CN106753846A - A kind of surface cleaning material and its preparation method and application - Google Patents

A kind of surface cleaning material and its preparation method and application Download PDF

Info

Publication number
CN106753846A
CN106753846A CN201611236918.1A CN201611236918A CN106753846A CN 106753846 A CN106753846 A CN 106753846A CN 201611236918 A CN201611236918 A CN 201611236918A CN 106753846 A CN106753846 A CN 106753846A
Authority
CN
China
Prior art keywords
cleaning material
surface cleaning
wax emulsion
grade
oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611236918.1A
Other languages
Chinese (zh)
Inventor
何旭添
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongshan Ke Xuan Surface Technology Co Ltd
Original Assignee
Zhongshan Ke Xuan Surface Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongshan Ke Xuan Surface Technology Co Ltd filed Critical Zhongshan Ke Xuan Surface Technology Co Ltd
Priority to CN201611236918.1A priority Critical patent/CN106753846A/en
Publication of CN106753846A publication Critical patent/CN106753846A/en
Pending legal-status Critical Current

Abstract

The invention provides a kind of surface cleaning material, by mass percentage, including following component：0.1 49% surfactant, 0.01 30% wax emulsion, 1 50% organic solvent and 0.1 5% inorganic non-metallic oxide micropowder, 10 98% water.Accordingly, present invention also offers a kind of preparation method and application of the surface cleaning material, the cleaning cloth made of it to surfaces such as automobiles when deep clean is carried out, only need to simple and quick wiping, excellent cleaning effect can be obtained, time-consuming about original 25 % or so, and with more preferable glossiness, human cost and time cost when reducing deep clean.The cleaning cloth that the present invention is provided simultaneously is reusable repeatedly, and the cost of raw material of cleaning significantly declines.

