CN106808880A

CN106808880A - A kind of manufacture craft of carved ware from glass and sandstone

Info

Publication number: CN106808880A
Application number: CN201510857599.5A
Authority: CN
Inventors: 姜蕾
Original assignee: Individual
Current assignee: Individual
Priority date: 2015-11-30
Filing date: 2015-11-30
Publication date: 2017-06-09

Abstract

The present invention relates to a kind of manufacture craft of carved ware from glass and sandstone, it comprises the following steps：1) product model is made；2) mold is made；3) glass raw material is processed；4) glue is prepared；5) cast product；6) solidify the demoulding, be made finished product.The casted article step 5) also include：A) laying ground floor cullet make ground floor decorative cover；B) by step 4) prepare glue cast on the ground floor cullet for having spread just；C) cullet in intermediate layer are laid；D) cast again glue；E) particulate cullet are filled, as third layer；F) glue is poured into a mould.Bian processes carved ware from glass and sandstone with manufacture craft of the invention, and small investment, occupied ground are small, low cost, instant effect, and can say capable processing according to processing the need for user.

Description

A kind of manufacture craft of carved ware from glass and sandstone

Technical field

The present invention relates to a kind of manufacture craft of ornament, more particularly to a kind of glass sandstone carving system The manufacture craft of product.

Background technology

Carved ware from glass and sandstone is the senior building ornament materials prepared using cullet, main to use In the place such as family and hotel, restaurant, station, its exploitation, section not only for cullet Save secondary energy sources and open approach, and the high-grade luxurious building better than lithotome can be produced Ornament materials, while also cleaning of social environment, reduces pollution.Current carved ware from glass and sandstone Many to be processed using equipment such as glass-melting furnace, Crystallizing treatment stoves, its equipment investment is more, occupancy Place is big, and complex process, product cost is of a relatively high, and because Mechanized Processing is to difference Granularity, different color and luster cullet position in the material are difficult to control to, it is difficult to according to the need of client Process the product for meeting the requirements of the customers.

The content of the invention

It is an object of the invention to regarding to the issue above, there is provided a kind of small investment, occupied ground be small, Low cost, instant effect, and system can be carved according to the glass sandstone that is processed is processed the need for user The manufacture craft of product.

To achieve the above object, the technical scheme of Bian of the present invention is：

A kind of manufacture craft of carved ware from glass and sandstone, it is characterised in that comprise the following steps：

Product model is made, from the softer material of quality, by 1:1 ratio sculpture products model；

Mold is made, diaphragm capsule is made first, the product model of making is then placed in diaphragm capsule It is interior, then take hydrated lime in powder and add water by 1: 1-1：2 ratios are mixed and stirred for uniformly being formed without The calcium plaster of particle, pours and casts from the diaphragm capsule, hardening5- 10Minute, product model is taken out, Diaphragm capsule is removed, into mold；

Processing glass raw material, is respectively crushed into after the glass cleaning for taking various different colours The glass particle of various granularities；

Prepare glue, extracting epoxy resin or the vertical line of doubling aqueous, Tianna solution, crystalBPress 2： 1：1 ratio mixes equal Uniform；

Cast product, first by step2)The mold being made is balanced, fixed；Next root Need to select step according to product design effect3)The corresponding granularity of processing, the cullet paving of color and luster In the bottom of mold, as ground floor decorative cover, by step4)The glue of preparation casts in On paving cullet just；Then the cullet of larger granularity are selected to fill to products thickness90%, then glue of casting, as intermediate layer；Finally particulate cullet are filled to product thickness, Casting glue, as third layer；

The solidification demoulding, treats step5)After the product solidification of cast, mold is sloughed, be made Finished product.

In step 1) in, the material on the softer ground can be timber, mud or foam.

In the step 2) may also include the step that repairs a die.

In step 1) and step 2) product model and mold production process be additionally included in mould The step of surface is coated with cured layer, cured thickness degree is0.3—0.5MM 。

In step4)Glue in also added with Transparent color oil, its additional proportion is every20mlGlue

One is added to drip color oil in water.

