CN106811691A - Ferroalloy - Google Patents
Ferroalloy Download PDFInfo
- Publication number
- CN106811691A CN106811691A CN201510849378.3A CN201510849378A CN106811691A CN 106811691 A CN106811691 A CN 106811691A CN 201510849378 A CN201510849378 A CN 201510849378A CN 106811691 A CN106811691 A CN 106811691A
- Authority
- CN
- China
- Prior art keywords
- ferroalloy
- iron
- aluminium
- present
- weight ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ferroalloy, by weight containing carbon 1-2%, aluminium 2-3%, vanadium 2-2.5%, zirconium 1-2%, tungsten 1-1.3%, zinc 1.2-1.5%, balance of iron and being difficult to the impurity for removing；Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.Wearability of the present invention is good, and service life is greatly prolonged.
Description
Technical field
The present invention relates to a kind of ferroalloy.
Background technology
Ferroalloy, adds when the ferroalloy of broad sense refers to steel-making as deoxidier, element additive etc.
Enter to make in molten iron steel to possess certain characteristic or reach a kind of product of certain requirement.Iron with it is a kind of or
The intermediate alloy of several element compositions, is mainly used in smelting iron and steel.In steel and iron industry typically also
The intermediate alloy of all steel-making, no matter whether iron content is referred to as " ferroalloy ".Existing iron
Wear Resistance is poor.
The content of the invention
(1) technical problem to be solved
The problem to be solved in the present invention is to provide a kind of ferroalloy, wear-resisting in the prior art to overcome
Property difference defect.
(2) technical scheme
To solve the technical problem, the present invention provides a kind of ferroalloy, carbon is contained by weight
1-2%, aluminium 2-3%, vanadium 2-2.5%, zirconium 1-2%, tungsten 1-1.3%, zinc 1.2-1.5%, remaining
Measure as iron and be difficult to the impurity for removing；Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.
Further, the carbon weight ratio is 2%.
Further, the aluminium weight ratio is 3%.
(3) beneficial effect
Ferroalloy of the invention, wearability is good, and service life is greatly prolonged.
Specific embodiment
With reference to embodiment, specific embodiment of the invention is described in further detail.
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
A kind of ferroalloy of the invention, contains carbon 1-2%, aluminium 2-3%, vanadium by weight
2-2.5%, zirconium 1-2%, tungsten 1-1.3%, zinc 1.2-1.5%, balance of iron and it is difficult to what is removed
Impurity；Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.The carbon weight ratio is 2%.
The aluminium weight ratio is 3%.
In sum, above-mentioned implementation method is not restricted implementation method of the invention, all
Modification or wait that the technical staff in field is carried out on the basis of substance of the invention
Effect deformation, in technology category of the invention.
Claims (3)
1. a kind of ferroalloy, it is characterised in that：By weight containing carbon 1-2%, aluminium 2-3%,
Vanadium 2-2.5%, zirconium 1-2%, tungsten 1-1.3%, zinc 1.2-1.5%, balance of iron and it is difficult to
The impurity for removing；Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.
2. ferroalloy according to claim 1, it is characterised in that：The carbon weight ratio
It is 2%.
3. ferroalloy according to claim 1, it is characterised in that：The aluminium weight ratio
It is 3%.