CN106739598A - A kind of package printing process - Google Patents
A kind of package printing process Download PDFInfo
- Publication number
- CN106739598A CN106739598A CN201611034623.6A CN201611034623A CN106739598A CN 106739598 A CN106739598 A CN 106739598A CN 201611034623 A CN201611034623 A CN 201611034623A CN 106739598 A CN106739598 A CN 106739598A
- Authority
- CN
- China
- Prior art keywords
- printing
- completion
- polyethylene heat
- ultraviolet curing
- shrinkage film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of package printing process, comprise the following steps:(1)Printing element is cut according to the packing instructions of packed article;(2)By polyethylene heat-shrinkage film according to step(1)The size for cutting the printing element of completion is cut;(3)Ultraviolet curing printing-ink is printed onto the front of polyethylene heat-shrinkage film;(4)By ultraviolet curing lamp to step(3)The polyethylene heat-shrinkage film of completion carries out ultraviolet curing;(5)In step(4)It is attached on printing element surface after solidifying the polyethylene heat-shrinkage film backside coating adhesive glue for completing;(6)Take a step(2)The polyethylene heat-shrinkage film of completion is cut, step is attached at after its backside coating adhesive glue(5)In the printing surface of semi-finished of completion.Package printing process of the invention, printing layer is smooth, feel is fine and smooth, and is reclaimed beneficial to paper.
Description
Technical field
The present invention relates to a kind of package printing process, belong to print field.
Background technology
At present when being printed using UV ray solidifying ink, the method for generally using is to first pass through printing equipment
Ultraviolet curing printing-ink is printed onto on stock, the ultraviolet for then being sent using ultraviolet curing lamp is consolidated to ultraviolet
Change printing-ink printing layer to be irradiated, ultraviolet curing printing-ink printing layer solidified, dried, so as to complete printing.Profit
The printed matter obtained with above-mentioned technique, its ultraviolet curing printing-ink printing layer is relatively rough, and visual effect and feel be not good enough.
Notification number discloses a kind of typography for the Chinese invention patent of CN101125500, solves above mentioned problem.But it is above-mentioned special
After sharp its ultraviolet curing printing-ink of disclosed typography is imprinted on paper, the bad removing treatment of ink marks influences the useless of later stage
Paper reclaims reconstruction, and environment protecting is poor.
The content of the invention
In view of the shortcomings of the prior art, the technical problems to be solved by the invention are to provide a kind of packages printing work
Skill, printing layer is smooth, feel is fine and smooth, and is reclaimed beneficial to paper.
In order to solve the above technical problems, the present invention is adopted the technical scheme that, a kind of package printing process, including following step
Suddenly:
(1)Printing element is cut according to the packing instructions of packed article;
(2)By polyethylene heat-shrinkage film according to step(1)The size for cutting the printing element of completion is cut;
(3)Ultraviolet curing printing-ink is printed onto the front of polyethylene heat-shrinkage film;
(4)By ultraviolet curing lamp to step(3)The polyethylene heat-shrinkage film of completion carries out ultraviolet curing;
(5)In step(4)It is attached on printing element surface after solidifying the polyethylene heat-shrinkage film backside coating adhesive glue for completing;
(6)Take a step(2)The polyethylene heat-shrinkage film of completion is cut, step is attached at after its backside coating adhesive glue
(5)In the printing surface of semi-finished of completion;
(7)In step(6)The printing surface of semi-finished of completion is pressurizeed by point-like grating mold so that printing semi-finished product table
Face forms groove pattern;
(8)In step(7)Ultraviolet curing off-set oil is coated by way of silk-screen printing in the groove of the groove pattern of completion
Ink;
(9)By ultraviolet curing lamp to step(8)The printing semi-finished product of completion carry out ultraviolet curing.
Optimization, above-mentioned package printing process is described in step(1)In printing element be tear-proof synthetic paper, paperboard
In one kind.
Optimization, above-mentioned package printing process, the step(4)After the completion of polyethylene heat-shrinkage film is attached at printing base
Before on material surface, to step(4)After the completion of polyethylene heat-shrinkage film carry out drying and processing, drying temperature is that 80-180 is Celsius
Degree.
Optimization, above-mentioned package printing process, the step(2)The size that cuts of middle polyethylene heat-shrinkage film is step
(1)Cut 1.5 times of the size of the printing material of completion.
Optimization, above-mentioned package printing process, the gravure pattern of the point-like grating mold is according to step(3)The figure of printing
Case makes.
Optimization, above-mentioned package printing process, the step(7)Pressurized treatments of the point-like grating mold to printing semi-finished product
It is hot pressing mode, hot pressing temperature is 80-180 degrees Celsius.
