CN106800853B - A kind of bathroom product coating and the preparation method and application thereof - Google Patents
A kind of bathroom product coating and the preparation method and application thereof Download PDFInfo
- Publication number
- CN106800853B CN106800853B CN201611257324.9A CN201611257324A CN106800853B CN 106800853 B CN106800853 B CN 106800853B CN 201611257324 A CN201611257324 A CN 201611257324A CN 106800853 B CN106800853 B CN 106800853B
- Authority
- CN
- China
- Prior art keywords
- parts
- priming paint
- fluorine
- bathroom product
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of bathroom product coating and the preparation method and application thereof, and bathroom product is made of with coating priming paint and finishing coat, and the raw material for preparing priming paint includes: polyacrylate emulsion, polyoxyethylene ether, calcium carbonate, food-grade barium sulfate；The raw material for preparing finishing coat includes: fluorine silicon carbon compound, polysiloxanes, poly- fluorine carbene, silane coupling agent, calcium carbonate, food-grade barium sulfate, silica, kaolin, titanium dioxide, defoaming agent；Preparation method: priming paint raw material is mixed, and obtains bright uniform mixed liquor to get priming paint；Fluorine silicon carbon compound, polysiloxanes, poly- fluorine carbene are mixed evenly, then successively silane coupling agent, calcium carbonate, food-grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent, uniformly sticky white oil liquid is stirred to get to get finishing coat.Bathroom product produced by the present invention can be good with water-resistant coating, and fungistatic effect is stablized, firm durable, and service life is stablized.
Description
Technical field
The present invention relates to coating composition fields, and in particular to a kind of bathroom product coating and preparation method thereof with answer
With.
Background technique
Coating is the laminar film material coated in body surface, thus the effects of playing protection, decoration and mark.It defends
Product is bathed, is the utensil used in the places such as toilet and bathroom, mostly ceramic-like and anti-rust metal class.Bathroom product makes
With ambient humidity is big, steam is heavy, temperature is high, bacterium easy to breed.Therefore, bathroom product surface can be carried out at coating coating
Reason, coating used must have the characteristics that hydrophobic antirust, antibacterial anti-pollution, solid durable, while must also have good skin to contact
Compatibility.
Presently commercially available toilet warterproof coating mainly may be summarized to be following a few classes: non-tar polyurethane waterproof applies
Material, acrylate waterproof paint, waterproof coating material of cement based polymer, novel JS type composite water-proof paint etc..In toilet decoration
When using above-mentioned classification coating can play good waterproof effect.However specific to bathroom product aspect, the painting of these types
Material can not be applicable in completely.The corrosion resistance of polyurethane-type coating and acrylic ester type coating is weaker, and cement base polymerize
Object coating and JS type composite coating more contain a certain proportion of inorganic material component, should not be used as sanitary ware coating.So needing
Design a kind of coating that suitable sanitary ware uses.
Fluorocarbon coating show hydrophobicity is strong, weatherability is high, adhesive force is big, chemical inertness is good, anti-microbial property is good, cleaning effect
The excellent many merits of fruit, comprehensive using effect are outstanding.In addition to this, the various numerous silicon trees constituted using silicon oxygen bond structure as core
Rouge or silicone rubber kinds material have outstanding biocompatibility.It can be seen that by fluorine carbon coating and silicone resin or fluorine silicon
Resin material carries out inventive combination, can obtain a kind of new coating used suitable for sanitary ware.
Chinese patent CN201510224619.5 discloses a kind of powdery paints for polypropylene sanitaryware and preparation
Methods and applications, using Special Resin, extraordinary curing agent, filler, pigment, adhesion promoter, auxiliary agent as raw material.But the patent
Adhesive force between the PP type coating and ceramic sanitary ware product of invention is weaker, de- using being easy under hygrothermal environment for a long time
It opens, and effective antifouling effect cannot be played.
Therefore, it is necessary to invent a kind of new coating based on fluorine silicon carbon compound, suitable for bathroom product.
Summary of the invention
The present invention is in view of the above-mentioned problems, provide a kind of bathroom product coating and the preparation method and application thereof.
