CN105153519A - Rod insulation material for insulating rod - Google Patents
Rod insulation material for insulating rod Download PDFInfo
- Publication number
- CN105153519A CN105153519A CN201510613351.4A CN201510613351A CN105153519A CN 105153519 A CN105153519 A CN 105153519A CN 201510613351 A CN201510613351 A CN 201510613351A CN 105153519 A CN105153519 A CN 105153519A
- Authority
- CN
- China
- Prior art keywords
- parts
- rod
- stainless steel
- steel wire
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rod insulation material for an insulating rod, and belongs to the field of hot-line work devices. The rod insulation material is used for the insulating rod and comprises a rod body. The rod body is of a hollow structure and is formed in the mode that two or three kinds of high-strength glass fibers, stainless steel wires and high-strength nylon fibers are knitted in a mixed mode to be filled with an evenly-mixed mixture in an injection molding mode, wherein the mixture is prepared from, by weight, 30 parts to 40 parts of high density polyethylene, 25 parts to 30 parts of polyvinyl chloride, 1 part to 5 parts of hard amide, 1 part to 3 parts of plasticizers, 2 parts to 6 parts of antioxidants, 3 parts to 6 parts of aluminum hydroxide and 1 part to 2 parts of aromatic acid anhydride. By means of the rod insulation material in the technical scheme, hot-line safe and rapid detection can be achieved, and the adopted rod insulation material can not generate a conductive phenomenon and is long in service life and high in reliability.
Description
Technical field
The invention belongs to hot line work device field, specifically, particularly relate to a kind of insulating bar body of rod insulating material.
Background technology
In field of electricity construction, for equipment transmission or not frequent operations such as on-pole switch, isolation switch and transformer fuse switches.In operating process, according to regulations stipulate, need to carry out electrical verification to each position, and with regard to existing instrument and condition, there is certain difficulty in electrical verification, often causes that electrical verification labor intensity is large, efficiency is low, poor stability, and very easily occur habitual violating the regulations, cause potential hidden danger to the person, equipment, restrict the raising of distribution management level simultaneously.
Summary of the invention
The object of the present invention is to provide a kind of insulating bar body of rod insulating material, it can realize the charged detection safely and fast of circuit, and rod body material used electric conduction phenomena can not occur, and long service life, reliability is high.
For achieving the above object, the present invention is achieved by the following technical solutions:
Insulating bar described in the present invention body of rod insulating material, comprise the body of rod, the described body of rod is hollow structure, after adopting high strength glass fiber, Stainless Steel Wire, two or three mixed weaving in high-strength nylon fiber mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 30 ~ 40 parts, polyvinyl chloride 25 ~ 30 parts, hard acid amides 1 ~ 5 part, 1 ~ 3 part, softening agent, antioxidant 2 ~ 6 parts, 3 ~ 6 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
Say further, the body of rod described in the application is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 32 ~ 38 parts, polyvinyl chloride 26 ~ 28 parts, hard acid amides 2 ~ 4 parts, 1 ~ 3 part, softening agent, antioxidant 3 ~ 5 parts, 4 ~ 5 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
Say further, the body of rod described in the application is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 35 parts, polyvinyl chloride 27 parts, hard acid amides 3 parts, 2 parts, softening agent, antioxidant 4 parts, 4.5 parts, aluminium hydroxide, aromatic anhydride 1.5 parts.
Say further, the high strength glass fiber described in the application, Stainless Steel Wire connect number ratio 2:1 according to warp direction, and the ratio that weft direction connects number ratio 1:3 weaves.
Say further, the diameter of the high strength glass fiber described in the application, Stainless Steel Wire selects 0.5mm ~ 1.5mm.
Say further, the diameter of the high strength glass fiber described in the application, Stainless Steel Wire selects 0.5mm or 0.8mm or 1.0mm or 1.2mm or 1.5mm.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention adopt in high strength glass fiber, Stainless Steel Wire, high-strength nylon fiber one or more be woven into skeleton construction, and mould filling has the case material of rational proportion in skeleton construction, make the rod body material described in the present invention when having good insulativity, ensure the firm of housing and stability, increase body of rod weight capacity when using and work-ing life, later stage replacement cost can be reduced relative to existing insulating bar rod body material, reduce maintenance cost.
Embodiment
Below in conjunction with embodiment, the technical scheme described in the application is described further.
