CN106750833A - A kind of highstrenghtpiston's inspection shaft and preparation method thereof - Google Patents
A kind of highstrenghtpiston's inspection shaft and preparation method thereof Download PDFInfo
- Publication number
- CN106750833A CN106750833A CN201710161498.3A CN201710161498A CN106750833A CN 106750833 A CN106750833 A CN 106750833A CN 201710161498 A CN201710161498 A CN 201710161498A CN 106750833 A CN106750833 A CN 106750833A
- Authority
- CN
- China
- Prior art keywords
- parts
- inspection shaft
- highstrenghtpiston
- auxiliary agent
- pnbr
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of highstrenghtpiston's inspection shaft and preparation method thereof, and the plastic inspection well is made up of the raw material of following weight portion：20 30 parts of high density polyethylene (HDPE), 20 30 parts of polyvinyl chloride, 5 10 parts of PNBR, 35 parts of stainless steel fibre, 13 parts of auxiliary agent, 0.5 2 parts of coupling agent, 36 parts of acrylonitrile butadient styrene, 12 parts of compatilizer, 5 10 parts of mica powder, 5 10 parts of montmorillonite, 13 parts of boron nitride fiber, 10 15 parts of polysulfone resin, 5 10 parts of polyoxymethylene.Each raw material of reasonable disposition of the present invention, the material excellent combination property of preparation, the inspection shaft of processing has intensity high, rigidity, impact strength and decay resistance, and good surface gloss, preferably can adaptively descend adverse circumstances.
Description
Technical field
The present invention relates to inspection shaft field, and in particular to a kind of highstrenghtpiston's inspection shaft and preparation method thereof.
Background technology
Inspection shaft is power supply, feedwater, draining, communication, cable television, gas pipe, the street lamp for Urban Underground infrastructure
Circuit etc. repair, it is easy for installation and set.Be generally located at pipeline intersection, turning, caliber or gradient change, Yi Jizhi
Spool section on locate at a certain distance, in order to inspect periodically, clean and dredge or down-hole operation inspection well shape structures.
With economic development and the aggravation of Urbanization Construction, inspection shaft pays concrete inspection well in advance by traditional clay brick, cement block
Develop into plastic inspection well.Plastic inspection well typically uses injection moulding successively, and moulding process link is few, and yield is high, and quality is steady
It is fixed.China issues for 2006《One residential draining plastic inspection well》, the development of plastic inspection well is promoted energetically, progressively take
For traditional inspection shaft, the fast development of plastic inspection well raw material is thereby promoted.Its surface of existing plastic inspection well is hard
Degree and intensity are also relatively poor, are not suitable for adverse circumstances and use, and service life is short.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of highstrenghtpiston's inspection shaft and preparation method thereof.
To realize object above, the present invention is achieved by the following technical programs：
A kind of highstrenghtpiston's inspection shaft, is made up of the raw material of following weight portion：High density polyethylene (HDPE) 20-30 parts, polychlorostyrene
Ethene 20-30 parts, PNBR 5-10 parts, stainless steel fibre 3-5 parts, auxiliary agent 1-3 parts, coupling agent 0.5-2 parts, propylene
Nitrile-BS 3-6 parts, compatilizer 1-2 parts, mica powder 5-10 parts, montmorillonite 5-10 parts, boron nitride fiber
1-3 parts, polysulfone resin 10-15 parts, polyoxymethylene 5-10 parts.
Preferably, it is made up of the raw material of following weight portion：25 parts of high density polyethylene (HDPE), 25 parts of polyvinyl chloride, powdered nitrile rubber
It is 8 parts of rubber, 4 parts of stainless steel fibre, 2 parts of auxiliary agent, 1.5 parts of coupling agent, 4 parts of acrylonitrile-butadiene-styrene copolymer, compatible
1.5 parts of agent, 7 parts of mica powder, 7 parts of montmorillonite, 2 parts of boron nitride fiber, 12 parts of polysulfone resin, 7 parts of polyoxymethylene.