Technical solution used by the present invention solves the above problems is: a kind of bathroom product coating, by priming paint and finishing coat
Composition, the raw material and its parts by weight for preparing priming paint include: 50 parts~70 parts of polyacrylate emulsion, polyoxyethylene ether 5 parts~8
Part, 1 part~1.5 parts of calcium carbonate, 0.5 part~1 part of food-grade barium sulfate；The raw material and its parts by weight for preparing finishing coat include: fluorine silicon
30 parts~40 parts of carbon compound, 20 parts~25 parts of polysiloxanes, 12 parts~18 parts of poly- fluorine carbene, 5 parts~7 parts of silane coupling agent,
0.8 part~1.5 parts of calcium carbonate, 0.3 part~0.7 part of food-grade barium sulfate, 0.4 part~0.8 part of silica, 0.2 part of kaolin
~0.5 part, 5 parts~8 parts of titanium dioxide, 2 parts~4 parts of defoaming agent；Wherein, fluorine silicon carbon compound is trifluoro propyl trimethyl silicane oxygen
Alkane, ten trifluoro octyl trimethoxy silanes, perfluoro capryl triethoxysilane, any in 17 fluorine ruthenium trimethoxysilanes
Kind is several.
Wherein using polyacrylate emulsion as the main film forming substance in priming paint, drying property is good；Polyoxy second
Alkene ether is used as surfactant, the contact wettability between reinforced polypropylene acid esters emulsion and bathroom product matrix,
Improve the flowing ride comfort of polyacrylate emulsion；Calcium carbonate and food-grade barium sulfate collectively constitute priming paint filler, and appropriateness increases
The sliminess for adding priming paint can also adjust the color of priming paint；
It, will using fluorine silicon carbon compound, polysiloxanes, according to fluorine carbene and silane coupling agent as the principle active component of finishing coat
This several substance is combined, and so that finishing coat is had outstanding hydrophobic performance, is improved the corrosion resistance of finishing coat, while and priming paint
With good matching；Calcium carbonate, food-grade barium sulfate, silica and kaolin have collectively constituted the filler of finishing coat, make
The wear-resisting property of finishing coat is improved, while keeping finishing coat granular size more uniform, is conducive to levelling；Titanium dioxide is as white face
Material uses, durable, mutually agrees with bathroom product color；Organic silicon defoaming agent for elimination prepare during finishing coat due to
The small air bubble for stirring and bringing into.
Further, the raw material for preparing the priming paint further includes any one of adhesion promoter, levelling agent or two kinds,
Additive amount is no more than the 2%~4% of priming paint raw material gross weight.
Further, adhesion promoter are as follows: cyano-acetoxy class adhesion promoter or the attachment of urea ring class are made every effort to promote
Into agent.
Further, levelling agent is poly(silicon aether) type levelling agent, polysiloxane type levelling agent, appointing in fluorine carbon type levelling agent
It is one or more of.
Further, defoaming agent are as follows: organic silicon defoaming agent.
Another goal of the invention of the invention, is to provide a kind of preparation method of above-mentioned bathroom product coating, including with
Lower step:
Step S1, prepares priming paint: the priming paint raw material of the parts by weight being mixed, is adopted under the conditions of 25 DEG C~35 DEG C of temperature
4h~8h is continuously stirred with the revolving speed of 80r/min~120r/min with magnetic stirring apparatus, obtains bright uniform mixed liquor, i.e.,
Obtain priming paint；
Step S2, prepares finishing coat: the fluorine silicon carbon compound of the parts by weight, polysiloxanes, poly- fluorine carbene being mixed, 5
DEG C~20 DEG C at a temperature of stirred evenly with the revolving speed of 150r/min~250r/min, then sequentially add the silane of the parts by weight
Coupling agent, calcium carbonate, food-grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent, then with 200r/min~
The revolving speed of 300r/min stirs 2h~3h, obtains uniformly sticky white oil liquid to get finishing coat；
Step S3, when using coating, first in three layers of bathroom product outer surface spray-applied primer, after to be dried, then in priming paint
Two layers of spray paint above are spontaneously dried to whole lacquer paintings.
Further, in step S1, the drying time of mixed liquor are as follows: 60min~120min.
Further, in step S1, the viscosity of mixed liquor are as follows: 18000 centipoises~25000 centipoises.
Further, in step S2, the viscosity of white oil liquid are as follows: 15000 centipoises~22000 centipoises.
Another goal of the invention of the invention is to provide a kind of above-mentioned bathroom product coating or above-mentioned preparation method system
The application of the bathroom product coating obtained, in squat type closestool, bathtub, bathroom cabinet, tap, shower, bathroom metallic support
In any outer surface coat and use.
