CN106747494A - Cremator a heatable brick bed face castable - Google Patents
Cremator a heatable brick bed face castable Download PDFInfo
- Publication number
- CN106747494A CN106747494A CN201611062397.2A CN201611062397A CN106747494A CN 106747494 A CN106747494 A CN 106747494A CN 201611062397 A CN201611062397 A CN 201611062397A CN 106747494 A CN106747494 A CN 106747494A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- equal
- less
- particle diameter
- electric smelting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses cremator a heatable brick bed face castable, is made up of the following raw material：The white flint clay aggregate of electric smelting M70 mullite aggregates, aluminium 45, the white flint clay micro mist of aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, the aquamaine stone flour of aluminium 60,71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro P803.Cremator a heatable brick bed face castable of the present invention is with cremator chassis, the 2100mm of prefabricated length 2200,780 680mm wide, the resistance to heated kang face of thick 120 150mm, liquid corrosion and fuel-firing gas-firing is produced to corrode during resistance to rapid heat cycle and the cremate of resistance to human body, long service life.
Description
Technical field
The present invention relates to cremator.More particularly, to cremator a heatable brick bed face castable.
Background technology
Human body is placed in cremate human body enters cremator on a heatable brick bed face, burner is to light, and a heatable brick bed face will be by high temperature and high speed
The erosion of flame and human body acidity body fluid, after cremate terminates, the strong cooling of cold air will be subject in stove, that is, family members wait after lowering the temperature
Bone ash is collected, whole process is serious test to a heatable brick bed face castable, it is desirable to which a heatable brick bed face high temperature resistant, resistance to rapid heat cycle, resistance to human body are cremated
During produce the erosion of the gas such as liquid corrosion and fuel-firing gas-firing.But the resistance to rapid heat cycle in cremator a heatable brick bed face of the prior art
Poor-performing, and corrosion-resistant, cause the service life in cremator a heatable brick bed face smaller.
The content of the invention
It is rotten it is an object of the present invention to provide generation liquid during a kind of resistance to rapid heat cycle and the cremate of resistance to human body
Erosion and the cremator a heatable brick bed face castable of fuel-firing gas-firing corrosion.
To reach above-mentioned purpose, the present invention uses following technical proposals：
Cremator a heatable brick bed face castable, is made up of the following raw material：The white flint clay aggregate of electric smelting M70 mullite aggregates, aluminium 45, aluminium
45 white flint clay micro mists, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, the aquamaine stone flour of aluminium 60,
71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro P803.
The white flint clay aggregate of electric smelting M70 mullite aggregates, aluminium 45, the white flint clay micro mist of aluminium 45, angstrom willing 95U silicon ashes, oxidation
Aluminium micro mist, Suzhou white clay, electric smelting M70 do not come fine powder, the aquamaine stone flour of aluminium 60, triumphant Northey match card 71 cement, additional 2520 steel fibre,
Explosion-proof fiber, BASF 2651F and the bright icepro P803 of Germany are marketable material, directly can commercially obtain.
Above-mentioned cremator a heatable brick bed face castable, the electric smelting M70 mullite aggregates are 40-60 weight portions.
Above-mentioned cremator a heatable brick bed face castable, the electric smelting M70 mullite aggregates are by particle diameter more than 0 and less than or equal to 1mm
Electric smelting M70 mullite aggregates, particle diameter be more than 3mm more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm, particle diameter
And the electric smelting M70 mullite aggregates and particle diameter less than or equal to 5mm are more than 5mm and the electric smelting M70 less than or equal to 8mm not
Carry out stone aggregate composition.
Above-mentioned cremator a heatable brick bed face castable, electric smelting M70 mullite aggregate of the particle diameter more than 0 and less than or equal to 1mm is 8-
The electric smelting M70 mullite aggregates of 12 weight portions, particle diameter more than 1mm and less than or equal to 3mm are 8-13 weight portions, particle diameter is more than
3mm and the electric smelting M70 mullite aggregates less than or equal to 5mm are 8-13 weight portions, particle diameter more than 5mm and less than or equal to 8mm
Electric smelting M70 mullite aggregates be 16-22 weight portions.
