CN106810724A - A kind of arrangements for automotive doors decoration epidermis and preparation method thereof - Google Patents
A kind of arrangements for automotive doors decoration epidermis and preparation method thereof Download PDFInfo
- Publication number
- CN106810724A CN106810724A CN201611196129.XA CN201611196129A CN106810724A CN 106810724 A CN106810724 A CN 106810724A CN 201611196129 A CN201611196129 A CN 201611196129A CN 106810724 A CN106810724 A CN 106810724A
- Authority
- CN
- China
- Prior art keywords
- parts
- arrangements
- automotive doors
- epidermis
- mao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of arrangements for automotive doors decoration epidermis,The material matched by following parts by weight is made,Including 25 30 parts of polyvinylidene chloride,15 20 parts of polyurethane,11 14 parts of nano aluminium oxide,32 35 parts of Sodium Benzoate,16 22 parts of Nano Silver,16 24 parts of bamboo charcoal powder,9 15 parts of pyrophosphate,12 14 parts of titanium potassium oxalate,35 parts of different n-nonanoic acid,13 14 parts of sulfydryl acid esters,69 parts of ammonium octamolybdate,13 17 parts of potassium ferrocyanide,14 18 parts of Lauxite,31 36 parts of cellulose acetate,15 20 parts of lithium carbonate,26 29 parts of butyl rubber,17 22 parts of 9 14 parts of GMA and MAO,Arrangements for automotive doors Decorative watch leatherware of the invention has antibacterial effect,Material is corrosion-resistant,It is anti-aging,Long service life.
Description
Technical field
The present invention relates to a kind of arrangements for automotive doors decoration epidermis and preparation method thereof.
Background technology
Car door is the passage that the vehicle that comes in and goes out is provided for driver and passenger, and completely cuts off interference outside car, is subtracted to a certain extent
Light side impact, protects occupant.Also the moulding with car door attractive in appearance of automobile is relevant.The quality of car door, is mainly reflected in, car door
Crashworthiness, the sealing property of car door, the folding convenience of car door also has other indexs using function etc. certainly.Crashworthiness
Can be particularly important, because when vehicle occurs side impact, buffer distance is very short, it is easy to just hurt occupant.In good car door extremely
I haven't seen you for ages two collision prevention girders, and the deal of collision prevention girders is heavier, that is to say, that good car door is laid particular stress on really.But can not
Say that car door is more heavy better.Present new automobile, if it be can guarantee that in security performance etc., designer can be by every means
Mitigate weight (such as with new material) of the vehicle including car door to reduce power consumption.Press car door quantity different, can be car point
It is two, three, four, five cars etc..Car for public affair purposes is mostly four, and the car for domestic use is existing
Four also have three and five (back door is raising type), and the sport car of Sport Utility is mostly then two.Car door is by its production work
Skill can be divided into following several:Monoblock type car door:Inner and outer plates are formed by bound edge after monoblock steel plate punched, the first mould of the mode of production
Input cost is larger, but can accordingly reduce related cubing fixture, and stock utilization is relatively low.Split type car door:By door frame assembly
Formed with car door inner and outer plates assembly welding, doorframe assembly can be produced using rolling mode, and cost is relatively low, and productivity ratio is higher, it is overall
Corresponding mould cost is relatively low, but later stage cubing fixture is relatively costly, and reliability of technology is poor.Monoblock type car door and separate type
It is not very big that door is differed in terms of holistic cost, mainly determines related structure type according to related modeling requirement.Due to
Current vehicle configuration requirement is higher, and production efficiency requirement is higher, car door overall structure tend to it is split type.The inspection of new car car door
Look into, whether the frame that first observe new car car door has tiny ripple, whether reexamine the A posts of new car, B posts, C posts problematic,
Whether there is corrosion on the prism that also check new car frame, be here the place for easily going wrong very much, because many people open the door
When, the barrier around vehicle body can be accidentally bumped against, so the lacquer painting corrosion of prism can be caused.
Existing arrangements for automotive doors decoration epidermis does not have antibacterial effect at present, and material is not corrosion-resistant, not anti-aging, uses the longevity
Life is not long.