Optimization, above-mentioned package printing process, the point-like grating mold can be plane or curved surface.
Optimization, above-mentioned package printing process is described to step(9)Completing the printing semi-finished product after solidification is carried out at drying
Reason, drying temperature is 80-180 degrees Celsius.
Optimization, above-mentioned package printing process, the step(4)Middle-ultraviolet lamp cure lamp irradiation time is 3-5 seconds, ultraviolet
The general power of line cure lamp is 10 kilowatts.
Optimization, above-mentioned package printing process, the step(9)Middle-ultraviolet lamp cure lamp irradiation time is 6-12 seconds, purple
The general power of outside line cure lamp is 10 kilowatts.
Package printing process of the invention, polyethylene heat-shrinkage film surface is printed onto by ultraviolet curing printing-ink, then
Polyethylene heat-shrinkage film is fitted on the printing element of papery, so when needing to be reclaimed, paper substrates will be attached at
The polyethylene heat-shrinkage film on surface remove after by paper substrates are reclaimed.Although some paper during removing
Matter base material is removed with polyethylene heat-shrinkage film, but is directly carried out on the surface of paper substrates relative in the prior art ultraviolet
Line cured printing ink is printed, and the technical scheme of the application can be reclaimed to remaining paper substrates, improve papery base
The rate of recovery of material.
Surface after the printing of ultraviolet curing printing-ink carries out the pressurization of point-like grating mold and is easily damaged printing surface,
Therefore the design of the application carries out point-like light again after covering second layer polyethylene heat-shrinkage film on the surface after the completion of one-step print
Grid mould pressurizing, prevents ultraviolet curing printing-ink from printing surface and sustains damage.
Two layers of polyethylene heat shrink films, while drying can cause shrinkage factor different, influence paper substrates because being heated difference
Planarization.The design of the application carries out drying heating respectively to two layers of polyethylene heat shrink films, prevents from causing because of first drying
Shrinkage factor it is different so that paper substrates produce fold.
Specific embodiment
Embodiment 1
The present invention is a kind of package printing process, is comprised the following steps:
(1)Printing element is cut according to the packing instructions of packed article;
(2)By polyethylene heat-shrinkage film according to step(1)The size for cutting the printing element of completion is cut;
(3)Ultraviolet curing printing-ink is printed onto the front of polyethylene heat-shrinkage film;
(4)By ultraviolet curing lamp to step(3)The polyethylene heat-shrinkage film of completion carries out ultraviolet curing;
(5)In step(4)It is attached on printing element surface after solidifying the polyethylene heat-shrinkage film backside coating adhesive glue for completing;
(6)Take a step(2)The polyethylene heat-shrinkage film of completion is cut, step is attached at after its backside coating adhesive glue
(5)In the printing surface of semi-finished of completion;
(7)In step(6)The printing surface of semi-finished of completion is pressurizeed by point-like grating mold so that printing semi-finished product table
Face forms groove pattern;
(8)In step(7)Ultraviolet curing off-set oil is coated by way of silk-screen printing in the groove of the groove pattern of completion
Ink;
(9)By ultraviolet curing lamp to step(8)The printing semi-finished product of completion carry out ultraviolet curing.
It is described in step(1)In printing element be tear-proof synthetic paper, paperboard in one kind.
The step(4)After the completion of polyethylene heat-shrinkage film is attached on printing element surface before, to step(4)It is complete
Polyethylene heat-shrinkage film after carries out drying and processing, and drying temperature is 80 degrees Celsius.
The step(2)The size that cuts of middle polyethylene heat-shrinkage film is step(1)Cut the chi of the printing material of completion
Very little 1.5 times.
The gravure pattern of the point-like grating mold is according to step(3)The pattern of printing makes.
The step(7)Point-like grating mold is hot pressing mode to printing the pressurized treatments of semi-finished product, and hot pressing temperature is 80
Degree Celsius.
The point-like grating mold can be plane or curved surface.
It is described to step(9)Completing the printing semi-finished product after solidification carries out drying and processing, and drying temperature is 80 degrees Celsius.
The step(4)Middle-ultraviolet lamp cure lamp irradiation time is 3 seconds, and the general power of ultraviolet curing lamp is 10 kilowatts.
The step(9)Middle-ultraviolet lamp cure lamp irradiation time is 6 seconds, and the general power of ultraviolet curing lamp is 10 kilowatts.