Description

A kind of surface cleaning material and its preparation method and application
Technical field
The present invention relates to chemical field, and in particular to a kind of surface cleaning material and its preparation method and application, can be extensive It is applied to the treatment of the surface cleaning such as automobile, ship, furniture, metal.
Background technology
Body of a motor car face coat assigns automobile beautiful outward appearance and excellent barrier propterty, can improve the use of automobile It is worth and extends its service life.Because automobile is sufficiently complex as vehicles use environment, dust, waste gas, combustion are born Material, highway asphalt, mud infringement, it is therefore desirable to which protection is scientifically cleaned to body of a motor car coating.
In general, the life-span of automotive coatings can be the service life phase with automobile under good maintenance and maintenance Near.And lacquer painting cleaning is mostly important part in automotive coatings maintenance, automotive coatings in the obstinate dura mater of removal, Ke Yitong Cross friction or chemolysis accelerates the removal of obstinate dura mater, while making lacquer painting smooth bright and clean.
At present, the automobile depth cleaning of commercialization is general by spraying solvent abstergent or with clay come cleaning agent, is doing Deep clean constantly needs manually to be wiped repeatedly dissolving or friction and can just obtain good cleaning effect, the time, human cost compared with It is high.Additionally, the process of liquid spray construction also results in the pollution of sky gas and water and soil.Accordingly, it would be desirable to developing one kind is easy to behaviour Make, effect is good, the cleaning material of environmental protection.
The content of the invention
Regarding to the issue above, the invention provides a kind of surface cleaning material, with excellent clean-up performance, it is only necessary to letter Single quick wipe, you can easy to use for base material provides good cleaning, safety is environment friendly and pollution-free, while reducing cleaning Human cost.
It is corresponding to be made present invention also offers the preparation method of the surface cleaning material and using the surface cleaning material A kind of application of cleaning cloth, can be widely used in the treatment of the surface cleaning such as vehicle, ship, furniture, metal, and the cleaning cloth can Repeatedly use.
In order to realize technical purpose of the invention, the present invention is adopted the following technical scheme that.
A kind of surface cleaning material, by mass percentage, including following component：The surfactant of 0.1-49%, The inorganic non-metallic oxide micropowder of the wax breast, the organic solvent of 1-50% and 0.1-5% of 0.01-30%, the water of 10-98%.
Preferably, the surfactant is alcohol ethers, phenolic ether class, in fatty acid ester surfactant at least one Kind.The alcohol ether surfactants can be AEO and its esters, alkyl alcohol ethoxylates and its salt At least one in class, propylene glycol monomethyl ether and its esters, Triton X-100；The phenol ether surfactant can be with Be in polyoxyethylene alkylphenol ether, APES, NPE, OPEO extremely Few one kind；The fatty acid ester surfactant can be polyxyethylated alkylolamides, the acid of pentaerythrite fat, glycerine At least one in boric acid fatty acid ester, neopelex, the sulfonate of fatty acid methyl ester ethoxylate.
Preferably, the organic solvent is alcohols, ether solvent or amine solvent.Wherein alcohols solvent can be specifically first Alcohol, ethanol, propyl alcohol, isopropanol, butanol, isobutanol, sec-butyl alcohol, the tert-butyl alcohol, amylalcohol, at least one in glycerine；The first Alcohol, ethanol, propyl alcohol, isopropanol, butanol, isobutanol, sec-butyl alcohol, the tert-butyl alcohol, amylalcohol, glycerine can be comprising 1-11 carbon The monohydric alcohol of atom and a small amount of polyalcohol.Ether solvent can be specifically ether, propyl ether, isopropyl ether, butyl ether, glycol dinitrate Ether, ethylene glycol diethyl ether, at least one in butyl cellosolve；The ether, propyl ether, isopropyl ether, butyl ether, glycol dinitrate Ether, ethylene glycol diethyl ether, butyl cellosolve refers to that oxygen atom is connected constituted compound with two alkyl.Amine solvent has Body can be ethylenediamine, oleyl amine, monoethanolamine, triethanolamine, diethanol amine, at least one of isopropanolamine；
Preferably, described wax emulsion can include animal wax, and vegetable wax, mineral wax, pertroleum wax or synthetic wax emulsify what is formed Wax emulsion；Specifically, the wax emulsion is paraffin wax emulsions, palm wax emulsion, crystallite wax emulsion, beeswax emulsion, Tissuemat E breast Liquid, polypropylene wax emulsion, Fischer-Tropsch wax emulsion, insect wax emulsion, wool wax emulsion covers smooth wax emulsion, at least one in emulsification wax emulsion Kind.
Preferably, the inorganic non-metallic oxide micropowder be silica, titanium oxide, cerium oxide, chromium oxide, zinc oxide, Aluminum oxide, magnesia, at least one in zirconium oxide micro mist.
Preferably, the average grain diameter of the inorganic non-metallic oxide micropowder is 0.01 μm -500 μm.In order that of the invention More excellent properties are obtained, the average grain diameter of inorganic non-metallic oxide micropowder is 0.1-50 μm.
A kind of preparation method of surface cleaning material, comprises the following steps：By proportioning, by water, organic solvent is added to instead Answer and stir in kettle；The wax emulsion of proportional quantity, inorganic non-metallic oxide micropowder, surfactant are sequentially added in order Stir, you can.
A kind of application of surface cleaning material, by fiber cloth, flannelette, in cotton one kind as carrier impregnation in cleaning material In, after the completion of dipping, the liquid of fiber cloth excess surface is removed, arrange excision forming.
Preferably, appropriate spices can also be added as needed in the cleaning material, the selection of spices can be according to consumption Person's likes adding, such as lemon extract, orange, flavoring apple essence.
The beneficial effects of the invention are as follows：The invention provides a kind of surface cleaning material and its preparation method and application, with Prior art is compared, with advantages below.
1. when surface cleaning material of the invention is used to carry out deep clean to automobile etc., it is only necessary to simple and quick wiping, Excellent cleaning effect can be obtained, with more preferable glossiness, human cost and time cost when reducing deep clean.
2. the cleaning cloth that compared with prior art, the present invention is provided is reusable repeatedly, and the cost of raw material of cleaning is big Amplitude declines.
Specific embodiment
In order to be better understood from the present invention, invention is described in detail with reference to specific embodiment.
Embodiment 1
A kind of surface cleaning material, by mass percentage, including following component：5% AEO, 0.01% Tissuemat E breast, 1% methyl alcohol and the ultrafine silica powder that 0.5% particle diameter is 0.5 micron, 93.49% water.
