CN106747250A - A kind of diatom ooze inner wall decoration wall material - Google Patents

A kind of diatom ooze inner wall decoration wall material Download PDF

Info

Publication number
CN106747250A
CN106747250A CN201611055355.6A CN201611055355A CN106747250A CN 106747250 A CN106747250 A CN 106747250A CN 201611055355 A CN201611055355 A CN 201611055355A CN 106747250 A CN106747250 A CN 106747250A
Authority
CN
China
Prior art keywords
parts
diatom ooze
dihydrogen phosphate
wall material
calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611055355.6A
Other languages
Chinese (zh)
Inventor
汪漭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Yu Jin Ecological Wood Materials Co Ltd
Original Assignee
Anhui Yu Jin Ecological Wood Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Yu Jin Ecological Wood Materials Co Ltd filed Critical Anhui Yu Jin Ecological Wood Materials Co Ltd
Priority to CN201611055355.6A priority Critical patent/CN106747250A/en
Publication of CN106747250A publication Critical patent/CN106747250A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：40 55 parts of diatom ooze, 24 parts of polyethylene glycol, 24 parts of acrylic resin, 23 parts of dimethyl sulfoxide (DMSO), 12 parts of sodium monofluorophosphate, 12 parts of dimethylethanolamine, 12 parts of expanded vermiculite, 0.8 1.2 parts of Tuo Malin, 10 15 parts of calcium carbonate, 57 parts of aluminium dihydrogen phosphate, 12 parts of pyrrolidones hydroxy acid sodium, 0.8 1.2 parts of ammonium dihydrogen phosphate, heptan 2.3 4.5 parts of 2 alkene, 2 methyl alcohol, 46 parts of strontium carbonate, 5 10 parts of europium oxide, 28 parts of dysprosia, 37 parts of methyl styrene, 0.1 0.3 parts of hexafluoroacetylacetone calcium, 1.5 3 parts of lithium magnesium silicate, 12 parts of phenthazine, 12 parts of benzotriazole, 2 0.1 0.9 parts of imidazolidinones.The present invention has that color is various, pattern abundant, safety and environmental protection the features such as outside, but also can be with various pollutants such as the peculiar smell in adsorption-decomposition function air, formaldehyde, with functions such as damping, ventilative, mould proof deodorant, purify air fire protection flame retardings, and there is excellent purifying formaldehyde rate and purifying formaldehyde effect persistence.

