CN106816240A - A kind of preparation method of acrylic glass fiber hose - Google Patents
A kind of preparation method of acrylic glass fiber hose Download PDFInfo
- Publication number
- CN106816240A CN106816240A CN201510889014.8A CN201510889014A CN106816240A CN 106816240 A CN106816240 A CN 106816240A CN 201510889014 A CN201510889014 A CN 201510889014A CN 106816240 A CN106816240 A CN 106816240A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylate
- glass fiber
- preparation
- reactive diluent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of acrylic glass fiber hose, comprise the following steps：S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into alkali-free glass fibre flexible pipe；Mixed in S2, selection acrylate, reactive diluent, initiator, auxiliary agent addition acetone solvent and be made Acrylic emulsion, wherein mass parts acrylate 65-75 parts, reactive diluent 20-30 parts, initiator 3-5 parts, auxiliary agent 0.1-0.3 parts；S3, obtained Acrylic emulsion in step S2 is coated on the glass fiber hose in S1, carries out heating, drying, be made F class B insulation flexible pipes, detected, be put in storage.The present invention is woven into pipe using alkali-free glass fibre, and is coated with heated drying of acrylate and is made F class B insulation flexible pipes, with reliable heat resistance, good electrical property, preferable flexibility, elasticity and flame-retarding characteristic.
Description
Technical field
The present invention relates to glassfiber insulation flexible pipe production technical field, more particularly to a kind of third
The preparation method of olefin(e) acid glass fiber hose.
Background technology
Glassfiber insulation flexible pipe is a kind of electric insulation product, is mainly used in electrical equipment and electrical row
Industry, being enclosed within carries out insulation protection outside terminal.Country's glass fiber hose is universal now
Produced using the method for the heated baking of solvent type insulated paint, its shortcoming has that " two is high by one
It is low ", i.e. highly energy-consuming, high pollution, poor efficiency.Insulating materials be both electric product have it is advanced
The key condition of technical indicator, is also important guarantor that electric product is capable of long-term safety reliability service
Card.In the process of manufacture of existing glass fiber insulating sleeve, after coated with resins
Glass fiber insulating sleeve carries out that curing operation is more complicated and solidification effect is bad, influences glass
The class of insulation of glass fibrous insulation sleeve pipe.
The content of the invention
A kind of defect problem in order to overcome above-mentioned prior art of the invention, there is provided acrylic glass
The preparation method of fiber hose, the method is woven into pipe using alkali-free glass fibre, and is coated with third
The heated drying of alkene acid ester resin is made F class B insulation flexible pipes, with reliable heat resistance, well
Electrical property, preferable flexibility, elasticity and flame-retarding characteristic.
To achieve the above object, the technical solution adopted by the present invention is：
A kind of preparation method of acrylic glass fiber hose, comprises the following steps：
S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into nothing
Alkali containing glass fibre flexible pipe；
S2, selection acrylate, reactive diluent, initiator, auxiliary agent add acetone molten
Mixed in agent and be made Acrylic emulsion, wherein mass parts acrylate 65-75
Part, reactive diluent 20-30 parts, initiator 3-5 parts, auxiliary agent 0.1-0.3 parts；
S3, the glass fibre that obtained Acrylic emulsion in step S2 is coated in S1 are soft
Guan Shang, carries out heating, drying, is made F class B insulation flexible pipes, is detected, is put in storage.
Further, 70 parts of acrylate in the S2,25 parts of reactive diluent,
4 parts of initiator, 0.2 part of auxiliary agent.
Further, the reactive diluent in the S2 is Isooctyl acrylate monomer, acrylic acid fourth
In ester, isodecyl acrylate, isobornyl acrylate mono-functional reactive's diluent it is a kind of with
On.
Further, the concentration of the reactive diluent is 50%-70%.
Further, the auxiliary agent in the S2 is levelling agent or defoamer.
Beneficial effects of the present invention：A kind of preparation method of acrylic glass fiber hose, the party
Method is woven into pipe using alkali-free glass fibre, and is coated with the heated drying of acrylate and is made
F class B insulation flexible pipes, with reliable heat resistance, good electrical property, preferable flexibility,
Elasticity and flame-retarding characteristic.
