CN106757602A - Fabric containing quantum energy fiber and preparation method thereof - Google Patents
Fabric containing quantum energy fiber and preparation method thereof Download PDFInfo
- Publication number
- CN106757602A CN106757602A CN201611180728.2A CN201611180728A CN106757602A CN 106757602 A CN106757602 A CN 106757602A CN 201611180728 A CN201611180728 A CN 201611180728A CN 106757602 A CN106757602 A CN 106757602A
- Authority
- CN
- China
- Prior art keywords
- quantum energy
- fiber
- content
- fabric
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fabric containing quantum energy fiber, include quantum energy fiber, FRC, stainless steel fibre and regenerated bamboo fiber, by weight, the content of the quantum energy fiber is 15% 25%, the content of the FRC is 20% 50%, the content of the stainless steel fibre is 1% 10%, and remaining is regenerated bamboo fiber.The present invention has advantages below and effect：Quantum energy fiber has excellent physical and chemical performance, with far infrared medical health care function, flame-retardant adhesive viscose rayon has good fire resistance, and not only friction factor is small between stainless steel fibre and FRC, and quiet, dynamic frictional coefficient is approached, and may be such that fabric is soft.Fabric not only has the repertoire of quantum energy fiber, it may have fire-retardant, antistatic and antibacterial and other effects, while stainless steel fibre can increase the activity of quantum energy present in quantum energy fiber energy so that the far infrared medical health effect of fabric is more preferable.
Description
Technical field
The present invention relates to fabric field, the fabric more particularly to containing quantum energy fiber and preparation method thereof.
Background technology
It is by a kind of release of QuantumEnergy companies of South Korea exploitation that quantum energy newly merges fiber (abbreviation quantum energy fiber)
The fiber of energy of a quantum.The fiber is after being ground into 500 nano-particles and the mixing of pure distilled water with inorganic ore, by a timing
Between fermentation process, quantum in absorption air and the quantum energy that is changed into the permanent natural heat energy of release and quantum energy occurs
Material, then implements melting radiation, the fibrous material of manufacture release quantum energy to it.The home textile product produced using the fiber is had
There are cool in summer and warm in winter, hydroscopic fast-drying, antibacterial deodorization and the function such as capable of releasing far infrared ray, be ecological, heath-function of new generation
Fiber.
At present, in the market application publication number is CN102767004A, and Shen Qing Publication day is that the China in November, 2012 No. 7 is special
Profit discloses the preparation method of a kind of quantum energy fibre blending yarn, fabric prepared therefrom and the fabric, including quantum energy is new
Fusion fiber, its percentage by weight is >=30%.The fabric prepared by the quantum energy fibre blending yarn is also provided, with
And the method for preparing the fabric.Exploitation to quantum energy fibre blending yarn and fabric employs blending mode, so both compared with
The good quantum energy that solves newly merges the relatively low weakness of fiber monofilament strength, and the function that quantum energy newly merges fiber has been played again
Characteristic.The home textile product that quantum energy newly merges fiber production has cool in summer and warm in winter, hydroscopic fast-drying, antibacterial deodorization and releasable remote
The functions such as infrared ray, are ecological, heath-function fibers of new generation.
Although this quantum energy newly merges fiber with cool in summer and warm in winter, hydroscopic fast-drying, antibacterial deodorization and other effects, this
Quantum energy newly merges fiber does not have antistatic, fire-retardant, it is impossible to electrostatic is easily produced for colliery, oil field, chemical industry etc. and causes fire
The engineering safety protection field of calamity.
The content of the invention
It is an object of the invention to provide a kind of fabric containing quantum energy fiber, with anlistatig effect.
Above-mentioned technical purpose of the invention technical scheme is that：A kind of face containing quantum energy fiber
Material, includes quantum energy fiber, FRC, stainless steel fibre and regenerated bamboo fiber, by weight, the quantum energy
The content of fiber is 15%-25%, and the content of the FRC is 20%-50%, the content of the stainless steel fibre
It is 1%-10%, remaining is regenerated bamboo fiber.
The further setting of the present invention is：The content of the quantum energy fiber is 17.5%-22.5%, the anti-flaming viscose
The content of fiber is 25%-40%, and the content of the stainless steel fibre is 1%-5%, and remaining is regenerated bamboo fiber.
The further setting of the present invention is：The content of the quantum energy fiber has 19.5%, the FRC
Content is 38%, and the content of the stainless steel fibre is 1%, and remaining is regenerated bamboo fiber.
