CN106747113A - Decoration integrated Light trabses based on foam cement and preparation method thereof - Google Patents
Decoration integrated Light trabses based on foam cement and preparation method thereof Download PDFInfo
- Publication number
- CN106747113A CN106747113A CN201710018078.XA CN201710018078A CN106747113A CN 106747113 A CN106747113 A CN 106747113A CN 201710018078 A CN201710018078 A CN 201710018078A CN 106747113 A CN106747113 A CN 106747113A
- Authority
- CN
- China
- Prior art keywords
- decoration
- cement
- framed
- integrated light
- foam cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of decoration integrated Light trabses based on foam cement and preparation method thereof.Decoration integrated Light trabses be filled in by foam cement light filler decoration it is framed it is interior constitute, the material such as polyvinyl chloride of the decoration framed use one side decoration carries out structure design according to application requirement and surface treatment is made.Its preparation method is：Cement mortar is sent into the framed interior foaming of decoration, foam process and curing condition is controlled, decoration integrated Light trabses are obtained；The Light trabses of preparation use one-shot forming, are easy to factory's continuous prodution, and production efficiency is high, are capable of achieving large scale cement board and prepare；And Light trabses are easy for installation, it is not required to carry out the work such as secondary decoration, greatly improves the construction speed of building；And there is controlling density and intensity, sound-insulating and heat-insulating, protection against the tide.
Description
Technical field
The present invention relates to a kind of Light trabses, more particularly to a kind of foam cement and dalle integral light composite wall
Plate, belongs to building materials field.
Background technology
With continuing to develop for construction industry, skyscraper is increasing.It is various to mitigate building deadweight, reduce beam column
Amount of reinforcement and construction costs, improve interior and utilize area, and with the lightweight of the comprehensive function such as heat-insulated, sound insulation, water-fast, fire prevention
Heat preservation decoration integrative materials for wall is favourably welcome.
Chinese patent CN201510378527.2, CN201610215544.9, CN201020193896.7 etc. disclose base
In the heat preservation decoration integrative wallboard of foamed cement material, but operating method is cumbersome, complex process；CN201610066089.0,
CN201320009025.9 etc. discloses decoration integrated wall board of a kind of light-weight environment-friendly and preparation method thereof, full-inorganic decoration
Used as skin-material, inorganic material is carried out from foaming as sandwich of layers plate.But inorganic plate water absorption issue cannot be obtained effectively
Solution.
The materials for wall of above patent disclosure makes assembly technology complexity, is unfavorable for that building industry batch production is popularized；
Mould is single, and cement board can be applied size-constrained；And inorganic plate water absorption issue cannot be well solved, service life is not
It is high.
The content of the invention
For the defect that prior art is present, it is to provide a kind of easy to use that the purpose of the present invention is, can arbitrarily be hindered
Every with decoration function, high-strength light is indeformable, the good decoration integrated Light trabses of insulation, moistureproof, flameproof effect.
It is to provide a kind of simple to operate, low cost to prepare the decoration integrated Light trabses that the purpose of the present invention is
Method.
In order to realize above-mentioned technical purpose, the invention provides a kind of decoration integrated light weight wall based on foam cement
Plate, the wallboard is filled in that decoration is framed interior to be constituted by foam cement light filler.
Decoration integrated Light trabses of the invention are outside by decorating framed and foam cement light filler global formation
Decoration it is framed with light weight, good toughness, small deformation the characteristics of, be combined into independent wallboard with light foaming cement, can be effective
Improve cement board waterproof, cracking resistance, bending resistance, anti-folding, resistance to compression and shock resistance, extend the life-span, and there is whole wallboard
It is lightweight, high-strength, the features such as sound-insulating and heat-insulating, fire-proof and damp-proof, heat preservation environment protection.Decoration integrated Light trabses can in plant produced,
Design size, shape, overcome the shortcoming that cannot produce large scale combined wall board in the prior art on request.
Preferred scheme, the decoration is framed for the negative and positive of one side decoration are framed.Negative and positive of the invention are framed including former
Framed and formpiston is framed, and formpiston is framed for containing foam cement slurry, framed without departing from formpiston in foam cement slurry foaming height
The former that closed before height is framed.The quality that foam cement needed for being calculated using the controllable principle of foam cement density is starched, can make
Cement mortar be just fully filled with it is whole framed.The framed stereochemical structure that can be designed to arbitrary dimension of decoration.More preferably it is length
Cube structure.Its size such as conventional 300mm × 300mm × 90mm, 600mm × 300mm × 90mm, 600mm × 600mm ×
90mm, 800mm × 800mm × 90mm, 450mm × 300mm × 90mm etc., it is also possible to bigger by particular design requirement design size
Dalle it is framed.The framed one side of decoration is carved with decorative pattern.As shown in figure 1, the framed one of face of decoration can
To be arbitrarily carved with beautiful decorative pattern, without being decorated in addition outside wallboard.
