CN106811960A - A kind of finishing technique for improving tricot de laine snug fit degree - Google Patents
A kind of finishing technique for improving tricot de laine snug fit degree Download PDFInfo
- Publication number
- CN106811960A CN106811960A CN201611209550.XA CN201611209550A CN106811960A CN 106811960 A CN106811960 A CN 106811960A CN 201611209550 A CN201611209550 A CN 201611209550A CN 106811960 A CN106811960 A CN 106811960A
- Authority
- CN
- China
- Prior art keywords
- laine
- tricot
- snug fit
- parts
- technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of finishing technique for improving tricot de laine snug fit degree, hydrophilic finiss technique is increased before dyeing and stamp processing technology, the hydroscopicity of tricot de laine can be effectively improved, prevention dyeing in advance and damage of the printing technology to fabric wettability, so as to reduce the friction level with skin;Antibacterial finishing process after dyeing and stamp can further improve the docile antibacterial ability of fabric, the postfinishing process that biology enzyme is combined with plasma can not only remove some residual slurries on tricot de laine, the softness of fabric is also effectively improved, so as to further increase the level of comfort of fabric.The present invention has the advantages that the fabrics feel soft after treatment, strength damage are small compared with common process, is prevented effectively from the generation to skin urtication sense phenomenon, comfort level enhancing.
Description
Technical field
The present invention relates to the Treatment technique for processing of fabric, more particularly to a kind of improve the whole of tricot de laine snug fit degree
Science and engineering skill.
Background technology
In recent years, the domestic various new finishing technique about Woolens' fabric is constantly shown one's talent, more particularly
For example antistatic easy nursing of functional treatment, three anti-, far-infrared negative-ion, antibacterial, moisture absorbing and sweat releasings, these techniques are strictly to impart
The many features of wool fabric, but an old problem that there is since being come out from wool fabric is not changed all the time
Kind, here it is the scratchy problem of wool fabric, especially tricot de laine, more and more consumer is liked such clothes now
Dress wears next to the skin, thus fabric snug fit degree, scratchy grade can or can not be produced to feel largely have influence on and disappear to skin
The dress ornament selection of the person of expense, if not can solve the problem of the snug fit degree of tricot de laine, can cause to consumer
Certain puzzlement, so as to limit its wider popularization and application.
Accordingly, it would be desirable to a kind of new technical scheme is solving the above problems.
The content of the invention
Goal of the invention:In order to solve the problems of prior art, avoided to skin urtication the invention provides one kind
Feel the raising tricot de laine snug fit degree that tricot de laine is soft, strength damage is small after generation, the treatment of phenomenon
Finishing technique.
Technical scheme:To reach above-mentioned purpose, the technical scheme is that:One kind improves tricot de laine snug fit
The finishing technique of degree, hydrophilic finiss technique is increased before the dyeing processing technique of tricot de laine and before stamp processing technology,
Antibacterial finishing process is increased after the dyeing processing technique of tricot de laine and after stamp processing technology, in wool fabric ready-made clothes
Postfinishing process in the postfinishing process that is combined with plasma using biology enzyme.
It is more highly preferred to, the hydrophilic treatment process is that the tricot de laine washed after soft treatment is put into hydrophilic finiss
First soaking at room temperature 10-15min in liquid, then be placed in 40-45 DEG C carry out warm treatment 22-28min after carry out padding treatment, pick-up rate
It is that 100%, 30-35 DEG C of low temperature is dried to 6-7 into dry.
Further, the hydrophilic finiss liquid is calculated by mass including following composition:Polyacrylic acid glycerol ester 10-14
Part, silane coupler 0.5-0.8 parts, dehydroactic acid 3-6 parts, bleeding agent 1-2 parts, hydrophilic surfactant active 0.8-1.6 parts.
Further, the silane coupler is kh560.
Further, the bleeding agent is JFC-E and JFC-2 mass ratioes are 4:1 mixture.
Further, the hydrophilic surfactant active is hydrophilic amino silicone oil.
It is more highly preferred to, the antibacterial finishing process is will be first by the tricot de laine after dyeing or stamp processing technology
First being placed in soaking at room temperature 10-15min in antibiotic finishing solution, then be placed in 40-45 DEG C of environment taken after warm processes 22-28min
Go out after washing 2-3 times to carry out to pad treatment, pick-up rate is that 100%, 30-35 DEG C of low temperature is dried to 7-8 into dry.