The invention has the advantages that
1. the present invention is constituted bathroom product coating using fluorine silicon-carbon class compound as main body, water resistance is good, antibacterial
Effect stability, firm durable, service life is stablized；Wherein using polyacrylate emulsion as the main film forming in priming paint
Substance, drying property are good；Polyoxyethylene ether is used as surfactant, reinforced polypropylene acid esters emulsion and bathroom system
Contact wettability between product matrix improves the flowing ride comfort of polyacrylate emulsion；Calcium carbonate and food-grade sulfuric acid
Barium collectively constitutes priming paint filler, and appropriateness increases the sliminess of priming paint, can also adjust the color of priming paint；With fluorine silicon carbon compound,
This several substance is combined, makes face by polysiloxanes, the principle active component according to fluorine carbene and silane coupling agent as finishing coat
Paint has outstanding hydrophobic performance, improves the corrosion resistance of finishing coat, while having good matching with priming paint；Carbonic acid
Calcium, food-grade barium sulfate, silica and kaolin have collectively constituted the filler of finishing coat, change the wear-resisting property of finishing coat
It is kind, while keeping finishing coat granular size more uniform, it is conducive to levelling；Titanium dioxide is used as white pigment, durable, and is defended
Bath product color is mutually agreed with；Organic silicon defoaming agent prepares the small air brought into during finishing coat due to stirring for elimination
Bubble；
2. the preparation method of present invention production bathroom product coating is easy, product condition is stablized；
3. bathroom product produced by the present invention can be applied not only to field of sanitary ware with coating, can also in low temperature and
It is used in terms of metal protection under hygrothermal environment.
Specific embodiment
The embodiment of the present invention is described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Embodiment 1
A kind of bathroom product coating, is made of priming paint and finishing coat, and the raw material and its parts by weight for preparing priming paint include: poly- third
50 parts of olefin(e) acid ester emulsion, 5 parts of polyoxyethylene ether, 1 part of calcium carbonate, 0.5 part of food-grade barium sulfate, the attachment of cyano-acetoxy class
2.35 parts of power promotor；The raw material and its parts by weight for preparing finishing coat include: 30 parts of trifluoro propyl trimethicone, polysiloxanes
20 parts, 12 parts of poly- fluorine carbene, 5 parts of silane coupling agent, 0.8 part of calcium carbonate, 0.3 part of food-grade barium sulfate, 0.4 part of silica,
0.2 part of kaolin, 5 parts of titanium dioxide, 2 parts of organic silicon defoaming agent.
Embodiment 2
A kind of bathroom product coating, is made of priming paint and finishing coat, and the raw material and its parts by weight for preparing priming paint include: poly- third
70 parts of olefin(e) acid ester emulsion, 8 parts of polyoxyethylene ether, 1.5 parts of calcium carbonate, 1 part of food-grade barium sulfate, urea ring class adhesion promoter
0.8 part, 0.4 part of polysiloxane type levelling agent, 0.44 part of levelling agent of fluorine carbon type；The raw material and its parts by weight for preparing finishing coat include:
10 parts of trifluoro propyl trimethicone, ten 12 parts of trifluoro octyl trimethoxy silanes, 15 parts of perfluoro capryl triethoxysilane,
17 3 parts of fluorine ruthenium trimethoxysilanes, 25 parts of polysiloxanes, 18 parts of poly- fluorine carbene, 7 parts of silane coupling agent, calcium carbonate 1.5
Part, 0.7 part of food-grade barium sulfate, 0.8 part of silica, 0.5 part of kaolin, 8 parts of titanium dioxide, 4 parts of organic silicon defoaming agent.
Embodiment 3
A kind of bathroom product coating, is made of priming paint and finishing coat, and the raw material and its parts by weight for preparing priming paint include: poly- third
60 parts of olefin(e) acid ester emulsion, 6.5 parts of polyoxyethylene ether, 1.2 parts of calcium carbonate, 0.7 part of food-grade barium sulfate, fluorine carbon type levelling agent
2.1 part；The raw material and its parts by weight for preparing finishing coat include: 15 parts of perfluoro capryl triethoxysilane, 17 fluorine decyl trimethoxies
20 parts of base silane, 22 parts of polysiloxanes, 15 parts of poly- fluorine carbene, 5 parts of silane coupling agent, 1.2 parts of calcium carbonate, food-grade barium sulfate
0.5 part, 0.6 part of silica, 0.3 part of kaolin, 6.5 parts of titanium dioxide, 3 parts of organic silicon defoaming agent.
