CN106750960A - A kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material and preparation method thereof - Google Patents
A kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material and preparation method thereof Download PDFInfo
- Publication number
- CN106750960A CN106750960A CN201611223575.5A CN201611223575A CN106750960A CN 106750960 A CN106750960 A CN 106750960A CN 201611223575 A CN201611223575 A CN 201611223575A CN 106750960 A CN106750960 A CN 106750960A
- Authority
- CN
- China
- Prior art keywords
- continuous glass
- polypropylene
- sheet material
- antioxidant
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material and preparation method thereof, wherein described crystalline p p sheet includes following raw material by weight:Polypropylene is 40~80 parts, and NYLON610 is 5~30 parts, and glass fibre is 20~60 parts, 0.5 1 parts of lubricant, 0.1~1.5 part of antioxidant.It is an advantage of the invention that:1, NYLON610 has high intensity, strong with glass fibre affinity;2, glass fibre compensate for the polypropylene characteristic not enough with NYLON610 rigidity.3, the addition of lubricant can greatly reduce the viscosity of melt polypropylene, so as to improve dipping effect of the polypropylene to glass fibre.4, the present invention prepared by sheet base in combination with power nylon high intensity and polyacrylic high tenacity.
Description
Technical field
The present invention relates to technical field of polymer materials, more particularly, to high-intensity high-tenacity continuous glass-fiber RPP
Sheet material and preparation method thereof.
Background technology
It is that one kind is different from short glass fiber RPP material that continuous glass-fiber increases crystalline p p sheet, due to glass fibre length
Difference, in the case of fiber content identical, continuous glass-fiber RPP compared with short glass fiber polypropylene, continuous glass-fiber increase
Glass in strong crystalline p p sheet is in continuously unidirectional arrangement, with intensity higher, modulus, toughness and more preferable dimensionally stable
Property.
Influenceing the principal element of continuous glass-fiber RPP sheet material physical property mainly has two aspects:1, polypropylene with
Polyacrylic interface fine structure has a significant impact to its performance;2, the mobility of polymer melt influences acrylic resin and gathers
The impregnation state of propylene, so as to influence the physical property of final continuous glass-fiber RPP sheet material.
In continuous glass-fiber RPP sheet material preparation process, polypropylene and glass need the combination could fully to send out
The high-strength characteristic of glass is waved, and polypropylene and glass are due to the connection without chemical bond, it usually needs additionally add maleic acid
Acid anhydride graft polypropylene is used as compatilizer of the glass in polypropylene, and the addition of graft can cause process small molecular
Distributing for acid anhydrides, is polluted to environment, it is therefore desirable to which compatilizer system is changed.Polyacrylic viscosity is lower, its stream
Dynamic property is better, and resin is more abundant to polyacrylic dipping.The preparation of continuous glass-fiber RPP is typically referred to using melting high
, used as material resin, for general linear polypropylene, melt index is higher, and strand is shorter, thus polypropylene for number polypropylene
The shock resistance of resin declines more obvious.Due to there is amido link on the strand of NYLON610, its surface parent to glass
It is moderate with power so that nylon molecules chain is preferable to the dipping effect of glass, and the carbochain in the middle of each amido link is more long, with polypropylene
Mutually there is stronger interface affinity, thus can be using NYLON610 as polypropylene and the interphase of glass, so as to reach polypropylene
It is indirectly connected to glass, so as to play humidification of the glass in polypropylene to greatest extent.
The content of the invention
The purpose of the present invention be overcome eutectic polypropylene mobility in continuous glass-fiber RPP production process it is low,
Melting means polypropene impact-resistant intensity difference high, and the odor dispersion problem that compatilizer maleic anhydride inoculated polypropylene is brought, carry
For a kind of method of modifying of high-intensity high-tenacity continuous glass-fiber RPP sheet material, the present invention can prepare mobility, compatible
Property, rigidity and all excellent modified polypropene sheet material of toughness.
The technical problems to be solved by the invention are:For above-mentioned technical disadvantages, a kind of continuous glass-fiber enhancing poly- third is proposed
Alkene sheet material and preparation method thereof, can strengthen polypropylene mobility and its dipping effect with glass fibre, increase the strong of material
Degree and toughness.
The purpose of the present invention is to be achieved through the following technical solutions:
A kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material, including the following raw material counted by weight:
Wherein, described polypropylene is melting means polypropylene high, and melt index is 10~50g/10min, and test condition is 230
℃×2.16kg。
Described NYLON610 molecular weight is 5000~15000g/mol.
The continuous glass-fiber is the special alkali-free glass fiber of polypropylene, and its surface is processed through silane coupler, the glass fibers long
Tie up a diameter of 5-20 μm.
The lubricant short chain polypropylene and polyethylene and ethylene copolymers.
The antioxidant be selected from Hinered phenols, hindered amines, phosphite ester or thioether kind antioxidant in one or more,
Including antioxidant 1010, irgasfos 168, antioxidant 3114, one or more in antioxidant 619 or antioxidant DSTP.
Polypropylene is two kinds of different phase materials from glass fibre, and both affinity are poor, and polypropylene soaks to glass fibre
After stain, also there is two-phase laminated flow situation under microstate, thus there is gap between glass and polypropylene, when environment temperature hair
During raw change, glass easily comes off from polypropylene matrix, so as to cause material failure.In the present invention, the addition of NYLON610
The effect of a linking glass and polypropylene matrix can be functioned well as, the amido link of NYLON610 is connected with glass surface, separately
One end fusion is in the mixed matrix of polypropylene and NYLON610.As can be seen here, the present invention dexterously uses polypropylene and nylon
610 is main resin matrix, so as to reach the indirect combination of polypropylene and glass in the case of without Graft Polypropylene,
And give full play to the effect of fiberglass reinforced.
