CN106811037B - A kind of Polyaspartic Polyurea coating and its application - Google Patents
A kind of Polyaspartic Polyurea coating and its application Download PDFInfo
- Publication number
- CN106811037B CN106811037B CN201710020708.7A CN201710020708A CN106811037B CN 106811037 B CN106811037 B CN 106811037B CN 201710020708 A CN201710020708 A CN 201710020708A CN 106811037 B CN106811037 B CN 106811037B
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- component
- polyaspartic
- polyether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of Polyaspartic Polyurea coating and its application, the Polyaspartic Polyurea coating includes: component A and B component；The component A includes polyaspartic ester, defoaming agent, dispersing agent, thixotropic agent, filler and water absorbing agent；The B component is polyether-modified polyisocyanates；It is 1:3~2:1 that component A and B component, which are mass ratio,.Poly-aspartic-acid carbamide paint of the invention has good flexibility and waterproofness, and adhesive force is stronger；These good characteristics enable coating of the invention preferably as the buffer layer of coating system, to greatly improve the ability that waterproof material resists environmental change in practical applications, extend and use the time, reduce maintenance cost.
Description
Technical field
The invention belongs to chemistry painting industry preparation technical field more particularly to a kind of Polyaspartic Polyurea coating and its
Using.
Background technique
Currently, the water-repellent paint used in the market has pitch, acrylate paint, polyurethane coating and modified coating.By
Poor in curing time length, weatherability, the light resistance of these water-repellent paints, coating can deform, fail after a period of use, will
Waterproof effect can be lost.
A kind of waterproof coating that carbamide paint is last decade to develop, the advantage protruded be instant mixing,
Continuous spray, ageing-resistant performance is more excellent, long using the time, nontoxic and pollution-free；But gel is too fast, be not easy to technical staff into
Row construction；Wellability is poor simultaneously, adhesive force is lower and difference of hardness etc..For this purpose, scientific and technical personnel continue to improve, develop poly- day
L-aminobutanedioic acid ester carbamide paint, can solve that gel time is too short and the demanding problem of construction equipment, improve the comprehensive of coating
Energy.Chinese invention patent (Patent No. CN200710173351.2) discloses a kind of Polyaspartic Polyurea water-repellent paint
Preparation method, the coating is based on polyaspartic ester, using polyisocyanates as curing agent.Coating of the present invention
Not only the excellent properties of traditional carbamide paint had been saved, but also to overcome gel time too fast, special equipment is needed to construct
The drawbacks of；The coating also has stronger adhesive force, good toughness and weather resistance etc..In order to meet client to coating more
Strict requirements, the performance of Polyaspartic Polyurea coating is up for further improving.
Summary of the invention
Present invention aims at the further comprehensive performances for improving Polyaspartic Polyurea coating, and provide a kind of poly-
Aspartate carbamide paint and its application, the weight that the present invention passes through raw material and adjustment raw material in reasonably replacement formula
Number to be measured, the adhesive force of Polyaspartic Polyurea coating is made to be strengthened, tensile strength and fracture elongation are improved,
And the up time is extended.
The technical solution of the present invention is as follows: a kind of Polyaspartic Polyurea coating, the Polyaspartic Polyurea
Coating includes: component A and B component；Wherein,
The component A includes polyaspartic ester, defoaming agent, wetting dispersing agent, thixotropic agent, filler and water absorbing agent；
The B component is polyether-modified polyisocyanates；
The mass ratio of the component A and B component is 1:3~2:1.
The polyaspartic ester is synthesized by polyamino monomer with unsaturated functional group monomer；The polyamino monomer
For ethylenediamine, butanediamine, hexamethylene diamine, making methylpentamethylenediamine diamine, toluenediamine, m-xylene diamine, 1,6 hexane diamines, isophorone two
At least one of amine, dimethyl diaminodiphenylmethane；The unsaturated functional group monomer is acrylic acid, acrylate, first
Base acrylate, dimethyl maleate, diethyl maleate, dibutyl maleate, two methyl ethyl ester of fumaric acid, dibutyl fumarate
At least one of.The aspartate increases steric effect, delays amino-functional by introducing unsaturated monomeric ester
Reaction speed between group and isocyano extends gel time so that reaction can be favorably accomplished controllably, improves skill
The convenience of art personnel construction.
