeel, more reduces the generation of dense smoke, and to reduce right
The pollution that environment is caused.However, the barbecue rack that the patent is provided, will roast merely by the change of structure and introduces oil with oil
Groove, but cannot avoid because of the grill corrosion phenomenon that other reasonses are produced.
The content of the invention
It is dust-proof from clearly it is an object of the invention to provide a kind of antibacterial high temperature resistant Defend salt fog to solve above-mentioned problem
Clean grill and its production technology, the grill are designed by multicoat, possess preferable antibacterial, dust-proof, Defend salt fog effect, and have
There is self-cleaning function, long service life can be used polytype food, the barbecue of multi-form, environmental protection and energy saving, production cost
It is low, it is good in economic efficiency.
To reach above-mentioned purpose, the technical scheme is that：
A kind of dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog, the material frame that the grill is used to hold food materials includes：Material
Frame body；It is coated on antimicrobial coating, high-temperaure coating and the dust-proof coating of the material frame body internal surface successively from the inside to the outside；
It is coated on the corrosion-resistant finishes of the material frame body outer surface, salt-fog preventing coating, moisture barrier coatings and from clear successively from the inside to the outside
Clean coating.
Further, the antimicrobial coating is nano-Ag particles antimicrobial coating.
Separately, the high-temperaure coating is polyvinyl chloride high-temperaure coating.
Separately have, the dust-proof coating is Nano-meter SiO_22Coating.
Again, the corrosion-resistant finishes is epoxy novolac coating.
Further, the salt-fog preventing coating is chlorinated polypropylene coating.
And, the moisture barrier coatings are polyurethane moisture barrier coatings.
Separately, the automatic cleaning coating is nano-TiO2Coating.
Again, the material disc body shape is disk or square, and surface sets grid or perforate.
Meanwhile, the present invention also provides a kind of production technology of the dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog, including such as
Lower step：
1) pre-treatment
Material frame body is taken, oil removing, rust cleaning, phosphatization, Passivation Treatment is carried out；
2) spray
2.1) by step 1) in material frame body feeding electrostatic sprayer after treatment, by table in shower nozzle correspondence material frame body
Face, covers material frame body outer surface, by nano-Ag particles powder, polyvinyl chloride high temperature resistant powder and Nano-meter SiO_22Powder is by interior
To material frame body internal surface is equably sprayed on successively outward, antimicrobial coating, resistance to height are sequentially formed in material frame body internal surface
Warm coating and dust-proof coating；
2.2) overturning step 2.1) material frame body after the completion of electrostatic spraying, material frame body outer surface correspondence shower nozzle hides
Interior surface, by pnenolic aldehyde epoxy powder, chlorinated polypropylene powder, polyurethane protection against the tide powder and nano-TiO2Powder by it is interior extremely
Material frame body outer surface is equably sprayed on successively outward, and corrosion-resistant finishes, anti-salt are sequentially formed in material frame body outer surface
Mist coating, moisture barrier coatings and automatic cleaning coating；
3) solidify
By step 2) the material frame body feeding baking oven after the completion of electrostatic spraying is heating and curing, and the temperature being heating and curing is 160 ~
180 DEG C, the time being heating and curing is 10 ~ 20min, is cooled to room temperature；
4) finishing polishing
Grinding process is carried out to the material frame body surface after curing process, makes surfacing, complete the antibacterial high temperature resistant resistance to
Corrode the production of guard.
Wherein, the material frame body internal surface is the one side of material frame body correspondence thermal source.
Separately, step 1) in phosphatization temperature be 60 ~ 70 DEG C, 15 ~ 20min of phosphating time；Step 2) in every layer of spraying of coating
30 ~ 40 DEG C of temperature, 50 ~ 60Kv of spray voltage, spray angle is 30 ~ 90 °, 0.3 ~ 0.5MPa of sprinkler pressure；Step 2) in every layer
Placed at room temperature after the completion of coating electrostatic spraying 1 ~ 2 hour.
