CN106746737A - A kind of building decoration color crystal glass and manufacture method - Google Patents
A kind of building decoration color crystal glass and manufacture method Download PDFInfo
- Publication number
- CN106746737A CN106746737A CN201710083041.5A CN201710083041A CN106746737A CN 106746737 A CN106746737 A CN 106746737A CN 201710083041 A CN201710083041 A CN 201710083041A CN 106746737 A CN106746737 A CN 106746737A
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- color crystal
- film layer
- building decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of building decoration color crystal glass; the color crystal glass is layer structure; with glass baseplate (1) as substrate; Low emissivity film layer (2) is provided with the front of glass baseplate (1); self-cleaning film layer (3) is provided with above Low emissivity film layer (2); colored glaze patterned layer (4) is provided with the back side of glass baseplate (1); color crystal coating (5) is provided with colored glaze patterned layer (4), protection layer (6) is provided with color crystal coating (5).The product possesses self-cleaning film layer；Can be self-cleaning as newly by natural rain drop erosion, reduce artificial cleaning cost and safety coefficient.Low emissivity film layer；Reduce the irradiation of sunlight middle-ultraviolet lamp; effectively protect indoor furniture aging life-span; plus back side coloured silk crystal coating; the colour crystal effect of highlighted sudden strain of a muscle can be realized in glass surface; reach preferable colour building decoration effect; it is truly realized and gives architectural design expert and application person bigger decoration space, while also makes up the market vacancy.
Description
Technical field
The present invention relates to a kind of building decoration color crystal glass and its manufacture method, belong to the technology neck of construction material manufacture
Domain.
Background technology
The need for modern development, building and ornament materials constantly develop to high-tech multifunctional direction.Ambetti and
The application of building decoration ambetti is more and more extensive, because the finely processed product of glass has more various colors and various functions
Realization, such as color crystalline substance, self-cleaning, control light, regulation temperature, reduce dry sound and improve the art of architecture and decorate.So glass
No longer it has been single transparent isolation daylighting effect, has been a kind of structural material and decoration functions section bar material of modern architecture.Glass
Glass plays an important role in the different field of the modern life.
People are to the various functions and appearance requirement of ambetti also more and more higher simultaneously.Not requiring nothing more than product has function
Type and require the beautiful air attractive in appearance of decorative appearance color.Existing architectural decorative glass typically only possesses single function and makees
With such as plated film, self-cleaning, Low emissivity, colour, light modulation.There are two big shortcomings in this ambetti：
1st, various functions and the various colored decorative effects with one of outward appearance can not be provided simultaneously with.
2nd, the long-term color under sunlight irradiation of the colored glaze of some pot-metal glasses forms weather stain, xanthochromia, even takes off
Fall.
The content of the invention
Technical problem：The object of the invention is directed to the Mobyneb building dress that above-mentioned 2 problems provide a kind of new structure
Decorations color crystal glass, while also disclosing the manufacture method of the decoration color crystal glass.
Technical scheme：The present invention is a kind of Mobyneb building decoration color crystal glass, and the color crystal glass is layer structure, with
Glass baseplate is substrate, and Low emissivity film layer is provided with the front of glass baseplate, and self-cleaning film is provided with above Low emissivity film layer
Layer, colored glaze patterned layer is provided with the back side of glass baseplate, color crystal coating is provided with colored glaze patterned layer, on color crystal coating
It is provided with protection layer.
The glass baseplate is the safety glass of 3-12mm.
The Low emissivity film layer is one or more layers metal-oxide film.Metal-oxide film can be argent system
Metal-oxide film.
The number of plies of the Low emissivity film layer is layer 2-3.
The self-cleaning film layer is Ti02The photocatalysis film that particle is constituted.
The color crystal coating is chromatic metallic epoxy coating.(epoxy resin solution adds the painting of chromatic metallic shimmering powder
Layer)
The protection layer is waterproof, anti-corrosion epoxy resin clear coat.
The preparation method of building decoration color crystal glass of the invention is comprised the following steps：
Step one, safety glass base materials,
Step 2 plates Low emissivity film layer in the safety glass base material front made, so that glass baseplate front is formed
Low emissivity film layer, to reduce the radiation of sunlight middle-ultraviolet lamp,
Step 3 carries out coating self-cleaning film layer treatment to the glass baseplate after plating low-radiation film, i.e., in low-radiation film
On layer spray one layer of self-cleaning film layer, reach can self-cleaning net effect,
Step 4 prints one layer of colored glaze patterned layer to the method for glass baseplate back side silk-screen printing,
Step 5 to covering color crystal coating with silk-screen printing in the colored glaze patterned layer at the glass baseplate back side,
Step 6 with the method for silk-screen printing on described color crystal coating to covering one layer of protection layer.
Beneficial effect：The present invention is increased at existing self-cleaning, the low emissivity glass back side using printing or spraying coating process
Transparent color hyaline layer, so as to realize polychromy with function in the building decorative color crystal glass of one.
The product possesses self-cleaning film layer；Can be self-cleaning as new by natural rain drop erosion, reduce artificial cleaning cost and
Safety coefficient.Low emissivity film layer；The irradiation of sunlight middle-ultraviolet lamp is reduced, indoor furniture aging life-span is effectively protected, the back side is added color
Crystal coating, can realize the colour crystal effect of highlighted sudden strain of a muscle in glass surface, reach preferable colour building decoration effect, really do
To giving architectural design expert and application person bigger decoration space, while also making up the market vacancy.
Brief description of the drawings
Fig. 1 is the schematic diagram of layer structure of the present invention.
Wherein have：Glass baseplate 1, Low emissivity film layer 2, self-cleaning film layer 3, colored glaze patterned layer 4, color crystal coating 5, protection are protected
Sheath 6.
