CN104551565A - Manufacturing method of thin steel plate pot - Google Patents
Manufacturing method of thin steel plate pot Download PDFInfo
- Publication number
- CN104551565A CN104551565A CN201410809514.1A CN201410809514A CN104551565A CN 104551565 A CN104551565 A CN 104551565A CN 201410809514 A CN201410809514 A CN 201410809514A CN 104551565 A CN104551565 A CN 104551565A
- Authority
- CN
- China
- Prior art keywords
- pot
- preparation
- thin steel
- steel sheet
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a thin steel plate pot. The manufacturing method comprises the following steps that S1, hot rolled steel plate materials are put into a pot mold and are subjected to rotating beating by a round bottom hammer; S2, a metal ball with a smooth surface is used for friction on the inner surface of a pot at high pressure; S3, the inner side surface of the pot is subjected to be polished; S4, metal paint is molten and atomized, and is then sprayed and coated onto the inner surface of the pot, and an alloy coating is formed on the inner surface of the pot; S5, a non-stick layer is coated and sprayed on the inner surface of the pot; S6, a heat insulation layer is coated and sprayed on the pot edge part at the outer surface of the pot. The manufacturing method has the advantages that holes on the inner surface of the pot body can be effectively reduced, and in addition, the inner surface has the advantages of wear resistance, smoothness, attractive appearance and non-sticky performance; through the arrangement of the heat insulation layer, the hand scald cannot easily occur when people use the pot, and important application values are realized.
Description
Technical field
The present invention relates to a kind of pot, be specifically related to a kind of preparation method of thin steel sheet non-stick cooker.
Background technology
Pot is the most general and conventional daily apparatus of daily life, as long as can say that the place of people must need the existence of pot.Because it is along with the life of people's every day, therefore, people are also higher with expectation to the requirement of pot.At present, pots a lot of on market still can not overcome the deficiency of sticky pot completely, and use time, pot edge place due to temperature higher, easily scald one's hand.
Summary of the invention
The object of this invention is to provide a kind of preparation method of thin steel sheet pot.The object of the invention is to be achieved through the following technical solutions:
A preparation method for thin steel sheet pot, the preparation method of described pot comprises the following steps:
S1: be placed on by hot-rolled steel plate in pot mould, rotates impact with round bottom hammer, forms the pot with fish scale flower;
S2: rub under the inner surface high pressure of pot by ganoid metal ball;
S3: polishing is carried out to the inner surface of pot;
S4: metallic paint is melted and is atomized, then be sprayed into the inner surface of pot, then form alloy coat at the inner surface of pot;
S5: spray antistick layer again at the inner surface of pot, this nonstick layer adopts non-stick resin spraying;
S6: at 3 ~ 5 centimeters spraying thermal insulation layers at the pot edge place of the outer surface of pot.
Further, in step S2, described metal ball comprises iron ball or steel ball.
Further, in step S4, the thickness of described alloy coat is 30 ~ 45 μm.
Further, in step S5, the thickness of described antistick layer is 40 ~ 45 μm.
Further, in step S6, the thickness of described thermal insulation layer is 80 ~ 120 μm.
The invention provides a kind of preparation method of thin steel sheet pot, its beneficial effect mainly had is: the method can effectively reduce the hole of inner surface of pot body, and makes inner surface have advantage that is wear-resisting, smooth, attractive in appearance and non-stick pan; Thermal insulation layer be arranged so that people are not easy to iron hand in use, it has important using value.
Detailed description of the invention
The preparation method of a kind of thin steel sheet pot described in the embodiment of the present invention, illustrates detailed description of the invention for specific experiment case below, should be appreciated that specific embodiment described herein only in order to explain the present invention, is not intended to limit the present invention.
Embodiment
The preparation method of thin steel sheet pot, comprises the following steps: S1: be placed on by hot-rolled steel plate in pot mould, rotates impact, impacts successively from four thoughtful centres, form the pot with fish scale flower with round bottom hammer; S2: under high pressure rub with the inner surface of ganoid metal ball at pot, some tiny spaces on surface are closed, and pressure can be 3 ~ 5Pa; Described metal ball can be iron ball, steel ball and other alloying pellet.S3: polishing is carried out to the inner surface of pot; S4: melted by metallic paint and be atomized, then be sprayed into the inner surface of pot, then form alloy coat at the inner surface of pot, like this spraying sooner evenly; The thickness of described alloy coat is 30 ~ 45 μm, preferably 40 μm; S5: spray antistick layer again at the inner surface of pot, this nonstick layer adopts non-stick resin spraying; The thickness of described antistick layer is 40 ~ 45 μm, preferably 42 ~ 43 μm; S6: at 3 ~ 5 centimeters spraying thermal insulation layers at the pot edge place of the outer surface of pot, 3 ~ 5 centimeters below namely from pot edge to it, concrete length can be determined according to the shape of pot; People are made to be not easy in use to iron hand.The thickness of described thermal insulation layer is 80 ~ 120 μm, preferably 100 μm.
The present invention is not limited to above-mentioned preferred forms; anyone can draw other various forms of products under enlightenment of the present invention; no matter but any change is done in its shape or structure; every have identical with the application or akin technical scheme, all drops within protection scope of the present invention.
Claims (5)
1. a preparation method for thin steel sheet pot, is characterized in that: the preparation method of described pot comprises the following steps:
S1: be placed on by hot-rolled steel plate in pot mould, rotates impact with round bottom hammer, forms the pot with fish scale flower;
S2: rub under the inner surface high pressure of pot by ganoid metal ball;
S3: polishing is carried out to the inner surface of pot;
S4: metallic paint is melted and is atomized, then be sprayed into the inner surface of pot, then form alloy coat at the inner surface of pot;
S5: spray antistick layer again at the inner surface of pot, this nonstick layer adopts non-stick resin spraying;
S6: at 3 ~ 5 centimeters spraying thermal insulation layers at the pot edge place of the outer surface of pot.
2. the preparation method of thin steel sheet pot according to claim 1, is characterized in that: in step S2, and described metal ball comprises iron ball or steel ball.
3. the preparation method of thin steel sheet pot according to claim 1, is characterized in that: in step S4, and the thickness of described alloy coat is 30 ~ 45 μm.
4. the preparation method of thin steel sheet pot according to claim 1, is characterized in that: in step S5, and the thickness of described antistick layer is 40 ~ 45 μm.
5. the preparation method of thin steel sheet pot according to claim 1, is characterized in that: in step S6, and the thickness of described thermal insulation layer is 80 ~ 120 μm.