CN106750965A - 一种双轮殻轴流风叶及其制备方法 - Google Patents
一种双轮殻轴流风叶及其制备方法 Download PDFInfo
- Publication number
- CN106750965A CN106750965A CN201611235197.2A CN201611235197A CN106750965A CN 106750965 A CN106750965 A CN 106750965A CN 201611235197 A CN201611235197 A CN 201611235197A CN 106750965 A CN106750965 A CN 106750965A
- Authority
- CN
- China
- Prior art keywords
- wheel shell
- flow leaf
- shell axial
- antioxidant
- silane coupler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及风叶及其制备方法。一种双轮殻轴流风叶,按质量百分比计由以下的材料注塑成型:PP65‑85%、玻璃纤维15‑25%、碳纤维1.0~5.0%、云母3.0‑20%、硅烷偶联剂DB792 0.1‑1.5%、硅烷偶联剂KBM‑4030.1‑1.5、环状酸酐型相容剂0.2‑2.0%、乙氧基化月桂酰胺0.5‑1.0%、载银无机抗菌剂0.2%‑1.0%、乙撑双硬脂酰胺0.5‑2.0%、甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物0.5‑3.0%、无卤阻燃剂0.5‑2.0%、抗氧剂0.5‑2.0%、光稳定剂0.1‑1.0%、热稳定剂0.1‑1.0%。该双轮殻轴流风叶具有较高的耐热、耐化学腐蚀、耐老化、防霉、防紫外线辐射等性能,高密度,高硬度,尺寸变形小,增加塑胶材料的拉伸强度。
Description
技术领域
本发明涉及风叶及其制备方法。
背景技术
随着生活水平的提高,人们对居住环境的要求越来越重视,作为在室内密闭环境下使用的空调器,其对风扇噪音的影响也日益受到关注。空调器室内机风扇是空调器的送风关键部件,因而对室内的风扇噪声的大小起着重要影响。
现有的空调器双轮殻轴流风叶大多采用普通玻纤增强PP、PP或PP等材料制作,由于本身的刚性和耐高温性能存在不足,运输过程中以及长期使用后容易发生变形,使用中会产生振动噪声加大的问题。
发明内容
为了解决上述的技术问题,本发明的第一个目的是提供一种双轮殻轴流风叶,该双轮殻轴流风叶具有较高的耐热、耐化学腐蚀、耐老化、防霉、防紫外线辐射等性能,高密度,高硬度,尺寸变形小,增加塑胶材料的拉伸强度。同时,该双轮殻轴流风叶又具备抗静电、抗菌性能、阻燃性能,提高老化性能和遇热分解性能。
为了实现上述的第一个目的,本发明采用了以下的技术方案:
一种双轮殻轴流风叶,该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
PP 65-85%
玻璃纤维 15-25%
碳纤维 1.0-5.0%
云母 3.0-20%
硅烷偶联剂DB792 0.1-1.5%
硅烷偶联剂KBM-403 0.1-1.5%
环状酸酐型相容剂 0.2-2.0%
乙氧基化月桂酰胺 0.5-1.0%
载银无机抗菌剂 0.2%-1.0%
乙撑双硬脂酰胺 0.5-2.0%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 0.5-3.0%
无卤阻燃剂 0.5-2.0%
抗氧剂 0.5-2.0%
光稳定剂 0.1-1.0%
热稳定剂 0.1-1.0%。
作为优选,所述的双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
PP 70-80%
玻璃纤维 18-20%
碳纤维 2.0~4.0%
云母 5.0-15%
硅烷偶联剂DB792 0.5-1.5%
硅烷偶联剂KBM-403 0.1-1.5%
环状酸酐型相容剂 0.5-2.0%
乙氧基化月桂酰胺 0.5-1.0%
载银无机抗菌剂 0.2%-1.0%
乙撑双硬脂酰胺 0.5-1.0%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 0.8-2.0%