The content of the invention
In view of this, there is antibacterial effect it is an object of the present invention to provide one kind, material is corrosion-resistant, anti-aging, service life
Arrangements for automotive doors decoration epidermis long.
In order to solve the above-mentioned technical problem, the technical scheme is that:
A kind of arrangements for automotive doors decorates epidermis, and the material matched by following parts by weight is made, including polyvinylidene chloride 25-
30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35 parts, Nano Silver 16-22 parts, bamboo charcoal powder 16-
24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, 13-14 parts of sulfydryl acid esters, ammonium octamolybdate 6-9
Part, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36 parts, lithium carbonate 15-20 parts, butyl rubber
26-29 parts, GMA 9-14 parts and MAO 17-22 parts.
Preferably, be made up of the material that following parts by weight are matched, including 25 parts of polyvinylidene chloride, polyurethane 15
Part, 11 parts of nano aluminium oxide, 32 parts of Sodium Benzoate, 16 parts of Nano Silver, 16 parts of bamboo charcoal powder, 9 parts of pyrophosphate, titanium potassium oxalate 12
Part, 3 parts of different n-nonanoic acid, 13 parts of sulfydryl acid esters, 6 parts of ammonium octamolybdate, 13 parts of potassium ferrocyanide, 14 parts of Lauxite, cellulose acetate
17 parts of 31 parts, 15 parts of lithium carbonate, 26 parts of butyl rubber, 9 parts of GMA and MAO.
Preferably, be made up of the material that following parts by weight are matched, including 27.5 parts of polyvinylidene chloride, polyurethane
17.5 parts, 12.5 parts of nano aluminium oxide, 33.5 parts of Sodium Benzoate, 19 parts of Nano Silver, 20 parts of bamboo charcoal powder, 12 parts of pyrophosphate, grass
13 parts of sour titanium potassium, 4 parts of different n-nonanoic acid, 13.5 parts of sulfydryl acid esters, 7.5 parts of ammonium octamolybdate, 15 parts of potassium ferrocyanide, Lauxite 16
Part, 33.5 parts of cellulose acetate, 17.5 parts of lithium carbonate, 27.5 parts of butyl rubber, 11.5 parts of GMA and
19.5 parts of MAO.
Preferably, be made up of the material that following parts by weight are matched, including 30 parts of polyvinylidene chloride, polyurethane 20
Part, 14 parts of nano aluminium oxide, 35 parts of Sodium Benzoate, 22 parts of Nano Silver, 24 parts of bamboo charcoal powder, 15 parts of pyrophosphate, titanium potassium oxalate 14
Part, 5 parts of different n-nonanoic acid, 14 parts of sulfydryl acid esters, 9 parts of ammonium octamolybdate, 17 parts of potassium ferrocyanide, 18 parts of Lauxite, cellulose acetate
22 parts of 36 parts, 20 parts of lithium carbonate, 29 parts of butyl rubber, 14 parts of GMA and MAO.
The invention solves the problems that another technical problem be that the preparation method that a kind of arrangements for automotive doors decorates epidermis is provided, including with
Lower step:
1) by polyvinylidene chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35
Part, Nano Silver 16-22 parts, bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, mercapto
13-14 parts of base acid esters soaks 6-8 minutes in putting into the hydrochloric acid solution of 1-2%, standby;
2) by step 1) during gained raw material puts into colloid mill, holdings rotating speed is 7800-8000r/min, and stirring 25-30 divides
Clock, it is standby;
3) by ammonium octamolybdate 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36
Part, lithium carbonate 15-20 parts, butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22
Part is put into reactor, and it is 150-200 DEG C to keep heating-up temperature, is heated 6-8 minutes, and rotating speed is 3500- in regulation kettle
4500r/min, it is standby;
4) by step 2) gained raw material and step 3) it is in molten by raw material heating during gained raw material puts into injection machine
State, injection moulding, natural cooling are carried out in injection mould, then put into banbury, and 4mm is transferred in roll spacing, and shaping obtains thin slice i.e.
Can.
