CN106750633A - A kind of anti-flammability high wear-resistant rubber formula - Google Patents
A kind of anti-flammability high wear-resistant rubber formula Download PDFInfo
- Publication number
- CN106750633A CN106750633A CN201611202684.9A CN201611202684A CN106750633A CN 106750633 A CN106750633 A CN 106750633A CN 201611202684 A CN201611202684 A CN 201611202684A CN 106750633 A CN106750633 A CN 106750633A
- Authority
- CN
- China
- Prior art keywords
- parts
- high wear
- resistant rubber
- flammability
- formulated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-flammability high wear-resistant rubber formula, it is characterised in that：Each component weight fraction is as follows in the formula：50~75 parts of butadiene rubber；12~25 parts of natural gum glue；6~8 parts of nano zine oxide；6~11 parts of di adipate；0.2~0.8 part of stearic acid；4,4 pairs of 3~10 parts of diphenylamines；2~3 parts of Organoalkyl acid phosphoric acid ester；38~60 parts of high wear-resistant carbon black；0.2~0.5 part of potassium stearate；1~2 part of sulphur；3~5 parts of plasticizer；8~12 parts of barium sulfate；10~25 parts of inorganic combustion inhibitor.Have compared with soft the invention provides one kind, low production cost, with more excellent chemically stable type, the good high wear-resistant rubber formula of fire resistance.
Description
Technical field
The present invention relates to rubber compounding, more particularly to a kind of anti-flammability high wear-resistant rubber formula.
Background technology,
Natural rubber early has been widely used space flight, aviation, oil, chemical industry, vapour as a kind of macromolecular material of function admirable
The fields such as car, shipbuilding.Its use condition is also ever-changing, in order to meet the performance requirement of parts, it is necessary in severe ring
Still there is high stability and long-life, most rubbers are all flammable or inflammable, and this is that it is upper in application under border
A major defect, therefore their fire resistance is most important.
The content of the invention
In order to solve the problems of the prior art, have compared with soft the invention provides one kind, low production cost has
More excellent chemically stable type, the good anti-flammability high wear-resistant rubber formula of fire resistance.
In order to solve the above problems, the technical solution used in the present invention is：
A kind of anti-flammability high wear-resistant rubber formula, it is characterised in that：Each component weight fraction is as follows in the formula：
50~75 parts of butadiene rubber；
12~25 parts of natural gum glue；
6~8 parts of nano zine oxide；
6~11 parts of di adipate；
0.2~0.8 part of stearic acid；
4,4- double 3~10 parts of diphenylamines；
2~3 parts of Organoalkyl acid phosphoric acid ester；
38~60 parts of high wear-resistant carbon black；
0.2~0.5 part of potassium stearate；
1~2 part of sulphur；
3~5 parts of plasticizer；
8~12 parts of barium sulfate；
10~25 parts of inorganic combustion inhibitor.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：The inorganic combustion inhibitor is antimony oxide.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：The plasticizer is softening oil.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：60 parts of the butadiene rubber, natural gum glue 20
Part.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：7 parts of the nano zine oxide, adipic acid two
9 parts of ester.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：Double 8 parts of the diphenylamines of 4, the 4-, organic alkane
2.5 parts of base acid phosphoric acid ester.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：48 parts of the high wear-resistant carbon black, potassium stearate
0.3 part.
A kind of foregoing anti-flammability high wear-resistant rubber formula, it is characterised in that：17 parts of inorganic combustion inhibitor.
The beneficial effects of the invention are as follows：According to the anti-flammability high wear-resistant rubber formula that the present invention is obtained, add with good
Work mobility, can facilitate and it is processed, the various rubbers being made, and low temperature flexibility is also preferable, and the rubber
There is stronger bonding force between skeleton to ensure the bonding effect of stabilization, and low production cost, good flame retardation effect, it is nonflammable
Burn, long service life, using more safe and reliable.
Specific embodiment
The following examples are only intended to illustrate the technical solution of the present invention more clearly, and can not limit the present invention with this
Protection domain.
A kind of anti-flammability high wear-resistant rubber formula, it is characterised in that：Each component weight fraction is as follows in the formula：
60 parts of butadiene rubber；
20 parts of natural gum glue；
7 parts of nano zine oxide；
9 parts of di adipate；
0.5 part of stearic acid；
4,4- double 8 parts of diphenylamines；
2.5 parts of Organoalkyl acid phosphoric acid ester；
48 parts of high wear-resistant carbon black；
0.3 part of potassium stearate；
1.5 parts of sulphur；
4 parts of plasticizer；
11 parts of barium sulfate；
17 parts of inorganic combustion inhibitor.
The inorganic combustion inhibitor is antimony oxide.The plasticizer is softening oil.
In sum：According to the anti-flammability high wear-resistant rubber formula that the present invention is obtained, with good processing fluidity, can
It is processed with facilitating, the various rubbers being made, low temperature flexibility is also preferable, and had between the rubber and skeleton
There is stronger bonding force to ensure the bonding effect of stabilization, and low production cost, good flame retardation effect, nonflammable, service life
It is long, using more safe and reliable.
General principle of the invention, principal character and advantage has been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, simply original of the invention is illustrated described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
All fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appending claims and its equivalent circle.
It is fixed.
Claims (8)
1. a kind of anti-flammability high wear-resistant rubber is formulated, it is characterised in that：Each component weight fraction is as follows in the formula：
50~75 parts of butadiene rubber；
12~25 parts of natural gum glue；
6~8 parts of nano zine oxide；
6~11 parts of di adipate；
0.2~0.8 part of stearic acid；
4,4- double 3~10 parts of diphenylamines；
2~3 parts of Organoalkyl acid phosphoric acid ester；
38~60 parts of high wear-resistant carbon black；
0.2~0.5 part of potassium stearate；
1~2 part of sulphur；
3~5 parts of plasticizer；
8~12 parts of barium sulfate；
10~25 parts of inorganic combustion inhibitor.
2. a kind of anti-flammability high wear-resistant rubber according to claim 1 is formulated, it is characterised in that：The inorganic combustion inhibitor is
Antimony oxide.
3. a kind of anti-flammability high wear-resistant rubber according to claim 2 is formulated, it is characterised in that：The plasticizer is softening
Oil.
4. a kind of anti-flammability high wear-resistant rubber according to claim 3 is formulated, it is characterised in that：The butadiene rubber 60
Part, 20 parts of natural gum glue.
5. a kind of anti-flammability high wear-resistant rubber according to claim 4 is formulated, it is characterised in that：The nano zine oxide 7
Part, 9 parts of di adipate.
6. a kind of anti-flammability high wear-resistant rubber according to claim 5 is formulated, it is characterised in that：The double hexichol of 4, the 4-
8 parts of amine, 2.5 parts of Organoalkyl acid phosphoric acid ester.
7. a kind of anti-flammability high wear-resistant rubber according to claim 6 is formulated, it is characterised in that：The high wear-resistant carbon black 48
Part, 0.3 part of potassium stearate.
8. a kind of anti-flammability high wear-resistant rubber according to claim 7 is formulated, it is characterised in that：17 parts of inorganic combustion inhibitor.