Further, the antibiotic finishing solution is calculated by mass including following composition:Chinese medicine antibacterial mixture 10-20
Part, nano-silver powder 0.5-1.2 parts, citric acid 3-6 parts, hydrophilic surfactant active 1-2 parts.
Further, the Chinese medicine antibacterial composition be the coptis, the stem pith of the rice-paper plant, folium artemisiae argyi, four kinds of traditional Chinese medicine quality ratios of fennel be 5:
2:5:1 mixture.
It is more highly preferred to, biology enzyme includes 20% albumen in the postfinishing process that the biology enzyme is combined with plasma
The pectase of enzyme, 30% phytase, 20% aspergillus oryzae, 10% cellulase and surplus.
Beneficial effect:A kind of finishing technique for improving tricot de laine snug fit degree provided by the present invention, in dyeing
With hydrophilic finiss technique is increased before stamp processing technology, the hydroscopicity of tricot de laine can be effectively improved, in advance prevention dyeing
Damage with printing technology to fabric wettability, so as to reduce the friction level with skin;Antibiotic finish after dyeing and stamp
Technique can further improve the docile antibacterial ability of fabric, and the postfinishing process that biology enzyme is combined with plasma can not only be removed
Some residual slurries on tricot de laine, also effectively improve the softness of fabric, so as to further increase the comfortable of fabric
Degree.The present invention has the advantages that the fabrics feel soft after treatment, strength damage are small compared with common process, is prevented effectively from
Generation to skin urtication sense phenomenon, comfort level enhancing.
Specific embodiment
The present invention is described in further detail with reference to implementation method:
Embodiment 1:
It is a kind of improve tricot de laine snug fit degree finishing technique, before the dyeing processing technique of tricot de laine and
Hydrophilic finiss technique is increased before stamp processing technology, after the dyeing processing technique of tricot de laine and after stamp processing technology
Increased antibacterial finishing process, in the postfinishing process of wool fabric ready-made clothes using biology enzyme combined with plasma it is rear whole
Science and engineering skill.
The hydrophilic treatment process is that the tricot de laine washed after soft treatment is put into hydrophilic finiss liquid into first room temperature
Soaking 10min, then be placed in 40 DEG C carries out carrying out padding treatment after warm processes 22min, and pick-up rate is 100%, and 30 DEG C of low temperature dry
It is dry to 6 one-tenth;The hydrophilic finiss liquid is calculated by mass including following composition:10 parts of polyacrylic acid glycerol ester, silane coupler 0.5
Part, 3 parts of dehydroactic acid, 1 part of bleeding agent, 0.8 part of hydrophilic surfactant active;Wherein, the silane coupler is kh560;Institute
It is 4 with JFC-2 mass ratioes that bleeding agent is stated for JFC-E:1 mixture;The hydrophilic surfactant active is hydrophilic amino silicon
Oil
The antibacterial finishing process is that will be initially positioned at antibacterial by the tricot de laine after dyeing or stamp processing technology
Soaking at room temperature 10min in dressing liquid, then be placed in 40 DEG C of environment carry out warm treatment 22min after take out washing 2 times after padded
Treatment, pick-up rate is 100%, and 30 DEG C of low temperature are dried to 7 one-tenth and do;The antibiotic finishing solution is calculated by mass including following composition:In
10 parts of medicine antimicrobial mixtures, 0.5 part of nano-silver powder, 3 parts of citric acid, 1 part of hydrophilic surfactant active;Wherein described Chinese medicine antibacterial
Composition be the coptis, the stem pith of the rice-paper plant, folium artemisiae argyi, four kinds of traditional Chinese medicine quality ratios of fennel be 5:2:5:1 mixture.
Biology enzyme includes 20% protease, 30% plant in the postfinishing process that the biology enzyme is combined with plasma
The pectase of sour enzyme, 20% aspergillus oryzae, 10% cellulase and surplus.
Embodiment 2:
It is a kind of improve tricot de laine snug fit degree finishing technique, before the dyeing processing technique of tricot de laine and
Hydrophilic finiss technique is increased before stamp processing technology, after the dyeing processing technique of tricot de laine and after stamp processing technology
Increased antibacterial finishing process, in the postfinishing process of wool fabric ready-made clothes using biology enzyme combined with plasma it is rear whole
Science and engineering skill.