In step5)In also include vibrations mold, the step of closely knit casted article.

Step6)Described solidification can be heat cure, and heating-up temperature is20—200°C 。Heating-up temperature is high can be accelerated hardening time.

Specific embodiment

The manufacture craft of carved ware from glass and sandstone of the present invention, comprises the following steps： 1)Make product model,2)Make mold,3)Processing glass raw material,4)Prepare glue,5)Cast product,6)The solidification demoulding, is made finished product.

The casted article step5)Also include：a)Laying ground floor cullet make ground floor decorative cover,b)By step4)The glue of preparation is cast in first for having spread just On layer cullet；c)The cullet in intermediate layer are laid,d)Cast again glue；_e) filling particulate cullet, as third layer,f)Casting glue.

Below with making30MMGlass sand rock carving system is illustrated as a example by heavy sheet glass sandstone reinforced mud carvings The manufacturing process of product：

From30MMHou Pao Droplets materials, press1: 1Ratio sculpture products model, in model Coat on surface0. 3-0. 5The thick dewaxing liquid of gangster；

Diaphragm capsule is made first, and then the froth pulp model of making is placed in diaphragm capsule, and With about30MMGlass high or batten fix product model, then take hydrated lime in powder add water by1: 2Ratio is mixed and stirred for the calcium plaster that equal Uniform is formed without particle, pours and casts from the diaphragm capsule, hardening 10 minutes（If adding water less than aforementioned proportion such as 1:1, firm time can be with shorter, now stone Cream is harder, and also faster stomata is also less for setting rate), product model is taken out, diaphragm capsule is removed, Into mold, check whether mold is smooth, have zero defect, if being repaired, then by paraffin After melting, in the every nook and cranny of mold, equal Uniform is pouredOne layer about 0.3—0.5MMThick thin wax, with It is easy to the demoulding；

The glass particle of various granularities is respectively crushed into after the glass cleaning for taking shades of colour, its bulky grain should be no more than shelled peanut size extracting epoxy resin or the vertical line of doubling aqueous, Tianna solution, crystalBPress2: 1： 1Ratio mixes equal Uniform, then every20mlAdd one to drip color oil in above-mentioned mixed liquor, be made the glue of slightly light color；

First by step2)The mold being made is balanced, and is around fixed with glass or batten, and mold surrounding and bottom are sealed with glass cement or dewaxing；Secondly the cullet for needing selection slightly broken according to product design effect are layered on the bottom of mold, and thickness is8MMLeft and right, as ground floor decorative cover, by step4)The glue of preparation is cast on the cullet for having spread just；Then select larger granularity cullet fill to27MMThickness, then glue of casting, as intermediate layer； Finally by the particulate cullet of sesame size fill to30MMThickness, glue of casting, used as third layer, and vibrations make its closely knit；

By step5)The product of cast is heated to80°C,Keep8Hour,（Also can be normal Temperature is lower to be kept3 — 7My god）After after product solidification, mold is sloughed, be made finished product.

Claims

1. the manufacture craft of carved ware from glass and sandstone according to claim 1, it is characterised in that：In step 1) in, the material on the softer ground is timber, mud Huo Pao Droplets.

2. according to claim1The manufacture craft of described carved ware from glass and sandstone, its feature It is：In the step 2) also include the step that repairs a die.

3. according to claim1The manufacture craft of described carved ware from glass and sandstone, its feature It is：In step 1) and step 2) product model and mold production process be additionally included in mould The step of tool surface is coated with cured layer, cured thickness degree is0.3—0.5MM 。

4. according to claim1The manufacture craft of described carved ware from glass and sandstone, its feature It is：In step4)Glue in also added with Transparent color oil, its additional proportion is every20mlOne is added to drip color oil in glue.

5. the manufacture craft of carved ware from glass and sandstone according to claim 1, its feature It is：In step5)In also include vibrations mold, the step of closely knit casted article.

6. according to claim1The manufacture craft of described carved ware from glass and sandstone, its feature It is：Step6)Described is cured as heat cure, and heating-up temperature is20—200°C 。