Above-mentioned cremator a heatable brick bed face castable, the white flint clay aggregate of the aluminium 45 is 14-22 weight portions.
Above-mentioned cremator a heatable brick bed face castable, the white flint clay aggregate of the aluminium 45 is by particle diameter more than 0 and less than or equal to 1mm's
The white flint clay aggregate of aluminium 45, particle diameter are more than 1mm and the white flint clay aggregate of the aluminium 45 less than or equal to 3mm, particle diameter more than 3mm and small
In or equal to 5mm the white flint clay aggregate of aluminium 45 and particle diameter be more than 5mm and the white flint clay bone of the aluminium 45 less than or equal to 8mm
Material composition.
Above-mentioned cremator a heatable brick bed face castable, particle diameter is more than 0 and the white flint clay aggregate of the aluminium 45 less than or equal to 1mm is 3.5-
5 weight portions, particle diameter are that 4-6.3 weight portions, particle diameter are more than 3mm more than 1mm and the white flint clay aggregate of the aluminium 45 less than or equal to 3mm
And the white flint clay aggregate of aluminium 45 less than or equal to 5mm is that 4-6.3 weight portions and particle diameter are more than 5mm and less than or equal to 8mm
The white flint clay aggregate of aluminium 45 be 2.5-4.4 weight portions.
Above-mentioned cremator a heatable brick bed face castable, the white flint clay micro mist of aluminium 45 is 2-3.2 weight portions, angstrom willing 95U silicon ashes are 2.5-
3.5 weight portions, alumina powder are 5.5-9 weight portions, Suzhou white clay is 1.5-2.7 weight portions, electric smelting M70 does not carry out fine powder and is
12-19 weight portions, the aquamaine stone flour of aluminium 60 are 2.5-3.5 weight portions, triumphant Northey match 71 cement of card are 2-3.2 weight portions, additional
2520 steel fibres are 2-3.2 weight portions, explosion-proof fiber is 0.1-0.2 weight portions, BASF 2651F is 0.15-0.25 weight
Part and the bright icepro P803 of Germany are 0.1-0.2 weight portions.
Above-mentioned cremator a heatable brick bed face castable, the granularity of the white flint clay micro mist of aluminium 45 is 8-11 μm, the granularity of angstrom willing 95U silicon ashes
For the granularity of 0.5-1.5 μm, alumina powder be 0.8-1.2 μm, the granularity of Suzhou white clay be 240 mesh, electric smelting M70 do not carry out fine powder
Granularity be 325 mesh, the aquamaine stone flour of aluminium 60 granularity for 60-120 mesh, triumphant Northey match card 71 cement for 1 kilogram is more than or equal to
600 square metres, additional 2520 length of steel fiber be 20-30mm, explosion-proof fiber length be 5-15mm.
Beneficial effects of the present invention are as follows：
Cremator a heatable brick bed face castable of the present invention, is matched somebody with somebody and raw material dosage by preferred feedstock combination, adjustment feed particles level,
With on cremator chassis, prefabricated 2200-2100mm long, width 780-680mm, the resistance to heated kang face of thickness 120-150mm, resistance to chilling urgency
Hot and resistance to human body produces liquid corrosion and fuel-firing gas-firing corrosion, long service life during cremating.