The hydrophilic treatment process is that the tricot de laine washed after soft treatment is put into hydrophilic finiss liquid into first room temperature
Soaking 15min, then be placed in 45 DEG C carries out carrying out padding treatment after warm processes 28min, and pick-up rate is 100%, and 35 DEG C of low temperature dry
It is dry to 7 one-tenth;The hydrophilic finiss liquid is calculated by mass including following composition:14 parts of polyacrylic acid glycerol ester, silane coupler 0.8
Part, 6 parts of dehydroactic acid, 2 parts of bleeding agent, 1.6 parts of hydrophilic surfactant active;Wherein, the silane coupler is kh560;Institute
It is 4 with JFC-2 mass ratioes that bleeding agent is stated for JFC-E:1 mixture;The hydrophilic surfactant active is hydrophilic amino silicon
Oil
The antibacterial finishing process is that will be initially positioned at antibacterial by the tricot de laine after dyeing or stamp processing technology
Soaking at room temperature 15min in dressing liquid, then be placed in 45 DEG C of environment carry out warm treatment 28min after take out washing 3 times after padded
Treatment, pick-up rate is 100%, and 35 DEG C of low temperature are dried to 8 one-tenth and do;The antibiotic finishing solution is calculated by mass including following composition:In
20 parts of medicine antimicrobial mixtures, 1.2 parts of nano-silver powder, 6 parts of citric acid, 2 parts of hydrophilic surfactant active;Wherein described Chinese medicine antibacterial
Composition be the coptis, the stem pith of the rice-paper plant, folium artemisiae argyi, four kinds of traditional Chinese medicine quality ratios of fennel be 5:2:5:1 mixture.
Biology enzyme includes 20% protease, 30% plant in the postfinishing process that the biology enzyme is combined with plasma
The pectase of sour enzyme, 20% aspergillus oryzae, 10% cellulase and surplus.
Embodiment 3:
It is a kind of improve tricot de laine snug fit degree finishing technique, before the dyeing processing technique of tricot de laine and
Hydrophilic finiss technique is increased before stamp processing technology, after the dyeing processing technique of tricot de laine and after stamp processing technology
Increased antibacterial finishing process, in the postfinishing process of wool fabric ready-made clothes using biology enzyme combined with plasma it is rear whole
Science and engineering skill.
The hydrophilic treatment process is that the tricot de laine washed after soft treatment is put into hydrophilic finiss liquid into first room temperature
Soaking 13min, then be placed in 43 DEG C carries out carrying out padding treatment after warm processes 26min, and pick-up rate is 100%, and 33 DEG C of low temperature dry
It is dry to 6 one-tenth;The hydrophilic finiss liquid is calculated by mass including following composition:12 parts of polyacrylic acid glycerol ester, silane coupler 0.7
Part, 4 parts of dehydroactic acid, 1.5 parts of bleeding agent, 1.2 parts of hydrophilic surfactant active;Wherein, the silane coupler is kh560;
The bleeding agent is JFC-E and JFC-2 mass ratioes are 4:1 mixture;The hydrophilic surfactant active is hydrophilic amino
Silicone oil.
The antibacterial finishing process is that will be initially positioned at antibacterial by the tricot de laine after dyeing or stamp processing technology
Soaking at room temperature 13min in dressing liquid, then be placed in 43 DEG C of environment carry out warm treatment 25min after take out washing 2 times after padded
Treatment, pick-up rate is 100%, and 33 DEG C of low temperature are dried to 8 one-tenth and do;The antibiotic finishing solution is calculated by mass including following composition:In
15 parts of medicine antimicrobial mixtures, 0.8 part of nano-silver powder, 5 parts of citric acid, 1.5 parts of hydrophilic surfactant active;Wherein described Chinese medicine resists
Bacteria composition be the coptis, the stem pith of the rice-paper plant, folium artemisiae argyi, four kinds of traditional Chinese medicine quality ratios of fennel be 5:2:5:1 mixture.
Biology enzyme includes 20% protease, 30% plant in the postfinishing process that the biology enzyme is combined with plasma
The pectase of sour enzyme, 20% aspergillus oryzae, 10% cellulase and surplus.
After technique according to above-mentioned three kinds of embodiments is processed common woolen knitting fabric, it is divided into three test groups
Woolen knitting fabric ready-made clothes is carried out with a control group take comfort test, every group of choosing
Take 50 and try object on without disease of skin health, investigation return visit is carried out after taking 3 days.
Take evaluation index as follows:
A grades:Occur entirely without scratchy phenomenon, it is comfortable and easy to wear, it is soft next to the skin.
