CN106752679A - Quick drying paint - Google Patents
Quick drying paint Download PDFInfo
- Publication number
- CN106752679A CN106752679A CN201611030558.XA CN201611030558A CN106752679A CN 106752679 A CN106752679 A CN 106752679A CN 201611030558 A CN201611030558 A CN 201611030558A CN 106752679 A CN106752679 A CN 106752679A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- molecular weight
- present
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of quick drying paint, belongs to technical field of coatings.The present invention is counted by weight, is made up of following raw material:Molecular weight is 200~250 20 parts~40 parts of epoxy resin, molecular weight is 450~500 30 parts~50 parts of epoxy resin, 15 parts~20 parts of latex powder, 10 parts~15 parts of cellulose ether, 30 parts~45 parts of closed perlite, 5 parts~8 parts of powdered whiting, 4 parts~6 parts of magnesia, 8 parts~15 parts of bamboo-carbon fibre, 5 parts~40 parts of pigment, 40 parts~45 parts of ethylene glycol, 1 part~5 parts and 60 parts~75 parts water of silicone oil.The present invention is combined by a certain percentage by by the epoxy resin of middle low-molecular-weight size, so as to combine the two compatible complementarity between other components;By adding latex powder and cellulose ether, so as to combine the two and the complementary intensity between other components, so as to accelerate its process of setting, shorten its solidification drying time.
Description
Technical field
The invention belongs to technical field of coatings, more particularly to a kind of quick drying paint.
Background technology
At present, the coating products generally existing setting time of in the market defect more long, therefore, it is being applied to high and cold, height
The house wall surface in the area such as warm equitemperature difference is larger, weather is more complicated is painted, often due to coating products generally existing
Solidification, drying time it is more long and cause coating paint failure.Therefore, a kind of solidification of demand, drying time short coating are abilities
The current urgent problem of field technique personnel.
The content of the invention
The invention provides a kind of quick drying paint, it can solve the solidification of existing coating products, drying time and more long ask
Topic.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is:
It is prepared from the following raw materials in parts by weight:
Molecular weight is 200~250 20 parts~40 parts of epoxy resin, and molecular weight is 450~500 epoxy resin 30 parts~50
Part, 15 parts~20 parts of latex powder, 10 parts~15 parts of cellulose ether, 30 parts~45 parts of closed perlite, powdered whiting 5 parts~8
Part, 4 parts~6 parts of magnesia, 8 parts~15 parts of bamboo-carbon fibre, 5 parts~40 parts of pigment, 40 parts~45 parts of ethylene glycol, silicone oil 1 part~5
Part and 60 parts~75 parts water.
Before construction, the raw material of above-mentioned weight portion is mixed, stirred, you can use.
Due to using above-mentioned technical proposal, the beneficial effect that the present invention is obtained to be:
1. the present invention is combined by a certain percentage by by the epoxy resin of middle low-molecular-weight size, so as to combine the two and other
Compatible complementarity between component, so as to accelerate its process of setting, shortens its solidification drying time.
2. the present invention is by adding latex powder and cellulose ether, mutual with intensity between other components so as to combine the two
Benefit property, so as to accelerate its process of setting, shortens its solidification drying time.
Specific embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only limited to
In following examples.
Embodiment 1 --- quick drying paint
Its raw material is:Molecular weight is 200 epoxy resin 200g, and molecular weight is 450 epoxy resin 300g, latex powder 150g,
Cellulose ether 100g, closed perlite 300g, powdered whiting 50g, magnesia 40g, bamboo-carbon fibre 80g, pigment 50g, second two
Alcohol 400g, silicone oil 10g and 600g water.
Before construction, above-mentioned raw materials are mixed, stirred, you can used.
The present embodiment gained coating solidifies drying in 4 hours completely after wall plaster smearing.
Embodiment 2 --- quick drying paint
Its raw material is:Molecular weight is 250 epoxy resin 400g, and molecular weight is 500 epoxy resin 500g, latex powder 200g,
Cellulose ether 150g, closed perlite 450g, powdered whiting 80g, magnesia 60g, bamboo-carbon fibre 150g, pigment 400g, second
Glycol 450g, silicone oil 50g and 750g water.
Before construction, above-mentioned raw materials are mixed, stirred, you can used.
The present embodiment gained coating solidifies drying in 4 hours completely after wall plaster smearing.
Embodiment 3 --- quick drying paint
Its raw material is:Molecular weight is 220 epoxy resin 350g, and molecular weight is 480 epoxy resin 450g, latex powder 160g,
Cellulose ether 140g, closed perlite 420g, powdered whiting 60g, magnesia 50g, bamboo-carbon fibre 120g, pigment 250g, second
Glycol 410g, silicone oil 30g and 680g water.
Before construction, above-mentioned raw materials are mixed, stirred, you can used.
The present embodiment gained coating solidifies drying in 3.5 hours completely after wall plaster smearing.
Claims (1)
1. a kind of quick drying paint, it is characterised in that be prepared from the following raw materials in parts by weight:
Molecular weight is 200~250 20 parts~40 parts of epoxy resin, and molecular weight is 450~500 epoxy resin 30 parts~50
Part, 15 parts~20 parts of latex powder, 10 parts~15 parts of cellulose ether, 30 parts~45 parts of closed perlite, powdered whiting 5 parts~8
Part, 4 parts~6 parts of magnesia, 8 parts~15 parts of bamboo-carbon fibre, 5 parts~40 parts of pigment, 40 parts~45 parts of ethylene glycol, silicone oil 1 part~5
Part and 60 parts~75 parts water.