Specific embodiment
Embodiment 1
The present embodiment cremator a heatable brick bed face castable, is made up of the following raw material：Electric smelting M70 mullite aggregates, the Bai Jiaobao of aluminium 45
The white flint clay micro mist of stone aggregate, aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, aluminium 60
Aquamaine stone flour, 71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro
P803。
Electric smelting M70 mullite aggregate, grain of the electric smelting M70 mullite aggregates by particle diameter more than 0 and less than or equal to 1mm
Footpath is more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm, particle diameter are more than 3mm and the electric smelting less than or equal to 5mm
The electric smelting M70 mullite aggregates composition of M70 mullite aggregates and particle diameter more than 5mm and less than or equal to 8mm.Particle diameter is more than 0
And the electric smelting M70 mullite aggregates less than or equal to 1mm be 9 kilograms, particle diameter be more than 1mm and the electric smelting M70 less than or equal to 3mm
Mullite aggregate is 10 kilograms, particle diameter is more than 3mm and the electric smelting M70 mullite aggregates less than or equal to 5mm are 10 kilograms, particle diameter
Electric smelting M70 mullite aggregates more than 5mm and less than or equal to 8mm are 17 kilograms.
Aluminium 45 white flint clay aggregate, particle diameter of the white flint clay aggregate of the aluminium 45 by particle diameter more than 0 and less than or equal to 1mm
The white flint clay aggregate of aluminium 45, particle diameter more than 1mm and less than or equal to 3mm is more than 3mm and white Jiao of the aluminium 45 less than or equal to 5mm
Jewel aggregate and particle diameter are more than 5mm and the white flint clay aggregate composition of the aluminium 45 less than or equal to 8mm.Particle diameter is more than 0 and is less than
Or the white flint clay aggregate of aluminium 45 equal to 1mm be 4 kilograms, particle diameter be more than 1mm and the white flint clay bone of the aluminium 45 less than or equal to 3mm
Expect for 5 kilograms, aluminium 45 white flint clay aggregate of the particle diameter more than 3mm and less than or equal to 5mm are that 5 kilograms and particle diameter are more than 5mm
And the white flint clay aggregate of aluminium 45 less than or equal to 8mm is 3 kilograms.
The white flint clay micro mist of aluminium 45 be the willing 95U silicon ashes of 2.3 kilogram, angstroms be 3 kilograms, alumina powder be 7 kilograms, Suzhou it is white
Mud be 2 kilograms, electric smelting M70 do not come fine powder for 14 kilograms, the aquamaine stone flour of aluminium 60 be 3 kilograms, triumphant Northey match card 71 cement be 2.3 thousand
Gram, additional 2520 steel fibre be 3 kilograms, explosion-proof fiber be 0.1 kilogram, BASF 2651F be 0.2 kilogram and German bright icepro
P803 is 0.1 kilogram.The granularity of the white flint clay micro mist of aluminium 45 is that the granularity of the willing 95U silicon ashes of 8 μm, angstroms is 1 μm, alumina powder
Granularity is 1 μm, the granularity of Suzhou white clay is that the granularity that 240 mesh, electric smelting M70 do not carry out fine powder is 325 mesh, the grain of the aquamaine stone flour of aluminium 60
Spend and be more than or equal to 600 square metres, additional 2520 steel fibre for 60-120 mesh, triumphant Northey match 71 cement specific surface areas of card are 1 kilogram
Dimension length is 25mm, the length of explosion-proof fiber is 10mm.
Embodiment 2
The present embodiment cremator a heatable brick bed face castable, is made up of the following raw material：Electric smelting M70 mullite aggregates, the Bai Jiaobao of aluminium 45
The white flint clay micro mist of stone aggregate, aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, aluminium 60
Aquamaine stone flour, 71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro
P803。
Electric smelting M70 mullite aggregate, grain of the electric smelting M70 mullite aggregates by particle diameter more than 0 and less than or equal to 1mm
Footpath is more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm, particle diameter are more than 3mm and the electric smelting less than or equal to 5mm
The electric smelting M70 mullite aggregates composition of M70 mullite aggregates and particle diameter more than 5mm and less than or equal to 8mm.Particle diameter is more than 0
And the electric smelting M70 mullite aggregates less than or equal to 1mm be 8 kilograms, particle diameter be more than 1mm and the electric smelting M70 less than or equal to 3mm
Mullite aggregate is 8 kilograms, electric smelting M70 mullite aggregate of the particle diameter more than 3mm and less than or equal to 5mm is 8 kilograms, particle diameter is big
Electric smelting M70 mullite aggregates in 5mm and less than or equal to 8mm are 16 kilograms.
