CN106752602A - A kind of heat-resistant fireproof delivery track and preparation method thereof - Google Patents
A kind of heat-resistant fireproof delivery track and preparation method thereof Download PDFInfo
- Publication number
- CN106752602A CN106752602A CN201611130660.7A CN201611130660A CN106752602A CN 106752602 A CN106752602 A CN 106752602A CN 201611130660 A CN201611130660 A CN 201611130660A CN 106752602 A CN106752602 A CN 106752602A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- resistant fireproof
- delivery track
- coalescents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat-resistant fireproof delivery track, including delivery track, delivery track outer surface is coated with one layer of heat-resistant fireproof layer, and heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 mix, and include following components in first component according to the mass fraction:33 37 parts of ATO pulvis, the epoxy resin of E 20:12 16 parts, alcohol-soluble acrylate:24 26 parts, phenmethylol:8 13 parts, fluorographite:17 22 parts, ethanol:9 12 parts, fire retardant:13 16 parts, thickener:57 parts, coalescents:11 13 parts;Include following components in second component according to the mass fraction:Ultra-violet absorber:9 11 parts, dispersant:59 parts, thickener:8 12 parts, coalescents:15 18 parts, sodium tetraborate:25 parts, mixed phosphate:37 parts, lead potassium hydrogen phthalate:13 parts, allyl alcohol:46 parts, auxiliary material:13 15 parts, solvent:20 35 parts, the present invention not only increases operating efficiency, and reduces the pollution to environment, strengthens the practicality of delivery track.
Description
Technical field
The present invention relates to storage facilities technical field, a kind of heat-resistant fireproof delivery track and its system are particularly related to
Preparation Method.
Background technology
Delivery track is a particularly important part in storage sector, and conveying track of the prior art is mostly fragile,
And caused casualties because long-term use friction is inflammable, to improve operating efficiency and security, the present invention proposes a kind of resistance to height
Fire-retardant delivery track of temperature and preparation method thereof.
The content of the invention
The technical problems to be solved by the invention are to propose a kind of high temperature resistant resistance for the shortcoming that above prior art is present
Combustion delivery track, including delivery track, delivery track outer surface are coated with one layer of heat-resistant fireproof layer, and heat-resistant fireproof layer is by first
The component of second two first in mass ratio:Second=7:2 mix, first and second in terms of mass fraction comprising following components:
Include following components in first component according to the mass fraction:33-37 parts of ATO pulvis, E-20 epoxy resin:12-16 parts, alcohol is molten
Property acrylate:24-26 parts, phenmethylol:8-13 parts, fluorographite:17-22 parts, ethanol:9-12 parts, fire retardant:13-
16 parts, thickener:5-7 parts, coalescents:11-13 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:9-11 parts, dispersant:5-9 parts, thickener:
8-12 parts, coalescents:15-18 parts, sodium tetraborate:2-5 parts, mixed phosphate:3-7 parts, lead potassium hydrogen phthalate:1-3 parts,
Allyl alcohol:4-6 parts, auxiliary material:13-15 parts, solvent:20-35 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:30-40%, azo two is different
Butyronitrile:20-25%, methyl methacrylate:10-15%, butyl acrylate:10-15%, butyl methacrylate:10-15%, with
Upper each component sum is 100%;
Fire retardant selects phosphotriester, and the thickener is in dioctyl phthalate or dibutyl phthalate
Kind, coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-
O, dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes with the following group by mass percentage
Point:Dysprosium:9-11%, cerium:20-22%, praseodymium:11-13%, neodymium:2-5%, remaining is lanthanum element, and above lanthanide rare each component sum is
100%。
The technical scheme that further limits of the invention is:
Foregoing heat-resistant fireproof delivery track, delivery track outer surface is coated with one layer of heat-resistant fireproof layer, heat-resistant fireproof
Layer is by first and second liang of components first in mass ratio:Second=7:2 mix, first and second in terms of mass fraction comprising following components:
Include following components in first component according to the mass fraction:33 parts of ATO pulvis, E-20 epoxy resin:12 parts, alcohol-soluble propylene
Acid ester resin:24 parts, phenmethylol:8 parts, fluorographite:17 parts, ethanol:9 parts, fire retardant:13 parts, thickener:5 parts, film forming is helped
Agent:11 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:9 parts, dispersant:5 parts, thickener:8 parts,
Coalescents:15 parts, sodium tetraborate:2 parts, mixed phosphate:3 parts, lead potassium hydrogen phthalate:1 part, allyl alcohol:4 parts, auxiliary material:
13 parts, solvent:20 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:30%, the isobutyl of azo two
Nitrile:20%, methyl methacrylate:10%th, butyl acrylate:10%, butyl methacrylate:10%, above each component sum is
100%;
Fire retardant selects phosphotriester, thickener to be the one kind in dioctyl phthalate or dibutyl phthalate,
Coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-O,
Dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes following components by mass percentage:
Dysprosium:9%, cerium:20%, praseodymium:11%, neodymium:2%, remaining is lanthanum element, and above lanthanide rare each component sum is 100%.