Embodiment 2
A kind of surface cleaning material, by mass percentage, including following component：49% alkyl alcohol ethoxylates, 1% it is micro- Brilliant wax breast, 5% ethanol and the ultrafine silica powder that 3% particle diameter is 0.1 micron, 42% water.
Embodiment 3
A kind of surface cleaning material, by mass percentage, including following component：0.1% propylene glycol monomethyl ether, 0.5% beeswax Emulsion, 1.3% propyl alcohol and the titanium oxide fine powder that 0.1% particle diameter is 0.01 micron, 98% water.
Embodiment 4
A kind of surface cleaning material, by mass percentage, including following component：38% Triton X-100,2% Polypropylene wax emulsion, 15% isopropanol and the alumina powder that 5% particle diameter is 5 microns, 40% water.
Embodiment 5
A kind of surface cleaning material, by mass percentage, including following component：10% polyoxyethylene alkylphenol ether, 3% Paraffin wax breast, 20% ether and the fine magnesium oxide micro-powder that 1% particle diameter is 1 micron, 66% water.
Embodiment 6
A kind of surface cleaning material, by mass percentage, including following component：20% APES, 4% take The brown wax breast of support, 25% tert-butyl alcohol and the ultrafine silica powder that 2% particle diameter is 10 microns, 49% water.
Embodiment 7
A kind of surface cleaning material, by mass percentage, including following component：5% NPE, 5% OP Wax emulsion, 30% butyl ether and the ultrafine silica powder that 4% particle diameter is 30 microns, 16% water.
Embodiment 8
A kind of surface cleaning material, by mass percentage, including following component：2% OPEO, 1% E waxes Emulsion, 35% ethylene glycol diethyl ether and the alumina powder that 2% particle diameter is 50 microns, 60% water.
Embodiment 9
A kind of surface cleaning material, by mass percentage, including following component：3% polyxyethylated alkylolamides, 1% Rice bran wax emulsion, 40% propyl ether and the ultrafine silica powder that 2% particle diameter is 500 microns, 54% water.
Embodiment 10
A kind of surface cleaning material, by mass percentage, including following component：6% acid of pentaerythrite fat, 1% S wax waxes The mixture of emulsion, 45% methyl alcohol and sec-butyl alcohol composition and the zinc oxide ultra_fine powderses that 1% particle diameter is 2 microns, 47% water.
Embodiment 11
A kind of surface cleaning material, by mass percentage, including following component：32% glycerine boric acid fatty acid ester, 30% Haze tallow emulsion, 25% diethanol amine and zirconium oxide micro mist that 3% particle diameter is 7 microns, 10% water.
Embodiment 12
A kind of surface cleaning material, by mass percentage, including following component：2% neopelex, 1% worm Wax emulsion, 8% monoethanolamine and the chromium oxide micro mist that 1% particle diameter is 12 microns, 88% water.
Embodiment 13
A kind of surface cleaning material, by mass percentage, including following component：2% alkyl alcohol ethoxylates sodium sulphate, 1% wool wax emulsion, 2% oleyl amine and the cerium oxide micro mist that 2% particle diameter is 1 micron, 93% water.
Embodiment 14
A kind of surface cleaning material, by mass percentage, including following component：2% sodium sulfate of polyethenoxy ether of fatty alcohol, 1% ground wax emulsion, 3% isopropanolamine and the ultrafine silica powder that 2% particle diameter is 2 microns, 92% water.
Embodiment 15
A kind of surface cleaning material, by mass percentage, including following component：2% AEO and poly- second two The mixture of alcohol octyl phenyl ether composition, 1% palm wax emulsion, 4% ethylenediamine and magnesia that 2% particle diameter is 2 microns The mixture micro mist constituted with aluminum oxide, 91% water.
A kind of preparation method of surface cleaning material, comprises the following steps：By proportioning, by water, organic solvent is added to instead Answer and stir in kettle；The wax emulsion of proportional quantity, inorganic non-metallic oxide micropowder, surfactant are sequentially added in order Stir, you can.
A kind of application of surface cleaning material, using fiber cloth as carrier impregnation in cleaning material, after the completion of dipping, clearly Except the liquid of fiber cloth excess surface, excision forming packaging is arranged.
According to the method described above and application, the surface cleaning material in embodiment 1-15 is made cleaning cloth, A1- is designated as respectively A15 products, to A1-A15 product pH value, glossiness test, cleaning efficiency, metalwork corrosivity, rubber parts erosion test, drift Washing performance carries out performance test, as a result as shown in table 1.
The performance test of the embodiment 1-15 products of table 1
Compile Number It is molten Liquid pH No. 45 steel corruption Corrosion is tested H62 brass is rotten Corrosion is tested LY12 duralumin Corrosion test Plastic parts is rotten Corrosion is tested It is rinsability Can test Quick wipe is clear Wash efficiency test Glossiness Test/GU
A1 6.2 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥85% 80
A2 8.7 1 grade 1 grade 1 grade 0 grade Have visible Residue ≥83% 84
A3 6.8 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥90% 82
A4 7.5 1 grade 1 grade 0 grade 0 grade Have visible Residue ≥86% 80
A5 6.5 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥95% 81
A6 7.2 0 grade 0 grade 1 grade 0 grade Without visible Residue ≥88% 83
A7 8.5 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥98% 85
A8 6.6 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥97% 85
A9 10. 3 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥95% 82
A1 0 6.2 1 grade 1 grade 0 grade 0 grade Without visible Residue ≥85% 85
A1 1 7.3 1 grade 1 grade 1 grade 0 grade Have visible Residue ≥82% 82
A1 2 6.5 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥87% 81
A1 3 6.8 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥89% 80
A1 4 9 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥85% 81
A1 5 7.1 0 grade 0 grade 0 grade 0 grade Without visible Residue ≥95% 86
Note：Cleaning cloth is wiped and can quickly clean a car in the present invention, and required time is about 5 minutes, and existing spraying solvent is clear Clean dose is taken around 20 minutes with clay come cleaning mode.
According to upper table data, it is apparent that the present invention provide a kind of surface cleaning material, to surfaces such as automobiles When carrying out deep clean, it is only necessary to simple and quick wiping, you can obtain excellent cleaning effect, institute is time-consuming to be about original 25% Left and right, and with more preferable glossiness, human cost and time cost when reducing deep clean.The present invention is provided simultaneously Cleaning cloth it is reusable repeatedly, the cost of raw material of cleaning significantly declines.
The basic principles, principal features and advantages of the present invention have been shown and described above.The technical staff of the industry should Understand, the invention is not limited in any way for above-described embodiment, it is all to be obtained by the way of equivalent or equivalent transformation Technical scheme, all falls within protection scope of the present invention.