Aluminium 45 white flint clay aggregate, particle diameter of the white flint clay aggregate of the aluminium 45 by particle diameter more than 0 and less than or equal to 1mm
The white flint clay aggregate of aluminium 45, particle diameter more than 1mm and less than or equal to 3mm is more than 3mm and white Jiao of the aluminium 45 less than or equal to 5mm
Jewel aggregate and particle diameter are more than 5mm and the white flint clay aggregate composition of the aluminium 45 less than or equal to 8mm.Particle diameter is more than 0 and is less than
Or the white flint clay aggregate of aluminium 45 equal to 1mm be 3.5 kilograms, particle diameter be more than 1mm and the white flint clay of aluminium 45 less than or equal to 3mm
Aggregate is 4 kilograms, particle diameter is more than 3mm and the white flint clay aggregate of the aluminium 45 less than or equal to 5mm is that 4 kilograms and particle diameter are more than
5mm and the white flint clay aggregate of the aluminium less than or equal to 8mm 45 are 2.5 kilograms.
The white flint clay micro mist of aluminium 45 is the willing 95U silicon ashes of 2 kilogram, angstroms for 2.5 kilograms, alumina powder are 5.5 kilograms, Suzhou
White clay is 1.5 kilograms, electric smelting M70 does not carry out fine powder for 12 kilograms, the aquamaine stone flour of aluminium 60 are 2.5 kilograms, triumphant Northey match 71 cement of card
For 2 kilograms, additional 2520 steel fibre be 2 kilograms, explosion-proof fiber be 0.1 kilogram, BASF 2651F be 0.15 kilogram and Germany
Bright icepro P803 is 0.1 kilogram.The granularity of the white flint clay micro mist of aluminium 45 is that the granularity of the willing 95U silicon ashes of 9 μm, angstroms is 0.5 μm, aluminum oxide
The granularity of micro mist is 0.5 μm, the granularity of Suzhou white clay is that the granularity that 240 mesh, electric smelting M70 do not carry out fine powder is 325 mesh, the aquamaine of aluminium 60
The granularity of stone flour be 60-120 mesh, triumphant Northey match card 71 cement specific surface areas be 1 kilogram more than or equal to 600 square metres, it is additional
2520 length of steel fiber are 20mm, the length of explosion-proof fiber is 5mm.
Embodiment 3
The present embodiment cremator a heatable brick bed face castable, is made up of the following raw material：Electric smelting M70 mullite aggregates, the Bai Jiaobao of aluminium 45
The white flint clay micro mist of stone aggregate, aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, aluminium 60
Aquamaine stone flour, 71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro
P803。
Electric smelting M70 mullite aggregate, grain of the electric smelting M70 mullite aggregates by particle diameter more than 0 and less than or equal to 1mm
Footpath is more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm, particle diameter are more than 3mm and the electric smelting less than or equal to 5mm
The electric smelting M70 mullite aggregates composition of M70 mullite aggregates and particle diameter more than 5mm and less than or equal to 8mm.Particle diameter is more than 0
And the electric smelting M70 mullite aggregates less than or equal to 1mm be 12 kilograms, particle diameter be more than 1mm and the electric smelting less than or equal to 3mm
M70 mullite aggregates are 13 kilograms, electric smelting M70 mullite aggregate of the particle diameter more than 3mm and less than or equal to 5mm is 13 kilograms,
Electric smelting M70 mullite aggregate of the particle diameter more than 5mm and less than or equal to 8mm is 22 kilograms.