There is excellent physical and chemical performance by using such scheme, quantum energy fiber, with far infrared health care
Function, flame-retardant adhesive viscose rayon has good fire resistance, is not only rubbed between stainless steel fibre and FRC
Factor is small, and Er Qiejing, dynamic frictional coefficient are approached, and may be such that fabric is soft.And when the places such as colliery carry out operation, ground
The bacterium of lower presence is also more, and regenerated bamboo fiber has unique antibacterial effect, can suppress the growth of bacterium.Finally cause face
Material not only has the repertoire of quantum energy fiber, it may have fire-retardant, antistatic and antibacterial and other effects, while stainless steel fibre
The activity of quantum energy present in quantum energy fiber energy can be increased so that the far infrared medical health effect of fabric is more preferable.
The purpose of the present invention also provides a kind of preparation method of the fabric containing quantum energy fiber.
Above-mentioned technical purpose of the invention technical scheme is that：One kind is by claim 1 to power
Profit requires the preparation method of the fabric containing quantum energy fiber described in any claim in 3, comprises the following steps：Spin → knit
Make → dyeing and finishing；(1) spinning process：Step 1：Regenerated bamboo fiber：Grab cotton (griping cotton machine) → shredding (opener) → coiled (coiled
Machine) → combing (carding machine) → drafting (drawing frame) → rove (fly frame), finally give A rove；Step 2：Quantum energy fiber,
FRC, stainless steel fibre：Cotton (griping cotton machine) → shredding (opener) → enter to the fiber after three kinds of shreddings is grabbed respectively
Row mixing (fiber mixer) → coiled (lapper) → combing (carding machine) → drafting (drawing frame) → rove (fly frame), most
B rove is obtained eventually；Step 3：Spun yarn (A rove feeds the spun yarn middle roller of spinning frame, and B rove feeds the spun yarn rear roller of spun yarn)
→ winder (bobbin-winding machine)；(2) weaving process：Warping → sizing → denting → jacquard fabric；(3) dyeing and finishing technology：It is put into mixing dye
Contaminated on liquid, time 10min → high temperature fixation, 200 DEG C of temperature, time 40min, fixation formula of liquid is：Soda ash 8-20g/L, salt
20-30g/L → washing, temperature 60 C, time 30min, the dispersion stain → soap of non-set after removal stock-dye → rear whole
Reason processing → drying.
B rove is can be derived that by using such scheme, quantum energy fiber, stainless steel fibre and FRC,
The A rove of regenerated bamboo fiber is fed into spinning frame simultaneously, because A rove is different with the fibre length of B rove, can be obtained in spun yarn
Go out the effect of the disconnected coloured silk yarn of stormy waves so that regenerated bamboo fiber can uniformly be distributed, and the overall anti-microbial property of fabric is more excellent.
The further setting of the present invention is：When step 1 is processed, humidification process is carried out to processing site so that relative humidity
Be 70%-80%, and spray water uniformly sprayed to the regeneration bamboo-carbon fibre after shredding, and stand 2-3 hours and carry out subsequently plus
Work.
By using such scheme, regenerated bamboo fiber moisture adsorption and releasing ability is especially strong, in the processing site weaving that humidity is relatively low
When, substantial amounts of electrostatic can be produced, cause roller, roller and the fleece of doffer's output is hiked up on carding machine, influence spinning matter
Amount.Air is more dry simultaneously more is also easy to produce electrostatic, and relative humidity (RH) has a direct impact to the performance of surface stored charge, phase
Higher to humidity, the time of storage of objects electric charge is shorter, and the mode that surface charge reduces (because relative humidity increases) can lead to
Cross compound or conduct, when relative humidity increases, the electrical conductivity of air is consequently increased.Carried out at humidification by regenerated fiber
Reason so that be conducive to suppressing the generation of electric charge, promote the leakage of electric charge, so as to improve electrostatic phenomenon, in the absence of wet viscous phenomenon, spins
Yarn is smooth.
The further setting of the present invention is：When step 3 is processed, the spinning speed of spinning frame is reduced, take the spinning speed to be
4500 revs/min -5500 revs/min.
By using such scheme, because stainless steel fibre proportion is 5-8 times of general fibre, it is centrifuged when spinning speed is too fast
Power is bigger than normal, so as to breakage phenomena occur.By reducing the spinning speed of spinning frame, reduce the centrifugal force of yarn, so as to reduce
End breakage rate, improves spinning efficiency.