无卤阻燃剂 0.8-1.5%
抗氧剂 0.8-1.5%
光稳定剂 0.1-1.0%
热稳定剂 0.1-1.0%。
作为优选,所述的抗氧剂选用抗氧剂1010、抗氧剂1076、抗氧剂CA、抗氧剂DNP和抗氧剂MB中的一种混多种混合。
作为优选,所述的无卤阻燃剂选用氮系阻燃剂或氮磷膨胀型阻燃剂。
作为优选,所述的光稳定剂选用受阻胺型光稳定剂与苯并噻唑类紫外线吸收剂。
作为优选,所述的热稳定剂选用钙锌稳定剂。
为了实现上述的第二个目的,本发明采用了以下的技术方案:
一种双轮殻轴流风叶的制备方法,该方法包括以下的步骤:将PP树脂、云母、硅烷偶联剂DB792、硅烷偶联剂KBM-403在高混机里混合10-15min;置于双螺杆挤出机的主喂料口中,从侧喂料口加入玻璃纤维、碳纤维和其他助剂,进行熔融挤出,经水槽冷却后切粒,再经干燥后拌合获得注塑颗粒;将注塑颗粒加入注塑成型机中进行注塑获得所述的双轮殻轴流风叶。
本发明由于采用了上述的技术方案,该双轮殻轴流风叶玻璃纤维为增强材料主体,同时加入了少量的碳纤维,使双轮殻轴流风叶具有较高的耐热、耐化学腐蚀、耐老化、防霉、防紫外线辐射等性能,高密度,高硬度,尺寸变形小,增加塑胶材料的拉伸强度。云母提高耐热温度,屏蔽紫外线,提高绝缘性能,提升玻纤在材料中的分散性,减少材料变形,提升制品尺寸稳定性。加入了硅烷偶联剂DB792、硅烷偶联剂KBM-403,提升树脂与玻纤、碳纤维之间的结合力,改善强度与电气性能,提高疏水性。环状酸酐型相容剂,提升树脂与玻纤、碳纤维之间的相溶性。乙氧基化月桂酰胺使改性材料具备抗静电性能。载银无机抗菌剂使改性材料具备抗菌性能。乙撑双硬脂酰胺改善材料的加工性能,提高流动性。抗氧剂提高树脂降解温度,甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物增加材料韧性,无卤阻燃剂提高材料的阻燃性,光稳定剂改善材料的耐光分解性能,提高老化性能,热稳定剂改善遇热分解性能。
本发明双轮殻轴流风叶具有较高的耐热、耐化学腐蚀、耐老化、防霉、防紫外线辐射等性能,高密度,高硬度,尺寸变形小,增加塑胶材料的拉伸强度。同时,该双轮殻轴流风叶又具备抗静电、抗菌性能、阻燃性能,提高老化性能和遇热分解性能。
具体实施方式
实施例1
一种双轮殻轴流风叶,该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
玻璃纤维 20%
碳纤维 2.5%
云母 5.0%
硅烷偶联剂DB792 1.0%
硅烷偶联剂KBM-403 1. 5%
环状酸酐型相容剂 0.5%
乙氧基化月桂酰胺 0.5%
载银无机抗菌剂 0.8%
乙撑双硬脂酰胺 1.5%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 1.0%
无卤阻燃剂 0.5%
抗氧剂 1.0%
光稳定剂 0.2%
热稳定剂 0.2%
PP 余量。
上述的双轮殻轴流风叶的制备方法,该方法包括以下的步骤:将PP树脂、云母、硅烷偶联剂DB792、硅烷偶联剂KBM-403在高混机里混合10-15min;置于双螺杆挤出机的主喂料口中,从侧喂料口加入玻璃纤维、碳纤维和其他助剂,进行熔融挤出,经水槽冷却后切粒,再经干燥后拌合获得注塑颗粒;将注塑颗粒加入注塑成型机中进行注塑获得所述的双轮殻轴流风叶。
实施例2
一种双轮殻轴流风叶,该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
玻璃纤维 16.0%
碳纤维 4.5%
云母 15.0%
硅烷偶联剂DB792 0.8%
硅烷偶联剂KBM-403 1. 5%
环状酸酐型相容剂 1.0%
乙氧基化月桂酰胺 0.8%
载银无机抗菌剂 0.5%
乙撑双硬脂酰胺 0.5%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 2.0%
无卤阻燃剂 1.5%
抗氧剂 1.0%
光稳定剂 0.2%
热稳定剂 0.2%
PP 余量。
上述的双轮殻轴流风叶的制备方法,该方法包括以下的步骤:将PP树脂、云母、硅烷偶联剂DB792、硅烷偶联剂KBM-403在高混机里混合10-15min;置于双螺杆挤出机的主喂料口中,从侧喂料口加入玻璃纤维、碳纤维和其他助剂,进行熔融挤出,经水槽冷却后切粒,再经干燥后拌合获得注塑颗粒;将注塑颗粒加入注塑成型机中进行注塑获得所述的双轮殻轴流风叶。
