CN106756443A - Ferroalloy - Google Patents
Ferroalloy Download PDFInfo
- Publication number
- CN106756443A CN106756443A CN201510828577.6A CN201510828577A CN106756443A CN 106756443 A CN106756443 A CN 106756443A CN 201510828577 A CN201510828577 A CN 201510828577A CN 106756443 A CN106756443 A CN 106756443A
- Authority
- CN
- China
- Prior art keywords
- ferroalloy
- iron
- molybdenum
- present
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ferroalloy, by weight containing titanium 1-2%, molybdenum 1-2%, vanadium 34%, 1-2% manganese, the copper of 2-3%, chromium 1.5-3%, zinc 0.5-1%, balance of iron and be difficult to the impurity for removing;Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.The present invention is prepared simply, and wearability is good, increases the service life.
Description
Technical field
The present invention relates to a kind of ferroalloy.
Background technology
Ferroalloy, adds when the ferroalloy of broad sense refers to steel-making as deoxidier, element additive etc.
Enter to make in molten iron steel to possess certain characteristic or reach a kind of product of certain requirement.Iron with it is a kind of or
The intermediate alloy of several element compositions, is mainly used in smelting iron and steel.In steel and iron industry typically also
The intermediate alloy of all steel-making, no matter whether iron content is referred to as " ferroalloy ".Existing iron
Wear Resistance is poor.
The content of the invention
(1) technical problem to be solved
The problem to be solved in the present invention is to provide a kind of ferroalloy, wear-resisting in the prior art to overcome
Property difference defect.
(2) technical scheme
To solve the technical problem, the present invention provides a kind of ferroalloy, titanium is contained by weight
1-2%, molybdenum 1-2%, the manganese of vanadium 34%, 1-2%, the copper of 2-3%, chromium 1.5-3%, zinc
0.5-1%, balance of iron and it is difficult to the impurity for removing;Above-mentioned dispensing is put into furnace after being sufficiently mixed
Middle heating.
Further, the titanium weight ratio is 1.2%.
Further, the weight of molybdenum ratio is 1.5%.
(3) beneficial effect
Ferroalloy of the invention, prepares simply, and wearability is good, increases the service life.
Specific embodiment
With reference to embodiment, specific embodiment of the invention is described in further detail.
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
A kind of ferroalloy of the invention, by weight containing titanium 1-2%, molybdenum 1-2%, vanadium 34%,
The manganese of 1-2%, the copper of 2-3%, chromium 1.5-3%, zinc 0.5-1%, balance of iron and is difficult to
The impurity for removing;Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.It is preferred that the titanium weight ratio
It is 1.2%.It is preferred that the weight of molybdenum ratio is 1.5%.
Ferroalloy of the invention, prepares simply, and wearability is good, increases the service life.
In sum, above-mentioned implementation method is not restricted implementation method of the invention, all
Modification or wait that the technical staff in field is carried out on the basis of substance of the invention
Effect deformation, in technology category of the invention.
Claims (3)
1. a kind of ferroalloy, it is characterised in that:By weight containing titanium 1-2%, molybdenum 1-2%,
The manganese of vanadium 34%, 1-2%, the copper of 2-3%, chromium 1.5-3%, zinc 0.5-1%, balance of iron
With the impurity for being difficult to remove;Above-mentioned dispensing is heated during furnace is put into after being sufficiently mixed.
2. ferroalloy according to claim 1, it is characterised in that:The titanium weight ratio
It is 1.2%.
3. ferroalloy according to claim 1, it is characterised in that:The weight of molybdenum ratio
It is 1.5%.