As above-mentioned technical proposal improve, the defoaming agent be in vinyl defoaming agent and organic silicon defoaming agent extremely
Few one kind, the dispersing agent are polyether amine wetting dispersing agent, and the thixotropic agent is silica, the filler be dicalcium powder,
At least one of barium sulfate, the water absorbing agent are silicates water absorbing agent.
The vinyl defoaming agent belongs to polyethers defoaming agent, and organic silicon defoaming agent is by silicone grease, emulsifier, waterproof
Agent, thickening agent etc. are formed through machinery emulsification, and main component is the linear polysiloxanes by keeping liquid at room temperature, and such as poly- two
Methyl-monosilane, fluorosilicone and ethylene glycol siloxanes etc.；There are many thixotropic agent, such as silica and kaolin, wherein dioxy
SiClx can be divided into precipitating and gas phase, and fumed silica has preferable mobility coating under the action of mechanical force；Filling
Material has talcum powder, dicalcium powder and barium sulfate etc., using dicalcium powder and barium sulfate as filler material, can be enhanced and draws high intensity and tearing
Intensity and hardness etc.；The polyether amine wetting dispersing agent active constituent is preferably polyether monoamine.
It as above-mentioned technical proposal improves, modified polyether used in the polyether-modified polyisocyanates is polycarbonate two
Alcohol, polytetrahydrofuran diol, polypropylene glycol, polyglycerol, polyethylene glycol, poly- second triol, poly- trimethylolpropane, polybutadiene
At least one of alcohol, polycaprolactone glycol.
It is further improved as above-mentioned technical proposal, the polyether-modified polyisocyanates is that polyether-modified toluene two is different
Cyanate.
It as above-mentioned technical proposal improves, the quality such as the component A and B component are.
It is further improved as above scheme, the component A includes the raw material of following parts by weight are as follows: poly-aspartic-acid
40~50 parts of ester, 1~4 part of defoaming agent, 1~3 part of wetting dispersing agent, 0.1~1 part of thixotropic agent, 44~55 parts of filler and water absorbing agent 2
~5 parts.
It is further improved as above scheme, the defoaming agent is 0.5~2 part of vinyl-based defoaming agent and 0.5~2
The mixture of part organic silicon defoaming agent；The filler is the mixture of 36~40 parts of dicalcium powders and 8~15 parts of barium sulfate.
Preferably, the vinyl defoaming agent is ZY-357, organic silicon defoaming agent LY-A series, and ZY-357 and LY-A
For etc. quality.Defoaming agent need to have certain incompatibility that can just play defoaming effect at foam system, in view of coating system
Complexity such as uses can enhance defoaming effect at the ZY-357 and LY-A of quality.
It is further improved as above scheme, the component A includes the raw material of following parts by weight are as follows: poly-aspartic
41 parts of acid esters, 1.5 parts of vinyl-based defoaming agent, 1.5 parts of organic silicon defoaming agent, 2.8 parts of polyether amine wetting dispersing agent, gas phase
0.7 part of silica, 37.5 parts of dicalcium powder, 11 parts of barium sulfate and 4 parts of silicates water absorbing agent；The B component is polyether-modified
100 parts of toluene di-isocyanate(TDI).Preferably, the polyether amine wetting dispersing agent is that Hensel steps L207, silicates water absorbing agent
For Sylosiv A3Powder.
In addition, the present invention also provides the Polyaspartic Polyurea coating as Polyaspartic Polyurea waterproof
The application of the floating coat of corrosion-inhibiting coating system.