The technology of the present invention effect major embodiment is in the following areas:The lithium carbonate of addition, Nano Silver, bamboo charcoal powder and pyrophosphate
With antibacterial effect;The polyvinylidene chloride of addition, butyl rubber, GMA and MAO are caused
Material is corrosion-resistant;The titanium potassium oxalate of addition, different n-nonanoic acid and sulfydryl acid esters have it is anti-aging, the preparation method of use cause raw material into
Type efficiency high, good stability is well mixed.
Specific embodiment
Embodiment 1
A kind of arrangements for automotive doors decorates epidermis, and the material matched by following parts by weight is made, is matched by following parts by weight
Material be made, including 25 parts of polyvinylidene chloride, 15 parts of polyurethane, 11 parts of nano aluminium oxide, 32 parts of Sodium Benzoate, Nano Silver
16 parts, 16 parts of bamboo charcoal powder, 9 parts of pyrophosphate, 12 parts of titanium potassium oxalate, 3 parts of different n-nonanoic acid, 13 parts of sulfydryl acid esters, 6 parts of ammonium octamolybdate,
13 parts of potassium ferrocyanide, 14 parts of Lauxite, 31 parts of cellulose acetate, 15 parts of lithium carbonate, 26 parts of butyl rubber, methacrylic acid
17 parts of 9 parts of ethylene oxidic ester and MAO.
A kind of arrangements for automotive doors decorates the preparation method of epidermis, comprises the following steps:
1) by polyvinylidene chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35
Part, Nano Silver 16-22 parts, bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, mercapto
13-14 parts of base acid esters soaks 6-8 minutes in putting into the hydrochloric acid solution of 1-2%, standby;
2) by step 1) during gained raw material puts into colloid mill, holdings rotating speed is 7800-8000r/min, and stirring 25-30 divides
Clock, it is standby;
3) by ammonium octamolybdate 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36
Part, lithium carbonate 15-20 parts, butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22
Part is put into reactor, and it is 150-200 DEG C to keep heating-up temperature, is heated 6-8 minutes, and rotating speed is 3500- in regulation kettle
4500r/min, it is standby;
4) by step 2) gained raw material and step 3) it is in molten by raw material heating during gained raw material puts into injection machine
State, injection moulding, natural cooling are carried out in injection mould, then put into banbury, and 4mm is transferred in roll spacing, and shaping obtains thin slice i.e.
Can.
Embodiment 2
A kind of arrangements for automotive doors decorates epidermis, and the material matched by following parts by weight is made, is matched by following parts by weight
Material be made, including 25 parts of polyvinylidene chloride, 15 parts of polyurethane, 11 parts of nano aluminium oxide, 32 parts of Sodium Benzoate, Nano Silver
16 parts, 16 parts of bamboo charcoal powder, 9 parts of pyrophosphate, 12 parts of titanium potassium oxalate, 3 parts of different n-nonanoic acid, 13 parts of sulfydryl acid esters, 6 parts of ammonium octamolybdate,
13 parts of potassium ferrocyanide, 14 parts of Lauxite, 31 parts of cellulose acetate, 15 parts of lithium carbonate, 26 parts of butyl rubber, methacrylic acid
17 parts of 9 parts of ethylene oxidic ester and MAO.
A kind of arrangements for automotive doors decorates the preparation method of epidermis, comprises the following steps:
1) by polyvinylidene chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35
Part, Nano Silver 16-22 parts, bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, mercapto
13-14 parts of base acid esters soaks 6-8 minutes in putting into the hydrochloric acid solution of 1-2%, standby;
2) by step 1) during gained raw material puts into colloid mill, holdings rotating speed is 7800-8000r/min, and stirring 25-30 divides
Clock, it is standby;
3) by ammonium octamolybdate 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36
Part, lithium carbonate 15-20 parts, butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22
Part is put into reactor, and it is 150-200 DEG C to keep heating-up temperature, is heated 6-8 minutes, and rotating speed is 3500- in regulation kettle
4500r/min, it is standby;
4) by step 2) gained raw material and step 3) it is in molten by raw material heating during gained raw material puts into injection machine
State, injection moulding, natural cooling are carried out in injection mould, then put into banbury, and 4mm is transferred in roll spacing, and shaping obtains thin slice i.e.