Aluminium 45 white flint clay aggregate, particle diameter of the white flint clay aggregate of the aluminium 45 by particle diameter more than 0 and less than or equal to 1mm
The white flint clay aggregate of aluminium 45, particle diameter more than 1mm and less than or equal to 3mm is more than 3mm and white Jiao of the aluminium 45 less than or equal to 5mm
Jewel aggregate and particle diameter are more than 5mm and the white flint clay aggregate composition of the aluminium 45 less than or equal to 8mm.Particle diameter is more than 0 and is less than
Or the white flint clay aggregate of aluminium 45 equal to 1mm be 5 kilograms, particle diameter be more than 1mm and the white flint clay bone of the aluminium 45 less than or equal to 3mm
Expect for 6.3 kilograms, particle diameter is more than 3mm and the white flint clay aggregate of aluminium 45 less than or equal to 5mm is that 6.3 kilograms and particle diameter are big
The white flint clay aggregate of aluminium 45 in 5mm and less than or equal to 8mm is 4.4 kilograms.
The white flint clay micro mist of aluminium 45 is the willing 95U silicon ashes of 3.2 kilogram, angstroms for 3.5 kilograms, alumina powder are 9 kilograms, Suzhou
White clay is 2.7 kilograms, electric smelting M70 does not carry out fine powder for 19 kilograms, the aquamaine stone flour of aluminium 60 are 3.5 kilograms, triumphant Northey match 71 cement of card
For 3.2 kilograms, additional 2520 steel fibre be 3.2 kilograms, explosion-proof fiber be 0.2 kilogram, BASF 2651F be 0.25 kilogram and
The bright icepro P803 of Germany is 0.2 kilogram.The granularity of the white flint clay micro mist of aluminium 45 be the willing 95U silicon ashes of 10 μm, angstroms granularity for 1.5 μm,
The granularity of alumina powder is 1.5 μm, the granularity of Suzhou white clay is that the granularity that 240 mesh, electric smelting M70 do not carry out fine powder is 325 mesh, aluminium
The granularity of 60 aquamaine stone flours is 60-120 mesh, triumphant Northey match 71 cement specific surface areas of card for 1 kilogram is more than or equal to 600 squares
Rice, additional 2520 length of steel fiber are 30mm, the length of explosion-proof fiber is 15mm.
Embodiment 4
The present embodiment cremator a heatable brick bed face castable, is made up of the following raw material：Electric smelting M70 mullite aggregates, the Bai Jiaobao of aluminium 45
The white flint clay micro mist of stone aggregate, aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, aluminium 60
Aquamaine stone flour, 71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro
P803。
Electric smelting M70 mullite aggregate, grain of the electric smelting M70 mullite aggregates by particle diameter more than 0 and less than or equal to 1mm
Footpath is more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm, particle diameter are more than 3mm and the electric smelting less than or equal to 5mm
The electric smelting M70 mullite aggregates composition of M70 mullite aggregates and particle diameter more than 5mm and less than or equal to 8mm.Particle diameter is more than 0
And the electric smelting M70 mullite aggregates less than or equal to 1mm be 11 kilograms, particle diameter be more than 1mm and the electric smelting less than or equal to 3mm
M70 mullite aggregates are 9 kilograms, particle diameter is more than 3mm and the electric smelting M70 mullite aggregates less than or equal to 5mm are 8 kilogram,
Electric smelting M70 mullite aggregate of the footpath more than 5mm and less than or equal to 8mm is 19 kilograms.
Aluminium 45 white flint clay aggregate, particle diameter of the white flint clay aggregate of the aluminium 45 by particle diameter more than 0 and less than or equal to 1mm
The white flint clay aggregate of aluminium 45, particle diameter more than 1mm and less than or equal to 3mm is more than 3mm and white Jiao of the aluminium 45 less than or equal to 5mm
Jewel aggregate and particle diameter are more than 5mm and the white flint clay aggregate composition of the aluminium 45 less than or equal to 8mm.Particle diameter is more than 0 and is less than
Or the white flint clay aggregate of aluminium 45 equal to 1mm be 4.5 kilograms, particle diameter be more than 1mm and the white flint clay of aluminium 45 less than or equal to 3mm
Aggregate is 5.5 kilograms, particle diameter is more than 3mm and the white flint clay aggregate of the aluminium 45 less than or equal to 5mm is 4.5 kilograms and particle diameter
The white flint clay aggregate of aluminium 45 more than 5mm and less than or equal to 8mm is 2.5 kilograms.