Specific embodiment
Below in conjunction with the accompanying drawings and implementation steps the invention will be further described：
As shown in figure 1, the color crystalline substance ambetti of the building of the present embodiment, including glass baseplate 1, the glass baseplate 1 is
Safety glass.Low emissivity film layer 2 is plated in the front of shown glass baseplate 1, and one layer of self-cleaning film layer is covered above the Low emissivity film layer
3。
The back up colored glaze patterned layer 4 of shown glass baseplate 1, the printed color crystal coating 5 in the colored glaze patterned layer 4,
Protection layer 6 is printed on the color crystal coating 5.
The manufacture method of the present embodiment building decoration color crystal glass, comprises the following steps：
It is color that step one, is cut into slices to required glass according to drawing requirement specification, the treatment of edging, tempering obtains building decoration
The safety glass of crystal glass；
Step 2, cleaning treatment is carried out with ionized water developing machine to the glass after tempering, glass baseplate 1 is obtained, in glass
The front of base material 1 plates the metal oxide film layer of two-layer or three layers of silver system using vacuum magnetic-control sputtering method, obtains Low emissivity
Film layer 2, energy exchange inside and outside energy absorption or control room is reduced to reduce the transmitance of the ultraviolet in sunlight, effectively drop
Low color degree of aging；
Step 3, to by plating Low emissivity film layer after glass carry out spray treatment, it is with spraying coating process that self-cleaning is molten
Liquid is uniformly sprayed onto above Low emissivity film layer 2, obtains self-cleaning film layer 3, and one layer of highdensity nanometer is formed in glass outer surface
Ultra-hydrophilic transparent film, water droplet is less than 10 degree with the contact angle of nano coating, floats the dust dirt for being attached to glass surface, with
The landing of moisture film gravity self-cleaning；
Walk Zou four, corresponding 200 mesh figure line half tone made using silk-screen printing technique at the back side of glass baseplate 1, with third
Olefin(e) acid resin transparent or colored glaze ink print, and from Far-infrared tunnel type drying oven, dry within 180 degree 5-10 minutes, obtain colored glaze
Patterned layer 4, reaches required colored glaze patterned layer effect；
Step 5, the mesh half tone of silk-screen printing technique 150 is used on the coating of colored glaze patterned layer 4, it is color with acrylic resin
Brilliant ink printed color crystal coating, is dried for 5-10 minutes from Far-infrared tunnel type drying oven 180 degree, obtains color crystal coating 5, is reached
Required color crystal coating effect；
Step 6, on the coating of color crystal coating 5 use the mesh half tone of silk-screen printing technique 100, from resistance to anti-corrosion material high
Printing corrosion protective covering, is dried for 10 minutes from Far-infrared tunnel type drying oven 180 degree, corrosion protective covering 6 is obtained, so as to reach
Prevent the corrosive chameleon of acid, alkali, salt.
Above is a kind of manufacture method of building decoration color crystal glass provided by the present invention is described in detail,
Specific case used herein is set forth to structural principle of the invention and implementation method, and above example is only intended to
Help understands the method for the present invention and its core concept, allows people to will appreciate that the content of the invention is simultaneously real according to thought of the invention
Apply, it is not intended to limit the scope of the present invention.What all Spirit Essences according to main technical schemes of the present invention were done etc.
Effect conversion is modified, and should be all included within the scope of the present invention.
Claims (8)
1. a kind of building decoration color crystal glass, it is characterised in that the color crystal glass is layer structure, with glass baseplate (1) as base
Bottom, Low emissivity film layer (2) is provided with the front of glass baseplate (1), and self-cleaning film layer is provided with above Low emissivity film layer (2)
(3) colored glaze patterned layer (4), is provided with the back side of glass baseplate (1), color crystal coating (5) is provided with colored glaze patterned layer (4),
Protection layer (6) is provided with color crystal coating (5).
2. building decoration color crystal glass according to claim 1, it is characterised in that the glass baseplate (1) is 3-12mm's
Safety glass.
3. building decoration color crystal glass according to claim 1, it is characterised in that the Low emissivity film layer (2) for one layer or
Multiple layer metal sull.
4. building decoration color crystal glass according to claim 3, it is characterised in that the number of plies of the Low emissivity film layer (2) is
Layer 2-3.
5. building decoration color crystal glass according to claim 1, it is characterised in that the self-cleaning film layer (3) is Ti02
The photocatalysis film that grain is constituted.
6. building decoration color crystal glass according to claim 1, it is characterised in that the color crystal coating (5) is chromatic metallic
Epoxy coating.
7. building decoration color crystal glass according to claim 1, it is characterised in that protection layer (6) is waterproof,
Anti-corrosion epoxy resin clear coat.
8. a kind of preparation method of building decoration color crystal glass as claimed in claim 1, it is characterised in that the preparation method bag
Include following steps：
Step one, makes safety glass base material (1),
Step 2 plates Low emissivity film layer (2) in safety glass base material (1) front made, so that glass baseplate (1) front
Low emissivity film layer (2) is formed, to reduce the radiation of sunlight middle-ultraviolet lamp,
Step 3 carries out coating self-cleaning film layer (3) treatment to the glass baseplate (1) after plating low-radiation film, i.e., in Low emissivity
In film layer (2) spray one layer of self-cleaning film layer (3), reach can self-cleaning net effect,
Step 4 prints one layer of colored glaze patterned layer (4) to the method for the glass baseplate (1) back side silk-screen printing,
Step 5 to covering color crystal coating (5) with silk-screen printing in the colored glaze patterned layer (4) at the glass baseplate (1) back side,
Step 6 with the method for silk-screen printing on described color crystal coating (5) to covering one layer of protection layer (6).