Embodiment 2
The present embodiment is with the difference of embodiment 1:The step(4)After the completion of polyethylene heat-shrinkage film is attached at printing base
Before on material surface, to step(4)After the completion of polyethylene heat-shrinkage film carry out drying and processing, drying temperature is 180 degrees Celsius.
The step(7)Point-like grating mold is hot pressing mode to the pressurized treatments for printing semi-finished product, and hot pressing temperature is 180 degrees Celsius.
It is described to step(9)Completing the printing semi-finished product after solidification carries out drying and processing, and drying temperature is 180 degrees Celsius.The step
(4)Middle-ultraviolet lamp cure lamp irradiation time is 5 seconds, the step(9)Middle-ultraviolet lamp cure lamp irradiation time is 12 seconds.
Embodiment 3
The present embodiment is with the difference of embodiment 1,2:The step(4)After the completion of polyethylene heat-shrinkage film is attached at printing
Before on substrate surface, to step(4)After the completion of polyethylene heat-shrinkage film carry out drying and processing, drying temperature is 120 Celsius
Degree.The step(7)Point-like grating mold is hot pressing mode to the pressurized treatments for printing semi-finished product, and hot pressing temperature is 120 Celsius
Degree.It is described to step(9)Completing the printing semi-finished product after solidification carries out drying and processing, and drying temperature is 150 degrees Celsius.The step
Suddenly(4)Middle-ultraviolet lamp cure lamp irradiation time is 4 seconds, the step(9)Middle-ultraviolet lamp cure lamp irradiation time is 8 seconds.
Certainly, described above is not limitation of the present invention, and the present invention is also not limited to the example above, the art
Those of ordinary skill, in essential scope of the invention, the change made, remodeling, addition or replace, should all belong to the present invention
Protection domain.
Claims (10)
1. a kind of package printing process, it is characterised in that:Comprise the following steps:
(1)Printing element is cut according to the packing instructions of packed article;
(2)By polyethylene heat-shrinkage film according to step(1)The size for cutting the printing element of completion is cut;
(3)Ultraviolet curing printing-ink is printed onto the front of polyethylene heat-shrinkage film;
(4)By ultraviolet curing lamp to step(3)The polyethylene heat-shrinkage film of completion carries out ultraviolet curing;
(5)In step(4)It is attached on printing element surface after solidifying the polyethylene heat-shrinkage film backside coating adhesive glue for completing;
(6)Take a step(2)The polyethylene heat-shrinkage film of completion is cut, step is attached at after its backside coating adhesive glue
(5)In the printing surface of semi-finished of completion;
(7)In step(6)The printing surface of semi-finished of completion is pressurizeed by point-like grating mold so that printing semi-finished product table
Face forms groove pattern;
(8)In step(7)Ultraviolet curing off-set oil is coated by way of silk-screen printing in the groove of the groove pattern of completion
Ink;
(9)By ultraviolet curing lamp to step(8)The printing semi-finished product of completion carry out ultraviolet curing.
2. package printing process according to claim 1, it is characterised in that:It is described in step(1)In printing element be
One kind in tear-proof synthetic paper, paperboard.
3. package printing process according to claim 1, it is characterised in that:The step(4)After the completion of by polyethylene heat
Before shrink film is attached on printing element surface, to step(4)After the completion of polyethylene heat-shrinkage film carry out drying and processing, dry
Dry temperature is 80-180 degrees Celsius.
4. package printing process according to claim 1, it is characterised in that:The step(2)Middle polyethylene heat-shrinkage film
Cut size for step(1)Cut 1.5 times of the size of the printing material of completion.
5. package printing process according to claim 1, it is characterised in that:The gravure pattern root of the point-like grating mold
According to step(3)The pattern of printing makes.
6. package printing process according to claim 1, it is characterised in that:The step(7)Point-like grating mold is to print
The pressurized treatments of brush semi-finished product are hot pressing mode, and hot pressing temperature is 80-180 degrees Celsius.
7. package printing process according to claim 1, it is characterised in that:The point-like grating mold can be plane or
Curved surface.
8. package printing process according to claim 1, it is characterised in that:It is described to step(9)Complete the print after solidification
Brush semi-finished product carry out drying and processing, and drying temperature is 80-180 degrees Celsius.
9. package printing process according to claim 1, it is characterised in that:The step(4)Middle-ultraviolet lamp cure lamp is shone
The time is penetrated for 3-5 second, the general power of ultraviolet curing lamp is 10 kilowatts.
10. package printing process according to claim 1, it is characterised in that:The step(9)Middle-ultraviolet lamp cure lamp is shone
The time is penetrated for 6-12 second, the general power of ultraviolet curing lamp is 10 kilowatts.