Embodiment 4
A kind of preparation method of bathroom product coating, comprising the following steps:
Step S1, prepares priming paint: the priming paint raw material of the parts by weight being mixed, magnetic force is used under the conditions of 25 DEG C of temperature
Agitating device continuously stirs 4h with the revolving speed of 80r/min, obtains bright uniform mixed liquor to get priming paint；Wherein, mixed liquor
Drying time is 60min, is 18000 centipoises；
Step S2, prepares finishing coat: the fluorine silicon carbon compound of the parts by weight, polysiloxanes, poly- fluorine carbene being mixed, 5
It is stirred evenly at a temperature of DEG C with the revolving speed of 150r/min, then sequentially adds the silane coupling agent, calcium carbonate, food of the parts by weight
Then grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent stir 2h with the revolving speed of 200r/min, obtain
Even sticky white oil liquid is to get finishing coat；Wherein, the viscosity of white oil liquid is 15000 centipoises；
Step S3, when using coating, first in three layers of bathroom product outer surface spray-applied primer, after to be dried, then in priming paint
Two layers of spray paint above are spontaneously dried to whole lacquer paintings.
Embodiment 5
A kind of preparation method of bathroom product coating, comprising the following steps:
Step S1, prepares priming paint: the priming paint raw material of the parts by weight being mixed, magnetic force is used under the conditions of 35 DEG C of temperature
Agitating device continuously stirs 8h with the revolving speed of 120r/min, obtains bright uniform mixed liquor to get priming paint；Wherein, mixed liquor
Drying time be 120min, viscosity be 25000 centipoises；
Step S2, prepares finishing coat: the fluorine silicon carbon compound of the parts by weight, polysiloxanes, poly- fluorine carbene being mixed, 20
It is stirred evenly at a temperature of DEG C with the revolving speed of 250r/min, then sequentially adds the silane coupling agent, calcium carbonate, food of the parts by weight
Then grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent stir 3h with the revolving speed of 300r/min, obtain
Even sticky white oil liquid is to get finishing coat；Wherein, the viscosity of white oil liquid is 22000 centipoises；
Step S3, when using coating, first in three layers of bathroom product outer surface spray-applied primer, after to be dried, then in priming paint
Two layers of spray paint above are spontaneously dried to whole lacquer paintings.
Embodiment 6
A kind of preparation method of bathroom product coating, comprising the following steps:
Step S1, prepares priming paint: the priming paint raw material of the parts by weight being mixed, magnetic force is used under the conditions of 30 DEG C of temperature
Agitating device continuously stirs 6h with the revolving speed of 100r/min, obtains bright uniform mixed liquor to get priming paint；Wherein, mixed liquor
Drying time be 90min, viscosity be 22000 centipoises；
Step S2, prepares finishing coat: the fluorine silicon carbon compound of the parts by weight, polysiloxanes, poly- fluorine carbene being mixed, 15
It is stirred evenly at a temperature of DEG C with the revolving speed of 200r/min, then sequentially adds the silane coupling agent, calcium carbonate, food of the parts by weight
Then grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent stir 2.5h with the revolving speed of 250r/min, obtain
Uniformly sticky white oil liquid is to get finishing coat；Wherein, the viscosity of white oil liquid is 18000 centipoises；
Step S3, when using coating, first in three layers of bathroom product outer surface spray-applied primer, after to be dried, then in priming paint
Two layers of spray paint above are spontaneously dried to whole lacquer paintings.
Embodiment 7
The bathroom product coating being prepared is coated on the outer surface of squat type closestool in use, first in toilet seat
Three layers of spray-applied primer of formula closestool outer surface, after to be dried, then two layers of spray paint on priming paint, it is spontaneously dried to whole lacquer paintings
?.
Embodiment 8
The bathroom product coating being prepared is coated to use on the outer surface of bathroom metallic support, is being bathed first
Room three floor of metallic support outer surface spray-applied primer, after to be dried, then two layers of spray paint on priming paint, certainly to whole lacquer paintings
It is so dry.
Embodiment 9
The bathroom product coating being prepared is coated to use on the outer surface of bathtub, is sprayed first in bathtub outer surface
It primes three layers, after to be dried, then two layers of spray paint on priming paint, it is spontaneously dried to whole lacquer paintings.
Experimental example 1
The performance for the bathroom product coating that Examples 1 to 6 is prepared is tested, test result is as shown in table 1.
Wherein, antibiotic property is according to GB/T21866-2008 standard testing；Waterproofness is according to GB/T16777-2008 standard testing；Heat resistance
According to GB/T16777-2008 standard testing；Adhesion strength is according to GB/T16777-2008 standard testing.