实施例3
一种双轮殻轴流风叶,该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
玻璃纤维 22.0%
碳纤维 1.0%
云母 10.0%
硅烷偶联剂DB792 1.5%
硅烷偶联剂KBM-403 1.5%
环状酸酐型相容剂 1.0%
乙氧基化月桂酰胺 0.8%
载银无机抗菌剂 0.5%
乙撑双硬脂酰胺 0.5%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 1.0%
无卤阻燃剂 1.5%
抗氧剂 1.0%
光稳定剂 0.2%
热稳定剂 0.2%
PP 余量。
上述的双轮殻轴流风叶的制备方法,该方法包括以下的步骤:将PP树脂、云母、硅烷偶联剂DB792、硅烷偶联剂KBM-403在高混机里混合10-15min;置于双螺杆挤出机的主喂料口中,从侧喂料口加入玻璃纤维、碳纤维和其他助剂,进行熔融挤出,经水槽冷却后切粒,再经干燥后拌合获得注塑颗粒;将注塑颗粒加入注塑成型机中进行注塑获得所述的双轮殻轴流风叶。
对本发明实施例1的双轮殻轴流风叶进行检测,检测参照Q/NLD 04-2014《离心、盘管风叶》,检测数据如下:
1.结构尺寸:高度: 198.O mm,外径:200.5 mm。
2.跳动量:
轴向跳动量 0.80 mm;径向跳动量 0.90mm。
3.剩余不平衡量:
转速为10OOr/min时,剩余不平衡量为上侧32.0um,下侧28.5um。
4.高低温试验:
1)试验条件:
将受试风叶放置在高低温试验箱中,从室温缓慢加热到+70℃±2℃ ,并保持2h后缓慢冷却,至-20℃ ±3℃ 保持lh,然后在室温条件下放置2h。
2)实验结果:
轴向跳动量0.82mm;径向跳动量 0.95mm。
转速为10OOr/min时,剩余不平衡量为上侧35.0um,下侧30.4um。
Claims (7)
1.一种双轮殻轴流风叶,其特征在于该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
PP 65-85%
玻璃纤维 15-25%
碳纤维 1.0-5.0%
云母 3.0-20%
硅烷偶联剂DB792 0.1-1.5%
硅烷偶联剂KBM-403 0.1-1.5%
环状酸酐型相容剂 0.2-2.0%
乙氧基化月桂酰胺 0.5-1.0%
载银无机抗菌剂 0.2%-1.0%
乙撑双硬脂酰胺 0.5-2.0%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 0.5-3.0%
无卤阻燃剂 0.5-2.0%
抗氧剂 0.5-2.0%
光稳定剂 0.1-1.0%
热稳定剂 0.1-1.0%。
2.根据权利要求1所述的一种双轮殻轴流风叶,其特征在于该双轮殻轴流风叶按质量百分比计由以下的材料注塑成型:
PP 70-80%
玻璃纤维 18-20%
碳纤维 2.0~4.0%
云母 5.0-15%
硅烷偶联剂DB792 0.5-1.5%
硅烷偶联剂KBM-403 0.1-1.5%
环状酸酐型相容剂 0.5-2.0%
乙氧基化月桂酰胺 0.5-1.0%
载银无机抗菌剂 0.2%-1.0%
乙撑双硬脂酰胺 0.5-1.0%
甲基丙烯酸甲酯—丁二烯—苯乙烯三元共聚物 0.8-2.0%
无卤阻燃剂 0.8-1.5%
抗氧剂 0.8-1.5%
光稳定剂 0.1-1.0%
热稳定剂 0.1-1.0%。
3.根据权利要求1所述的一种双轮殻轴流风叶,其特征在于抗氧剂选用抗氧剂1010、抗氧剂1076、抗氧剂CA、抗氧剂DNP和抗氧剂MB中的一种混多种混合。
4.根据权利要求1所述的一种双轮殻轴流风叶,其特征在于无卤阻燃剂选用氮系阻燃剂或氮磷膨胀型阻燃剂。
5.根据权利要求1所述的一种双轮殻轴流风叶,其特征在于光稳定剂选用受阻胺型光稳定剂与苯并噻唑类紫外线吸收剂。
6.根据权利要求1所述的一种双轮殻轴流风叶,其特征在于热稳定剂选用钙锌稳定剂。
7.权利要求1所述的一种双轮殻轴流风叶的制备方法,其特征在于该方法包括以下的步骤:将PP树脂、云母、硅烷偶联剂DB792、硅烷偶联剂KBM-403在高混机里混合10-15min;置于双螺杆挤出机的主喂料口中,从侧喂料口加入玻璃纤维、碳纤维和其他助剂,进行熔融挤出,经水槽冷却后切粒,再经干燥后拌合获得注塑颗粒;将注塑颗粒加入注塑成型机中进行注塑获得所述的双轮殻轴流风叶。