Preferred scheme, the framed medial surface of decoration has carried out surface hydrophilic treatment.It is roughened using the chromic acid containing chromic acid
Liquid carries out surface coarsening, matrix surface is formed pit shape micro-rough face, greatly increases surface area, is conducive to decoration framed
More close and firm is combined and foam cement light filler between.Surface hydrophilic processing procedure is carried out to decorating framed medial surface
For：Framed use chromic acid coarsening solution roughening treatment will be decorated using chemical roughening method.As the framed utilization concentration of PVC be 300~
The chromic acid coarsening solution of 500g/L processes 15~20min at a temperature of 50~70 DEG C；The framed utilization high chromic acid content coarsening solution (chromic acid of ABS
300~500g/L, 150~250g/L of sulfuric acid) roughening treatment.
More preferably scheme, the decoration is framed by least one of polyvinyl chloride, polyethylene, polypropylene, ABS material structure
Into.Can also be metal material or other inorganic material, but most preferably polyvinyl chloride, polyethylene, polypropylene, ABS etc. are organic
Material.
Preferred scheme, the foam cement light filler includes cement matrix and additive.
More preferably scheme, the cement matrix includes portland cement, magnesia cement, sulphate aluminium cement, iron aluminic acid
Salt cement or alumina cement；The additive includes at least one of polypropylene fibre, flyash, slag, wollastonite powder.
It is framed decorating present invention also offers the preparation method of the decoration integrated Light trabses based on foam cement
Cast-in-place foam cement slurry is filled in formpiston, close former, after the completion of foaming, conserved to age, obtained final product.
Preferred scheme, the foaming is mutually tied using chemical blowing process, physical blowing method or chemical blowing with physical blowing
The method of conjunction.
Preferred scheme, the foaming is mutually tied using chemical blowing process, physical blowing method or chemical blowing with physical blowing
The method of conjunction.Chemical blowing process is that, by cement and other inorganic material, additive etc., the stirring that adds water is added appropriate for slurry
Hydrogen peroxide stir after-pouring rapidly in framed, natural curing.Physical blowing method by cement and other inorganic material,
Additive is added water and stirs into homogeneous slurry, and then the foam that foaming machine is produced is stirred evenly with slurry, pour into it is framed in, it is naturally foster
Shield.The method that can also be combined using physical blowing and chemical blowing, will cement and other inorganic material, additive add water
It is slurry to stir, and then the foam that foaming machine is produced stirs with slurry, adds appropriate hydrogen peroxide and stirs rapidly
After-pouring in framed, natural curing.
Matched molds of the invention are framed to be after dalle cut into required size, with PUR by the dress of well cutting
Decoratice board is bonded, and forms open framed.It is open framed using production line die sinking manufacture if industrial production.
Compared with prior art, technical scheme has the advantages that：
1st, the decoration integrated Light trabses of foam cement proposed by the present invention are by foam cement and the framed global formation of decoration
Independent wallboard is constituted, installs simple, convenient, simplify wall preparation technology.
2nd, the decoration integrated Light trabses of foam cement proposed by the present invention can need to customize suitable dimension according to application
Decoration with structure is framed.Meanwhile, cast-in-place foam cement slurry has preferable mobility with thing figuration, it is possible to use formpiston is framed
The foam cement decorative wall panels of oversize are prepared as the foaming mould of cement board, foam cement factory is compensate for single
Deficiency on the insulation board size of mould production.
3rd, the plastics that are included in the decoration integrated Light trabses of foam cement proposed by the present invention are framed to be not susceptible to deformation
Or Material shrinkage, coat of plaster will not be caused to ftracture because shrinkage factor is different from coat of plaster contact after construction.Meanwhile, it is framed to change
Kind cement board waterproof, cracking resistance, bending resistance, anti-folding, resistance to compression and shock resistance, extend the life-span.
4th, framed integrated with foam cement in the decoration integrated Light trabses of foam cement proposed by the present invention, face is close
Degree is low, lightweight and high-strength；Internal packing material cement board is loose structure, and thermal conductivity factor is low, and sound-insulating and heat-insulating, fire prevention are anti-
Tide；Can adulterate using industrial residues, environmental protection such as flyash, slags.
5th, the decoration integrated Light trabses of foam cement proposed by the present invention make simple, easy for installation, and wallboard can be with
Various floral designs are decorated as needed, secondary decoration is saved, and are a kind of materials for wall technologies with marked improvement.
Brief description of the drawings
In order to illustrate more clearly of the present embodiment or technical scheme of the prior art, below will be to embodiment or existing skill
The accompanying drawing to be used needed for art description is briefly described.To those skilled in the art, creative work is not being paid
On the premise of, other accompanying drawings can also be obtained according to this accompanying drawing.
【Fig. 1】It is integral light wallboard of the invention；A is sectional view, and B is overall appearance figure.
Specific embodiment
The present invention is elaborated below in conjunction with the accompanying drawings, embodiment carries out reality under premised on technical solution of the present invention
Apply, give detailed implementation method and specific operating process, but protection scope of the present invention is not limited only to following embodiments.