B grades:Somewhat there is scratchy phenomenon, dress is more comfortable, and pliability is still good.
C grades:Substantially, wearing comfort is not good, and pliability is not good for scratchy phenomenon.
Pay a return visit result as shown in table 1:
Table 1:Take return visit result
A grades of evaluation | B grades of evaluation | C grades of evaluation | Comfort level qualification rate (A grades+B grades) | |
Embodiment 1 | 32 | 14 | 4 | 92% |
Embodiment 2 | 33 | 13 | 4 | 92% |
Embodiment 3 | 35 | 12 | 3 | 94% |
Tradition control | 12 | 14 | 24 | 52% |
Be can be seen that from upper table data, the finishing technique and traditional work of a kind of raising tricot de laine snug fit degree of the present invention
Skill compares, and with preferably snug fit degree, is prevented effectively from and occurs to the scratchy phenomenon of skin, is extensively liked by consumer.
It should be pointed out that above specific embodiment is only illustrative of the invention and is not intended to limit the scope of the invention,
Read after the present invention, modification of the those skilled in the art to the various equivalent form of values of the invention falls within and weighed appended by the application
Profit requires limited range.
Claims (10)
1. it is a kind of improve tricot de laine snug fit degree finishing technique, it is characterised in that:Add in the dyeing of tricot de laine
Before work technique and hydrophilic finiss technique is increased before stamp processing technology, after the dyeing processing technique of tricot de laine and stamp
Antibacterial finishing process is increased after processing technology, biology enzyme and plasma are used in the postfinishing process of wool fabric ready-made clothes
With reference to postfinishing process.
2. it is according to claim 1 improve tricot de laine snug fit degree finishing technique, it is characterised in that:The parent
Water treatment technology is that the tricot de laine washed after soft treatment is put into hydrophilic finiss liquid into first soaking at room temperature 10-15min, then
Being placed in 40-45 DEG C carries out carrying out padding treatment after warm processes 22-28min, and pick-up rate is that 100%, 30-35 DEG C of low temperature is dried to 6-
7 one-tenth are done.
3. it is according to claim 2 improve tricot de laine snug fit degree finishing technique, it is characterised in that the parent
Water dressing liquid is calculated by mass including following composition:10-14 parts of polyacrylic acid glycerol ester, silane coupler 0.5-0.8 parts, dehydrogenation
Acetic acid 3-6 parts, bleeding agent 1-2 parts, hydrophilic surfactant active 0.8-1.6 parts.
4. it is according to claim 3 improve tricot de laine snug fit degree finishing technique, it is characterised in that:The silicon
Alkane coupling agent is kh560.
5. it is according to claim 3 improve tricot de laine snug fit degree finishing technique, it is characterised in that:It is described to ooze
Saturating agent is JFC-E and JFC-2 mass ratioes are 4:1 mixture.
6. it is according to claim 3 improve tricot de laine snug fit degree finishing technique, it is characterised in that:The parent
Aqueous tenside is hydrophilic amino silicone oil.
7. it is according to claim 1 improve tricot de laine snug fit degree finishing technique, it is characterised in that:It is described anti-
Bacterium finishing technique is room temperature leaching in being initially positioned at antibiotic finishing solution by the tricot de laine after dyeing or stamp processing technology
Bubble 10-15min, then be placed in 40-45 DEG C of environment carry out warm treatment 22-28min after take out washing 2-3 times after carry out padding place
Reason, pick-up rate is that 100%, 30-35 DEG C of low temperature is dried to 7-8 into dry.
8. the finishing technique for improving tricot de laine snug fit degree according to claim 4, it is characterised in that described anti-
Bacterium dressing liquid is calculated by mass including following composition:10-20 parts of Chinese medicine antibacterial mixture, nano-silver powder 0.5-1.2 parts, citric acid
3-6 parts, hydrophilic surfactant active 1-2 parts.
9. it is according to claim 8 improve tricot de laine snug fit degree finishing technique, it is characterised in that:In described
Medicine bactericidal composition be the coptis, the stem pith of the rice-paper plant, folium artemisiae argyi, four kinds of traditional Chinese medicine quality ratios of fennel be 5:2:5:1 mixture.
10. it is according to claim 1 improve tricot de laine snug fit degree finishing technique, it is characterised in that:It is described
Biology enzyme includes 20% protease, 30% phytase, 20% in the postfinishing process that biology enzyme is combined with plasma
The pectase of aspergillus oryzae, 10% cellulase and surplus.