Specific embodiment
Embodiment 1
A kind of preparation method of acrylic glass fiber hose, comprises the following steps：
S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into nothing
Alkali containing glass fibre flexible pipe；
S2, selection acrylate, reactive diluent, initiator, auxiliary agent add acetone molten
Mixed in agent and be made Acrylic emulsion, wherein 65 parts of mass parts acrylate,
30 parts of reactive diluent, 5 parts of initiator, 0.3 part of auxiliary agent；Reactive diluent is acrylic acid
Different monooctyl ester, butyl acrylate, isodecyl acrylate, isobornyl acrylate mono-functional reactive
One or more of diluent, the concentration of reactive diluent is 50%；Auxiliary agent is levelling agent or disappears
Infusion；
S3, the glass fibre that obtained Acrylic emulsion in step S2 is coated in S1 are soft
Guan Shang, carries out heating, drying, is made F class B insulation flexible pipes, is detected, is put in storage.
Embodiment 2
A kind of preparation method of acrylic glass fiber hose, comprises the following steps：
S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into nothing
Alkali containing glass fibre flexible pipe；
S2, selection acrylate, reactive diluent, initiator, auxiliary agent add acetone molten
Mixed in agent and be made Acrylic emulsion, wherein 75 parts of mass parts acrylate,
20 parts of reactive diluent, 3 parts of initiator, 0.1 part of auxiliary agent；Reactive diluent is acrylic acid
Different monooctyl ester, butyl acrylate, isodecyl acrylate, isobornyl acrylate mono-functional reactive
One or more of diluent, the concentration of reactive diluent is 70%；Auxiliary agent is levelling agent or disappears
Infusion；
S3, the glass fibre that obtained Acrylic emulsion in step S2 is coated in S1 are soft
Guan Shang, carries out heating, drying, is made F class B insulation flexible pipes, is detected, is put in storage.
Embodiment 3
A kind of preparation method of acrylic glass fiber hose, comprises the following steps：
S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into nothing
Alkali containing glass fibre flexible pipe；
S2, selection acrylate, reactive diluent, initiator, auxiliary agent add acetone molten
Mixed in agent and be made Acrylic emulsion, wherein 70 parts of mass parts acrylate,
25 parts of reactive diluent, 4 parts of initiator, 0.2 part of auxiliary agent；Reactive diluent is acrylic acid
Different monooctyl ester, butyl acrylate, isodecyl acrylate, isobornyl acrylate mono-functional reactive
One or more of diluent, the concentration of reactive diluent is 60%；Auxiliary agent is levelling agent or disappears
Infusion；
S3, the glass fibre that obtained Acrylic emulsion in step S2 is coated in S1 are soft
Guan Shang, carries out heating, drying, is made F class B insulation flexible pipes, is detected, is put in storage.
A kind of preparation method of acrylic glass fiber hose, the method uses alkali-free glass fibre
Pipe is woven into, and is coated with the heated drying of acrylate and be made F class B insulation flexible pipes, had
Reliable heat resistance, good electrical property, preferable flexibility, elasticity and flame-retarding characteristic.
Embodiment described above is only that the preferred embodiment of the present invention is described, and
It is non-that the spirit and scope of the present invention are defined.The premise of design concept of the present invention is not being departed from
Under, all variations and modifications that this area ordinary person makes to technical scheme,
Protection scope of the present invention should be dropped into.
Claims (5)
1. a kind of preparation method of acrylic glass fiber hose, it is characterised in that：Including with
Lower step：
S1, choosing alkali-free glass fibre base pipe, to carry out full circle by logical base machine moulding, is woven into nothing
Alkali containing glass fibre flexible pipe；
S2, selection acrylate, reactive diluent, initiator, auxiliary agent add acetone molten
Mixed in agent and be made Acrylic emulsion, wherein mass parts acrylate 65-75
Part, reactive diluent 20-30 parts, initiator 3-5 parts, auxiliary agent 0.1-0.3 parts；
S3, the glass fibre that obtained Acrylic emulsion in step S2 is coated in S1 are soft
Guan Shang, carries out heating, drying, is made F class B insulation flexible pipes, is detected, is put in storage.
2. a kind of preparation method of acrylic glass fiber hose as claimed in claim 1,
It is characterized in that：70 parts of acrylate, 25 parts of reactive diluent in the S2, draw
4 parts of agent of hair, 0.2 part of auxiliary agent.
3. a kind of preparation method of acrylic glass fiber hose as claimed in claim 1,
It is characterized in that：Reactive diluent in the S2 is Isooctyl acrylate monomer, butyl acrylate,
One or more of isodecyl acrylate, isobornyl acrylate mono-functional reactive's diluent.
4. a kind of preparation method of acrylic glass fiber hose as claimed in claim 3,
It is characterized in that：The concentration of the reactive diluent is 50%-70%.
5. a kind of preparation method of acrylic glass fiber hose as claimed in claim 1,
It is characterized in that：Auxiliary agent in the S2 is levelling agent or defoamer.