In addition, the present invention also provides a kind of Polyaspartic Polyurea waterproof and anticorrosion coating system, the poly- lucid asparagus
Propylhomoserin ester polyurea water-proof corrosion-inhibiting coating system includes the Polyaspartic Polyurea coating.
Polyaspartic Polyurea waterproof and anticorrosion coating system includes sealing bottom coating, floating coat, weather-proof finishing coat, sheet
Invention using Polyaspartic Polyurea coating as the elastic cord breaker in coating system, the floating coat can absorb substrate because
It stretches caused by a variety of causes, not will lead to level and generate biggish deformation and rupture；Floating coat has very strong attached
Put forth effort, delamination will not be caused, play drum, extended using the time.
The beneficial effects of the present invention are: Polyaspartic Polyurea coating of the present invention includes: component A and B component, A
Component includes aspartate, defoaming agent, wetting dispersing agent, thixotropic agent, filler and water absorbing agent, and B component is polyether-modified more
Isocyanates, and the parts by weight of raw materials various in component A are adjusted, so that various raw materials is combined, improves poly-
The comprehensive performance of asparatate carbamide paint: 1) extending gel time, constructs convenient for technical staff；2) enhance flexibility: such as
Tensile strength, tearing strength and elongation at break etc.；3) adhesive force is improved.Polyaspartic Polyurea coating is as painting Material
When the middle layer of system, it is adapted to environmental change, extend coating uses the time.
Specific embodiment
Purposes, technical schemes and advantages in order to better illustrate the present invention, below in conjunction with specific embodiment to the present invention
It is described further.
Embodiment 1
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
Carbamide paint synthesis raw material and parts by weight be respectively as follows: 46 parts of polyaspartic ester, polyether-modified 2 parts of silicon class defoaming agent,
2.6 parts of polyethers Ammonia wetting dispersing agent, 0.4 part of fumed silica, 44 parts of talcum powder and 5 parts of water absorbing agent；The B component is poly-
50 parts of ether modified toluene diisocyanate.
Polyaspartic ester described in this implementation column is Bayer NH1420, and polyether-modified silicon class defoaming agent is ten thousand one-tenth BYC-
710, polyether amine wetting dispersing agent is that Hensel steps FM-300, water absorbing agent Dibaa-30X, polyether-modified toluene di-isocyanate(TDI)
Modified polyether used is polycarbonate glycol.
Embodiment 2
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
The raw material and parts by weight of carbamide paint synthesis are respectively as follows: 40 parts of polyaspartic ester, 1 part of vinyl-based defoaming agent, polyethers
1 part of amine wetting dispersing agent, 1 part of fumed silica, 55 parts of dicalcium powder and 2 parts of water absorbing agent；The B component is polyether-modified first
300 parts of phenylene diisocyanate.
Polyaspartic ester described in this implementation column is Bayer NH1420, and vinyl-based defoaming agent is ZY-357, polyethers
Amine wetting dispersing agent is that Hensel steps FM-300, water absorbing agent Dibaa-30X, modified used in polyether-modified toluene di-isocyanate(TDI)
Polyethers is polytetramethylene glycol.
Embodiment 3
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
The raw material and parts by weight of carbamide paint synthesis are respectively as follows: 50 parts of polyaspartic ester, 4 parts of organic silicon defoaming agent, polyethers
3 parts of amine wetting dispersing agent, 0.1 part of kaolin, 45 parts of calcium carbonate and 3.9 parts of water absorbing agent；The B component is polyether-modified toluene
200 parts of diisocyanate.
Polyaspartic ester described in this implementation column is Bayer NH1420 and Bayer NH1520 (the two ratio is 4:5),
Organic silicon defoaming agent is the rich DF-853 of moral, and polyether amine wetting dispersing agent is that Hensel steps FM-300, water absorbing agent Dibaa-
30X, modified polyether used in polyether-modified toluene di-isocyanate(TDI) are polypropylene glycol.