The performance test results of bathroom product coating made from table 1
As a result: coating made from Examples 1 to 6 reliably can inhibit common bacteria to breed, waterproof heat resistant, and with bathroom system
Product are easy to form to consolidate solid adhesive layer.
Conclusion: bathroom product made from the application is firm with coating protecting performance, practical.
These are only the preferred embodiment of the present invention, is not intended to restrict the invention, for those skilled in the art
For member, the invention may be variously modified and varied.All within the spirits and principles of the present invention, it is made it is any modification,
Equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of bathroom product coating, is made of priming paint and finishing coat, which is characterized in that prepare the raw material and its again of the priming paint
Amount part includes: 50 parts~70 parts of polyacrylate emulsion, and 5 parts~8 parts of polyoxyethylene ether, 1 part~1.5 parts of calcium carbonate, food
0.5 part~1 part of barium sulfate of grade；The raw material and its parts by weight for preparing the finishing coat include: 30 parts~40 parts of fluorine silicon carbon compound, are gathered
20 parts~25 parts of siloxanes, 12 parts~18 parts of poly- fluorine carbene, 5 parts~7 parts of silane coupling agent, 0.8 part~1.5 parts of calcium carbonate, food
0.3 part~0.7 part of grade barium sulfate, 0.4 part~0.8 part of silica, 0.2 part~0.5 part of kaolin, titanium dioxide 5 parts~8
Part, 2 parts~4 parts of defoaming agent；Wherein, the fluorine silicon carbon compound is trifluoro propyl trimethicone, ten trifluoro octyl front threes
Any one or more of oxysilane, perfluoro capryl triethoxysilane, 17 fluorine ruthenium trimethoxysilanes.
2. bathroom product coating according to claim 1, which is characterized in that it further includes attached for preparing the raw material of the priming paint
Any one of adhesion promoter, levelling agent or two kinds, additive amount are no more than the 2%~4% of priming paint raw material gross weight.
3. bathroom product coating according to claim 2, which is characterized in that the adhesion promoter are as follows: cyano second
Acyl-oxygen base class adhesion promoter or urea ring class adhesion promoter.
4. bathroom product coating according to claim 2, which is characterized in that the levelling agent is poly(silicon aether) type levelling
Any one or more of agent, polysiloxane type levelling agent, fluorine carbon type levelling agent.
5. bathroom product coating according to claim 1, which is characterized in that the defoaming agent are as follows: organic silicon defoaming
Agent.
6. a kind of preparation method of bathroom product coating according to any one of claims 1 to 5, which is characterized in that
The following steps are included:
Step S1, prepares priming paint: the priming paint raw material of the parts by weight being mixed, magnetic is used under the conditions of 25 DEG C~35 DEG C of temperature
Power agitating device continuously stirs 4h~8h with the revolving speed of 80r/min~120r/min, obtains bright uniform mixed liquor the bottom of to get
Paint；
Step S2, prepares finishing coat: by the fluorine silicon carbon compound of the parts by weight, polysiloxanes, poly- fluorine carbene mix, 5 DEG C~
It is stirred evenly at a temperature of 20 DEG C with the revolving speed of 150r/min~250r/min, then sequentially adds the silane coupled of the parts by weight
Agent, calcium carbonate, food-grade barium sulfate, silica, kaolin, titanium dioxide and defoaming agent, then with 200r/min~300r/
The revolving speed of min stirs 2h~3h, obtains uniformly sticky white oil liquid to get finishing coat；
Step S3, when using coating, first in three layers of bathroom product outer surface spray-applied primer, after to be dried, then on priming paint
It two layers of spray paint, is spontaneously dried to whole lacquer paintings.
7. preparation method according to claim 6, which is characterized in that in step S1, the drying time of the mixed liquor are as follows:
60min~120min.
8. preparation method according to claim 6, which is characterized in that in step S1, the viscosity of the mixed liquor are as follows:
18000 centipoises~25000 centipoises.
9. preparation method according to claim 6, which is characterized in that in step S2, the viscosity of the white oil liquid
Are as follows: 15000 centipoises~22000 centipoises.
10. any in a kind of bathroom product coating according to any one of claims 1 to 5 or claim 6~9
The application of bathroom product coating made from preparation method described in, which is characterized in that in squat type closestool, bathtub, bathroom
Cabinet, tap, shower, outer surface any in bathroom metallic support, which coat, to be used.