The beneficial effects of the present invention are：
The grill material frame includes being coated on successively from the inside to the outside antimicrobial coating, the high temperature resistant of the material frame body internal surface
Coating and dust-proof coating；Be coated on successively from the inside to the outside the corrosion-resistant finishes of the material frame body outer surface, salt-fog preventing coating,
Moisture barrier coatings and automatic cleaning coating, material frame are designed by multicoat, possess preferable antibacterial, dust-proof, Defend salt fog effect, and have
There is self-cleaning function, long service life can be used polytype food, the barbecue of multi-form, environmental protection and energy saving, production cost
It is low, it is good in economic efficiency.
Brief description of the drawings
Fig. 1 is a kind of structural representation of the dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog provided by the present invention.
Specific embodiment
Below by specific embodiment, the present invention is described further, but embodiment is not intended to limit protection of the invention
Scope.
A kind of reference picture 1, dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog of the present invention, the grill is used to contain
The material frame for putting food materials includes：Material frame body 1；It is coated on the antibacterial of the inner surface of material frame body 1 successively from the inside to the outside
Coating 2, high-temperaure coating 3 and dust-proof coating 4；It is coated on the corrosion-resistant of the outer surface of material frame body 1 successively from the inside to the outside
Coating 5, salt-fog preventing coating 6, moisture barrier coatings 7 and automatic cleaning coating 8.
Further, the antimicrobial coating 2 is nano-Ag particles antimicrobial coating.
Separately, the high-temperaure coating 3 is polyvinyl chloride high-temperaure coating.
Separately have, the dust-proof coating 4 is Nano-meter SiO_22Coating.
Again, the corrosion-resistant finishes 5 is epoxy novolac coating.
Further, the salt-fog preventing coating 6 is chlorinated polypropylene coating.
And, the moisture barrier coatings 7 are polyurethane moisture barrier coatings.
Separately, the automatic cleaning coating 8 is nano-TiO2Coating.
Meanwhile, the present invention also provides a kind of production technology of the dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog, including such as
Lower step：
1) pre-treatment
Material frame body is taken, oil removing, rust cleaning, phosphatization, Passivation Treatment is carried out；
2) spray
2.1) by step 1) in the feeding electrostatic sprayer of material frame body 1 after treatment, by table in shower nozzle correspondence material frame body 1
Face, covers the outer surface of material frame body 1, by nano-Ag particles powder, polyvinyl chloride high temperature resistant powder and Nano-meter SiO_22Powder by
It is interior to being equably sprayed on material frame body internal surface successively outward, sequentially form antimicrobial coating 2, resistance in material frame body internal surface
High temperature coating 3 and dust-proof coating 4；
2.2) overturning step 2.1) material frame body 1 after the completion of electrostatic spraying, by the outer surface of material frame body 1 correspondence shower nozzle,
Inner surface is covered, by pnenolic aldehyde epoxy powder, chlorinated polypropylene powder, polyurethane protection against the tide powder and nano-TiO2Powder is by interior
To being equably sprayed on the outer surface of material frame body 1 successively outward, the outer surface of material frame body 1 sequentially form corrosion-resistant finishes 5,
Salt-fog preventing coating 6, moisture barrier coatings 7 and automatic cleaning coating 8；
3) solidify
By step 2) the feeding baking oven of material frame body 1 after the completion of electrostatic spraying is heating and curing, and the temperature being heating and curing is 160 ~
180 DEG C, the time being heating and curing is 10 ~ 20min, is cooled to room temperature；
4) finishing polishing
Grinding process is carried out to the material frame body surface after curing process, makes surfacing, complete the antibacterial high temperature resistant resistance to
Corrode the production of guard.
Wherein, the material frame body internal surface is the one side of material frame body correspondence thermal source.
Separately, step 1) in phosphatization temperature be 60 ~ 70 DEG C, 15 ~ 20min of phosphating time；Step 2) in every layer of spraying of coating
30 ~ 40 DEG C of temperature, 50 ~ 60Kv of spray voltage, spray angle is 30 ~ 90 °, 0.3 ~ 0.5MPa of sprinkler pressure；Step 2) in every layer
Placed at room temperature after the completion of coating electrostatic spraying 1 ~ 2 hour.
Again, the material disc body 1 is shaped as disk or square, and surface sets grid or perforate.
The dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog provided by the present invention and its production technology, it is used to hold
Carrying the material disc of food materials includes being coated on successively from the inside to the outside antimicrobial coating, the high-temperaure coating of the material frame body internal surface
And dust-proof coating；It is coated on corrosion-resistant finishes, salt-fog preventing coating, the protection against the tide of the material frame body outer surface successively from the inside to the outside
Coating and automatic cleaning coating, material disc are designed by multicoat, possess preferable antibacterial, dust-proof, Defend salt fog effect, and with certainly
Cleaning function, long service life can be used polytype food, the barbecue of multi-form, environmental protection and energy saving, low production cost, warp
Ji is profitable.
It should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although with reference to compared with
Good embodiment has been described in detail to the present invention, it will be understood by those within the art that, can be to the technology of invention
Scheme is modified or equivalent, and without deviating from the scope of technical solution of the present invention, it all should cover in power of the invention
In sharp claimed range.
Claims (10)
1. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog, it is characterised in that the grill is used to hold the thing of food materials
Bin includes：
Material frame body；
It is coated on antimicrobial coating, high-temperaure coating and the dust-proof coating of the material frame body internal surface successively from the inside to the outside；
Be coated on successively from the inside to the outside the corrosion-resistant finishes of the material frame body outer surface, salt-fog preventing coating, moisture barrier coatings and
Automatic cleaning coating.
2. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described anti-
Bacterium coating is nano-Ag particles antimicrobial coating.
3. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described resistance to
High temperature coating is polyvinyl chloride high-temperaure coating.
4. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described anti-
Dirt coating is Nano-meter SiO_22Coating.
5. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described resistance to
Corrosion resistant coating is epoxy novolac coating.
6. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described anti-
Salt fog coating is chlorinated polypropylene coating.
7. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that described anti-
Damp coating is polyurethane moisture barrier coatings.
8. the dust-proof automatically cleaning grill of a kind of antibacterial high temperature resistant Defend salt fog according to claim 1, it is characterised in that it is described from
Cleaning coating is nano-TiO2Coating.
9. a kind of production technology of the dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog as any one of claim 1 ~ 8,
It is characterised in that it includes following steps：
1) pre-treatment
Material frame body is taken, oil removing, rust cleaning, phosphatization, Passivation Treatment is carried out；
2) spray
2.1) by step 1) in material frame body feeding electrostatic sprayer after treatment, by table in shower nozzle correspondence material frame body
Face, covers material frame body outer surface, by nano-Ag particles powder, polyvinyl chloride high temperature resistant powder and Nano-meter SiO_22Powder is by interior
To material frame body internal surface is equably sprayed on successively outward, antimicrobial coating, resistance to height are sequentially formed in material frame body internal surface
Warm coating and dust-proof coating；
2.2) overturning step 2.1) material frame body after the completion of electrostatic spraying, material frame body outer surface correspondence shower nozzle hides
Interior surface, by pnenolic aldehyde epoxy powder, chlorinated polypropylene powder, polyurethane protection against the tide powder and nano-TiO2Powder by it is interior extremely
Material frame body outer surface is equably sprayed on successively outward, and corrosion-resistant finishes, anti-salt are sequentially formed in material frame body outer surface
Mist coating, moisture barrier coatings and automatic cleaning coating；
3) solidify
By step 2) the material frame body feeding baking oven after the completion of electrostatic spraying is heating and curing, and the temperature being heating and curing is 160 ~
180 DEG C, the time being heating and curing is 10 ~ 20min, is cooled to room temperature；
4) finishing polishing
Grinding process is carried out to the material frame body surface after curing process, makes surfacing, complete the antibacterial high temperature resistant resistance to
Corrode the production of guard.
10. a kind of production technology of the dust-proof automatically cleaning grill of antibacterial high temperature resistant Defend salt fog according to claim 9, its feature
Be, step 1) in phosphatization temperature be 60 ~ 70 DEG C, 15 ~ 20min of phosphating time；Step 2) in every layer of spraying temperature of coating 30 ~
40 DEG C, 50 ~ 60Kv of spray voltage, spray angle is 30 ~ 90 °, 0.3 ~ 0.5MPa of sprinkler pressure；Step 2) in every layer of coating electrostatic
Placed at room temperature after the completion of spraying 1 ~ 2 hour.