The white flint clay micro mist of aluminium 45 be the willing 95U silicon ashes of 3 kilogram, angstroms be 2.5 kilograms, alumina powder be 8 kilograms, Suzhou it is white
Mud be 2.5 kilograms, electric smelting M70 do not come fine powder for 12 kilograms, the aquamaine stone flour of aluminium 60 be 2.5 kilograms, triumphant Northey match card 71 cement be 3
Kilogram, additional 2520 steel fibre be 2 kilograms, explosion-proof fiber be 0.15 kilogram, BASF 2651F be 0.15 kilogram and Germany it is bright
It is 0.2 kilogram to insult P803.The granularity of the white flint clay micro mist of aluminium 45 is that the granularity of the willing 95U silicon ashes of 11 μm, angstroms is 1.5 μm, aluminum oxide
The granularity of micro mist is 1.5 μm, the granularity of Suzhou white clay is that the granularity that 240 mesh, electric smelting M70 do not carry out fine powder is 325 mesh, the aquamaine of aluminium 60
The granularity of stone flour be 60-120 mesh, triumphant Northey match card 71 cement specific surface areas be 1 kilogram more than or equal to 600 square metres, it is additional
2520 length of steel fiber are 25mm, the length of explosion-proof fiber is 12mm.
Cremator a heatable brick bed face is respectively prepared using the cremator a heatable brick bed face castable of embodiment 1- embodiments 4, according to GB/T
7322-2007 tests refractoriness, according to GB/T 5072-2008 test cold crushing strengths, is surveyed according to GB/T 30873-2014
Examination thermal shock resistance.Test result is as follows：
Cremator a heatable brick bed face is respectively prepared using the cremator a heatable brick bed face castable of embodiment 1- embodiments 4, then in certain funeral
Shop carries out experimental test.Being respectively prepared cremator a heatable brick bed face using the cremator a heatable brick bed face castable of embodiment 1 continuously can use 1 year
Cremate corpse 2880 times altogether, being respectively prepared cremator a heatable brick bed face using the cremator a heatable brick bed face castable of embodiment 2 can continuously make
Amounted to cremate corpse 1920 times with 8 months, being respectively prepared cremator a heatable brick bed face using the cremator a heatable brick bed face castable of embodiment 3 can be with
Continuous to amount to cremate corpse 2160 times using 9, being respectively prepared cremator a heatable brick bed face using the cremator a heatable brick bed face castable of embodiment 4 can
Amounted to cremate corpse 2400 times using 10 months with continuous.
Obviously, the above embodiment of the present invention is only intended to clearly illustrate example of the present invention, and is not right
The restriction of embodiments of the present invention, for those of ordinary skill in the field, may be used also on the basis of the above description
To make other changes in different forms, all of implementation method cannot be exhaustive here, it is every to belong to this hair
Obvious change that bright technical scheme is extended out changes row still in protection scope of the present invention.
Claims (9)
1. cremator a heatable brick bed face castable, it is characterised in that be made up of the following raw material：Electric smelting M70 mullite aggregates, the Bai Jiaobao of aluminium 45
The white flint clay micro mist of stone aggregate, aluminium 45, angstrom willing 95U silicon ashes, alumina powder, Suzhou white clay, electric smelting M70 do not come fine powder, aluminium 60
Aquamaine stone flour, 71 cement of triumphant Northey match card, additional 2520 steel fibre, explosion-proof fiber, BASF 2651F and German bright icepro
P803。
2. cremator a heatable brick bed face castable according to claim 1, it is characterised in that the electric smelting M70 mullite aggregates are
40-60 weight portions.