Foregoing heat-resistant fireproof delivery track, delivery track outer surface is coated with one layer of heat-resistant fireproof layer, high temperature resistant
Flame-retardant layer is by first and second liang of components first in mass ratio:Second=7:2 mix, first and second in terms of mass fraction comprising following components:
Include following components in first component according to the mass fraction:33-37 parts of ATO pulvis, E-20 epoxy resin:16 parts, alcohol-soluble
Acrylate:26 parts, phenmethylol:13 parts, fluorographite:22 parts, ethanol:12 parts, fire retardant:16 parts, thickener:7 parts,
Coalescents:13 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:11 parts, dispersant:9 parts, thickener:12
Part, coalescents:18 parts, sodium tetraborate:5 parts, mixed phosphate:7 parts, lead potassium hydrogen phthalate:3 parts, allyl alcohol:It is 6 parts, auxiliary
Material:15 parts, solvent:35 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:40%, the isobutyl of azo two
Nitrile:25%, methyl methacrylate:15%th, butyl acrylate:15%, butyl methacrylate:15%, above each component sum is
100%;
Fire retardant selects phosphotriester, thickener to be the one kind in dioctyl phthalate or dibutyl phthalate,
Coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-O,
Dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes following components by mass percentage:
Dysprosium:11%, cerium:22%, praseodymium:13%, neodymium:5%, remaining is lanthanum element, and above lanthanide rare each component sum is 100%.
Foregoing heat-resistant fireproof delivery track, the epoxide equivalent 500-550g/eq of E-20 epoxy resin.
Foregoing heat-resistant fireproof delivery track and preparation method thereof, the method is comprised the following steps that:
(1)15-22min, stirring speed are stirred during ATO pulvis and alcohol-soluble acrylate in first component is delivered into agitator
It is 95-105r/min to spend, and is subsequently adding E-20 epoxy resin stirring 12-16min, and mixing speed is 110-120 r/min, waits and fills
Divide after being well mixed and sequentially add fluorographite, ethanol, fire retardant and phenmethylol, finally add plasticizer and coalescents
Adjusting coating is to suitable viscosity, and the first component being filtrated to get in heat-resistant fireproof layer is stand-by;
(2)To adding sodium tetraborate, auxiliary material and dispersant in allyl alcohol and sending into mixer, 12-16min, mixing speed are stirred
It is 140-145r/min, is subsequently adding ultra-violet absorber and neck potassium hydrogen phthalate, stir 20-25min, mixing speed is
110-115r/min, wait be sufficiently mixed it is uniform after mixed phosphate and thickener added into mixer, in high shear masterpiece
With lower high-speed stirred 15-20min, mixing speed is 300-320 r/min, finally adds appropriate coalescents and solvent adjustment
Coating is to suitable viscosity, and the component B that filtering can obtain in heat-resistant fireproof layer is stand-by;
(3)By step(2)In the second component for preparing be sprayed on step(1)In in the first component for preparing, after superposition mixing i.e.
Obtain heat-resistant fireproof layer;
(4)Obtained heat-resistant fireproof layer is sprayed on natural air drying on delivery track and can obtain heat-resistant fireproof conveyor track
Road.