Preferably, the auxiliary agent includes stabilizer, plasticizer, antioxidant, lubricant, fire retardant.
Preferably, the polysulfone resin is bisphenol-a polysulfone resin.
The preparation method of highstrenghtpiston's inspection shaft, step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, poly-
Sulphone resin is added in high mixer, mixes 10-15min, obtains material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, mix
5-10min, adds stainless steel fibre, boron nitride fiber, stirs 5-10min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould,
Machine-shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.
Beneficial effect of the present invention：The present invention with high density polyethylene (HDPE) and polyvinyl chloride as base material, the polysulfone resin of addition and
Polyoxymethylene improves the intensity and rigidity of material, and boron nitride fiber further improves its impact resistance, PNBR
Toughening effect can be played, each raw material of reasonable disposition of the present invention, the material excellent combination property of preparation, the inspection shaft of processing has
Intensity high, rigidity, impact strength and decay resistance, and good surface gloss, preferably adaptively lower can dislike
Bad environment.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.
Embodiment 1：
A kind of highstrenghtpiston's inspection shaft, is made up of the raw material of following weight portion：25 parts of high density polyethylene (HDPE), polyvinyl chloride
25 parts, 8 parts of PNBR, 4 parts of stainless steel fibre, 2 parts of auxiliary agent, 1.5 parts of coupling agent, acrylonitrile-butadiene-styrene (ABS) it is common
4 parts of polymers, 1.5 parts of compatilizer, 7 parts of mica powder, 7 parts of montmorillonite, 2 parts of boron nitride fiber, 12 parts of polysulfone resin, polyoxymethylene
7 parts.
The preparation method of highstrenghtpiston's inspection shaft, step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, poly-
Sulphone resin is added in high mixer, mixes 12min, obtains material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, mix
8min, adds stainless steel fibre, boron nitride fiber, stirs 5min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould,
Machine-shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.
Embodiment 2：
A kind of highstrenghtpiston's inspection shaft, is made up of the raw material of following weight portion：27 parts of high density polyethylene (HDPE), polyvinyl chloride
24 parts, 7 parts of PNBR, 3.5 parts of stainless steel fibre, 2.5 parts of auxiliary agent, 1 part of coupling agent, acrylonitrile-butadiene-styrene (ABS)
5 parts of copolymer, 2 parts of compatilizer, 8 parts of mica powder, 8 parts of montmorillonite, 1.5 parts of boron nitride fiber, 14 parts of bisphenol-a polysulfone resin,
8 parts of polyoxymethylene, wherein, auxiliary agent includes stabilizer, plasticizer, antioxidant, lubricant, fire retardant.
The preparation method of highstrenghtpiston's inspection shaft, step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, double
Phenol A type polysulfone resins are added in high mixer, mix 15min, obtain material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, mix
10min, adds stainless steel fibre, boron nitride fiber, stirs 5min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould,
Machine-shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.
Embodiment 3：
A kind of highstrenghtpiston's inspection shaft, is made up of the raw material of following weight portion：20 parts of high density polyethylene (HDPE), polyvinyl chloride
30 parts, 5 parts of PNBR, 5 parts of stainless steel fibre, 1 part of auxiliary agent, 2 parts of coupling agent, acrylonitrile-butadiene-styrene (ABS) copolymerization
3 parts of thing, 2 parts of compatilizer, 5 parts of mica powder, 10 parts of montmorillonite, 1 part of boron nitride fiber, 15 parts of bisphenol-a polysulfone resin, polyoxy are sub-
5 parts of methyl, wherein, auxiliary agent includes stabilizer, plasticizer, antioxidant, lubricant, fire retardant.
The preparation method of highstrenghtpiston's inspection shaft, step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, double
Phenol A type polysulfone resins are added in high mixer, mix 10min, obtain material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, mix
10min, adds stainless steel fibre, boron nitride fiber, stirs 10min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould,
Machine-shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.
