CN106810969A - Environment-friendly interior wall coating - Google Patents
Environment-friendly interior wall coating Download PDFInfo
- Publication number
- CN106810969A CN106810969A CN201510846678.6A CN201510846678A CN106810969A CN 106810969 A CN106810969 A CN 106810969A CN 201510846678 A CN201510846678 A CN 201510846678A CN 106810969 A CN106810969 A CN 106810969A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- interior wall
- wall coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly interior wall coating, the coating is made up of following components:Water 240-250 parts, alkaloid 1-3 parts, dispersant 2-8 parts, sulfonated oil 2-3 parts, paint antifoaming agent 2-6 parts, oyster shell whiting 250-400 parts, titanium dioxide 120-140 parts, talcum powder 30-80 parts, acrylic emulsion 150-300 parts, adhesion agent 10-30 parts, ethanol 1-2 parts, preservative 2-4 parts, said components are in parts by weight.With oyster shell whiting as raw material, shown using electron microscope observation, shell powder contains many duck eyes, volatile materials formaldehyde once enters duck eye, and the distinctive calcium carbonate of shell will be broken down into harmless water and carbon dioxide.Without noxious materials such as formaldehyde, ammonia and benzene classes, VOC reaches zero-emission, health environment-friendly.Can be directly used for the new metope of cement and lime and humidity, the environment of various slight erosion gases.
Description
Technical field
The present invention relates to paint field, specifically a kind of environment-friendly interior wall coating free from environmental pollution.
Background technology
With the progress of science and technology, the raising of human living standard, people are to indoor environment, the requirement more and more higher of air quality, common interior wall coating, and production technology is relatively easy, cost is relatively low, but its combination property aspect declines such as cohesive force, water resistance, resistance to spontaneous corrosion, and pollution environment, with certain toxicity, the development trend of the not following oyster shell whiting wall covering of this kind of oyster shell whiting wall covering.Therefore provide a kind of to human body and the relatively cheap environment-friendly interior wall coating of environmentally friendly, free from environmental pollution, price, the need for market.
The content of the invention
It is an object of the invention to provide a kind of to human body and the good environment protection interior wall of environmentally friendly, free from environmental pollution, performance
Coating.
In order to solve the above technical problems, the technical solution adopted by the present invention is:
Environment-friendly interior wall coating, the coating is made up of following components:250 parts of water 240-, alkaloid 1-3 parts, dispersant 2-8 parts, sulfonated oil 2-3 parts, paint antifoaming agent 2-6 parts, oyster shell whiting 250-400 parts, titanium dioxide 120-140 parts, talcum powder 30-80 parts, acrylic emulsion 150-300 parts, adhesion agent 10-30 parts, ethanol 1-2 parts, preservative 2-4 parts, said components are in parts by weight.
The concentration of the ethanol is
80-90%。
The alkaloid is Herba Ephedrae alkaloid.
As a result of above-mentioned structure, with oyster shell whiting as raw material, shown using electron microscope observation, shell powder contains
Have many duck eyes, volatile materials formaldehyde once enters duck eye, the distinctive calcium carbonate of shell will be broken down into human body without
Harmful water and carbon dioxide.Without noxious materials such as formaldehyde, ammonia and benzene classes, VOC reaches zero-emission, health
Environmental protection.Can be directly used for the new metope of cement and lime and humidity, the environment of various slight erosion gases.Simple production process, into
This is relatively low, there is very strong practicality and promotional value, can be widely used for family, public place etc..
Specific embodiment
Embodiment 1
Environment-friendly interior wall coating of the present invention, the coating is made up of following components(In parts by weight):250 parts of water, 1 part of Herba Ephedrae alkaloid, 2 parts of dispersant, 2 parts of sulfonated oil, 2 parts of paint antifoaming agent, 250 parts of oyster shell whiting, 120 parts of titanium dioxide, 30 parts of talcum powder, 150 parts of acrylic emulsion, 10 parts of adhesion agent, 1 part of ethanol, the concentration of the ethanol is 80%, 2 parts of preservative.
Collocation method is first to mix well and add again component big content the few component content mixing of component plus a small amount of water, then adds part water to mix well again, and all components are gradually added into by this method, and the water of surplus is finally supplied by proportioning, is more than normal-temperature operation.
Embodiment 2
Environment-friendly interior wall coating of the present invention, the coating is made up of following components(In parts by weight):310 parts of water, 2 parts of Herba Ephedrae alkaloid, 5 parts of dispersant, 2 parts of sulfonated oil, 4 parts of paint antifoaming agent, 300 parts of oyster shell whiting, 125 parts of titanium dioxide, 40 parts of talcum powder, 280 parts of acrylic emulsion, 15 parts of adhesion agent, 1 part of ethanol, the concentration of the ethanol is 85%, 3 parts of preservative.
Collocation method is first to mix well and add again component big content the few component content mixing of component plus a small amount of water, then adds part water to mix well again, and all components are gradually added into by this method, and the water of surplus is finally supplied by proportioning, is more than normal-temperature operation.
Embodiment 3
Environment-friendly interior wall coating of the present invention, the coating is made up of following components(In parts by weight):250 parts of water, 3 parts of Herba Ephedrae alkaloid, 8 parts of dispersant, 3 parts of sulfonated oil, 6 parts of paint antifoaming agent, 400 parts of oyster shell whiting, 140 parts of titanium dioxide, 80 parts of talcum powder, 300 parts of acrylic emulsion, 30 parts of adhesion agent, 2 parts of ethanol, the concentration of the ethanol is 90%, 4 parts of preservative.
Collocation method is first to mix well and add again component big content the few component content mixing of component plus a small amount of water, then adds part water to mix well again, and all components are gradually added into by this method, and the water of surplus is finally supplied by proportioning, is more than normal-temperature operation.
In a word, although the present invention illustrates above-mentioned preferred embodiment, although it should be noted that those skilled in the art
Member can carry out various change and remodeling, unless such change and remodeling deviate from the scope of the present invention, otherwise should be construed as being included in protection scope of the present invention.
Claims (3)
1. a kind of environment-friendly interior wall coating, it is characterised in that:The coating is made up of following components:Water 240-
250 parts, alkaloid 1-3 parts, dispersant 2-8 parts, sulfonated oil 2-3 parts, paint antifoaming agent 2-6 parts, oyster shell whiting 250-400 parts, titanium dioxide 120-140 parts, talcum powder 30-80 parts, acrylic emulsion 150-300 parts, adhesion agent 10-30 parts, ethanol 1-2 parts, preservative 2-4 parts, said components are in parts by weight.
2. the environment-friendly interior wall coating according to claim 1, it is characterised in that:The concentration of the ethanol is 80-90%.
3. the environment-friendly interior wall coating according to claim 1, it is characterised in that:The alkaloid is Herba Ephedrae alkaloid.