It is using technical scheme beneficial effect:ATO pulvis is employed in the present invention, ATO pulvis has good
Dispersion effect, and be increased in the present invention sodium tetraborate, mixed phosphate and neck potassium hydrogen phthalate, it is good with ATO pulvis
Good cooperation so that the stability of ATO pulvis is more consolidated, and improves the operating efficiency of the method;Containing ultraviolet in the present invention
Light absorbers, can strengthen absorptivity of the heat-resistant fireproof layer to ultraviolet, improve the performance of the coating, and the solvent in the present invention is adopted
It is water, reduces production cost, protects natural environment;The heat-resistant fireproof layer that the present invention is prepared has preferably attachment
Power and excellent heat-resistant fireproof, improve life-span and the utilization rate of the product, improve the practicality of delivery track, and
It is easy to operate and the method step is simple.
Specific embodiment
Embodiment 1
The present embodiment provides a kind of heat-resistant fireproof delivery track, and delivery track outer surface is coated with one layer of heat-resistant fireproof layer,
Heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 are mixed, and first and second are included with the following group in terms of mass fraction
Point:
Include following components in first component according to the mass fraction:33 parts of ATO pulvis, E-20 epoxy resin:12 parts, alcohol-soluble propylene
Acid ester resin:24 parts, phenmethylol:8 parts, fluorographite:17 parts, ethanol:9 parts, fire retardant:13 parts, thickener:5 parts, film forming is helped
Agent:11 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:9 parts, dispersant:5 parts, thickener:8 parts,
Coalescents:15 parts, sodium tetraborate:2 parts, mixed phosphate:3 parts, lead potassium hydrogen phthalate:1 part, allyl alcohol:4 parts, auxiliary material:
13 parts, solvent:20 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:35%, the isobutyl of azo two
Nitrile:22%, methyl methacrylate:13%th, butyl acrylate:15%, butyl methacrylate:15%, above each component sum is
100%;
Fire retardant selects phosphotriester, thickener to be the one kind in dioctyl phthalate or dibutyl phthalate,
Coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-O,
Dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes following components by mass percentage:
Dysprosium:9%, cerium:20%, praseodymium:11%, neodymium:2%, remaining is lanthanum element, and above lanthanide rare each component sum is 100%;E-20 epoxies
The epoxide equivalent 500g/eq of resin;
Above-mentioned heat-resistant fireproof delivery track and preparation method thereof, comprises the following steps:
(1)15min, mixing speed are stirred during ATO pulvis and alcohol-soluble acrylate in first component is delivered into agitator
Be 95r/min, be subsequently adding E-20 epoxy resin stirring 12min, mixing speed is 110r/min, wait be sufficiently mixed it is uniform after according to
Secondary addition fluorographite, ethanol, fire retardant and phenmethylol, finally add plasticizer and coalescents adjusting coating to suitable
Viscosity, the first component being filtrated to get in heat-resistant fireproof layer is stand-by;
(2)To adding sodium tetraborate, auxiliary material and dispersant in allyl alcohol and sending into mixer, 12min is stirred, mixing speed is
140r/min, is subsequently adding ultra-violet absorber and neck potassium hydrogen phthalate, stirs 20min, and mixing speed is 110r/min,
Etc. be sufficiently mixed it is uniform after mixed phosphate and thickener added into mixer, the high-speed stirred under high shear
15min, mixing speed is 300r/min, finally adds appropriate coalescents and solvent adjustment coating to suitable viscosity, filtering
The component B that can obtain in heat-resistant fireproof layer is stand-by;
(3)By step(2)In the second component for preparing be sprayed on step(1)In in the first component for preparing, after superposition mixing i.e.
Obtain heat-resistant fireproof layer;
(4)Obtained heat-resistant fireproof layer is sprayed on natural air drying on delivery track and can obtain heat-resistant fireproof conveyor track
Road.