Embodiment 1: a kind of insulating bar body of rod insulating material, comprise the body of rod, the described body of rod is hollow structure, after adopting high strength glass fiber, Stainless Steel Wire, two or three mixed weaving in high-strength nylon fiber mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 30 ~ 40 parts, polyvinyl chloride 25 ~ 30 parts, hard acid amides 1 ~ 5 part, 1 ~ 3 part, softening agent, antioxidant 2 ~ 6 parts, 3 ~ 6 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
Embodiment 2: a kind of insulating bar body of rod insulating material, comprise the body of rod, the described body of rod is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 32 ~ 38 parts, polyvinyl chloride 26 ~ 28 parts, hard acid amides 2 ~ 4 parts, 1 ~ 3 part, softening agent, antioxidant 3 ~ 5 parts, 4 ~ 5 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
Embodiment 3: a kind of insulating bar body of rod insulating material, comprise the body of rod, the described body of rod is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 35 parts, polyvinyl chloride 27 parts, hard acid amides 3 parts, 2 parts, softening agent, antioxidant 4 parts, 4.5 parts, aluminium hydroxide, aromatic anhydride 1.5 parts.
Embodiment 4: a kind of insulating bar body of rod insulating material, comprise the body of rod, wherein said high strength glass fiber, Stainless Steel Wire connect quantity 2:1 according to warp direction, and the ratio that weft direction connects quantity 1:3 weaves.Wherein the diameter of high strength glass fiber, Stainless Steel Wire selects 0.5mm or 0.8mm or 1.0mm or 1.2mm or 1.5mm, fully can ensure load-bearing and the toughness of basic framework.Rest part is identical with the content in embodiment 1 to embodiment 3.
High strength glass fiber in above-mentioned, the diameter of Stainless Steel Wire can meet the necessary strength and toughness forming support, can not occur fracture or diastrophic problem after hanging over certainweight object in operation use procedure.Work-ing life of the present invention can not only be increased, and can use range be expanded, the idle of production material can not be caused, make rational use of resources.
The qualitative lifting of above-mentioned materials is the first step ensured personal safety, skeleton construction is woven into by one or more in employing high strength glass fiber, Stainless Steel Wire, high-strength nylon fiber, and mould filling has the case material of rational proportion in skeleton construction, make the rod body material described in the present invention when having good insulativity, ensure the firm of housing and stability, increase body of rod weight capacity when using and work-ing life, later stage replacement cost can be reduced relative to existing insulating bar rod body material, reduce maintenance cost.
Claims (6)
1. an insulating bar body of rod insulating material, comprise the body of rod, it is characterized in that: the described body of rod is hollow structure, after adopting high strength glass fiber, Stainless Steel Wire, two or three mixed weaving in high-strength nylon fiber mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 30 ~ 40 parts, polyvinyl chloride 25 ~ 30 parts, hard acid amides 1 ~ 5 part, 1 ~ 3 part, softening agent, antioxidant 2 ~ 6 parts, 3 ~ 6 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
2. insulating bar body of rod insulating material according to claim 1, it is characterized in that: the described body of rod is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 32 ~ 38 parts, polyvinyl chloride 26 ~ 28 parts, hard acid amides 2 ~ 4 parts, 1 ~ 3 part, softening agent, antioxidant 3 ~ 5 parts, 4 ~ 5 parts, aluminium hydroxide, aromatic anhydride 1 ~ 2 part.
3. insulating bar body of rod insulating material according to claim 2, it is characterized in that: the described body of rod is hollow structure, adopt high strength glass fiber, after Stainless Steel Wire mixed weaving mould filling have mix by the composition of following weight part: high density polyethylene(HDPE) 35 parts, polyvinyl chloride 27 parts, hard acid amides 3 parts, 2 parts, softening agent, antioxidant 4 parts, 4.5 parts, aluminium hydroxide, aromatic anhydride 1.5 parts.
4. insulating bar body of rod insulating material according to claim 3, it is characterized in that: described high strength glass fiber, Stainless Steel Wire connect number ratio 2:1 according to warp direction, the ratio that weft direction connects number ratio 1:3 weaves.
5. insulating bar body of rod insulating material according to claim 4, is characterized in that: the diameter of described high strength glass fiber, Stainless Steel Wire selects 0.5mm ~ 1.5mm.
6. insulating bar body of rod insulating material according to claim 5, is characterized in that: the diameter of described high strength glass fiber, Stainless Steel Wire selects 0.5mm or 0.8mm or 1.0mm or 1.2mm or 1.5mm.