Embodiment 4：
A kind of highstrenghtpiston's inspection shaft, is made up of the raw material of following weight portion：30 parts of high density polyethylene (HDPE), polyvinyl chloride
20 parts, 10 parts of PNBR, 3 parts of stainless steel fibre, 3 parts of auxiliary agent, 0.5 part of coupling agent, acrylonitrile-butadiene-styrene (ABS)
It is 6 parts of copolymer, 1 part of compatilizer, 10 parts of mica powder, 5 parts of montmorillonite, 3 parts of boron nitride fiber, 10 parts of bisphenol-a polysulfone resin, poly-
10 parts of Oxymethylene, wherein, auxiliary agent includes stabilizer, plasticizer, antioxidant, lubricant, fire retardant.
The preparation method of highstrenghtpiston's inspection shaft, step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, double
Phenol A type polysulfone resins are added in high mixer, mix 15min, obtain material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, mix
5min, adds stainless steel fibre, boron nitride fiber, stirs 5min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould,
Machine-shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality
Body or operation make a distinction with another entity or operation, and not necessarily require or imply these entities or deposited between operating
In any this actual relation or order.And, term " including ", "comprising" or its any other variant be intended to
Nonexcludability is included, so that process, method, article or equipment including a series of key elements not only will including those
Element, but also other key elements including being not expressly set out, or also include being this process, method, article or equipment
Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that
Also there is other identical element in process, method, article or equipment including the key element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention has been described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic；And these modification or
Replace, do not make the spirit and scope of the essence disengaging various embodiments of the present invention technical scheme of appropriate technical solution.
Claims (5)
1. a kind of highstrenghtpiston's inspection shaft, it is characterised in that be made up of the raw material of following weight portion：High density polyethylene (HDPE) 20-
30 parts, polyvinyl chloride 20-30 parts, PNBR 5-10 parts, stainless steel fibre 3-5 parts, auxiliary agent 1-3 parts, coupling agent 0.5-2
Part, acrylonitrile-butadiene-styrene copolymer 3-6 parts, compatilizer 1-2 parts, mica powder 5-10 parts, montmorillonite 5-10 parts, nitridation
Boron fibre 1-3 parts, polysulfone resin 10-15 parts, polyoxymethylene 5-10 parts.
2. highstrenghtpiston's inspection shaft as claimed in claim 1, it is characterised in that be made up of the raw material of following weight portion：It is high
25 parts of density polyethylene, 25 parts of polyvinyl chloride, 8 parts of PNBR, 4 parts of stainless steel fibre, 2 parts of auxiliary agent, coupling agent 1.5
Part, 4 parts of acrylonitrile-butadiene-styrene copolymer, 1.5 parts of compatilizer, 7 parts of mica powder, 7 parts of montmorillonite, boron nitride fiber 2
Part, 12 parts of polysulfone resin, 7 parts of polyoxymethylene.
3. highstrenghtpiston's inspection shaft as claimed in claim 2, it is characterised in that the auxiliary agent include stabilizer, plasticizer,
Antioxidant, lubricant, fire retardant.
4. highstrenghtpiston's inspection shaft as claimed in claim 2, it is characterised in that the polysulfone resin is bisphenol-a polysulfone
Resin.
5. the preparation method of the highstrenghtpiston's inspection shaft as described in claim 1-4 is any, it is characterised in that step is as follows：
1) by high density polyethylene (HDPE), polyvinyl chloride, PNBR, acrylonitrile-butadiene-styrene copolymer, polysulfones tree
Fat is added in high mixer, mixes 10-15min, obtains material A；
2) to mica powder, montmorillonite, coupling agent, compatilizer, auxiliary agent and polyoxymethylene is added in material A, 5- is mixed
10min, adds stainless steel fibre, boron nitride fiber, stirs 5-10min, obtains material B；
3) in material B being put into injection machine, extruding obtains melt in the presence of screw rod, is molded into mould, processes
Shaping；
4) mould is cooled to room temperature, opens mould, obtain semi-finished product, repair flash, got product.