Embodiment 2
The present embodiment provides a kind of heat-resistant fireproof delivery track, and delivery track outer surface is coated with one layer of heat-resistant fireproof layer,
Heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 are mixed, and first and second are included with the following group in terms of mass fraction
Point:
Include following components in first component according to the mass fraction:33-37 parts of ATO pulvis, E-20 epoxy resin:16 parts, alcohol-soluble
Acrylate:26 parts, phenmethylol:13 parts, fluorographite:22 parts, ethanol:12 parts, fire retardant:16 parts, thickener:7 parts,
Coalescents:13 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:11 parts, dispersant:9 parts, thickener:12
Part, coalescents:18 parts, sodium tetraborate:5 parts, mixed phosphate:7 parts, lead potassium hydrogen phthalate:3 parts, allyl alcohol:It is 6 parts, auxiliary
Material:15 parts, solvent:35 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:40%, the isobutyl of azo two
Nitrile:20%, methyl methacrylate:13%th, butyl acrylate:15%, butyl methacrylate:12%, above each component sum is
100%;
Fire retardant selects phosphotriester, thickener to be the one kind in dioctyl phthalate or dibutyl phthalate,
Coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-O,
Dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes following components by mass percentage:
Dysprosium:11%, cerium:22%, praseodymium:13%, neodymium:5%, remaining is lanthanum element, and above lanthanide rare each component sum is 100%;E-20 epoxies
The epoxide equivalent 550g/eq of resin
Above-mentioned heat-resistant fireproof delivery track and preparation method thereof, comprises the following steps:
(1)22min, mixing speed are stirred during ATO pulvis and alcohol-soluble acrylate in first component is delivered into agitator
It is 105r/min, is subsequently adding E-20 epoxy resin stirring 16min, mixing speed is 120 r/min, is waited after being sufficiently mixed uniformly
Fluorographite, ethanol, fire retardant and phenmethylol are sequentially added, plasticizer and coalescents adjusting coating to conjunction is finally added
Suitable viscosity, the first component being filtrated to get in heat-resistant fireproof layer is stand-by;
(2)To adding sodium tetraborate, auxiliary material and dispersant in allyl alcohol and sending into mixer, 16min is stirred, mixing speed is
145r/min, is subsequently adding ultra-violet absorber and neck potassium hydrogen phthalate, stirs 25min, and mixing speed is 115r/min,
Etc. be sufficiently mixed it is uniform after mixed phosphate and thickener added into mixer, the high-speed stirred under high shear
20min, mixing speed is 320 r/min, finally adds appropriate coalescents and solvent adjustment coating to suitable viscosity, is filtered
The component B that can obtain in heat-resistant fireproof layer is stand-by;
(3)By step(2)In the second component for preparing be sprayed on step(1)In in the first component for preparing, after superposition mixing i.e.
Obtain heat-resistant fireproof layer;
(4)Obtained heat-resistant fireproof layer is sprayed on natural air drying on delivery track and can obtain heat-resistant fireproof conveyor track
Road.
Embodiment 3
The present embodiment provides a kind of heat-resistant fireproof delivery track, and delivery track outer surface is coated with one layer of heat-resistant fireproof layer,
Heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 are mixed, and first and second are included with the following group in terms of mass fraction
Point:
Include following components in first component according to the mass fraction:35 parts of ATO pulvis, E-20 epoxy resin:14 parts, alcohol-soluble propylene
Acid ester resin:25 parts, phenmethylol:11 parts, fluorographite:20 parts, ethanol:11 parts, fire retardant:14 parts, 6 parts of thickener, film forming
Auxiliary agent:12 parts;
Include following components in second component according to the mass fraction:Ultra-violet absorber:10 parts, dispersant:7 parts, thickener:10
Part, coalescents:16 parts, sodium tetraborate:3 parts, mixed phosphate:5 parts, lead potassium hydrogen phthalate:2 parts, allyl alcohol:It is 5 parts, auxiliary
Material:14 parts, solvent:30 parts;
Wherein, alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:30%, the isobutyl of azo two
Nitrile:25%, methyl methacrylate:15%th, butyl acrylate:15%, butyl methacrylate:15%, above each component sum is
100%;
Fire retardant selects phosphotriester, thickener to be the one kind in dioctyl phthalate or dibutyl phthalate,
Coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, and ultra-violet absorber is UV-O,
Dispersant is DP-518, and solvent is water, and auxiliary material is compound rare-earth, and compound rare-earth includes following components by mass percentage:
Dysprosium:9-11%, cerium:20-22%, praseodymium:11-13%, neodymium:2-5%, remaining is lanthanum element, and above lanthanide rare each component sum is
100%;The epoxide equivalent 520g/eq of E-20 epoxy resin
Above-mentioned heat-resistant fireproof delivery track and preparation method thereof, comprises the following steps:
(1)18min, mixing speed are stirred during ATO pulvis and alcohol-soluble acrylate in first component is delivered into agitator
It is 100r/min, is subsequently adding E-20 epoxy resin stirring 14min, mixing speed is 115r/min, is waited after being sufficiently mixed uniformly
Fluorographite, ethanol, fire retardant and phenmethylol are sequentially added, plasticizer and coalescents adjusting coating to conjunction is finally added
Suitable viscosity, the first component being filtrated to get in heat-resistant fireproof layer is stand-by;
(2)To adding sodium tetraborate, auxiliary material and dispersant in allyl alcohol and sending into mixer, 14min is stirred, mixing speed is
143r/min, is subsequently adding ultra-violet absorber and neck potassium hydrogen phthalate, stirs 22min, and mixing speed is 113r/min,
Etc. be sufficiently mixed it is uniform after mixed phosphate and thickener added into mixer, the high-speed stirred under high shear
18min, mixing speed is 310 r/min, finally adds appropriate coalescents and solvent adjustment coating to suitable viscosity, is filtered
The component B that can obtain in heat-resistant fireproof layer is stand-by;
(3)By step(2)In the second component for preparing be sprayed on step(1)In in the first component for preparing, after superposition mixing i.e.