Claims (8)

1. a kind of surface cleaning material, it is characterised in that：By mass percentage, including following component：Live on the surface of 0.1-49% The inorganic non-metallic oxide micropowder of property agent, the wax emulsion of 0.01-30%, the organic solvent of 1-50% and 0.1-5%, 10-98%'s Water.
2. a kind of surface cleaning material according to claim 1, it is characterised in that：The surfactant is alcohol ethers, Phenolic ether class, at least one in fatty acid ester surfactant.
3. a kind of surface cleaning material according to claim 1, it is characterised in that：The wax emulsion is palm wax emulsion, Paraffin wax emulsions, the smooth wax emulsion of illiteracy, polythene wax emulsion, polypropylene wax emulsion, beeswax emulsion, crystallite wax emulsion, Fischer-Tropsch wax emulsion, At least one of insect wax emulsion.
4. a kind of surface cleaning material according to claim 1, it is characterised in that：The organic solvent is alcohols, ethers Or at least one of amine solvent.
5. a kind of surface cleaning material according to claim 1, it is characterised in that：The inorganic non-metallic oxide micropowder It is silica, titanium oxide, cerium oxide, chromium oxide, zinc oxide, aluminum oxide, magnesia, at least one in zirconium oxide micro mist.
6. a kind of surface cleaning material according to claim 1-5, it is characterised in that：The inorganic non-metallic oxide is micro- The average grain diameter of powder is 0.01 μm -500 μm.
7. the preparation method of a kind of surface cleaning material according to claim any one of 1-6, it is characterised in that including such as Lower step：By proportioning, by water, organic solvent stirs in being added to reactor；The wax breast of proportional quantity is sequentially added in order Liquid, inorganic non-metallic oxide micropowder, surfactant stir, you can.
8. the application of a kind of surface cleaning material according to claim any one of 1-7, it is characterised in that：By fiber cloth, A kind of flannelette, the cloth in cotton in cleaning material, after the completion of dipping, removes fiber cloth excess surface as carrier impregnation Liquid, arranges excision forming packaging.
CN201611236918.1A 2016-12-28 2016-12-28 A kind of surface cleaning material and its preparation method and application Pending CN106753846A (en)