3. cremator a heatable brick bed face castable according to claim 2, it is characterised in that the electric smelting M70 mullite aggregates by
Particle diameter is more than 0 and the electric smelting M70 mullite aggregates less than or equal to 1mm, particle diameter are more than 1mm and the electric smelting less than or equal to 3mm
M70 mullite aggregates, particle diameter more than 3mm and electric smelting M70 mullite aggregates and particle diameter less than or equal to 5mm more than 5mm and
Electric smelting M70 mullite aggregates composition less than or equal to 8mm.
4. cremator a heatable brick bed face castable according to claim 3, it is characterised in that particle diameter is more than 0 and less than or equal to 1mm
Electric smelting M70 mullite aggregates for 8-12 weight portions, particle diameter be more than 1mm and the electric smelting M70 mullite aggregates less than or equal to 3mm
For 8-13 weight portions, particle diameter be 8-13 weight portions more than 3mm and electric smelting M70 mullite aggregates less than or equal to 5mm, particle diameter it is big
Electric smelting M70 mullite aggregates in 5mm and less than or equal to 8mm are 16-22 weight portions.
5. cremator a heatable brick bed face castable according to claim 1, it is characterised in that the white flint clay aggregate of the aluminium 45 is
14-22 weight portions.
6. cremator a heatable brick bed face castable according to claim 5, it is characterised in that the white flint clay aggregate of the aluminium 45 is by grain
Footpath is more than 0 and the white flint clay aggregate of the aluminium 45 less than or equal to 1mm, particle diameter are more than 1mm and the aluminium 45 less than or equal to 3mm is white burnt
Jewel aggregate, particle diameter more than 3mm and the white flint clay aggregate of the aluminium 45 less than or equal to 5mm and particle diameter more than 5mm and less than or
The white flint clay aggregate composition of aluminium 45 equal to 8mm.
7. cremator a heatable brick bed face castable according to claim 6, it is characterised in that particle diameter is more than 0 and less than or equal to 1mm
The white flint clay aggregate of aluminium 45 for 3.5-5 weight portions, particle diameter be more than 1mm and the white flint clay aggregate of the aluminium 45 less than or equal to 3mm
For 4-6.3 weight portions, particle diameter more than 3mm and the white flint clay aggregate of aluminium 45 less than or equal to 5mm for 4-6.3 weight portions and
Particle diameter is more than 5mm and the white flint clay aggregate of the aluminium 45 less than or equal to 8mm is 2.5-4.4 weight portions.
8. cremator a heatable brick bed face castable according to claim 1, it is characterised in that the white flint clay micro mist of aluminium 45 is 2-3.2
Weight portion, angstrom willing 95U silicon ashes are 2.5-3.5 weight portions, alumina powder is 5.5-9 weight portions, Suzhou white clay is 1.5-2.7 weights
Amount part, electric smelting M70 do not carry out fine powder for 12-19 weight portions, the aquamaine stone flour of aluminium 60 are 2.5-3.5 weight portions, triumphant Northey match Ka71Shui
Mud is 2-3.2 weight portions, additional 2520 steel fibre is 2-3.2 weight portions, explosion-proof fiber is 0.1-0.2 weight portions, BASF
2651F is that 0.15-0.25 weight portions icepro P803 bright with Germany is 0.1-0.2 weight portions.
9. cremator a heatable brick bed face castable according to claim 8, it is characterised in that the granularity of the white flint clay micro mist of aluminium 45 is
8-10 μm, the granularity of angstrom willing 95U silicon ashes be 0.5-1.5 μm, the granularity of alumina powder be 0.8-1.2 μm, the grain of Suzhou white clay
Spend for the granularity that 240 mesh, electric smelting M70 do not carry out fine powder be 325 mesh, the aquamaine stone flour of aluminium 60 granularity be 60-120 mesh, Kai Nuosisai
Block 71 cement to be 1 kilogram is 20-30mm, the length of explosion-proof fiber more than or equal to 600 square metres, additional 2520 length of steel fiber
It is 5-15mm to spend.