Can.
Embodiment 3
A kind of arrangements for automotive doors decorates epidermis, and the material matched by following parts by weight is made, is matched by following parts by weight
Material be made, including 25 parts of polyvinylidene chloride, 15 parts of polyurethane, 11 parts of nano aluminium oxide, 32 parts of Sodium Benzoate, Nano Silver
16 parts, 16 parts of bamboo charcoal powder, 9 parts of pyrophosphate, 12 parts of titanium potassium oxalate, 3 parts of different n-nonanoic acid, 13 parts of sulfydryl acid esters, 6 parts of ammonium octamolybdate,
13 parts of potassium ferrocyanide, 14 parts of Lauxite, 31 parts of cellulose acetate, 15 parts of lithium carbonate, 26 parts of butyl rubber, methacrylic acid
17 parts of 9 parts of ethylene oxidic ester and MAO.
A kind of arrangements for automotive doors decorates the preparation method of epidermis, comprises the following steps:
1) by polyvinylidene chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35
Part, Nano Silver 16-22 parts, bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, mercapto
13-14 parts of base acid esters soaks 6-8 minutes in putting into the hydrochloric acid solution of 1-2%, standby;
2) by step 1) during gained raw material puts into colloid mill, holdings rotating speed is 7800-8000r/min, and stirring 25-30 divides
Clock, it is standby;
3) by ammonium octamolybdate 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36
Part, lithium carbonate 15-20 parts, butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22
Part is put into reactor, and it is 150-200 DEG C to keep heating-up temperature, is heated 6-8 minutes, and rotating speed is 3500- in regulation kettle
4500r/min, it is standby;
4) by step 2) gained raw material and step 3) it is in molten by raw material heating during gained raw material puts into injection machine
State, injection moulding, natural cooling are carried out in injection mould, then put into banbury, and 4mm is transferred in roll spacing, and shaping obtains thin slice i.e.
Can.
Experimental example
Experimental subjects:Choose general-utility car door trim epidermis, cars door trim epidermis and automobile of the invention
Door trim epidermis is contrasted.
Requirement of experiment:Above-mentioned general-utility car door trim epidermis, cars door trim epidermis and vapour of the invention
Car door trim epidermal thickness is consistent with weight.
Experimental technique:Antibacterial effect is measured using the standard methods of JIS Z 2801;The anti-aging time is by aging examination
Tryoff is detected, and adjusts test temperature temperature for 120 DEG C, and relative humidity is 85%, and air pressure is 106kPa, ozone concentration
It is 45%, ultraviolet illumination intensity is 25uw/cm2, obtains the aging time;Anticorrosion effect uses DB63/T 687-2007
Standard is measured using the wet corrosion resistance test case of superelevation.
Concrete outcome is as shown in the table:
With reference to upper table, the data that different arrangements for automotive doors decorate epidermis gained under identical experimental technique, this hair are contrasted
More preferably, anti-aging and decay resistance is more preferably for the antibacterial effect of bright arrangements for automotive doors decoration epidermis.
The technology of the present invention effect major embodiment is in the following areas:The lithium carbonate of addition, Nano Silver, bamboo charcoal powder and pyrophosphate
With antibacterial effect;The polyvinylidene chloride of addition, butyl rubber, GMA and MAO are caused
Material is corrosion-resistant;The titanium potassium oxalate of addition, different n-nonanoic acid and sulfydryl acid esters have it is anti-aging, the preparation method of use cause raw material into
Type efficiency high, good stability is well mixed.
Certainly, it is more than representative instance of the invention, in addition, the present invention can also have other various specific implementations
The technical scheme that mode, all use equivalents or equivalent transformation are formed, all falls within the scope of protection of present invention.
Claims (5)
1. a kind of arrangements for automotive doors decorates epidermis, it is characterised in that:The material matched by following parts by weight is made, including poly- inclined two
Vinyl chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35 parts, Nano Silver 16-22 parts,
Bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, 13-14 parts of sulfydryl acid esters, eight molybdenums
Sour ammonium 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36 parts, lithium carbonate 15-20 parts,
Butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22 parts.