Description

A kind of diatom ooze inner wall decoration wall material
Technical field
The present invention relates to a kind of construction material, specially a kind of diatom ooze inner wall decoration wall material.
Background technology
Diatom ooze has been widely used at present as a kind of new environment friendly inorganic interior decoration wall material, diatomite therein Itself has porous, and the Main Function in coating is to adsorb and adjust humidity, and as nano titanium oxide and anion The carrier of powder, diatom is adsorbed onto by the porous of diatom ooze by free formaldehyde present in room air and other pernicious gases In mash layer, harmless carbon dioxide and water is broken down into by the decomposition of nano titanium oxide and negative ion powder, from And the purpose and moisture absorption and desorption property for reaching purify air have effect well to regulation indoor air humidity.But in coastal area and The southern excessive easy generation mould of the long-term humidity of plum rain season air grows, and diatom ooze metope become mildewed, changed colour, and powder loosens de- Fall, so as to limit the use scope of diatom ooze.
Wall material refers to relevant wall plastering construction, the class material processed common mortar surface.With now Environmental ecology is presented unstability, and many problem of environmental pollutions and environmental pollution form emerge in an endless stream, and people couple cease with itself The requirement of the indoor wall decoration that manner of breathing is closed also increasingly is increased, and indoor wall decoration is increasingly becoming the opera involving much singing and action of house fitting-up, city Popular various indoor wall decoration wall materials on field.At present, the representative wall surface decoration wall material of in the market has breast Shellac varnish, wallpaper, ceramic tile etc., also band a little harm while these decoration wall materials bring numerous selections, though emulsion paint than It is more environmentally friendly, but just apply the harmful substance that some volatiles are unavoidably had when on the wall；Though wallpaper color is various, pattern is rich Richness, paving not environmentally, fire protection flame retarding it is poor, though ceramic tile is easy to clean, but can aggravate the load to wall, it is easy to fall off.Therefore, one Novel environment friendly wall material --- diatom ooze wall material came into vogue kind in recent years, and diatom ooze wall material main raw material(s) is natural diatomaceous earth, With functions such as elimination formaldehyde, purify air, fire protection flame retardings, but the most of diatom ooze wall material of in the market has elimination The efficiency of formaldehyde is low, the problem of purifying formaldehyde effect persistence difference, causes effectively to purify the air of a room, and product quality is not Consumer demand can be met.
The content of the invention
It is an object of the invention to provide a kind of diatom ooze inner wall decoration wall material.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：Diatom ooze 40-55 parts, poly- second Glycol 2-4 parts, acrylic resin 2-4 parts, dimethyl sulfoxide (DMSO) 2-3 parts, sodium monofluorophosphate 1-2 parts, dimethylethanolamine 1-2 parts, Expanded vermiculite 1-2 parts, Tuo Malin 0.8-1.2 parts, calcium carbonate 10-15 parts, aluminium dihydrogen phosphate 5-7 parts, pyrrolidones hydroxy acid sodium 1-2 Part, ammonium dihydrogen phosphate 0.8-1.2 part, 2.3-4.5 parts of hept-2-ene" -2- methyl alcohol, strontium carbonate 4-6 parts, europium oxide 5-10 parts, aoxidize Dysprosium 2-8 parts, methyl styrene 3-7 parts, 0.1-0.3 parts of hexafluoroacetylacetone calcium, lithium magnesium silicate 1.5-3 parts, phenthazine 1-2 parts, Benzotriazole 1-2 parts, 0.1-0.9 parts of 2- imidazolidinones.
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：40 parts of diatom ooze, poly- second 4 parts of glycol, 2 parts of acrylic resin, 2 parts of dimethyl sulfoxide (DMSO), 2 parts of sodium monofluorophosphate, 1 part of dimethylethanolamine, expanded vermiculite 1 Part, 1.2 parts of Tuo Malin, 10 parts of calcium carbonate, 7 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 0.8 part of ammonium dihydrogen phosphate, hept- 4.5 parts of 2- alkene -2- methyl alcohol, 4 parts of strontium carbonate, 10 parts of europium oxide, 2 parts of dysprosia, 7 parts of methyl styrene, hexafluoroacetylacetone calcium 0.1 part, 1.5 parts of lithium magnesium silicate, 1 part of phenthazine, 2 parts of benzotriazole, 0.1 part of 2- imidazolidinones.
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：50 parts of diatom ooze, poly- second 3 parts of glycol, 3 parts of acrylic resin, 3 parts of dimethyl sulfoxide (DMSO), 1 part of sodium monofluorophosphate, 1 part of dimethylethanolamine, expanded vermiculite 1 Part, 1 part of Tuo Malin, 12 parts of calcium carbonate, 6 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 1 part of ammonium dihydrogen phosphate, hept- 2- 3 parts of alkene -2- methyl alcohol, 5 parts of strontium carbonate, 8 parts of europium oxide, 6 parts of dysprosia, 4 parts of methyl styrene, 0.2 part of hexafluoroacetylacetone calcium, 2 parts of lithium magnesium silicate, 2 parts of phenthazine, 2 parts of benzotriazole, 0.5 part of 2- imidazolidinones.
Beneficial effects of the present invention：The present invention has that color is various, pattern abundant, safety and environmental protection the features such as outside, but also Can be with various pollutants such as the peculiar smell in adsorption-decomposition function air, formaldehyde, with damping, ventilative, mould proof deodorant, purify air fire prevention The function such as fire-retardant, and have excellent purifying formaldehyde rate and purifying formaldehyde effect persistence.
Specific embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：40 parts of diatom ooze, polyethylene glycol 2 parts, 2 parts of acrylic resin, 2 parts of dimethyl sulfoxide (DMSO), 1 part of sodium monofluorophosphate, 1 part of dimethylethanolamine, 1 part of expanded vermiculite, support 0.8 part of horse beautiful jade, 10 parts of calcium carbonate, 5 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 0.8 part of ammonium dihydrogen phosphate, hept-2-ene"- 2.3 parts of 2- methyl alcohol, 4 parts of strontium carbonate, 5 parts of europium oxide, 2 parts of dysprosia, 3 parts of methyl styrene, 0.1 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 1 part of phenthazine, 1 part of benzotriazole, 0.1 part of 2- imidazolidinones.
Embodiment 2
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：40 parts of diatom ooze, polyethylene glycol 4 parts, 2 parts of acrylic resin, 2 parts of dimethyl sulfoxide (DMSO), 2 parts of sodium monofluorophosphate, 1 part of dimethylethanolamine, 1 part of expanded vermiculite, support 1.2 parts of horse beautiful jade, 10 parts of calcium carbonate, 7 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 0.8 part of ammonium dihydrogen phosphate, hept-2-ene"- 4.5 parts of 2- methyl alcohol, 4 parts of strontium carbonate, 10 parts of europium oxide, 2 parts of dysprosia, 7 parts of methyl styrene, 0.1 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 1 part of phenthazine, 2 parts of benzotriazole, 0.1 part of 2- imidazolidinones.
Embodiment 3
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：50 parts of diatom ooze, polyethylene glycol 3 parts, 3 parts of acrylic resin, 3 parts of dimethyl sulfoxide (DMSO), 1 part of sodium monofluorophosphate, 1 part of dimethylethanolamine, 1 part of expanded vermiculite, support 1 part of horse beautiful jade, 12 parts of calcium carbonate, 6 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 1 part of ammonium dihydrogen phosphate, hept-2-ene" -2- first 3 parts of alcohol, 5 parts of strontium carbonate, 8 parts of europium oxide, 6 parts of dysprosia, 4 parts of methyl styrene, 0.2 part of hexafluoroacetylacetone calcium, magnesium silicate 2 parts of lithium, 2 parts of phenthazine, 2 parts of benzotriazole, 0.5 part of 2- imidazolidinones.
Embodiment 4
A kind of diatom ooze inner wall decoration wall material, its is composed of the following components by weight：55 parts of diatom ooze, polyethylene glycol 4 parts, 4 parts of acrylic resin, 3 parts of dimethyl sulfoxide (DMSO), 2 parts of sodium monofluorophosphate, 2 parts of dimethylethanolamine, 2 parts of expanded vermiculite, support 1.2 parts of horse beautiful jade, 15 parts of calcium carbonate, 7 parts of aluminium dihydrogen phosphate, 2 parts of pyrrolidones hydroxy acid sodium, 1.2 parts of ammonium dihydrogen phosphate, hept-2-ene"- 4.5 parts of 2- methyl alcohol, 6 parts of strontium carbonate, 10 parts of europium oxide, 8 parts of dysprosia, 7 parts of methyl styrene, 0.3 part of hexafluoroacetylacetone calcium, 3 parts of lithium magnesium silicate, 2 parts of phenthazine, 2 parts of benzotriazole, 0.9 part of 2- imidazolidinones.
Above content is only to structure example of the present invention and explanation, affiliated those skilled in the art couple Described instantiation is made various modifications or supplement or is substituted using similar mode, as long as will not past this right Scope defined in book is sought, the protection domain of invention all should be belonged to.