The further setting of the present invention is：By weight, the Final finishing processing includes antistatic process, the composition of formula
It is as follows with ratio：Antistatic additive 6g；Glacial acetic acid 0.5g；Softening agent 3g；Water 1L.
The antibacterial effect of fabric can be increased by using such scheme, antistatic additive, softening agent can increase fabric
Flexibility so that fabric touches up more comfortable smooth, and glacial acetic acid can increase the color fastness of fabric.
The further setting of the present invention is：Fabric after the postfinishing process also needs to carry out calendering, temperature 70 C, car
Fast 30m/min.
By using such scheme, calendering can increase surface brightness, while because there is stainless steel fibre in fabric, its car
Speed is also appropriate to be reduced to 30m/min.
In sum, the invention has the advantages that：By the preparation method so that quantum energy fiber, stainless steel
Fiber, viscose fibre and regenerated bamboo fiber can be mixed uniformly so that during spun yarn, because of A rove and B rove
Fibre length it is different, the effect of the disconnected coloured silk yarn of stormy waves can be formed in spun yarn；Stainless steel fibre in fabric also being capable of Zhan Eng
The liveness of quantum energy in family's quantum energy fiber, while the antistatic behaviour having, anti-flammability and antibacterial effect are also more notable,
Suitable for various places.
Specific embodiment
Technical solution of the present invention is not limited to act specific embodiment set forth below, also including between each specific embodiment
Any combination.
Fabric containing quantum energy fiber, includes quantum energy fiber, FRC, stainless steel fibre and regeneration bamboo
Fiber, the degree of each component is by weight.Referring to table 1, table 1 is the embodiment of the present invention to design parameter in each embodiment
The related data of 1 to embodiment 5.
Table 1 is related data of the embodiment of the present invention 1 to embodiment 5.
Shown by embodiment 1-5, the content that stainless steel fibre contains increases, the fracture strength for mixing spun yarn becomes in reduction
Gesture, while being not very big on the antistatic rate influence of fabric, in order that obtaining fabric while stainless steel fibre content increases
With good antistatic rate and united fracture strength, stainless steel fibre content is better closer to 1%, chooses stainless steel fine
Dimension hplc is 1%.The fracture strength of spun yarn is higher, and its elongation at break is just relatively lower.
The far infrared transmissivity of fabric rises with the rising of quantum energy fiber content simultaneously, but to 20% or so
When, the increased effect of far infrared emissivity not obvious, while because quantum energy fiber is used as a kind of new fibrous material,
Its purchase cost is higher, while ensureing that fabric has good far infrared transmissivity, controls its production cost.
The content that fire-retardant rate and antibiotic rate have FRC and regenerated bamboo fiber respectively is determined.
To sum up, when the technical program stainless steel fibre content is 1%, fabric have good antistatic effect and
Fracture strength.
The preparation method of the fabric containing quantum energy fiber in of the invention, including spinning → weaving → dyeing and finishing.
Spinning process：Step 1：Regenerated bamboo fiber：Grab cotton (griping cotton machine) → shredding (opener) → coiled (lapper) →
Combing (carding machine) → drafting (drawing frame) → rove (fly frame), finally gives A rove；Step 2：It is quantum energy fiber, fire-retardant
Viscose rayon, stainless steel fibre：Cotton (griping cotton machine) → shredding (opener) → mixed to the fiber after three kinds of shreddings is grabbed respectively
(fiber mixer) → coiled (lapper) → combing (carding machine) → drafting (drawing frame) → rove (fly frame) is closed, it is final to obtain
To B rove；Step 3：Spun yarn (A rove feeds the spun yarn middle roller of spinning frame, and B rove feeds the spun yarn rear roller of spun yarn) → network
Cylinder (bobbin-winding machine).In step 1, humidification process is carried out to processing site so that relative humidity is 70%-80%, and to shredding
Regeneration bamboo-carbon fibre afterwards uniformly sprays spray water, and stands 2-3 hours and carry out following process；When step 3 is processed, reduce thin
The spinning speed of yarn machine, it is 4500 revs/min -5500 revs/min to take spinning speed.
Weaving process：Weaving process：Warping → sizing → denting → jacquard fabric.It is noted that tensioner control yarn tension
Uniformity, while the speed of integral weaving be intended to reduce, it is to avoid there is breakage phenomena because there is stainless steel fibre.