2. a kind of arrangements for automotive doors as claimed in claim 1 decorates epidermis, it is characterised in that:The material matched by following parts by weight
Material is made, including 25 parts of polyvinylidene chloride, 15 parts of polyurethane, 11 parts of nano aluminium oxide, 32 parts of Sodium Benzoate, Nano Silver 16
Part, 16 parts of bamboo charcoal powder, 9 parts of pyrophosphate, 12 parts of titanium potassium oxalate, 3 parts of different n-nonanoic acid, 13 parts of sulfydryl acid esters, 6 parts of ammonium octamolybdate, Asia
13 parts of the potassium ferricyanide, 14 parts of Lauxite, 31 parts of cellulose acetate, 15 parts of lithium carbonate, 26 parts of butyl rubber, methacrylic acid contracting
17 parts of 9 parts of water glyceride and MAO.
3. a kind of arrangements for automotive doors as claimed in claim 1 decorates epidermis, it is characterised in that:The material matched by following parts by weight
Material is made, including 27.5 parts of polyvinylidene chloride, 17.5 parts of polyurethane, 12.5 parts of nano aluminium oxide, 33.5 parts of Sodium Benzoate, receives
19 parts of rice silver, 20 parts of bamboo charcoal powder, 12 parts of pyrophosphate, 13 parts of titanium potassium oxalate, 4 parts of different n-nonanoic acid, 13.5 parts of sulfydryl acid esters, eight molybdic acids
7.5 parts of ammonium, 15 parts of potassium ferrocyanide, 16 parts of Lauxite, 33.5 parts of cellulose acetate, 17.5 parts of lithium carbonate, butyl rubber
19.5 parts of 27.5 parts, 11.5 parts of GMA and MAO.
4. a kind of arrangements for automotive doors as claimed in claim 1 decorates epidermis, it is characterised in that:The material matched by following parts by weight
Material is made, including 30 parts of polyvinylidene chloride, 20 parts of polyurethane, 14 parts of nano aluminium oxide, 35 parts of Sodium Benzoate, Nano Silver 22
Part, 24 parts of bamboo charcoal powder, 15 parts of pyrophosphate, 14 parts of titanium potassium oxalate, 5 parts of different n-nonanoic acid, 14 parts of sulfydryl acid esters, 9 parts of ammonium octamolybdate, Asia
17 parts of the potassium ferricyanide, 18 parts of Lauxite, 36 parts of cellulose acetate, 20 parts of lithium carbonate, 29 parts of butyl rubber, methacrylic acid contracting
22 parts of 14 parts of water glyceride and MAO.
5. a kind of arrangements for automotive doors decorates the preparation method of epidermis, it is characterised in that:Comprise the following steps:
1) by polyvinylidene chloride 25-30 parts, polyurethane 15-20 parts, nano aluminium oxide 11-14 parts, Sodium Benzoate 32-35 parts,
Nano Silver 16-22 parts, bamboo charcoal powder 16-24 parts, pyrophosphate 9-15 parts, titanium potassium oxalate 12-14 parts, different n-nonanoic acid 3-5 parts, mercaptan acid
Soaked 6-8 minutes in the ester 13-14 parts of hydrochloric acid solution for putting into 1-2%, it is standby;
2) by step 1) during gained raw material puts into colloid mill, holdings rotating speed is 7800-8000r/min, stirring 25-30 minutes,
It is standby;
3) by ammonium octamolybdate 6-9 parts, potassium ferrocyanide 13-17 parts, Lauxite 14-18 parts, cellulose acetate 31-36 parts, carbon
Sour lithium 15-20 parts, butyl rubber 26-29 parts, GMA 9-14 parts and MAO 17-22 parts input
To in reactor, it is 150-200 DEG C to keep heating-up temperature, is heated 6-8 minutes, and rotating speed is 3500-4500r/min in regulation kettle,
It is standby;
4) by step 2) gained raw material and step 3) it is in molten condition, note by raw material heating during gained raw material puts into injection machine
Entering carries out injection moulding, natural cooling in mould, then puts into banbury, and 4mm is transferred in roll spacing, shaping obtains thin slice.