Embodiment 4
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
The raw material and mass fraction of carbamide paint synthesis are respectively as follows: 41 parts of polyaspartic ester, 1.5 parts of vinyl-based defoaming agent, have
1.5 parts of machine silicon class defoaming agent, 2.8 parts of polyether amine wetting dispersing agent, 0.7 part of fumed silica, 37.5 parts of dicalcium powder, sulfuric acid
11 parts and 4 parts of silicates water absorbing agent of barium；The B component is 100 parts of polyether-modified toluene di-isocyanate(TDI).
Polyaspartic ester described in this implementation column is Bayer NH1420, and vinyl defoaming agent is ZY-357, organosilicon
Class defoaming agent LY-A, polyether amine wetting dispersing agent are that Hensel steps L207, and silicates water absorbing agent is Sylosiv A3Powder, polyethers
Modified polyether used in modified toluene diisocyanate is polycaprolactone glycol.
Embodiment 5
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
The raw material and mass fraction of carbamide paint synthesis are respectively as follows: 41 parts of polyaspartic ester, 2 parts of vinyl-based defoaming agent, organic
0.5 part of silicon class defoaming agent, 2 parts of polyether amine wetting dispersing agent, 0.5 part of fumed silica, 36 parts of dicalcium powder, 15 parts of barium sulfate
With 3 parts of silicates water absorbing agent；The B component is 100 parts of polyether-modified toluene di-isocyanate(TDI).
Polyaspartic ester, defoaming agent described in the present embodiment, wetting dispersing agent, water absorbing agent and polyether-modified polyisocyanate cyanogen
The polyethers of acid is the same as embodiment 4.
Embodiment 6
A kind of embodiment of Polyaspartic Polyurea coating of the invention, polyaspartic ester described in the present embodiment
The raw material and mass fraction of carbamide paint synthesis are respectively as follows: 43 parts of polyaspartic ester, 0.5 part of vinyl-based defoaming agent, have
2 parts of machine silicon class defoaming agent, 3 parts of polyether amine wetting dispersing agent, 0.1 part of fumed silica, 40 parts of dicalcium powder, 8 parts of barium sulfate
With 3.4 parts of silicates water absorbing agent；The B component is 100 parts of polyether-modified toluene di-isocyanate(TDI).
Polyaspartic ester, defoaming agent described in the present embodiment, wetting dispersing agent, water absorbing agent and polyether-modified polyisocyanate cyanogen
The polyethers of acid is the same as embodiment 4.
Embodiment 7
The Polyaspartic Polyurea coating comprehensive performance of the embodiment of the present invention 1~6 is measured, measurement result is shown in
Reference substance is poly- day disclosed in Chinese invention patent (Patent No. CN200710173351.2) in Tables 1 and 2, table 1 and mark table 2
L-aminobutanedioic acid ester polyurea waterproof coating material.Surface drying time is referring to GB/T1728-1989 standard with the time is done solid work；Drawing high intensity is ginseng
According to GB/T16777-2008 standard (test temperature is 25 DEG C)；Elongation at break is referring to GB/T16777-2008 standard；Tearing
Intensity is referring to GB/T529-2008 standard；Adhesive force is measured with tension method, is marked referring to GB/T5210-2006
It is quasi-；Hardness is referring to GB/T2411-1989 standard；Impermeability is to measure 30min in 0.3mpa environment, is referring to GB/
T16777-2008 standard；Low-temperature bending is referring to HG-T3831-2006 standard.
Table 1 is the performance measurement of Polyaspartic Polyurea coating
Table 2 is the performance measurement of Polyaspartic Polyurea coating
In summary measurement result, it can be deduced that Polyaspartic Polyurea coating of the invention is compared with reference substance:
1) curing time is similar, and gel time is about 30 or 20min, constructs convenient for technical staff；2) tensile strength, tearing strength
It is strengthened with elongation at break, the flexibility of Polyaspartic Polyurea coating is more excellent；3) waterproof, and low temperature does not go out
Existing crackle；4) adhesive force is stronger, and hardness is harder.The Polyaspartic Polyurea coating of embodiment 4 is relative to other embodiments
For, performance is relatively comprehensively and good.