Whole dyeing technique：It is put on mixing dye liquor and contaminates, time 10min → high temperature fixation, 200 DEG C of temperature, time 40min, Gu
Color formula of liquid is：Soda ash 8-20g/L, salt 20-30g/L → washing, temperature 60 C, time 30min, after removal stock-dye not
The dispersion stain of set → soap → Final finishing processing, including antistatic treatment is carried out to fabric, the composition and ratio of formula are such as
Under (by weight)：Antistatic additive 6g；Glacial acetic acid 0.5g；Softening agent 3g；Water 1L → calendering, temperature 70 C, speed 30m/min →
Drying.
Spinning process cause A rove and B rove blending be in spun yarn when, because A rove is different with the fibre length of B rove,
The effect of the disconnected coloured silk yarn of stormy waves is can be derived that, while quantum energy fiber, FRC, stainless steel fibre are just entered in fiber
Row mixing so that the anti-flammability of fabric, antistatic behaviour and far infrared transmission are more uniform.By Final finishing, one can be entered
The antistatic rate of the increase fabric of step so that fabric is not likely to produce electrostatic in use, suitable different processing site is entered to exercise
With.
This specific embodiment is only explanation of the invention, and it is not limitation of the present invention, people in the art
Member can make the modification without creative contribution to the present embodiment as needed after this specification is read, but as long as at this
All protected by Patent Law in the right of invention.
Claims (8)
1. a kind of fabric containing quantum energy fiber, it is characterised in that：Include quantum energy fiber, FRC, stainless steel
Fiber and regenerated bamboo fiber, by weight, the content of the quantum energy fiber is 15%-25%, the FRC
Content be 20%-50%, the content of the stainless steel fibre is 1%-10%, and remaining is regenerated bamboo fiber.
2. the fabric containing quantum energy fiber according to claim 1, it is characterised in that：The content of the quantum energy fiber is
17.5%-22.5%, the content of the FRC is 25%-40%, and the content of the stainless steel fibre is 1%-
5%, remaining is regenerated bamboo fiber.
3. the fabric containing quantum energy fiber according to claim 2, it is characterised in that：The content of the quantum energy fiber has
19.5%, the content of the FRC is 38%, and the content of the stainless steel fibre is 1%, and remaining is fine for regeneration bamboo
Dimension.
4. the preparation of a kind of fabric containing quantum energy fiber as described in any claim in claim 1 to claim 3
Method, it is characterised in that：Comprise the following steps：Spinning → weaving → dyeing and finishing；
(1) spinning process：
Step 1：Regenerated bamboo fiber：Grab cotton (griping cotton machine) → shredding (opener) → coiled (lapper) → combing (carding machine) →
Drafting (drawing frame) → rove (fly frame), finally gives A rove；
Step 2：Quantum energy fiber, FRC, stainless steel fibre：Grab respectively cotton (griping cotton machine) → shredding (opener) →
Mixed (fiber mixer) → coiled (lapper) → combing (carding machine) → drafting (drafting to the fiber after three kinds of shreddings
Machine) → rove (fly frame), finally give B rove；
Step 3：Spun yarn (A rove feeds the spun yarn middle roller of spinning frame, and B rove feeds the spun yarn rear roller of spun yarn) → winder
(bobbin-winding machine)；
(2) weaving process：Warping → sizing → denting → jacquard fabric；
(3) dyeing and finishing technology：It is put on mixing dye liquor and contaminates, time 10min → high temperature fixation, 200 DEG C of temperature, time 40min, fixation
Formula of liquid is：Soda ash 8-20g/L, salt 20-30g/L → washing, temperature 60 C, time 30min is not solid after removal stock-dye
The dispersion stain → soap → Final finishing processing → drying.
5. the preparation method of the fabric containing quantum energy fiber according to claim 4, it is characterised in that：When step 1 is processed,
Humidification process is carried out to processing site so that relative humidity is 70%-80%, and it is uniform to the regeneration bamboo-carbon fibre after shredding
Spraying spray water, and stand 2-3 hours carries out following process.
6. the preparation method of the fabric containing quantum energy fiber according to claim 5, it is characterised in that：When step 3 is processed,
The spinning speed of spinning frame is reduced, it is 4500 revs/min -5500 revs/min to take spinning speed.
7. the preparation method of the fabric containing quantum energy fiber according to claim 6, it is characterised in that：By weight, institute
Stating Final finishing processing includes antistatic process, and the composition and ratio of formula are as follows：
8. the preparation method of the fabric containing quantum energy fiber according to claim 7, it is characterised in that：The rear finishing duplex
Fabric after skill also needs to carry out calendering, temperature 70 C, speed 30m/min.