Obtain heat-resistant fireproof layer;
(4)Obtained heat-resistant fireproof layer is sprayed on natural air drying on delivery track and can obtain heat-resistant fireproof conveyor track
Road.
In addition to the implementation, the present invention can also have other embodiment.All use equivalents or equivalent transformation shape
Into technical scheme, all fall within the protection domain of application claims.
Claims (5)
1. a kind of heat-resistant fireproof delivery track, including delivery track, it is characterised in that:The delivery track outer surface is coated with
One layer of heat-resistant fireproof layer, the heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 mix, the first
Second is in terms of mass fraction comprising following components:
Include following components in the first component according to the mass fraction:33-37 parts of ATO pulvis, E-20 epoxy resin:12-16 parts,
Alcohol-soluble acrylate:24-26 parts, phenmethylol:8-13 parts, fluorographite:17-22 parts, ethanol:9-12 parts, fire retardant:
13-16 parts, thickener:5-7 parts, coalescents:11-13 parts;
Include following components in the second component according to the mass fraction:Ultra-violet absorber:9-11 parts, dispersant:5-9 parts, increase
Thick dose:8-12 parts, coalescents:15-18 parts, sodium tetraborate:2-5 parts, mixed phosphate:3-7 parts, lead potassium hydrogen phthalate:
1-3 parts, allyl alcohol:4-6 parts, auxiliary material:13-15 parts, solvent:20-35 parts;
Wherein, the alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:30-40%, azo
Bis-isobutyronitrile:20-25%, methyl methacrylate:10-15%, butyl acrylate:10-15%, butyl methacrylate:10-
15%, above each component sum is 100%;
The fire retardant selects phosphotriester, the thickener to be in dioctyl phthalate or dibutyl phthalate
One kind, the coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, described purple
Ultraviolet absorbers are UV-O, and described dispersant is DP-518, and described solvent is water, and the auxiliary material is compound rare-earth, institute
State compound rare-earth includes following components by mass percentage:Dysprosium:9-11%, cerium:20-22%, praseodymium:11-13%, neodymium:2-5%, its
Remaining is lanthanum element, and above lanthanide rare each component sum is 100%.
2. heat-resistant fireproof delivery track according to claim 1, it is characterised in that:The delivery track outer surface coating
There is one layer of heat-resistant fireproof layer, the heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 mix, described
First and second in terms of mass fraction comprising following components:
Include following components in the first component according to the mass fraction:33 parts of ATO pulvis, E-20 epoxy resin:12 parts, alcohol-soluble
Acrylate:24 parts, phenmethylol:8 parts, fluorographite:17 parts, ethanol:9 parts, fire retardant:13 parts, thickener:5 parts, into
Film auxiliary agent:11 parts;
Include following components in the second component according to the mass fraction:Ultra-violet absorber:9 parts, dispersant:5 parts, thickener:8
Part, coalescents:15 parts, sodium tetraborate:2 parts, mixed phosphate:3 parts, lead potassium hydrogen phthalate:1 part, allyl alcohol:It is 4 parts, auxiliary
Material:13 parts, solvent:20 parts;
Wherein, the alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:35%, azo two is different
Butyronitrile:22%, methyl methacrylate:13%th, butyl acrylate:15%, butyl methacrylate:15%, above each component sum
It is 100%;
The fire retardant selects phosphotriester, the thickener to be in dioctyl phthalate or dibutyl phthalate
One kind, the coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, described purple
Ultraviolet absorbers are UV-O, and described dispersant is DP-518, and described solvent is water, and the auxiliary material is compound rare-earth, institute
State compound rare-earth includes following components by mass percentage:Dysprosium:9%, cerium:20%, praseodymium:11%, neodymium:2%, remaining is lanthanum element,
Above lanthanide rare each component sum is 100%.