Polyaspartic Polyurea coating of the invention has good flexibility and waterproofness, and adhesive force is stronger；This
A little good characteristics enable coating of the invention preferably as the floating coat in coating system, to become the buffering of coating
Layer, greatly improves the ability that waterproof material resists environmental change in practical applications, extends and uses the time, reduce maintenance at
This.
Finally, it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than protects to the present invention
The limitation of range is protected, although the invention is described in detail with reference to the preferred embodiments, those skilled in the art should
Understand, can modify to technical solution of the present invention or replace on an equal basis, without departing from the essence of technical solution of the present invention
And range.
Claims (9)
1. a kind of Polyaspartic Polyurea coating, it is characterised in that: the Polyaspartic Polyurea coating includes A group
Point and B component；Wherein,
The component A includes polyaspartic ester, defoaming agent, wetting dispersing agent, thixotropic agent, filler and water absorbing agent；The A group
Raw material of the subpackage containing following parts by weight are as follows: 40~50 parts of polyaspartic ester, 1~4 part of defoaming agent, wetting dispersing agent 1~3
Part, 0.1~1 part of thixotropic agent, 44~55 parts of filler and 2~5 parts of water absorbing agent；
The B component is polyether-modified polyisocyanates；
The mass ratio of the component A and B component is 1:3~2:1.
2. Polyaspartic Polyurea coating as described in claim 1, it is characterised in that: the defoaming agent disappears for vinyl
At least one of infusion and organic silicon defoaming agent, the wetting dispersing agent are polyether amine wetting dispersing agent, the thixotroping
Agent is silica, and the filler is at least one of dicalcium powder, barium sulfate, and the water absorbing agent is silicates water absorbing agent.
3. Polyaspartic Polyurea coating as described in claim 1, it is characterised in that: the polyether-modified polyisocyanic acid
Modified polyether used in ester is polycarbonate glycol, polytetrahydrofuran diol, polypropylene glycol, polyglycerol, polyethylene glycol, poly- second three
At least one of alcohol, poly- trimethylolpropane, polytetramethylene glycol, polycaprolactone glycol.
4. Polyaspartic Polyurea coating as claimed in claim 3, it is characterised in that: the polyether-modified polyisocyanic acid
Ester is polyether-modified toluene di-isocyanate(TDI).
5. such as the described in any item Polyaspartic Polyurea coating of Claims 1 to 4, it is characterised in that: the component A with
B component be etc. quality.
6. Polyaspartic Polyurea coating as claimed in claim 5, it is characterised in that: the defoaming agent is 0.5~2 part
The mixture of vinyl-based defoaming agent and 0.5~2 part of organic silicon defoaming agent；The filler be 36~40 parts of dicalcium powders and 8~
The mixture of 15 parts of barium sulfate.
7. Polyaspartic Polyurea coating as claimed in claim 5, it is characterised in that: the component A includes following heavy
The raw material of amount part is are as follows: 41 parts of polyaspartic ester, 1.5 parts of vinyl-based defoaming agent, 1.5 parts of organic silicon defoaming agent, poly-
2.8 parts of ether amines class wetting dispersing agent, 0.7 part of fumed silica, 37.5 parts of dicalcium powder, 11 parts of barium sulfate and silicates water suction
4 parts of agent；The B component is 100 parts of polyether-modified toluene di-isocyanate(TDI).
8. as Polyaspartic Polyurea coating according to any one of claims 1 to 7 is poly- as polyaspartic ester
The application of the floating coat of urea waterproof and anticorrosion coating.
9. a kind of Polyaspartic Polyurea waterproof and anticorrosion coating, it is characterised in that: include any one of claim 1~7
The Polyaspartic Polyurea coating.