The lubricant short chain propylene and ethylene copolymer, and the lubricant such as stearic acid, butyl stearate for generally using
The problems such as impact property of material being damaged, and there may be precipitation frosting, and short chain propylene is solved just with ethylene copolymer
Problem above.
The preparation method of above-mentioned high-intensity high-tenacity continuous glass-fiber RPP sheet material, comprises the following steps:
(1) polypropylene, NYLON610, antioxidant, lubricant are added in high-speed mixer and are fully mixed;
(2) mixture that step (1) is obtained is added to melting mixing in double screw extruder;
(3) blend melt is expressed into special dipping die cavity, continuous glass fibre is then drawn through dipping former
Head, cooling is in blocks, obtains continuous glass-fiber RPP sheet material.Extrusion temperature is respectively:100 DEG C, 180 DEG C, 200 DEG C, 220
DEG C, 240 DEG C, 260 DEG C, 280 DEG C, 300 DEG C.Engine speed is 350rpm.
It is an advantage of the invention that:
1, polyacrylic viscosity can be selected in a wide range, and low viscosity polypropylene is selected without limitation;
2, it is not necessary to add small molecule class flow ability modifying agent, effectively prevent material from separating out frosting problem.
3, it is not necessary to add maleic anhydride inoculated polypropylene, effectively prevent distributing for the small molecule smell such as acid anhydrides.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following examples will be helpful to the technology of this area
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that to the common skill of this area
For art personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.This belongs to the present invention
Protection domain.
Embodiment 1~2
The present embodiment is related to a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material and preparation method thereof, the method
It is as follows:
Step one, weighs raw material by weight ratio, and each component and its data are shown in Table 1;
Step 2, the raw material for weighing by weight ratio is put into high-speed mixer and mixing 1~5 minute, and then blowing uses extruder
Melting mixing, comprises the following steps that:
The first step:Polypropylene, NYLON610, antioxidant, lubricant are proportionally added into extruder, by extrusion
After machine plasticizing, it is transported in high-temperature fusant groove, high temperature groove internal temperature is 250~280 DEG C, the temperature of screw extruder is 240
~270 DEG C.Wherein polypropylene is provided by Exxon Mobil Corporation, and the trade mark is PP7555;NYLON610 is provided by E.I.Du Pont Company, board
Number be NC010;Antioxidant is using the 1010,168 of BASF AG's offer;Lubricant is provided by Exxon Mobil Corporation, board
Number be SP8999.
Second step, by continuous glass-fiber with the speed drawing of 5~20m/min by high-temperature fusant groove, the length of melt tank
It is 2~5m, after being sufficiently impregnated, cooling is in blocks, obtains high-intensity high-tenacity continuous glass-fiber RPP sheet material.
Table 1
By sample obtained in embodiment 1~4, performance test tensile property test is carried out:Carried out by ISO 527-2 standards,
Draw speed is 50mm/min;Bending property is tested:Carried out by the standards of ISO 178, rate of bending is 2mm/min, concrete outcome
It is shown in Table 2:
Table 2
By upper table 2 it can be seen that inventive samples have mechanical performance higher.
The present invention can also have other embodiment, and all technical schemes formed using equal replacement or equivalent transformation are existed
Within the scope of protection of present invention.
Claims (8)
1. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material, it is characterised in that:Counted by weight including following
Raw material:
2. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 1, it is characterised in that:Institute
The polypropylene stated is melting means polypropylene high, and melt index is 10~50g/10min, and test condition is 230 DEG C × 2.16kg.
3. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 1, it is characterised in that:Institute
The NYLON610 molecular weight stated is 5000~15000g/mol.
4. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 1, it is characterised in that:Institute
Continuous glass-fiber is stated for the special alkali-free glass fiber of polypropylene, its surface is processed through silane coupler, a diameter of 5- of long glass fibres
20μm。
5. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 1, it is characterised in that:Institute
Lubricant is stated for short chain polypropylene and polyethylene and ethylene copolymers.
6. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 1, it is characterised in that:Institute
Antioxidant is stated selected from one or more in Hinered phenols, hindered amines, phosphite ester or thioether kind antioxidant.
7. a kind of high-intensity high-tenacity continuous glass-fiber RPP sheet material according to claim 6, it is characterised in that:Institute
State antioxidant and be selected from antioxidant 1010, irgasfos 168, antioxidant 3114, the one kind or several in antioxidant 619 or antioxidant DSTP
Kind.
8. the preparation method of one of any described high-intensity high-tenacity continuous glass-fiber RPP sheet materials of claim 1-7,
It is characterized in that:Comprise the following steps:
(1) polypropylene, NYLON610, antioxidant, lubricant are added in high-speed mixer and are fully mixed;
(2) mixture that step (1) is obtained is added to melting mixing in double screw extruder;
(3) blend melt is expressed into special dipping die cavity, continuous glass fibre is then drawn through dipping die head, it is cold
But in flakes, continuous glass-fiber RPP sheet material is obtained.Extrusion temperature is respectively:100 DEG C, 180 DEG C, 200 DEG C, 220 DEG C, 240
DEG C, 260 DEG C, 280 DEG C, 300 DEG C.Engine speed is 350rpm.