CN106750836A - A kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure - Google Patents
A kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure Download PDFInfo
- Publication number
- CN106750836A CN106750836A CN201710199995.2A CN201710199995A CN106750836A CN 106750836 A CN106750836 A CN 106750836A CN 201710199995 A CN201710199995 A CN 201710199995A CN 106750836 A CN106750836 A CN 106750836A
- Authority
- CN
- China
- Prior art keywords
- parts
- fast assembling
- disassembling
- antioxidant
- support rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, belong to power construction device field, for the folding of livewire work breaker in middle, it includes the fast assembling-disassembling body of rod, the fast assembling-disassembling body of rod is provided with charge monitoring device, it is characterised in that：The fast assembling-disassembling body of rod is made up of the composition of following weight portion：30~40 parts of high density polyethylene (HDPE), 35~40 parts of high strength glass fiber, 3~5 parts of antioxidant, 2~4 parts of plasticizer, 2~4 parts of fire retardant, 10~15 parts of ceramic, 2~3 parts of titanate coupling agent, 1~2 part of ferrous sulfate, 1~2 part of styrene butadiene styrene block copolymer.In view of above-mentioned technical proposal, is made of new material, with insulating properties and service life higher, the safety of personnel and equipment during powered switching manipulation can be fully ensured that.
Description
Technical field
The invention belongs to power construction device field, specifically, more particularly to it is a kind of suitable for the quick of operations involving high pressure
Dismounting insulating support rod.
Background technology
Generally require to carry out folding to the band electric switch in circuit during operations involving high pressure, due to band electric switch and operation
There is larger voltage difference between bar, so needing the action bars there are insulating properties very high, prevent from occurring in operation
Damage, potential safety hazard is brought to charging equipment, power network and personnel.
The content of the invention
It is an object of the invention to provide a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, it uses new
Material is made, and with insulating properties and service life higher, can fully ensure that during powered switching manipulation personnel and set
Standby safety.
To reach above-mentioned purpose, the present invention is achieved by the following technical solutions：
A kind of heretofore described fast assembling-disassembling insulating support rod suitable for operations involving high pressure, including fast assembling-disassembling bar
Body, the fast assembling-disassembling body of rod is provided with charge monitoring device, and the fast assembling-disassembling body of rod is made up of the composition of following weight portion：
It is 30~40 parts of high density polyethylene (HDPE), 35~40 parts of high strength glass fiber, 3~5 parts of antioxidant, 2~4 parts of plasticizer, fire-retardant
2~4 parts of agent, 10~15 parts of ceramic, 2~3 parts of titanate coupling agent, 1~2 part of ferrous sulfate, styrene butadiene
1~2 part of styrene block copolymer.
Further speaking, the fast assembling-disassembling body of rod described herein is made up of the composition of following weight portion：High density is gathered
32 parts of ethene, 38 parts of high strength glass fiber, 4 parts of antioxidant, 3 parts of plasticizer, 3 parts of fire retardant, 12 parts of ceramic, metatitanic acid
2 parts of ester coupling agent, 1 part of ferrous sulfate, 2 parts of styrene butadiene styrene block copolymer.
Further speaking, antioxidant described herein is antioxidant 1010, antioxidant 2246, antioxidant
Any one selected in 264 and DLTP.
Further speaking, high density polyethylene (HDPE) described herein, high strength glass fiber, antioxidant, plasticizer,
Fire retardant, ceramic, titanate coupling agent, ferrous sulfate, styrene butadiene styrene block copolymer are according to upper
State and high speed mixer is put into after weight portion is weighed, the temperature of high speed mixer is 120~125 DEG C.
Further speaking, the temperature of high temperature batch mixer described herein is 125 DEG C.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention can be made of new material, with insulating properties and service life higher, can be fully ensured that
The safety of personnel and equipment during powered switching manipulation.
Specific embodiment
Technical scheme described herein is described further with reference to embodiment.
Embodiment 1：A kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, including the fast assembling-disassembling body of rod, it is described
The fast assembling-disassembling body of rod is provided with charge monitoring device, and the fast assembling-disassembling body of rod is made up of the composition of following weight portion：High density
30~40 parts of polyethylene, 35~40 parts of high strength glass fiber, 3~5 parts of antioxidant, 2~4 parts of plasticizer, fire retardant 2~4
Part, 10~15 parts of ceramic, 2~3 parts of titanate coupling agent, 1~2 part of ferrous sulfate, styrene butadiene styrene
1~2 part of block copolymer.
Embodiment 2：A kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, including the fast assembling-disassembling body of rod, it is described
The fast assembling-disassembling body of rod is provided with charge monitoring device, and the fast assembling-disassembling body of rod is made up of the composition of following weight portion：High density
32 parts of polyethylene, 38 parts of high strength glass fiber, 4 parts of antioxidant, 3 parts of plasticizer, 3 parts of fire retardant, 12 parts of ceramic, titanium
2 parts of acid esters coupling agent, 1 part of ferrous sulfate, 2 parts of styrene butadiene styrene block copolymer.
Embodiment 3：A kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, the antioxidant is antioxidant
High density polyethylene (HDPE), high strength glass fiber, antioxidant, plasticizer, fire retardant, ceramic, titanate esters idol described in 2246
Connection agent, ferrous sulfate, styrene butadiene styrene block copolymer put into mixed at a high speed after being weighed according to above-mentioned weight portion
Material machine, the temperature of high speed mixer is 120~125 DEG C.Remainder is identical with embodiment 1 or embodiment 2.
In view of above-described embodiment, the composition composition body of rod using above-mentioned weight portion of the invention, can realize in hyperbaric environment
Under to the disconnection with electric switch and closed procedure, and service life improves 50% relative to existing action bars, and properties refer to
Mark leads over the similar-type products of existing market sale, with promotional value and market prospects higher.
Claims (5)
1. a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure, including the fast assembling-disassembling body of rod, the fast assembling-disassembling bar
Body is provided with charge monitoring device, it is characterised in that：The fast assembling-disassembling body of rod is made up of the composition of following weight portion：High density
30~40 parts of polyethylene, 35~40 parts of high strength glass fiber, 3~5 parts of antioxidant, 2~4 parts of plasticizer, fire retardant 2~4
Part, 10~15 parts of ceramic, 2~3 parts of titanate coupling agent, 1~2 part of ferrous sulfate, styrene butadiene styrene
1~2 part of block copolymer.
2. a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure according to claim 1, it is characterised in that：Institute
The fast assembling-disassembling body of rod is stated to be made up of the composition of following weight portion：32 parts of high density polyethylene (HDPE), 38 parts of high strength glass fiber, antioxygen
4 parts of agent, 3 parts of plasticizer, 3 parts of fire retardant, 12 parts of ceramic, 2 parts of titanate coupling agent, 1 part of ferrous sulfate, styrene
2 parts of butadiene styrene block copolymerization thing.
3. a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure according to claim 2, it is characterised in that：Institute
State antioxidant for select in antioxidant 1010, antioxidant 2246, antioxidant 264 and DLTP any one.
4. a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure according to claim 3, it is characterised in that：Institute
State high density polyethylene (HDPE), high strength glass fiber, antioxidant, plasticizer, fire retardant, ceramic, titanate coupling agent, sulphur
Sour ferrous, styrene butadiene styrene block copolymer puts into high speed mixer after being weighed according to above-mentioned weight portion, high
The temperature of fast batch mixer is 120~125 DEG C.
5. a kind of fast assembling-disassembling insulating support rod suitable for operations involving high pressure according to claim 4, it is characterised in that：Institute
The temperature for stating high temperature batch mixer is 125 DEG C.