Claims (3)

1. a kind of diatom ooze inner wall decoration wall material, it is characterised in that its is composed of the following components by weight：Diatom ooze 40- 55 parts, polyethylene glycol 2-4 parts, acrylic resin 2-4 parts, dimethyl sulfoxide (DMSO) 2-3 parts, sodium monofluorophosphate 1-2 parts, dimethyl ethanol Amine 1-2 parts, expanded vermiculite 1-2 parts, Tuo Malin 0.8-1.2 parts, calcium carbonate 10-15 parts, aluminium dihydrogen phosphate 5-7 parts, pyrrolidones 1-2 parts of hydroxy acid sodium, ammonium dihydrogen phosphate 0.8-1.2 parts, 2.3-4.5 parts of hept-2-ene" -2- methyl alcohol, strontium carbonate 4-6 parts, europium oxide 5- 10 parts, dysprosia 2-8 parts, methyl styrene 3-7 parts, 0.1-0.3 parts of hexafluoroacetylacetone calcium, lithium magnesium silicate 1.5-3 parts, fen thiophene Piperazine 1-2 parts, benzotriazole 1-2 parts, 0.1-0.9 parts of 2- imidazolidinones.
2. a kind of diatom ooze inner wall decoration wall material according to claim 1, it is characterised in that it is by with the following group by weight It is grouped into：40 parts of diatom ooze, 4 parts of polyethylene glycol, 2 parts of acrylic resin, 2 parts of dimethyl sulfoxide (DMSO), 2 parts of sodium monofluorophosphate, diformazan 1 part of ethylethanolamine, 1 part of expanded vermiculite, 1.2 parts of Tuo Malin, 10 parts of calcium carbonate, 7 parts of aluminium dihydrogen phosphate, pyrrolidones hydroxy acid sodium 1 Part, 0.8 part of ammonium dihydrogen phosphate, 4.5 parts of hept-2-ene" -2- methyl alcohol, 4 parts of strontium carbonate, 10 parts of europium oxide, 2 parts of dysprosia, methylbenzene 7 parts of ethene, 0.1 part of hexafluoroacetylacetone calcium, 1.5 parts of lithium magnesium silicate, 1 part of phenthazine, 2 parts of benzotriazole, 2- imidazolidinones 0.1 part.
3. a kind of diatom ooze inner wall decoration wall material according to claim 1, it is characterised in that it is by with the following group by weight It is grouped into：50 parts of diatom ooze, 3 parts of polyethylene glycol, 3 parts of acrylic resin, 3 parts of dimethyl sulfoxide (DMSO), 1 part of sodium monofluorophosphate, diformazan 1 part of ethylethanolamine, 1 part of expanded vermiculite, 1 part of Tuo Malin, 12 parts of calcium carbonate, 6 parts of aluminium dihydrogen phosphate, 1 part of pyrrolidones hydroxy acid sodium, 1 part of ammonium dihydrogen phosphate, 3 parts of hept-2-ene" -2- methyl alcohol, 5 parts of strontium carbonate, 8 parts of europium oxide, 6 parts of dysprosia, 4 parts of methyl styrene, 0.2 part of hexafluoroacetylacetone calcium, 2 parts of lithium magnesium silicate, 2 parts of phenthazine, 2 parts of benzotriazole, 0.5 part of 2- imidazolidinones.
CN201611055355.6A 2016-11-25 2016-11-25 A kind of diatom ooze inner wall decoration wall material Pending CN106747250A (en)