Embodiment 1
(1) PVC board is cut into 2 pieces of 300mm × 300mm, 4 pieces of 300mm × 50mm, 4 pieces of rectangular slabs of 300mm × 40mm
Block, open cuboid formpiston is framed and a former is framed to become one with melt viscosity, and framed medial surface does hydrophilic treated, i.e.,
PVC board inner side is first wiped with hexamethylene carries out pre- roughening, then puts it into roughening in 60 DEG C of chromic acid coarsening solution (chromic acid 400g/L)
20min。
(2) by 100 parts of P.O.42.5 cement, 0.5 portion of PP chopped strands, 2 portions of glauber salt, 1.5 portions of foam stabilizers with 50 part 45
DEG C hot water stirs 3min after, be rapidly added 5.5 parts of hydrogen peroxide, and pour into simultaneously framed after high-speed stirred 8s, then close collection
Former into decoration aspect is framed, and a weight can be added a cover to prevent foam cement from starching spilling.After the completion of to be foamed room temperature conserve to
Age.
After testing, filling heat preservation decoration integrative partition plate surface density 59Kg/m2, compression strength 3.6MPa, moisture content
8%.
Embodiment 2
(1) PVC board is cut into 2 pieces of 300mm × 300mm, 4 pieces of 300mm × 50mm, 4 pieces of rectangular slabs of 300mm × 40mm
Block, open cuboid formpiston is framed and a former is framed to become one with melt viscosity, and framed medial surface does hydrophilic treated, i.e.,
PVC board inner side is first wiped with hexamethylene carries out pre- roughening, then puts it into roughening in 60 DEG C of chromic acid coarsening solution (chromic acid 400g/L)
20min。
(2) by 100 parts of P.O.42.5 cement, 0.5 portion of PP chopped strands, 2 portions of glauber salt, 1.5 portions of foam stabilizers with 50 part 40
DEG C hot water stirs 3min after, be rapidly added 4.8 parts of hydrogen peroxide, and pour into simultaneously framed after high-speed stirred 8s, then close collection
Former into decoration aspect is framed, and a weight can be added a cover to prevent foam cement from starching spilling, and then room temperature was conserved to age.
After testing, partition plate surface density 78Kg/m3, compression strength 3.9MPa, moisture content 9.4%.
Embodiment 3
(1) ABS plates are cut into 2 pieces of 300mm × 300mm, 4 pieces of 300mm × 50mm, 4 pieces of rectangular slabs of 300mm × 40mm
Block, open cube formpiston is framed and a former is framed to become one with melt viscosity, and framed medial surface does hydrophilic treated, i.e.,
Put it into roughening 20min in 60 DEG C of high chromic acid content coarsening solutions (chromic acid 400g/L, sulfuric acid 200g/L).
(2) by 100 parts of P.O.42.5 cement, 0.5 portion of PP chopped strands, 2 portions of glauber salt, 1.5 portions of foam stabilizers with 50 part 45
DEG C hot water stirs 3min after, be rapidly added 5 parts of hydrogen peroxide, and pour into simultaneously framed after high-speed stirred 8s, then close integrated
The former of decoration aspect is framed, and a weight can be added a cover to prevent foam cement from starching spilling, and then room temperature was conserved to age.
After testing, partition plate surface density 67Kg/m3, compression strength 3.7MPa, moisture content 8.6%.
Claims (8)
1. a kind of decoration integrated Light trabses based on foam cement, it is characterised in that：Filled out by foam cement light filler
Fill and decorating framed interior composition.
2. decoration integrated Light trabses based on foam cement according to claim 1, it is characterised in that：The decoration
It is framed for one side decoration negative and positive it is framed.
3. decoration integrated Light trabses based on foam cement according to claim 2, it is characterised in that：The decoration
Framed medial surface has carried out surface hydrophilic treatment.
4. decoration integrated Light trabses based on foam cement according to any one of claims 1 to 3, its feature exists
In：The decoration is framed to be made up of at least one of polyvinyl chloride, polyethylene, polypropylene, ABS material.
5. decoration integrated Light trabses based on foam cement according to claim 1, it is characterised in that：The foaming
Cement light inserts includes cement matrix and additive.
6. decoration integrated Light trabses based on foam cement according to claim 5, it is characterised in that：The cement
Base material includes portland cement, magnesia cement, sulphate aluminium cement, ferrous aluminate cement or alumina cement；The additive bag
Include at least one of polypropylene fibre, flyash, slag, wollastonite powder.
7. the preparation method of the decoration integrated Light trabses based on foam cement described in any one of claim 1~6, it is special
Levy and be：Cast-in-place foam cement slurry is filled in framed formpiston is decorated, close former, after the completion of foaming, conserved to age,
Obtain final product.
8. the preparation method of the decoration integrated Light trabses based on foam cement according to claim 7, its feature exists
In：The method being combined using chemical blowing process, physical blowing method or chemical blowing and physical blowing that foams.