3. heat-resistant fireproof delivery track according to claim 1, it is characterised in that:The delivery track outer surface coating
There is one layer of heat-resistant fireproof layer, the heat-resistant fireproof layer is by first and second liang of components first in mass ratio:Second=7:2 mix, described
First and second in terms of mass fraction comprising following components:
Include following components in the first component according to the mass fraction:33-37 parts of ATO pulvis, E-20 epoxy resin:16 parts, alcohol
Soluble acrylic ester resin:26 parts, phenmethylol:13 parts, fluorographite:22 parts, ethanol:12 parts, fire retardant:16 parts, thickener:
7 parts, coalescents:13 parts;
Include following components in the second component according to the mass fraction:Ultra-violet absorber:11 parts, dispersant:9 parts, thickener:
12 parts, coalescents:18 parts, sodium tetraborate:5 parts, mixed phosphate:7 parts, lead potassium hydrogen phthalate:3 parts, allyl alcohol:6 parts,
Auxiliary material:15 parts, solvent:35 parts;
Wherein, the alcohol-soluble acrylate is made up of following composition by mass percentage:Ethanol:40%, azo two is different
Butyronitrile:20%, methyl methacrylate:13%th, butyl acrylate:15%, butyl methacrylate:12%, above each component sum
It is 100%;
The fire retardant selects phosphotriester, the thickener to be in dioctyl phthalate or dibutyl phthalate
One kind, the coalescents are the one kind in ethylene glycol ethyl ether, butyl glycol ether, ethylene glycol or propane diols, described purple
Ultraviolet absorbers are UV-O, and described dispersant is DP-518, and described solvent is water, and the auxiliary material is compound rare-earth, institute
State compound rare-earth includes following components by mass percentage:Dysprosium:11%, cerium:22%, praseodymium:13%, neodymium:5%, remaining is lanthanum element,
Above lanthanide rare each component sum is 100%.
4. heat-resistant fireproof delivery track according to claim 1, it is characterised in that:The ring of described E-20 epoxy resin
Oxygen equivalent 500-550g/eq.
5. a kind of preparation method of heat-resistant fireproof delivery track, any right will during the preparation method is provided with claim 1-4
Seek described heat-resistant fireproof delivery track, it is characterised in that the preparation method is comprised the following steps:
(1)15-22min, stirring speed are stirred during ATO pulvis and alcohol-soluble acrylate in first component is delivered into agitator
It is 95-105r/min to spend, and is subsequently adding E-20 epoxy resin stirring 12-16min, and mixing speed is 110-120 r/min, waits and fills
Divide after being well mixed and sequentially add fluorographite, ethanol, fire retardant and phenmethylol, finally add plasticizer and coalescents
Adjusting coating is to suitable viscosity, and the first component being filtrated to get in heat-resistant fireproof layer is stand-by;
(2)To adding sodium tetraborate, auxiliary material and dispersant in allyl alcohol and sending into mixer, 12-16min, mixing speed are stirred
It is 140-145r/min, is subsequently adding ultra-violet absorber and neck potassium hydrogen phthalate, stir 20-25min, mixing speed is
110-115r/min, wait be sufficiently mixed it is uniform after mixed phosphate and thickener added into mixer, in high shear masterpiece
With lower high-speed stirred 15-20min, mixing speed is 300-320 r/min, finally adds appropriate coalescents and solvent adjustment
Coating is to suitable viscosity, and the component B that filtering can obtain in heat-resistant fireproof layer is stand-by;
(3)By step(2)In the second component for preparing be sprayed on step(1)In in the first component for preparing, after superposition mixing i.e.
Obtain heat-resistant fireproof layer;
(4)Obtained heat-resistant fireproof layer is sprayed on natural air drying on delivery track and can obtain heat-resistant fireproof conveyor track
Road.